Sol-gel synthesis of nanometer silicon/silicon suboxide/carbon anode material

A stacked Si/SiO_(x)/C composite anode material with carbon-coated structure was prepared by sol-gel method combined with carbothermal reduction using organic silicon.The results of X-ray diffractometry, scanning electron microscopy, and elemental analysis show that the Si/SiO_(x)/C material is a secondary particle with a porous micronanostructure, and the presence of nanometer silicon does not affect the carbothermal reduction and carbon coating.Electrochemical test results indicate that the specific capacity and first coulombic efficiency of SiO_(x)/C composite with nanometer silicon can be increased to 1 946.05 mAh/g and 76.49%,respectively.The reversible specific capacity of Si/SiO_(x)/C material blended with graphite is 749.69 mAh/g after 100 cycles at a current density of 0.1 C,and the capacity retention rate is up to 89.03%.Therefore, the composite has excellent electrochemical cycle stability.

热电材料的研究及进展

In 1823,Thomas Seebeck first discovered the thermoelectric effect.A temperature difference across any electric conductor junction will generate a corresponding voltage difference.Probably the most familiar use of this so called Seebeck effect is thermocouple.When an electric current passing through junction which is composed of two dissimilar conductors results in the absorption or release of the heat,this is the Peltier effect.This effect makes thermoelectric refrigerator or heating devices possible.Moreover a power generator can be also invented from the application of thermoelectric materials.Thermoelectric materials are those which possess high thermoelectric figure of merit.The major problem for thermoelectric materials is poor efficiency.They are now used only in the fields in which cost is not a big problem such as space and some other instruments.Thermoelectric materials are not widely used nowadays.

Preparation, Characterization and Photocatalytic Activity of Fe, La Co-doped Nanometer Titanium Dioxide Photocatalysts

A series of photocatalysts of un-doped, single-doped and co-doped nanometer titanium diox- ide （TiO2） have been successfully prepared by template method using Fe（NO3）3.9H2O, La（NO3）3.6H2O, and tetrabutyl titanate as precursors and glucan as template. Scanning electron microscopy, X-ray diffraction, and N2 adsorption-desorption measurement were employed to characterize the morphology, crystal structure and surface structure of the samples. The photo-absorbance of the obtained catalysts was measured by UV-Vis absorption spectroscopy, and the photocatalytic activities of the prepared samples under UV and visible light were estimated by measuring the degradation rate of methyl orange in an aqueous solution. The characterizations indicated that the prepared photocatalysts consisted of anatase phase and possessed high surface area of ca. 163-176 m2/g. It was shown that the Fe and La co-doped nano-TiO2 could be activated by visible light and could thus be used as an effective catalyst in photo-oxidation reactions. The synergistic effect of Fe and La co-doping played an important role in improving the photocatalytic activity. In addition, the possibility of cyclic usage of co-doped nano-TiO2 was also confirmed, the photocatalytic activity of codoped nano-TiO2 remained above 89.6% of the fresh sample after being used four times.

Synthesis of α-Fe_2O_3@SnO_2 core-shell nanoparticles via low-temperature molten salt reaction route

A cost-effective carbon-free nanocoating strategy was developed for the synthesis of ultra-fine SnO2 coatingα-Fe2O3 core-shell nanoparticles. This strategy only involves a two-step molten salt reaction at low temperature of 300 °C. The as-preparedα-Fe2O3@SnO2 core-shell nanocomposites show enhanced electrochemical performances than the bareα-Fe2O3 nanoparticles. This involved metal oxide nanocoating method is easy to be carried out, and the heat treatment temperature is much lower than that of other traditional solid-state annealing method and many carbon or metal oxide nanocoating methods. The molten salt method may also be used to produce other metal oxides coating nanostructures as the electrode materials for lithium-ion batteries.

Preparation and Characterization of Nanometer TiO_2 by Hydrolysis Precipitation Method

Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.

