The Y 2O 3-CeO 2-ZrO 2 powders were prepared using a co-precipitation process and the corresponding coatings were prepared by plasma spraying. The results show that an optimal composition exists in Y 2O 3-doped ...The Y 2O 3-CeO 2-ZrO 2 powders were prepared using a co-precipitation process and the corresponding coatings were prepared by plasma spraying. The results show that an optimal composition exists in Y 2O 3-doped CeO 2-ZrO 2, but not in CeO 2-doped Y 2O 3-ZrO 2. The powders mainly contain tetragonal phase and a trace amount of monoclinic phase. The homogeneity in composition, large agglomerate size, ideal particle size distribution and high flowability were obtained. The as-sprayed coatings are composed of non-transformable tetragonal phase, tz′structure, and resistant to transformation under thermal or mechanical stresses.展开更多
文摘The Y 2O 3-CeO 2-ZrO 2 powders were prepared using a co-precipitation process and the corresponding coatings were prepared by plasma spraying. The results show that an optimal composition exists in Y 2O 3-doped CeO 2-ZrO 2, but not in CeO 2-doped Y 2O 3-ZrO 2. The powders mainly contain tetragonal phase and a trace amount of monoclinic phase. The homogeneity in composition, large agglomerate size, ideal particle size distribution and high flowability were obtained. The as-sprayed coatings are composed of non-transformable tetragonal phase, tz′structure, and resistant to transformation under thermal or mechanical stresses.