The photo-controlled/living radical polymerization of methacrylic acid (MAA) was performed at room temperature by irradiation with a high-pressure mercury lamp using azo initiators and 4-methoxy-2,2,6,6-tetramethylpip...The photo-controlled/living radical polymerization of methacrylic acid (MAA) was performed at room temperature by irradiation with a high-pressure mercury lamp using azo initiators and 4-methoxy-2,2,6,6-tetramethylpiperidine-1-oxyl as the mediator in the presence of (4-tert-butylphenyl)diphenylsulfonium triflate (tBuS) as the accelerator. Whereas the bulk polymerization yielded polymers with a bimodal molecular weight distribution in both the absence and presence of tBuS, the solution polymerization in methanol produced unimodal polymers with the molecular weight distribution of 2.0 - 2.3 in the presence of tBuS. The molecular weight distribution of the resulting poly (MAA) decreased with an in- crease in tBuS. The dilution of the monomer concentration also reduced the molecular weight distribution. The use of the initiator with a low 10-h half-life temperature also effectively controlled the molecular weight. The livingness of the polymerization was confirmed by obtaining linear increases in the first-order conversion versus time, the molecular weight versus the conversion, and the molecular weight versus the reciprocal of the initiator concentration.展开更多
The title block copolymer (defined as PSUEA) containing pendant,self-complementary quadruple hydrogen bonding sites has been prepared successfully by three steps.First,poly(styrene-b-2-hydroxyethyl acrylate) (defined ...The title block copolymer (defined as PSUEA) containing pendant,self-complementary quadruple hydrogen bonding sites has been prepared successfully by three steps.First,poly(styrene-b-2-hydroxyethyl acrylate) (defined as PSHEA) was prepared by living radical polymerizing 2-hydroxyethyl acrylate (HEA) initiated by polystyrene (PSt) macro- initiator,which was prepared via nitroxide-mediated polymerization (NMP) technique.After treated by excessive 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate (IPDI),...展开更多
文摘The photo-controlled/living radical polymerization of methacrylic acid (MAA) was performed at room temperature by irradiation with a high-pressure mercury lamp using azo initiators and 4-methoxy-2,2,6,6-tetramethylpiperidine-1-oxyl as the mediator in the presence of (4-tert-butylphenyl)diphenylsulfonium triflate (tBuS) as the accelerator. Whereas the bulk polymerization yielded polymers with a bimodal molecular weight distribution in both the absence and presence of tBuS, the solution polymerization in methanol produced unimodal polymers with the molecular weight distribution of 2.0 - 2.3 in the presence of tBuS. The molecular weight distribution of the resulting poly (MAA) decreased with an in- crease in tBuS. The dilution of the monomer concentration also reduced the molecular weight distribution. The use of the initiator with a low 10-h half-life temperature also effectively controlled the molecular weight. The livingness of the polymerization was confirmed by obtaining linear increases in the first-order conversion versus time, the molecular weight versus the conversion, and the molecular weight versus the reciprocal of the initiator concentration.
基金supported by the National Natural Science Foundation of China (No.20574041).
文摘The title block copolymer (defined as PSUEA) containing pendant,self-complementary quadruple hydrogen bonding sites has been prepared successfully by three steps.First,poly(styrene-b-2-hydroxyethyl acrylate) (defined as PSHEA) was prepared by living radical polymerizing 2-hydroxyethyl acrylate (HEA) initiated by polystyrene (PSt) macro- initiator,which was prepared via nitroxide-mediated polymerization (NMP) technique.After treated by excessive 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate (IPDI),...