Preparation of Co/S co-doped carbon catalysts for excellent methylene blue degradation

S and Co co-doped carbon catalysts were prepared via pyrolysis of MOF-71 and thiourea mixtures at 800℃at a mass ratio of MOF-71 to thiourea of 1:0.1 to effectively activate peroxymonosulfate(PMS)for methylene blue(MB)degradation.The effects of two different mixing routes were identified on the MB degradation performance.Particularly,the catalyst obtained by the alcohol solvent evaporation(MOF-AEP)mixing route could degrade 95.60%MB(50 mg/L)within 4 min(degradation rate:K=0.78 min^(-1)),which was faster than that derived from the direct grinding method(MOF-DGP,80.97%,K=0.39 min^(-1)).X-ray photoelectron spectroscopy revealed that the Co-S content of MOF-AEP(43.39at%)was less than that of MOF-DGP(54.73at%),and the proportion of C-S-C in MOF-AEP(13.56at%)was higher than that of MOF-DGP(10.67at%).Density functional theory calculations revealed that the adsorption energy of Co for PMS was -2.94 eV when sulfur was doped as C-S-C on the carbon skeleton,which was higher than that when sulfur was doped next to cobalt in the form of Co-S bond(-2.86 eV).Thus,the C-S-C sites might provide more contributions to activate PMS compared with Co-S.Furthermore,the degradation parameters,including pH and MOF-AEP dosage,were investigated.Finally,radical quenching experiments and electron paramagnetic resonance(EPR)measurements revealed that ^(1)O_(2)might be the primary catalytic species,whereas·O~(2-)might be the secondary one in degrading MB.

In situ formation of multiple catalysts for enhancing the hydrogen storage of MgH_(2) by adding porous Ni_(3)ZnC_(0.7)/Ni loaded carbon nanotubes microspheres

MgH_(2) is considered one of the most promising hydrogen storage materials because of its safety,high efficiency,high hydrogen storage quantity and low cost characteristics.But some shortcomings are still existed:high operating temperature and poor hydrogen absorption dynamics,which limit its application.Porous Ni_(3)ZnC_(0.7)/Ni loaded carbon nanotubes microspheres(NZC/Ni@CNT)is prepared by facile filtration and calcination method.Then the different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%)is added to the MgH_(2) by ball milling.Among the three samples with different amount of NZC/Ni@CNT(2.5,5.0 and 7.5 wt%),the MgH_(2)-5 wt%NZC/Ni@CNT composite exhibits the best hydrogen storage performances.After testing,the MgH_(2)-5 wt%NZC/Ni@CNT begins to release hydrogen at around 110℃ and hydrogen absorption capacity reaches 2.34 wt%H_(2) at 80℃ within 60 min.Moreover,the composite can release about 5.36 wt%H_(2) at 300℃.In addition,hydrogen absorption and desorption activation energies of the MgH_(2)-5 wt%NZC/Ni@CNT composite are reduced to 37.28 and 84.22 KJ/mol H_(2),respectively.The in situ generated Mg_(2)NiH_(4)/Mg_(2)Ni can serve as a"hydrogen pump"that plays the main role in providing more activation sites and hydrogen diffusion channels which promotes H_(2) dissociation during hydrogen absorption process.In addition,the evenly dispersed Zn and MgZn2 in Mg and MgH_(2) could provide sites for Mg/MgH_(2) nucleation and hydrogen diffusion channel.This attempt clearly proved that the bimetallic carbide Ni_(3)ZnC_(0.7) is a effective additive for the hydrogen storage performances modification of MgH_(2),and the facile synthesis of the Ni_(3)ZnC_(0.7)/Ni@CNT can provide directions of better designing high performance carbide catalysts for improving MgH_(2).

