Near net shaped Ti−45Al−7Nb−0.3W alloy(at.%)parts were manufactured by hot isostatic pressing(HIP).The microstructure and high-temperature mechanical properties of the alloy were investigated by X-ray diffractometry(X...Near net shaped Ti−45Al−7Nb−0.3W alloy(at.%)parts were manufactured by hot isostatic pressing(HIP).The microstructure and high-temperature mechanical properties of the alloy were investigated by X-ray diffractometry(XRD),scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The results show that at a temperature of 700℃,the peak yield stress(YS)and ultimate tensile stress(UTS)of alloy are 534 and 575 MPa,respectively,and the alloy shows satisfactory comprehensive mechanical properties at 850℃.The alloy exhibits superplastic characteristics at 1000℃ with an initial strain rate of 5×10^−5 s^−1.When the tensile temperature is below 750℃,the deformation mechanisms are dislocation movements and mechanical twinning.Increasing the tensile temperature above 800℃,grain boundary sliding and grain rotation occur more frequently due to the accumulation of dislocations at grain boundary.展开更多
Fabrication characteristics are unstable in direct foaming method. Therefore, most of near net-shape metallic foams are produced, and investigated by powder metallurgy. Direct foaming method, however, has many benefi...Fabrication characteristics are unstable in direct foaming method. Therefore, most of near net-shape metallic foams are produced, and investigated by powder metallurgy. Direct foaming method, however, has many benefits （i.e. reduce the unit cost of goods and fabrication process etc.） to fabrication of metallic foams. In this article, the fabrication characteristic of near net-shape metallic foams by direct foaming method was evaluated. Al and Plaster was used for base material and mould material respectively. Ca and TiH2 were added to molten Al as thickening and blowing agent for stable condition of bubbles. Thickening time was about 10 min with a stirring speed of 600 r/min. Foaming time was 30-120 s for evaluation of the optimum foaming condition. Amount of agent was selected by pre-experimental data. Porosity of near net-shape goods was measured by Archimedes method. On the other hand, it seems that increasing poring time and thickening agent make the poor porosity展开更多
In order to overcome the shortcomings of conventional hot pressing, a novel near net-shape technique, called radial hot pressing, for P/M parts with large height-to-diameter (H/D) ratio was introduced. Effects of proc...In order to overcome the shortcomings of conventional hot pressing, a novel near net-shape technique, called radial hot pressing, for P/M parts with large height-to-diameter (H/D) ratio was introduced. Effects of processing parameters on the microstructures and density of P/M TiAl base alloy valves were studied. Results show that the radial hot pressing is an effective technique for manufacturing valves with a H/D ratio of about 10:1, and the perfect joint interface between the Mo sheet and the parts is helpful for subsequent HIPing.展开更多
粉末近净成形(Powder metallurgy near net shaping,PM-NNS)技术能够制备出具有优异综合力学性能的粉末合金复杂部件。介绍了粉末热等静压(Hot isostatic pressing,HIP)近净成形技术原理及优势,综述了近年来国内外粉末近净成形在航天发...粉末近净成形(Powder metallurgy near net shaping,PM-NNS)技术能够制备出具有优异综合力学性能的粉末合金复杂部件。介绍了粉末热等静压(Hot isostatic pressing,HIP)近净成形技术原理及优势,综述了近年来国内外粉末近净成形在航天发动机领域的研究现状,从工艺路线和构件研制两方面展开,简述了构件制备过程的影响因素及缺陷控制,结合中国科学院金属研究所粉末近净成形技术在航天发动机领域的研究及应用情况,总结了粉末近净成形技术当前存在的主要问题及发展方向,以期进一步拓宽该技术的应用范围。展开更多
基金Project(51774335)supported by the National Natural Science Foundation of ChinaProject(2019JJ40374)supported by the Natural Science Foundation of Hunan Province,ChinaProject(CSUZC202004)supported by the Open Sharing Fund for the Large-scale Instruments and Equipments of Central South University,China。
文摘Near net shaped Ti−45Al−7Nb−0.3W alloy(at.%)parts were manufactured by hot isostatic pressing(HIP).The microstructure and high-temperature mechanical properties of the alloy were investigated by X-ray diffractometry(XRD),scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The results show that at a temperature of 700℃,the peak yield stress(YS)and ultimate tensile stress(UTS)of alloy are 534 and 575 MPa,respectively,and the alloy shows satisfactory comprehensive mechanical properties at 850℃.The alloy exhibits superplastic characteristics at 1000℃ with an initial strain rate of 5×10^−5 s^−1.When the tensile temperature is below 750℃,the deformation mechanisms are dislocation movements and mechanical twinning.Increasing the tensile temperature above 800℃,grain boundary sliding and grain rotation occur more frequently due to the accumulation of dislocations at grain boundary.
文摘Fabrication characteristics are unstable in direct foaming method. Therefore, most of near net-shape metallic foams are produced, and investigated by powder metallurgy. Direct foaming method, however, has many benefits （i.e. reduce the unit cost of goods and fabrication process etc.） to fabrication of metallic foams. In this article, the fabrication characteristic of near net-shape metallic foams by direct foaming method was evaluated. Al and Plaster was used for base material and mould material respectively. Ca and TiH2 were added to molten Al as thickening and blowing agent for stable condition of bubbles. Thickening time was about 10 min with a stirring speed of 600 r/min. Foaming time was 30-120 s for evaluation of the optimum foaming condition. Amount of agent was selected by pre-experimental data. Porosity of near net-shape goods was measured by Archimedes method. On the other hand, it seems that increasing poring time and thickening agent make the poor porosity
文摘In order to overcome the shortcomings of conventional hot pressing, a novel near net-shape technique, called radial hot pressing, for P/M parts with large height-to-diameter (H/D) ratio was introduced. Effects of processing parameters on the microstructures and density of P/M TiAl base alloy valves were studied. Results show that the radial hot pressing is an effective technique for manufacturing valves with a H/D ratio of about 10:1, and the perfect joint interface between the Mo sheet and the parts is helpful for subsequent HIPing.
文摘粉末近净成形(Powder metallurgy near net shaping,PM-NNS)技术能够制备出具有优异综合力学性能的粉末合金复杂部件。介绍了粉末热等静压(Hot isostatic pressing,HIP)近净成形技术原理及优势,综述了近年来国内外粉末近净成形在航天发动机领域的研究现状,从工艺路线和构件研制两方面展开,简述了构件制备过程的影响因素及缺陷控制,结合中国科学院金属研究所粉末近净成形技术在航天发动机领域的研究及应用情况,总结了粉末近净成形技术当前存在的主要问题及发展方向,以期进一步拓宽该技术的应用范围。