High-level Stark Effect and Spectrum of Spherical Nanometer System

In the electric field and layer-to-layer interaction energy, the law of split-level of high-level Stark effect of spherical nanometer system is explored as well as the frequency of spectrum, intensity and size effect of coefficient of spontaneous radiation. Taking three layers CdS/HgS spherical nanometer system as an example, the influence of the electric field and layer-to- layer interaction energy is explored on Stark effect and spectrum. The results show that in the Stark effect system, the energy level is split based on 1, 3, ..., （2n-1）, when it is in the electric field only, similar to the hydrogen atoms; and in the electric field and layer-to-layer interaction, it is split based on 1, 4, ~ -., n2; with the quantum transition, the frequency of the spectrum decreases with the increasing size of the system; apart from a few spectral lines, the intensity of most spectral lines will decreased as the size increases; while the coefficient of spontaneous radiation will increase with the increasing size; the electric field will cause the changes of spectrum frequency; its spectrum frequency shift is proportional to the square of the electric field intensity; apart from a few spectral lines, the frequency shift of spectral lines that is caused by the electric field and layer-to-layer interaction will decrease as the size increases; the interaction will make the level of electronic energy level lower slightly （the order of magnitude is between 10-7-10-9 eV）, the slightly increased spectrum intensity and the slightly increased value of coefficient of spontaneous radiation, but it will not influence the frequency of spectrum, intensity, and the trend that coefficient of spontaneous radiation changes with the size; when the size is smaller, the layer-to-layer interaction effect will be significant.

Physical mechanism of seismic attenuation in a two-phase medium

High-frequency seismic attenuation is conventionally attributed to anelastic absorption. In this paper, I present three studies on high-frequency seismic attenuation and propose that the physical mechanism results from the interference of elastic microscopic multiple scattering waves. First, I propose a new theory on wave propagation in a two-phase medium which is based on the concept that the basic unit for wave propagation is a nano- mass point. As a result of the elasticity variations of pore fluid and rock framework, micro multiple scattering waves would emerge at the wavelength of the seismic waves passing through the two-phase medium and their interference and overlap would generate high- frequency seismic attenuation. Second, I present a study of the frequency response of seismic transmitted waves by modeling thin-layers with thicknesses no larger than pore diameters. Results indicate that high-frequency seismic waves attenuate slightly in a near-surface water zone but decay significantly in a near-surface gas zone. Third, I analyze the seismic attenuation characteristics in near-surface water and gas zones using dual-well shots in the Songliao Basin, and demonstrate that the high-frequency seismic waves attenuate slightly in water zones but in gas zones the 160-1600 Hz propagating waves decay significantly. The seismic attenuation characteristics from field observations coincide with the modeling results. Conclusions drawn from these studies theoretically support seismic attenuation recovery.

ISOLATION DESIGN AND SIMULATIONAL EXPERIMENT OF NANOMETER MICRO MOVEMENT TEST-BED

The relation of mass, stiffness and rate of damping is obtained by using the mechanical analysis of the obstructive vibration system of two dimensions for the design of the obstructive vibration system of more freedom and the micro vibration test bed. The result of stimulational experiment indicates that the isolation of vibration of this system is satisfactory. The design method of vibration can be used as the reference to ultra precision machine tool, super micro orientation machanism and so on.

A Novel Interconnect Crosstalk Parallel RLC Analyzable Model Based on the 65nm CMOS Process

Based on the 65nm CMOS process,a novel parallel RLC coupling interconnect analytical model is presented synthetically considering parasitical capacitive and parasitical inductive effects. Applying function approximation and model order-reduction to the model, we derive a closed-form and time-domain waveform for the far-end crosstalk of a victim line under ramp input transition. For various interconnect coupling sizes, the proposed RLC coupling analytical model enables the estimation of the crosstalk voltage within 2.50% error compared with Hspice simulation in a 65nm CMOS process. This model can be used in computer-aided-design of nanometer SOCs.

Synthesis of Nanometer Cobalt Blue Pigment by Microemulsion Method and Control of Diameter of Particle

The nanometer cobalt blue pigments were prepared by microemulsion method. Using dynamic light scattering(DLS) test method, the influences of water content on the size of liquid drop of microemulsion and the liquid drop of microemulsion on the final diameter of nanometer particle were studied in the course of preparation. Accordingly, the method to control the diameter of nanometer particle by changing water content was established. The nanometer cobalt blue particles were confirmed by XRD and TEM. Color parameters of pigments were determined. The quantum size effect of the pigments was discussed.

