Zinc neutral leaching residue（ZNLR） from hydrometallurgical zinc smelting processing can be determined as hazardous intermediate containing considerable amounts of Cd and Zn which have great threats to the environme...Zinc neutral leaching residue（ZNLR） from hydrometallurgical zinc smelting processing can be determined as hazardous intermediate containing considerable amounts of Cd and Zn which have great threats to the environment. The ZNLR contained approximately 35.99% Zn, 15.93% Fe and 0.26% Cd, and Cd mainly existed as ferrites in the ZNLR in this research. Reductive acid leaching of ZNLR was investigated. The effects of hydrazine sulfate concentration, initial sulfuric acid concentration, temperature, duration and liquid-to-solid ratio on the extraction of Cd, Zn and Fe were examined. The extraction efficiencies of Cd, Zn and Fe reached 90.81%, 95.83% and 94.19%, respectively when the leaching parameters were fixed as follows： hydrazine sulfate concentration, 33.3 g/L; sulfuric acid concentration, 80 g/L; temperature, 95 °C; duration of leaching, 120 min; liquid-to-solid ratio, 10 m L/g and agitation, 400 r/min. XRD and SEM-EDS analyses of the leaching residue confirmed that lead sulfate（Pb SO4） and hydrazinium zinc sulfate（（N2H5）2Zn（SO4）2） were the main phases remaining in the reductive leaching residue.展开更多
Neutral leach residue of zinc calcine （NLRZC） was mechanically activated by a stirring ball mill. Subsequently, the changes in physicochemical properties and dissolution kinetics in sulphuric acid were studied. The ...Neutral leach residue of zinc calcine （NLRZC） was mechanically activated by a stirring ball mill. Subsequently, the changes in physicochemical properties and dissolution kinetics in sulphuric acid were studied. The crystalline structure, morphology, particle size and specific surface area of the non-activated and mechanically activated NLRZC were characterized by X-ray diffraction, scanning electron microscope, particle size analyzer and volumetric adsorption analyzer, respectively. The characterization results indicate that mechanical activation （MA） induced remarkable changes in the physicochemical properties of NLRZC. The leaching experiments show that MA significantly enhances the leaching reactivity of NLRZC using the zinc extraction as evaluating index. After NLRZC is mechanically activated for 30 min and 60 min, the activation energy decreases from 56.6 kJ/mol of non-activated NLRZC to 36.1 kJ/mol and 29.9 kJ/mol, respectively. The reaction orders of the non-activated, 30 and 60 min activated NLRZC dissolution with respect to H2SO4 concentration were found to be 0.34, 0.30, and 0.29, respectively.展开更多
基金Project(2012FJ1010)supported by the Key Project of Science and Technology of Hunan ProvinceChina+2 种基金Project(51474247)supported by the National Natural Science Foundation of ChinaProject(2012GS430201)supported by the Science and Technology Program for Public WellbeingChina
文摘Zinc neutral leaching residue（ZNLR） from hydrometallurgical zinc smelting processing can be determined as hazardous intermediate containing considerable amounts of Cd and Zn which have great threats to the environment. The ZNLR contained approximately 35.99% Zn, 15.93% Fe and 0.26% Cd, and Cd mainly existed as ferrites in the ZNLR in this research. Reductive acid leaching of ZNLR was investigated. The effects of hydrazine sulfate concentration, initial sulfuric acid concentration, temperature, duration and liquid-to-solid ratio on the extraction of Cd, Zn and Fe were examined. The extraction efficiencies of Cd, Zn and Fe reached 90.81%, 95.83% and 94.19%, respectively when the leaching parameters were fixed as follows： hydrazine sulfate concentration, 33.3 g/L; sulfuric acid concentration, 80 g/L; temperature, 95 °C; duration of leaching, 120 min; liquid-to-solid ratio, 10 m L/g and agitation, 400 r/min. XRD and SEM-EDS analyses of the leaching residue confirmed that lead sulfate（Pb SO4） and hydrazinium zinc sulfate（（N2H5）2Zn（SO4）2） were the main phases remaining in the reductive leaching residue.
基金Project(51064002)supported by the National Natural Science Foundation of ChinaProject(0728238)supported by the Natural Science Foundation of Guangxi Province,China
文摘Neutral leach residue of zinc calcine （NLRZC） was mechanically activated by a stirring ball mill. Subsequently, the changes in physicochemical properties and dissolution kinetics in sulphuric acid were studied. The crystalline structure, morphology, particle size and specific surface area of the non-activated and mechanically activated NLRZC were characterized by X-ray diffraction, scanning electron microscope, particle size analyzer and volumetric adsorption analyzer, respectively. The characterization results indicate that mechanical activation （MA） induced remarkable changes in the physicochemical properties of NLRZC. The leaching experiments show that MA significantly enhances the leaching reactivity of NLRZC using the zinc extraction as evaluating index. After NLRZC is mechanically activated for 30 min and 60 min, the activation energy decreases from 56.6 kJ/mol of non-activated NLRZC to 36.1 kJ/mol and 29.9 kJ/mol, respectively. The reaction orders of the non-activated, 30 and 60 min activated NLRZC dissolution with respect to H2SO4 concentration were found to be 0.34, 0.30, and 0.29, respectively.