Critical role of carbon support in metal nanoaggregate facilitating Fe-N-C catalyst for PEM fuel cell application

Metal nanoaggregates can simultaneously enhance the activity and stability of Fe-N-C catalysts in proton-exchange-membrane fuel cells(PEMFC).Previous studies on the relevant mechanism have focused on the direct interaction between FeN_(4)active sites and metal nanoaggregates.However,the role of carbon support that hosts metal nanoaggregates and active sites has been overlooked.Here,a Fe-N-C catalyst encapsulating inactive gold nanoparticles is prepared as a model catalyst to investigate the electronic tuning of Au nanoparticles(NPs)towards the carbon support.Au NPs donate electrons to carbon support,making it rich inπelectrons,which reduces the work function and regulates the electronic configuration of the FeN_(4)sites for an enhanced ORR activity.Meanwhile,the electron-rich carbon support can mitigate the electron depletion of FeN_(4)sites caused by carbon support oxidation,thereby preserving its high activity.The yield and accumulation of H_(2)O_(2)are thus alleviated,which delays the oxidation of the catalyst and benefits the stability.Due to the electron-rich carbon support,the composite catalyst achieves a top-level peak power density of 0.74 W/cm^(2) in a 1.5 bar H_(2)-air PEMFC,as well as the improved stability.This work elucidates the key role of carbon support in the performance enhancement of the FeN-C/metal nanoaggregate composite catalysts for fuel cell application.

Enhanced stability of nitrogen-doped carbon-supported palladium catalyst for oxidative carbonylation of phenol

Enhancing the stability of supported noble metal catalysts emerges is a major challenge in both science and industry.Herein,a heterogeneous Pd catalyst(Pd/NCF)was prepared by supporting Pd ultrafine metal nanoparticles(NPs)on nitrogen-doped carbon;synthesized by using F127 as a stabilizer,as well as chitosan as a carbon and nitrogen source.The Pd/NCF catalyst was efficient and recyclable for oxidative carbonylation of phenol to diphenyl carbonate,exhibiting higher stability than Pd/NC prepared without F127 addition.The hydrogen bond between chitosan(CTS)and F127 was enhanced by F127,which anchored the N in the free amino group,increasing the N content of the carbon material and ensuring that the support could provide sufficient N sites for the deposition of Pd NPs.This process helped to improve metal dispersion.The increased metal-support interaction,which limits the leaching and coarsening of Pd NPs,improves the stability of the Pd/NCF catalyst.Furthermore,density functional theory calculations indicated that pyridine N stabilized the Pd^(2+)species,significantly inhibiting the loss of Pd^(2+)in Pd/NCF during the reaction process.This work provides a promising avenue towards enhancing the stability of nitrogen-doped carbon-supported metal catalysts.

Structure design and electrochemical properties of carbon-based single atom catalysts in energy catalysis:A review

Single atom catalysts(SACs) possessing regulated electronic structure, high atom utilization, and superior catalytic efficiency have been studied in almost all fields in recent years. Carbon-based supporting SACs are becoming popular materials because of their low cost, high electron conductivity, and controllable surface property. At the stage of catalysts preparation, the rational design of active sites is necessary for the substantial improvement of activity of catalysts. To date, the reported design strategies are mainly about synthesis mechanism and synthetic method. The level of understanding of design strategies of carbon-based single atom catalysts is requiring deep to be paved. The design strategies about manufacturing defects and coordination modulation of catalysts are presented. The design strategies are easy to carry out in the process of drawing up preparation routes. The components of carbon-based SACs can be divided into two parts: active site and carbon skeleton. In this review, the manufacture of defects and coordination modulation of two parts are introduced, respectively. The structure features and design strategies from the active sites and carbon skeletons to the overall catalysts are deeply discussed.Then, the structural design of different nano-carbon SACs is introduced systematically. The characterization of active site and carbon skeleton and the detailed mechanism of reaction process are summarized and analyzed. Next, the applications in the field of electrocatalysis for oxygen conversion and hydrogen conversion are illustrated. The relationships between the superior performance and the structure of active sites or carbon skeletons are discussed. Finally, the conclusion of this review and prospects on the abundant space for further promotion in broader fields are depicted. This review highlights the design and preparation thoughts from the parts to the whole. The detailed and systematic discussion will provide useful guidance for design of SACs for readers.

