Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B)...Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that Al2O3 particle growth was inhibited by TiC particles in C. but TiB2 particles could not hinder Al2O3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 ...Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 composite coatings were measured using microhardness tester and block-on-ring tribometer,respectively,and the comparison with those of Ni-P coatings or Ni-P-micro Al2O3 coating was given.The influences of aging temperature on their hardness and wear resistance were analyzed.The results showed that the nano Al2O3 particles were distributed uniformly in the Ni-P-Al2O3 coatings.Among three kinds of Ni-P based coatings,the hardness and wear resistance of Ni-P-nano Al2O3 coatings were largest,and the maximum values could be obtained at 400 ℃.This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni-P coatings.展开更多
文摘Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that Al2O3 particle growth was inhibited by TiC particles in C. but TiB2 particles could not hinder Al2O3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。
基金Item Sponsored by Jiangsu Natural Science Foundation of China(04KJB430013)Jiangsu Key Laboratory of Friction Wear Opening Foundation
文摘Ni-P-nano Al2O3 composite coatings were deposited by electroless plating,and their microstructures were observed by SEM（scanning electron microscope）.The microhardness and the wear resistance of the Ni-P-nano Al2O3 composite coatings were measured using microhardness tester and block-on-ring tribometer,respectively,and the comparison with those of Ni-P coatings or Ni-P-micro Al2O3 coating was given.The influences of aging temperature on their hardness and wear resistance were analyzed.The results showed that the nano Al2O3 particles were distributed uniformly in the Ni-P-Al2O3 coatings.Among three kinds of Ni-P based coatings,the hardness and wear resistance of Ni-P-nano Al2O3 coatings were largest,and the maximum values could be obtained at 400 ℃.This indicated that the precipitation of nano Al2O3 particles would improve the hardness and wear resistance of the Ni-P coatings.