In this work,the effects of temperature and cooling rate on the precipitation of carbides in nickel-saving metastable austenitic stainless steel were studied.The test results show that the temperature range of carbide...In this work,the effects of temperature and cooling rate on the precipitation of carbides in nickel-saving metastable austenitic stainless steel were studied.The test results show that the temperature range of carbide precipitation in the test steel was 500-950℃,and 750℃was the most sensitive temperature.However,when completely solution treated samples were cooled from high to room temperature at a cooling rate of more than 50 K/s,no carbides precipitated.The carbide precipitates increased the yield strength but decreased the corrosion resistance of the steel,with little impact on toughness.展开更多
文摘In this work,the effects of temperature and cooling rate on the precipitation of carbides in nickel-saving metastable austenitic stainless steel were studied.The test results show that the temperature range of carbide precipitation in the test steel was 500-950℃,and 750℃was the most sensitive temperature.However,when completely solution treated samples were cooled from high to room temperature at a cooling rate of more than 50 K/s,no carbides precipitated.The carbide precipitates increased the yield strength but decreased the corrosion resistance of the steel,with little impact on toughness.