Al-6Mg alloy with trace Sc addition was prepared by means of melting-casting.The samples of the welded joints of Al-6Mg alloy with trace Sc addition were made by method of manual argon-arc welding.Neutral salt spray t...Al-6Mg alloy with trace Sc addition was prepared by means of melting-casting.The samples of the welded joints of Al-6Mg alloy with trace Sc addition were made by method of manual argon-arc welding.Neutral salt spray test was carried out by referring to GB/T10125-1997 and GB6384-1986 practice.Exfoliation testing was carried out in accordance with the method of Al-Mg alloy exfoliation corrosion test.The corrosion behaviors of the welded joints of AlMg alloy with high level of Mg and trace Sc addition were studied.The microstructures of the welded joints were observed by using optical microscope and transmission electron microscope.The corrosion resistance mechanism of the alloy was also involved.This work intended to determine if the welded joints of Al-6Mgalloy with trace Sc addition can have excellent corrosion resistance, when their strength are clearly improved.The results show that trace content of Sc refines the grains of alloys effectively, raises remarkably the corrosion resistance of the welded joints of Al-6Mg alloy with trace Sc addition.The corrosion resistance mechanisms are that there is free of continuous grain boundary precipitation or network which could be susceptible to corrosion in the microstructure of welded joints.展开更多
Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticor...Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticorrosive treatment over metal substrate followed by a systematic coating scheme. The trivalent chromium coating was deposited over three aluminium alloys namely AA6063, AA7075 and AA6082. The variation in corrosion resistance property of trivalent chromium over each aluminium alloy has been studied in detail. The Neutral Salt Spray (NSS) test result shows that trivalent chromium coating over AA7075 alloy is affected by pitting corrosion compared to other two alloys. In addition to that, NSS test also proves that thickness of the layer does not have any influence corrosion resistance property of trivalent chromium coating. Furthermore, ions in trivalent chromium coating was identified using Secondary Neutral Mass Spectroscopy (SNMS) and degradation of coating in a corrosive liquid studied using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) instrument to understand mechanism of corrosion. The results indicated that both coating and substrate is involved in corrosion process. The number of elements dissolved in to salt solution reveals the weak ionic bonding of coating towards substrates. In comparison, AA7075 alloy has weaker bonding than AA6082 and AA6063 series. The alloying elements such as zinc and copper are removed from substrate by corrosive solution.展开更多
文摘Al-6Mg alloy with trace Sc addition was prepared by means of melting-casting.The samples of the welded joints of Al-6Mg alloy with trace Sc addition were made by method of manual argon-arc welding.Neutral salt spray test was carried out by referring to GB/T10125-1997 and GB6384-1986 practice.Exfoliation testing was carried out in accordance with the method of Al-Mg alloy exfoliation corrosion test.The corrosion behaviors of the welded joints of AlMg alloy with high level of Mg and trace Sc addition were studied.The microstructures of the welded joints were observed by using optical microscope and transmission electron microscope.The corrosion resistance mechanism of the alloy was also involved.This work intended to determine if the welded joints of Al-6Mgalloy with trace Sc addition can have excellent corrosion resistance, when their strength are clearly improved.The results show that trace content of Sc refines the grains of alloys effectively, raises remarkably the corrosion resistance of the welded joints of Al-6Mg alloy with trace Sc addition.The corrosion resistance mechanisms are that there is free of continuous grain boundary precipitation or network which could be susceptible to corrosion in the microstructure of welded joints.
文摘Considering aviation and space sectors, aluminium alloys are commonly used due to its excellent mechanical and physical properties. Though satellite hard-ware is confined to controlled environment, it requires anticorrosive treatment over metal substrate followed by a systematic coating scheme. The trivalent chromium coating was deposited over three aluminium alloys namely AA6063, AA7075 and AA6082. The variation in corrosion resistance property of trivalent chromium over each aluminium alloy has been studied in detail. The Neutral Salt Spray (NSS) test result shows that trivalent chromium coating over AA7075 alloy is affected by pitting corrosion compared to other two alloys. In addition to that, NSS test also proves that thickness of the layer does not have any influence corrosion resistance property of trivalent chromium coating. Furthermore, ions in trivalent chromium coating was identified using Secondary Neutral Mass Spectroscopy (SNMS) and degradation of coating in a corrosive liquid studied using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) instrument to understand mechanism of corrosion. The results indicated that both coating and substrate is involved in corrosion process. The number of elements dissolved in to salt solution reveals the weak ionic bonding of coating towards substrates. In comparison, AA7075 alloy has weaker bonding than AA6082 and AA6063 series. The alloying elements such as zinc and copper are removed from substrate by corrosive solution.