Effects of Ni on microstructure and properties of aluminum-stainless steel TIG welding-brazing joint with Al-Si filler were studied. Different mass percentage of Ni powder was added in the flux separately. Results of ...Effects of Ni on microstructure and properties of aluminum-stainless steel TIG welding-brazing joint with Al-Si filler were studied. Different mass percentage of Ni powder was added in the flux separately. Results of tensile tests show that a significant improvement on mechanical properties of the butt joint is obtained using the modified flux. Moreover, obvious differences on microstructures of the interfaces were observed with Ni addition, that two intermetallic compound （IMC） layers at the interface change to one layer and the IMC thickness also decreases. Finally, effect mechanism of Ni was analyzed and discussed. Ni addition leads to an enrichment of element Si at the brazing interface, and furthermore suppresses the formation of intermetaUic compound. The reduction of IMC thickness is the main reason for the improvement of joint properties.展开更多
基金Acknowledgement The authors would like to appreciate the financial support from the National Natural Science Foundation of China （Grant No. 50874033）.
文摘Effects of Ni on microstructure and properties of aluminum-stainless steel TIG welding-brazing joint with Al-Si filler were studied. Different mass percentage of Ni powder was added in the flux separately. Results of tensile tests show that a significant improvement on mechanical properties of the butt joint is obtained using the modified flux. Moreover, obvious differences on microstructures of the interfaces were observed with Ni addition, that two intermetallic compound （IMC） layers at the interface change to one layer and the IMC thickness also decreases. Finally, effect mechanism of Ni was analyzed and discussed. Ni addition leads to an enrichment of element Si at the brazing interface, and furthermore suppresses the formation of intermetaUic compound. The reduction of IMC thickness is the main reason for the improvement of joint properties.