Nanometer α-Fe2O3 catalysts were prepared by hydrolyzation in high temperature. Three kinds of precipitators, NaOH, (NH4)2CO3 and urea were used to compare the effect in the process of hydrolyzation. Nanometer size...Nanometer α-Fe2O3 catalysts were prepared by hydrolyzation in high temperature. Three kinds of precipitators, NaOH, (NH4)2CO3 and urea were used to compare the effect in the process of hydrolyzation. Nanometer sizer, transmission electron microscopy (TEM) and X-ray diffraction (XRD) were employed to test the profiles and diameters of the product particles. The test results indicate that the production is nanometer α-Fe2O3 with narrow particle size distribution (PSD) and good dispersibility. The catalysts are mixed with ammonia perchlorate (AP) in 1.0 wt.%. And the composite particles of catalysts with AP are prepared using a new solvent-nonsolvent method. Differential thermal analyzer (DTA) is employed to analysis the thermal decomposition of the composite particles and pure AP sample. The results imply that the thermal decomposition curve peaks of the samples in which nanometer α-Fe2O3 catalysts are added appear comparatively more ahead than that of pure AP sample. Among these mixtures added nanometer material, the smaller the particle diameter of catalyst is, the more ahead the thermal decomposition curve peaks of AP appear. The high and low temperature thermal decomposition curve peaks of AP mixed with the catalyst deposed by urea are more ahead of 77.8?℃ and 9.7?℃ than that of pure AP, respectively. The mechanism of the catalyst deposed by urea with smaller diameter and the distinct catalysis of the particles on the thermal decomposition of AP are discussed.展开更多
The spherical Y2O3∶Eu3+ luminescent particles with size of 0.5~3 μm and smooth surface were synthesized by hydrothermal method. The resulted Y2O3∶Eu3+ precursors and the calcined particles were characterized by dif...The spherical Y2O3∶Eu3+ luminescent particles with size of 0.5~3 μm and smooth surface were synthesized by hydrothermal method. The resulted Y2O3∶Eu3+ precursors and the calcined particles were characterized by differential thermal analysis (DTA) and thermogravimetric (TG) analysis, X-ray diffraction (XRD), Fourier-transform IR spectroscopy (FTIR), scanning electron microscopy (SEM) and photoluminescence spectra (PL). FTIR, TG-DTA, XRD measurements show that the precursors are crystal with hydroxyl and carbonate group, and the pure cubic yttria is obtained after annealing above 700 ℃. The SEM images indicate that the Y2O3∶Eu3+ particles are in spherical shape and with smooth surface. PL analysis shows that the particles present characteristic red emission of Eu3+.展开更多
文摘Nanometer α-Fe2O3 catalysts were prepared by hydrolyzation in high temperature. Three kinds of precipitators, NaOH, (NH4)2CO3 and urea were used to compare the effect in the process of hydrolyzation. Nanometer sizer, transmission electron microscopy (TEM) and X-ray diffraction (XRD) were employed to test the profiles and diameters of the product particles. The test results indicate that the production is nanometer α-Fe2O3 with narrow particle size distribution (PSD) and good dispersibility. The catalysts are mixed with ammonia perchlorate (AP) in 1.0 wt.%. And the composite particles of catalysts with AP are prepared using a new solvent-nonsolvent method. Differential thermal analyzer (DTA) is employed to analysis the thermal decomposition of the composite particles and pure AP sample. The results imply that the thermal decomposition curve peaks of the samples in which nanometer α-Fe2O3 catalysts are added appear comparatively more ahead than that of pure AP sample. Among these mixtures added nanometer material, the smaller the particle diameter of catalyst is, the more ahead the thermal decomposition curve peaks of AP appear. The high and low temperature thermal decomposition curve peaks of AP mixed with the catalyst deposed by urea are more ahead of 77.8?℃ and 9.7?℃ than that of pure AP, respectively. The mechanism of the catalyst deposed by urea with smaller diameter and the distinct catalysis of the particles on the thermal decomposition of AP are discussed.
文摘The spherical Y2O3∶Eu3+ luminescent particles with size of 0.5~3 μm and smooth surface were synthesized by hydrothermal method. The resulted Y2O3∶Eu3+ precursors and the calcined particles were characterized by differential thermal analysis (DTA) and thermogravimetric (TG) analysis, X-ray diffraction (XRD), Fourier-transform IR spectroscopy (FTIR), scanning electron microscopy (SEM) and photoluminescence spectra (PL). FTIR, TG-DTA, XRD measurements show that the precursors are crystal with hydroxyl and carbonate group, and the pure cubic yttria is obtained after annealing above 700 ℃. The SEM images indicate that the Y2O3∶Eu3+ particles are in spherical shape and with smooth surface. PL analysis shows that the particles present characteristic red emission of Eu3+.