纳米材料在印刷中的研究现状

研究纳米材料在油墨、纸张及印刷机中的应用,能够提高印刷材料的性能,改善印刷材料的缺陷,为印刷工业的发展带来新的活力。纳米是一种长度计量单位,翻译于英文＂nanometer＂,是微观世界的单位长度。纳米技术是诞生于20世界80年代末的新兴技术,是研究结构尺寸在1nm到100nm之间物质的工程技术。研究纳米材料在印刷中的应用,能够提高印刷性能,改善印刷材料的缺陷,为印刷业发展提供更广阔的空间。

Preparation and Characterization of Nanometer TiO2 by Hydrolysis Precipitation Method

Nanometer TiO 2 powders were obtained from TiOSO 4 and studied by XRD, TEM and BET. The result indicated that pH and heat treatment temperature have great effects on their grain size and crystal phase structure. Annealed at 500 ℃, nanometer TiO 2 with a specific surface area of 101.39 m 2 ·g -1 and a grain size about 10 nm were obtained(pH=5); and with a specific surface area of 95.48 m 2 ·g -1 and a grain size about 30 nm were obtained(pH=10). The research indicated that crystal phase transformation of rutile at 750 ℃made great promotion in grain size growth.

INVESTIGATION ON MAGNETISM OF THE NANOMETER GRANULAR FILMS

The quantum phenomenological model has been proposed to investigate the magnetic property of nanometer magnetic granular film in an applied magnetic field.The magnetoresistance of the granular films with two distinct magnetic phases has been calculated by using Born approximation.The results show that the average scattering cross section of the magnetic cluster decreases with the increasing number n of the atom.The origin of the giant magnetoresistance comes from the spin dependent scattering between conduction electrons and magnetic granules and the field dependence of magnetoresistance and the quadratic relation of magnetoresistance on the rate of magnetic moment are in good agreement with the experiments reported.

Preparation of poly （methyl methacrylate）／nanometer calcium carbonate composite by in-situ emulsion polymerization

Methyl methacrylate (MMA) emulsion polymerization in the presence of nanometer calcium carbonate(nano-CaCO3) surface modified with γ-methacryloxypropyltrimethoxysilane (MPTMS) was carried out to prepare poly (methyl methacrylate) (PMMA)/nano-CaCO3 composite. The reaction between nano-CaCO3 and MPTMS, and the grafting of PMMA onto nano-CaCO3 were confirmed by infrared spectrum. The grafting ratio and grafting efficiency of PMMA on nano-CaCO3 modified with MPTMS were much higher than that on nano-CaCO3 modified with stearic acid. The grafting ratio of PMMA increased as the weight ratio between MMA and nano-CaCO3 increased, while the grafting efficiency of PMMA decreased. Transmission electron micrograph showed that nano-CaCO3 covered with PMMA was formed by in-situ emulsion polymerization.

Rapid communication Preparation of TiO_2 nanometer thin films with high photocatalytic activity by reverse micellar method

Two kinds of TiO_2 nanometer thin films were prepared on stainless steel bythe reverse micellar and sol-gel methods, respectively. The calcined TiO_ 2 thin films werecharacterized by X-ray diffraction (XRD), atomic force microscopy (AFM), BET surface area and X-rayphotoelectron spectroscopy (XPS). Photocatalytic activity was evaluated by photocatalyticdecoloration of methyl orange aqueous solution. The results showed that the TiO_2 thin filmsprepared by reverse micellar method (designated as RM-TiO_2 films) showed higher photocatalyticactivity than those by sol-gel method (designated as SG-TiO_2 films). This is attributed to the factthat the former is composed of smaller monodispersed spherical particles with a size of about 15 nmand possesses higher surface areas.

Study on Properties of Composite Oxides TiO_2/SiO_2

The nanometer particles of TiO_2 and TiO_2/SiO_2 oxides wereprepared by sol-gel supercritical fluid drying method. The propertiesof TiO_2 and TiO_2/SiO_2 were characterized by means of BET(Brunner-Emmett- Teller method), TEM (transmission electronmicroscopy), SEM (scanning electron microscopy), XRD (X-ray diffrac-tion) and FTIR (Fourier transform-infrared) techniques. The effectsof different preparation route, prehydrolysis and non-prehydrolysis,on the properties of TiO_2/SiO_2 oxide were also examined.

