This article discusses and analyzes the law of nitrogen increase in liquid steel and the main factors affect-ing the nitrogen increasing of molten steel,through the way of adding nitrogen to molten steel by bottom blo...This article discusses and analyzes the law of nitrogen increase in liquid steel and the main factors affect-ing the nitrogen increasing of molten steel,through the way of adding nitrogen to molten steel by bottom blowing nitrogen gas in LF refining process.It is considered that the main factors affecting the nitrogen increasing instability of molten steel are the initial temperature of LF refining,nitrogen relative element,surface active elements[O]and[S]of steel liquid,and bottom blowing rate of ladle.The large-scale production practice shows that T[O]not more than 50×10-6 and[S]is not more than 0.020 in LF refining at the initial temperature of not less than 1570.The liquid steel nitrogen enrichment test is carried out by ladle bottom blowing nitrogen gas after 20 min of refining,the flow rate is set as(6.0~7.0)NL/min per ton,and it is turned to 2 NL/min at 6 min before the end of refining,the nitrogen increasing rate of liquid steel is basically stable at(5~6)×10-6 per minute.展开更多
Bubble defect is one of the main defects of an automobile sheet.To solve this defect,the technology for nitrogen-argon mixed gas blowing on the tundish stopper is developed,the theoretical research on nitrogen absorpt...Bubble defect is one of the main defects of an automobile sheet.To solve this defect,the technology for nitrogen-argon mixed gas blowing on the tundish stopper is developed,the theoretical research on nitrogen absorption in the molten steel is performed,the nitrogen-argon mixed gas blowing equipment is developed and experimented in the plant.The expected effect is achieved in the industrial test,and the slab inclusion density and quality degradation ratio of the automobile sheet are significantly reduced.展开更多
文摘This article discusses and analyzes the law of nitrogen increase in liquid steel and the main factors affect-ing the nitrogen increasing of molten steel,through the way of adding nitrogen to molten steel by bottom blowing nitrogen gas in LF refining process.It is considered that the main factors affecting the nitrogen increasing instability of molten steel are the initial temperature of LF refining,nitrogen relative element,surface active elements[O]and[S]of steel liquid,and bottom blowing rate of ladle.The large-scale production practice shows that T[O]not more than 50×10-6 and[S]is not more than 0.020 in LF refining at the initial temperature of not less than 1570.The liquid steel nitrogen enrichment test is carried out by ladle bottom blowing nitrogen gas after 20 min of refining,the flow rate is set as(6.0~7.0)NL/min per ton,and it is turned to 2 NL/min at 6 min before the end of refining,the nitrogen increasing rate of liquid steel is basically stable at(5~6)×10-6 per minute.
文摘Bubble defect is one of the main defects of an automobile sheet.To solve this defect,the technology for nitrogen-argon mixed gas blowing on the tundish stopper is developed,the theoretical research on nitrogen absorption in the molten steel is performed,the nitrogen-argon mixed gas blowing equipment is developed and experimented in the plant.The expected effect is achieved in the industrial test,and the slab inclusion density and quality degradation ratio of the automobile sheet are significantly reduced.