Recent advances in metal-free catalysts for the synthesis of cyclic carbonates from CO_2 and epoxides

The aim of ＂green chemistry＂ and ＂atom economy＂ is to utilize carbon dioxide and replace harmful reactants such as CO and phosgene for the production of cyclic carbonates. In this paper, metal-free catalysts including organic bases, ionic liquids, supported catalysts, organic copolymers and carbon materials for the synthesis of cyclic carbonates by the cycloaddition of carbon dioxide to epoxides are reviewed. Recent advances in the design of the catalysts and the understanding of the reaction mechanism are summarized and discussed. The synergistic effects of organic bases and hydrogen bond donors, organic bases and nucleophilic anions, hydrogen bond donors and nucleophilic anions and active components and supports are highlighted. The challenge is to develop metal-free catalysts suitable for carbon dioxide capture and fixation. The ultimate goal is to synthesize cyclic carbonates in a flow reactor directly using carbon dioxide from industrial flue gas at ambient temperature and atmospheric pressure. By using synergetic effects, a multi-functional approach can meet the design strategy of metal-free catalysts for carbon dioxide adsorption and activation as well as epoxide ring opening.

Effect of NH_4^+ exchange on CuY catalyst for oxidative carbonylation of methanol

NaY and ion exchanged NaNH4Y zeolite with NH4NO3 were used as the support to prepare CuY cata‐lysts by a high temperature anhydrous interaction between the support and copper （II） acety‐lacetonate Cu（acac）2. The catalysts were used for the oxidative carbonylation of methanol to dime‐thyl carbonate （DMC） at atmospheric pressure. The textural and acidic properties of NaNH4Y zeolite and the CuY catalysts were investigated by X‐ray diffraction, scanning electron microscopy, N2 ad‐sorption‐desorption, temperature programmed reduction of H2, X‐ray photoelectron spectroscopy and temperature programmed desorption of NH3. With increasing NH4NO3 concentration, the NH4＋exchange degree increased while the crystallinity of the zeolite remained intact. Crystalline CuO was formed when the NH4＋exchange degree of NaNH4Y was low, and the corresponding CuY catalyst showed low catalytic activity. With increasing of the NH4＋exchange degree of NaNH4Y, the content of surface bound Cu＋active centers increased and the catalytic activity of the corresponding CuY catalyst also increased. The surface bound Cu＋content reached its maximum when the NH4＋ex‐change degree of NaNH4Y reached towards saturation. The CuY exhibited optimal catalytic activity with 267.3 mg/（g·h） space time yield of DMC, 6.9%conversion of methanol, 68.5%selectivity of DMC.

Co_3O_4 supported on N,P-doped carbon as a bifunctional electrocatalyst for oxygen reduction and evolution reactions

Noble metals, such as platinum, ruthenium and iridium‐group metals, are often used as oxygen reduction or evolution reaction （ORR/OER） electrocatalysts. To reduce the cost and provide an application of bifunctional catalysis, in this work, cobalt oxide supported on nitrogen and phospho‐rus co‐doped carbon （Co3O4/NPC） was fabricated and examined as a bifunctional electrocatalyst for OER and ORR. To prepare Co3O4/NPC, NPC was pyrolyzed from melamine and phytic acid support‐ed on carbon, followed by the solvothermal synthesis of Co3O4 on NPC. Linear sweep voltammetry was used to evaluate the activity for OER and ORR. For OER, Co3O4/NPC showed an onset potential of 0.54 V （versus the saturated calomel electrode） and a current density of 21.95 mA/cm2 at 0.80 V, which was better than both Co3O4/C and NPC. The high activity of Co3O4/NPC was attributed to a synergistic effect of the N, P co‐dopants and Co3O4. For ORR, Co3O4/NPC exhibited an activity close to commercial Pt/C in terms of the diffusion limited current density （–4.49 vs–4.76 mA/cm2 at–0.80 V）, and Co3O4 played the key role for the catalysis. Chronoamperometry （current versus time） was used to evaluate the stability, which showed that Co3O4/NPC maintained 46%current after the chronoamperometry test for OER and 95% current for ORR. Overall, Co3O4/NPC exhibited high activity and improved stability for both OER and ORR.