Formation regularity of phases in nanometer powders of Al-Fe alloy prepared by gas evaporation

Nanometer powders of Al Fe alloy were prepared by gas evaporation. The formation regularity of the phases in the as prepared powders and the morphology of the particles were examined. The experimental results show that chemical composition of the master alloy is the key factor which controls the chemical composition of the compound phases in nanometer powders at given evaporating temperature, the compound phases with high Fe mole fraction will form with increasing of Fe content in master alloy. Only Al 13 Fe 4, FeAl 2 and Al 2Fe compound phases form in nanometer powders in present experiment, changing of the pressure of Ar can only alter relative amounts of the compound phases in the powders. Nanometer particles with inhomogeneous tissue were obtained, which is very different from that of pure Al and Fe nanometer particles. When mole fraction of Fe in particles increases, the inhomogeneity is enhanced. [

Methylprednisolone microsphere sustained-release membrane inhibits scar formation at the site of peripheral nerve lesion

Corticosteroids are widely used for the treatment of acute central nervous system injury. However, their bioactivity is limited by their short half-life. Sustained release of glucocorticoids can prolong their efficacy and inhibit scar formation at the site of nerve injury. In the present study, we wrapped the anastomotic ends of the rat sciatic nerve with a methylprednisolone sustained-release membrane. Compared with methylprednisone alone or methylprednisone microspheres, the methylprednisolone microsphere sustained-release membrane reduced tissue adhesion and inhibited scar tissue formation at the site of anastomosis. It also increased sciatic nerve function index and the thickness of the myelin sheath. Our findings show that the methylprednisolone microsphere sustained-release membrane effectively inhibits scar formation at the site of anastomosis of the peripheral nerve, thereby promoting nerve regeneration.

Tribological performance of nanometer samarium borate

Nanometer crystal samarium borate with a particle size of 20～40?nm was prepared using replacing solvent drying technique. The wear resistance and load carrying capacity of 500SN base oil could be improved and the friction coefficient could be decreased by the addition of nanometer samarium borate. But the dosage of samarium borate nanoparticles had to be controlled at a relatively low level, a higher concentration of nanoparticles was not of beneficial to the tribological performance of the oil. The optimal dosage of nanometer samarium borate is 1.0%. Tribochemical reactions took place in the tribological process, which resulted in the formation of deposition products including diboron trioxide and disamarium trioxide. Fe 2B and FeB were also found on the wear scar. The improvement of tribological properties of the oil comes from the formation of deposition layer and permeating layer. [

Removal of Cd（II） by Nanometer AIO（OH） Loaded on Fiberglass with Activated Carbon Fiber Felt as Carrier

A new nanometer material, nanometer AlO（OH） loaded on the fiberglass with activated carbon fibers felt（ACF） as the carrier, was prepared by hydrolytic reaction for the removal of Cd（II） from aqueous solution using column adsorption experiment. As was confirmed by XRD determination, the hydrolysis production loaded on fiberglass was similar to the orthorhombic phase AlO（OH）. SEM images showed that AlO（OH） particles were in the form of small aggregated clusters. The Thomas model was applied for estimating the kinetic parameters and the saturated adsorption ability of Cd（II） adsorption on the new adsorbent. The results showed that the maximum adsorption capacity of Cd（II） was 128.50 mg·g^-1 and 117.86 mg·g^-1 for the adsorbent mass of 0.3289 g and the adsorbent mass of 0.2867 g, respectively. The elution experiment result indicated that the adsorbed Cd ions was easily desorbed from the material with 0.1 mol·L^-1 HCl solution. Adsorption-desorption cycles showed the feasibility of repealed uses of the composited material. The adsorption capacities were influenced by pH and the initial Cd（II） concentration. The amount adsorbed was greatest at pH 6.5 and the initial Cd（II） concentration of 0.07 mg·L^-1, respectively. Nanometer AlO（OH） played a major role in the adsorption process, whereas the fiberglass and ACF were assistants in the process of removing Cd（II）. In addition, the adsorption capacities for Cd（II） were obviously reduced from 128.50 mg·L^-1 to 64.28 mg·L^-1 when Pb ions were present because Pb ions took up more adsorption sites.