In addition to the specific surface area,surface topography and characteristics such as the pore size,pore size distribution,and micro/mesopores ratio are factors that determine the performance of porous carbons(PCs)i...In addition to the specific surface area,surface topography and characteristics such as the pore size,pore size distribution,and micro/mesopores ratio are factors that determine the performance of porous carbons(PCs)in the fields of energy,catalysis,and adsorption.Based on the mechanism of weight loss of polyaspartic acid at high temperatures,this study provided a new method for adjusting the surface morphology of PCs by changing the cross-linking ratio of the precursor,where cross-linked polyaspartic acid was used as precursor without additional activating agents.N2 adsorption analysis indicated that the specific surface area of the obtained PCs was as high as 1458 m2·g-1,of which I 200 m2·g-1was the contribution of the microporous area and the highest pore volume was 1.13 cm3·g-1,of which the micropore volume was 0.636cm3·g-1.The thermogravimetric analysis results of the precursor,and also the scanning electron microscopy and Brunauer-Emmet-Teller analysis results of the carboniza-tion product confirmed that the prepared PCs presented multilevel pore structure,and the diameters of most pores were 0.78 and 3.97 nm;moreover,the pore size distribution was relatively uniform.This conferred the PCs the ultrahigh hydrogen adsorption capacity of up to 4.52 wt-%at 77 K and 1.13 bar,in addition to their great energy storage and catalytic potental.展开更多
基金This work was supported by the Beijing Natural Science Foundation(No.2162031)the National Natural Science Foundation of China(Grant Nos.21390202,21436002 and 21865026).
文摘In addition to the specific surface area,surface topography and characteristics such as the pore size,pore size distribution,and micro/mesopores ratio are factors that determine the performance of porous carbons(PCs)in the fields of energy,catalysis,and adsorption.Based on the mechanism of weight loss of polyaspartic acid at high temperatures,this study provided a new method for adjusting the surface morphology of PCs by changing the cross-linking ratio of the precursor,where cross-linked polyaspartic acid was used as precursor without additional activating agents.N2 adsorption analysis indicated that the specific surface area of the obtained PCs was as high as 1458 m2·g-1,of which I 200 m2·g-1was the contribution of the microporous area and the highest pore volume was 1.13 cm3·g-1,of which the micropore volume was 0.636cm3·g-1.The thermogravimetric analysis results of the precursor,and also the scanning electron microscopy and Brunauer-Emmet-Teller analysis results of the carboniza-tion product confirmed that the prepared PCs presented multilevel pore structure,and the diameters of most pores were 0.78 and 3.97 nm;moreover,the pore size distribution was relatively uniform.This conferred the PCs the ultrahigh hydrogen adsorption capacity of up to 4.52 wt-%at 77 K and 1.13 bar,in addition to their great energy storage and catalytic potental.