Effect of CeO_2 addition on Ni/Al_2O_3 catalysts for methanation of carbon dioxide with hydrogen

The Ni-CeO2/Al2O3 catalysts with a nickel content of 15 wt% prepared via impregnating boehmite were found to be highly active and stable for methanation of carbon dioxide with hydrogen at a H2/CO2 molar ratio of 4. The effects of CeO2 content and reaction temperature on the performance of the Ni-CeO2/Al2O3 catalysts were studied in detail. The results showed that the catalytic performance was strongly dependent on the CeO2 content in Ni-CeO2/Al2O3 catalysts and that the catalysts with 2 wt% CeO2 had the highest catalytic activity among the tested ones at 350 ℃. The XRD and H2-TPR characterizations revealed that the addition of CeO2 decreased the reduction temperature by altering the interaction between Ni and Al2O3, and improved the reducibility of the catalyst. Preliminary stability test of 120 h on stream over the Ni-2CeO2/Al2O3 catalyst at 350 ℃ revealed that the catalyst was much better than the unpromoted one.

One-pot Synthesis of Dimethyl Carbonate in the Presence of a Two-component Catalyst

The one-pot synthesis of dimethyl carbonate（DMC） with co-production of propy-lene carbonate（PC） and propylene glycol（PG） from propylene oxide（ PO）, carbon dioxide and methanol as the starting materials was investigated. The catalyst adopted here was a mixture of tetrabutyl ammonium bromide and sodium methoxide. It was found that un- der the reaction conditions of t = 150 ℃, p =3-4 MPa and 2 h, the PO conversion could reach 100%, the DMC, PC and the PG selectivities were 49. 7%, 42. 7% and 49. 8%, respectively, and the selectivity of by-products was below 10%.

A Novel Carbon Nanotube-Supported NiP Amorphous Alloy Catalyst and Its Hydrogenation Activity

A carbon nanotube-supported NiP amorphous catalyst （NiP/CNT） was prepared by induced reduction. Benzene hydrogenation was used as a probe reaction for the study of catalytic activity. The effects of the support on the activity and thermal stability of the supported catalyst were discussed based on various characterizations, including XRD, TEM, ICP, XPS, H2-TPD, and DTA. In comparison with the NiP amorphous alloy, the benzene conversion on NiP/CNT catalyst was lower, but the specific activity of NiP/CNT was higher, which is attributed to the dispersion produced by the support, an electron-donating effect, and the hydrogen-storage ability of CNT. The NiP/CNT thermal stability was improved because of the dispersion and electronic effects and the good heat-conduction ability of the CNT support.

Nanocarbons and their hybrids as catalysts for non-aqueous lithium–oxygen batteries

Rechargeable lithium-oxygen (Li–O2) batteries have been considered as the most promising candidates for energy storage and conversion devices because of their ultra high energy density. Until now, the critical scientific challenges facing Li–O2batteries are the absence of advanced electrode architectures and highly efficient electrocatalysts for both oxygen reduction reaction (ORR) and oxygen evolution reaction (OER), which seriously hinder the commercialization of this technology. In the last few years, a number of strategies have been devoted to exploring new catalysts with novel structures to enhance the battery performance. Among various of oxygen electrode catalysts, carbon-based materials have triggered tremendous attention as suitable cathode catalysts for Li–O2batteries due to the reasonable structures and the balance of catalytic activity, durability and cost. In this review, we summarize the recent advances and basic understandings related to the carbon-based oxygen electrode catalytic materials, including nanostructured carbon materials (one-dimensional (1D) carbon nanotubes and carbon nanofibers, 2D graphene nanosheets, 3D hierarchical architectures and their doped structures), and metal/metal oxide-nanocarbon hybrid materials (nanocarbon supporting metal/metal oxide and nanocarbon encapsulating metal/metal oxide). Finally, several key points and research directions of the future design for highly efficient catalysts for practical Li–O2batteries are proposed based on the fundamental understandings and achievements of this battery field. © 2016 Science Press

Efficient conversion of fructose to 5-hydroxymethylfurfural over sulfated porous carbon catalyst

Sulfated porous carbon （PC-SO3H） catalyst was successfully synthesized from one-pot treatment of porous polydivinylbenzene in H2SO4 at 250 ℃, which exhibited very good catalytic performances in the production of 5-hydroxymethylfurfural from fructose.

