The shrinkage of the cement paste with low water-cement ratio at different relative humidity was observed and analyzed with ESEM and deformation map technique.The crack morphology was observed with different magnifica...The shrinkage of the cement paste with low water-cement ratio at different relative humidity was observed and analyzed with ESEM and deformation map technique.The crack morphology was observed with different magnification with SEM and FESEM,and the formation of the crack was observed with AFM between two C-S-H nano particles.The observation by multi technique at multi scale indicated that the shrinkage was increase with the decrease of the humidity due to the increase of the pressure of the capillary pressure,the morphology of the crack in smaller scale was similar to that in the bigger scale,the smaller crack distributed in the latticework of the bigger ones,and the crack propagated along the gap between two nano particles of C-S-H with weaker bonding.展开更多
In this study,we attempted to investigate the spatial gradient distributions of thermal shock-induced damage to granite with respect to associated deterioration mechanisms.First,thermal shock experiments were conducte...In this study,we attempted to investigate the spatial gradient distributions of thermal shock-induced damage to granite with respect to associated deterioration mechanisms.First,thermal shock experiments were conducted on granite specimens by slowly preheating the specimens to high temperatures,followed by rapid cooling in tap water.Then,the spatial gradient distributions of thermal shock-induced damage were investigated by computed tomography(CT)and image analysis techniques.Finally,the influence of the preheating temperature on the spatial gradients of the damage was discussed.The results show that the thermal shock induced by rapid cooling can cause more damage to granite than that induced by slow cooling.The thermal shock induced by rapid cooling can cause spatial gradient distributions of the damage to granite.The damage near the specimen surface was at a maximum,while the damage inside the specimen was at a minimum.In addition,the preheating temperature can significantly influence the spatial gradient distributions of the thermal shock-induced damage.The spatial gradient distribution of damage increased as the preheating temperature increased and then decreased significantly over 600C.When the preheating temperature was sufficiently high(e.g.800C),the gradient can be ignored.展开更多
The Van Hoof effect is a phase shift existing between the radial velocity curves of hydrogen and metallic lines within the atmosphere of pulsating stars.In this article,we present a study of this phenomenon through th...The Van Hoof effect is a phase shift existing between the radial velocity curves of hydrogen and metallic lines within the atmosphere of pulsating stars.In this article,we present a study of this phenomenon through the spectra of the brightest pulsating star RR Lyr of RR Lyrae stars recorded for 22 yr.We based ourselves,on the one hand,on 1268 spectra(41 nights of observation)recorded between the years 1994 and 1997 at the Observatory of Haute Provence(OHP,France)previously observed by Chadid and Gillet,and on the other hand on 1569 spectra(46nights of observation)recorded at our Oukaimeden Observatory(Morocco)between 2015 and 2016.Through this study,we have detected information on atmospheric dynamics that had not previously been detected.Indeed,the Van Hoof effect which results in a clear correlation between the radial velocities of hydrogen and those of the metallic lines has been observed and analyzed at different Blazhko phases.A correlation between the radial velocities of different metallic lines located in the lower atmosphere has been observed as well.For the first time,we were able to show that the amplitude of the radial velocity curves deduced from the lines of hydrogen and that of FeⅡ(λ4923.921?)increases toward the minimum of the Blazhko cycle and decreases toward the maximum of the same Blazhko cycle.Furthermore,we found that the Van Hoof effect is also modulated by the Blazhko effect.Thus,toward the minimum of the Blazhko cycle the Van Hoof effect is more visible and at the maximum of the Blazhko cycle,this effect is minimal.We also observed the temporal evolution of the amplitudes of the radial velocities of the lower and upper atmosphere.When observed over a long time,we can interpret it as a function of the Blazhko phases.展开更多
基金Funded by the National Basic Research Program of China (No. 2009CB23201)the Open Foundation of National Key Laboratory of Green Building Materials(No.CBM-08-KFl 03)+1 种基金the Self-determined and Innovative Research Funds of WUT(2010-IV-066)the Foundamental Research Funds for the Central Universities
文摘The shrinkage of the cement paste with low water-cement ratio at different relative humidity was observed and analyzed with ESEM and deformation map technique.The crack morphology was observed with different magnification with SEM and FESEM,and the formation of the crack was observed with AFM between two C-S-H nano particles.The observation by multi technique at multi scale indicated that the shrinkage was increase with the decrease of the humidity due to the increase of the pressure of the capillary pressure,the morphology of the crack in smaller scale was similar to that in the bigger scale,the smaller crack distributed in the latticework of the bigger ones,and the crack propagated along the gap between two nano particles of C-S-H with weaker bonding.
基金funded by the National Natural Science Foundation of China,China(Grant Nos.51778021,51627812 and 51678403)。
文摘In this study,we attempted to investigate the spatial gradient distributions of thermal shock-induced damage to granite with respect to associated deterioration mechanisms.First,thermal shock experiments were conducted on granite specimens by slowly preheating the specimens to high temperatures,followed by rapid cooling in tap water.Then,the spatial gradient distributions of thermal shock-induced damage were investigated by computed tomography(CT)and image analysis techniques.Finally,the influence of the preheating temperature on the spatial gradients of the damage was discussed.The results show that the thermal shock induced by rapid cooling can cause more damage to granite than that induced by slow cooling.The thermal shock induced by rapid cooling can cause spatial gradient distributions of the damage to granite.The damage near the specimen surface was at a maximum,while the damage inside the specimen was at a minimum.In addition,the preheating temperature can significantly influence the spatial gradient distributions of the thermal shock-induced damage.The spatial gradient distribution of damage increased as the preheating temperature increased and then decreased significantly over 600C.When the preheating temperature was sufficiently high(e.g.800C),the gradient can be ignored.
文摘The Van Hoof effect is a phase shift existing between the radial velocity curves of hydrogen and metallic lines within the atmosphere of pulsating stars.In this article,we present a study of this phenomenon through the spectra of the brightest pulsating star RR Lyr of RR Lyrae stars recorded for 22 yr.We based ourselves,on the one hand,on 1268 spectra(41 nights of observation)recorded between the years 1994 and 1997 at the Observatory of Haute Provence(OHP,France)previously observed by Chadid and Gillet,and on the other hand on 1569 spectra(46nights of observation)recorded at our Oukaimeden Observatory(Morocco)between 2015 and 2016.Through this study,we have detected information on atmospheric dynamics that had not previously been detected.Indeed,the Van Hoof effect which results in a clear correlation between the radial velocities of hydrogen and those of the metallic lines has been observed and analyzed at different Blazhko phases.A correlation between the radial velocities of different metallic lines located in the lower atmosphere has been observed as well.For the first time,we were able to show that the amplitude of the radial velocity curves deduced from the lines of hydrogen and that of FeⅡ(λ4923.921?)increases toward the minimum of the Blazhko cycle and decreases toward the maximum of the same Blazhko cycle.Furthermore,we found that the Van Hoof effect is also modulated by the Blazhko effect.Thus,toward the minimum of the Blazhko cycle the Van Hoof effect is more visible and at the maximum of the Blazhko cycle,this effect is minimal.We also observed the temporal evolution of the amplitudes of the radial velocities of the lower and upper atmosphere.When observed over a long time,we can interpret it as a function of the Blazhko phases.