Utilization of TiO_(2)/gC_(3)N_(4)nanoadditive to boost oxidative properties of vegetable oil for tribological application

The emergence of vegetable oil as a promising alternative lubricant in the tribological application space has fueled research for making these oils as useful as mineral oils.Tribological modification of vegetable oil by the addition of TiO_(2)/gC_(3)N_(4)nanocomposite(as a nanoadditive)was studied here.The dispersion of the nanoadditive in the vegetable oil showed good oil dispersion stability without the addition of any surfactant.The tribological studies were conducted in a four-ball tester using ASTM standard D5183.In addition,the effect of temperature on tribological performance was also studied to understand the oxidation behavior of vegetable oil.The results showed a significant improvement in friction and wear properties of the optimized nano-oil.The mechanism behind the improvement in friction and wear properties is annotated in this paper.

Microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy by micro-arc oxidation

The microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy obtained in silicate-,borate- and aluminate-based electrolyte without and with nanoadditive Al2O3 and TiO2 by micro-arc oxidation（MAO） were studied by scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy（EDS）,X-ray diffraction（XRD）,microhardness and friction-abrasion tests,respectively.SEM results show that coatings with nanoadditive have less porosities than those without nanoadditive.XRD results reveal that nanoadditive-containing coatings contain more oxides compared with nanoadditive-free coatings in all cases,which are consistent with the EDS analysis.Mechanical properties tests show that nanoadditive Al2O3-containing coatings have higher microhardness values compared with the other coatings obtained in silicate-,borate- and aluminate-based electrolyte.On the other hand,nanoadditive has a positive effect on improving the wearing-resistance of MAO coatings in all cases.Furthermore,the borate-MAO coatings present an inferior anti-wearing property compared with the silicate- and aluminate-MAO coatings for both the nanoadditive-free and nanoadditive-containing coatings.

Study on the mechanism of rapid formation ofu ultra-thick tribofilm by CeO_(2)nano additive and ZDDP

CeO_(2)nanoparticles are potential anti-wear additives because of their outstanding anti-wear and load-bearing capacity.However,the shear-sintering tribo-film formation mechanism of oxide nanoparticles limits the tribo-film formation rate and thickness greatly.In this study,by compounding with zinc dioctyl dithiophosphate(ZDDP),ultra-fine CeO_(2)nanoparticles modified with oleylamine(OM)can quickly form 2μm ultra-thick tribo-film,which is 10-15 times thicker than that of ZDDP and CeO_(2),respectively.The ultra-thick tribo-film presents a nanocomposite structure with amorphous phosphate as binder and nano-CeO_(2)as filling phase,which leads to the highest loading capacity of composite additives.The results of adsorption experiments tested by dissipative quartz crystal microbalance(QCM-D)showed that the Ps value of additive has nothing to do with its equilibrium adsorption mass,but is directly proportional to its adsorption rate in 10 s.The compound additive of CeO_(2)and ZDDP presented the co-deposition mode of ZDDP monolayer rigid adsorption and CeO_(2)viscoelastic adsorption on the metal surface,which showed the highest adsorption rate in 10 s.It is found that the tribo-film must have high film forming rate and wear resistance at the same time in order to achieve super thickness.Cerium phosphate was formed from ZDDP and CeO,through tribochemistry reaction,which promotes the formation of an ultra-thick tribo-film with nanocomposite structure,which not only maintains the low friction characteristics of CeO,but also realizes high Pg and high load-carrying capacity.

Dispersion–tribological property relationship in mineral oils containing 2D layered α-zirconium phosphate nanoplatelets

Inorganic nanomaterials exhibit superior friction-reduction and anti-wear properties in oils. In this study, 2D layered α-zirconium phosphate (α-ZrP) nanosheets intercalated with different amines have been synthesized to study their dispersion stabilities in lubricating oil and tribological applications. The intercalated amines should be sufficiently long and lipophilic to provide stabilization to α-ZrP nanosheets in mineral oil. The results of tribological tests illustrate that with the addition of well-dispersed nanosheets, the coefficient of friction (COF) and pin volume loss reduce by ~47% and 75%, respectively. The excellent dispersion stability enables the nanosheets to flow into the contact area at the beginning, and thereby protect the rubbing surface. A reduction in the van der Waals forces between the adjacent layers induced by the intercalated amines transforms the friction between adjacent layers from pin disk to sliding, leading to a decrease in the COF under hydrodynamic lubrication. The study provides a new method to enhance the tribological properties via tuning the dispersion stabilities of nanomaterials in oils.