N, F?Codoped Microporous Carbon Nanofibers as Efficient Metal?Free Electrocatalysts for ORR

Currently, the oxygen reduction reaction(ORR) mainly depends on precious metal platinum(Pt) catalysts. However, Pt-based catalysts have several shortcomings, such as high cost, scarcity, and poor long-term stability. Therefore, development of e cient metal-free electrocatalysts to replace Pt-based electrocatalysts is important. In this study, we successfully prepared nitrogen-and fluorinecodoped microporous carbon nanofibers(N, F-MCFs) via electrospinning polyacrylonitrile/polyvinylidene fluoride/polyvinylpyrrolidone(PAN/PVDF/PVP) tricomponent polymers followed by a hydrothermal process and thermal treatment, which was achieved for the first time in the literature. The results indicated that N, F-MCFs exhibit a high catalytic activity(E_(onset): 0.94 V vs. RHE, E_(1/2): 0.81 V vs. RHE, and electron transfer number: 4.0) and considerably better stability and methanol tolerance for ORR in alkaline solutions as compared to commercial Pt/carbon(Pt/C, 20 wt%) catalysts. Furthermore, in acidic media, N, F-MCFs showed a four-electron transfer pathway for ORR. This study provides a new strategy for in situ synthesis of N, F-MCFs as highly e cient metal-free electrocatalysts for ORR in fuel cells.

Simultaneous catalytic hydrolysis of carbonyl sulfide and carbon disulfide over Al_2O_3-K/CAC catalyst at low temperature

In this work, a series of coal-based active carbon （CAC） catalysts loaded by A1203 were prepared by sol-gel method and used for the simulta- neous catalytic hydrolysis of carbonyl sulfide （COS） and carbon disulfide （CS2） at relatively low temperatures of 30-70 ℃. The influences of calcinations temperatures and operation conditions such as： reaction temperature, 02 concentration, gas hourly space velocity （GHSV） and relative humidity （RH） were also discussed respectively. The results showed that catalysts with 5.0 wt% A1203 calcined at 300 ℃ had supe- rior activity for the simultaneous catalytic hydrolysis of COS and CS2. When the reaction temperature was above 50 ℃, catalytic hydrolysis activity of COS could be enhanced but that of CS2 was inhibited. Too high RH could make the catalytic hydrolysis activities of COS and CS2 decrease. A small amount of 02 introduction could enhance the simultaneous catalytic hydrolysis activities of COS and CS2.

Effect of the graphitic degree of carbon supports on the catalytic performance of ammonia synthesis over Ba-Ru-K/HSGC catalyst

A series of high surface area graphitic carbon materials （HSGCs） were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x （x is the ball-milling time in hour） catalysts was studied using ammonia synthesis as a probe reaction. The graphitic degree and pore structure of HSGC-x supports could be successfully tuned via the variation of ball-milling time. Ru nanoparticles of different Ba-Ru-K/HSGC-x catalysts are homogeneously distributed on the supports with the particle sizes ranging from 1.6 to 2.0 nm. The graphitic degree of the support is closely related to its facile electron transfer capability and so plays an important role in improving the intrinsic catalytic performance of Ba-Ru-K/HSGC-x catalyst.

Doping effects of manganese on the catalytic performance and structure of NiMgO catalysts for controllabe synthesis of multi-walled carbon nanotubes

Doping effects of manganese （Mn） on catalytic performance and structure evolution of NiMgO catalysts for synthesis of multi-walled carbon nanotubes （MWCNTs） from methane were investigated for the first time. Addition of Mn in NiMgO catalyst can greatly improve the MWCNTs yield. Mno.2NiMgO catalyst among the tested ones gives the highest MWCNTs yield as 2244%, which is two times higher than that of the catalyst without Mn. The structure evolution, reduction behaviors and surface chemical properties of MnNiMgO catalysts with various Mn contents were studied in detail. It was found that the stable solid solution of NiMgO2 formed in NiMgO catalyst was disturbed by the addition of Mn. Instead, another solid solution of MnMg608 is formed. More amount of Ni can be reduced and dispersed on the catalyst surface to be acted as active sites. Importantly, the changes of Ni content on the surface are correlated with the Ni particle size and the outer diameter of MWCNTs, suggesting the controllable synthesis of MWCNTs over MnNiMgO catalysts.

Preparation and Characterization of Carbon Nanotubes-Coated Cordierite for Catalyst Supports

The carbon nanotubes-coated cordierite （CNTs-cordierite） was fabricated by pyrolysis of ethine on cordierite with iron catalyst, which was penetrated into the cordierite substrate by vacuum impregnation. The cordierite substrate, carbon naontubes, and CNTs-cordierite were characterized by SEM, TEM/HREM, BET, and TGA. The results show that the carbon nanotubes were distributed uniformly on the surface of cordierite. A significant increase in BET surface area and pore volume was observed, and a suitable pore-size distribution was obtained. On the CNTs-cordierite, carbon nanotubes penetrated into the cordierite substrate, which led to a remarkable stability of the CNTs against ultrasound maltreatment. Growth time is an important factor for thermostability and texture of the sample. The mass increased but the purity decreased with the growth time, which caused the exothermic peak shift to low temperature, and the corresponding full width half maximum （FWHM） of the peak in DTG increased.

Self-reducing bifunctional Ni-W/SBA-15 catalyst for cellulose hydrogenolysis to low carbon polyols

A series of self-reducing bifunctional Ni-W/SBA-15 catalysts were synthesized using biomass-based carbon source as the reducing agent without conventional further reduction step. The self-reducing catalysts were performed on the hydrogenolysis of cellulose to low carbon polyols. The effects of calcination temperature and metallic loading contents for cellulose hydrogenolysis reaction were investigated detailedly.The optimal calcination temperature was found to be 673 K by TG analysis. The active metal nanoparticles with a better dispersion were observed using SEM and element mapping technology. The yield of low carbon polyols using the catalyst with the receipt of 10%Ni-15%W/SBA-15-673 K can reach as high as68.14%, of which the ethylene glycol(EG) accounts for 61.04%.

One step NaBH_4 reduction of Pt-Ru-Ni catalysts on different types of carbon supports for direct ethanol fuel cells : Synthe sis and characte rization

The ternary catalyst Pt75Ru5Ni20 was conducted on various types of carbon supports including functionalized Vulcan XC-72R(f-CB),functionalized multi-walled carbon nanotubes(f-MWCNT),and mesoporous carbon(PC-Zn-succinic)by sodium borohydride chemical reduction method to improve the ethanol electrooxidation reaction(EOR)for direct ethanol fuel cell(DEFC).It was found that the particle size of the metals on f-MWCNT was 5.20 nm with good particle dispersion.The alloy formation of ternary catalyst was confirmed by XRD and more clearly described by SEM element mapping,which was relevant to the efficiency of the catalysts.Moreover,the mechanism of ethanol electrooxidation reaction based on the surface reaction was more understanding.The activity and stability for ethanol electrooxidation reaction(EOR)were investigated using cyclic voltammetry and chronoamperometry,respectively.The highest activity and stability for EOR were observed from Pt75Ru5Ni20/f-MWCNT due to a good metal-carbon interaction.Ru and Ni presented in Pt-Ru-Ni alloy improved the activity and stability of ternary catalysts for EOR.Moreover,the reduction of Pt content in ternary catalyst led to the catalyst cost deduction in DEFC.