Microwave dielectric ceramics should be improved to advance mobile communication technologies further.In this study,we prepared Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics with nonstoichiometric Sr^(2+)ratios based on our ...Microwave dielectric ceramics should be improved to advance mobile communication technologies further.In this study,we prepared Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics with nonstoichiometric Sr^(2+)ratios based on our previously reported SrY_(2)O_(4) microwave dielectric ceramic,which has a low dielectric constant and an ultrahigh quality factor(Q value).The ceramic exhibited a 33.6% higher Q-by-frequency(Q×f)value(Q≈12,500)at x=0.02 than SrY_(2)O_(4).All Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics exhibited pure phase structures,although variations in crystal-plane spacings were observed.The ceramics are mainly composed of Sr-O,Y1-O,and Y_(2)-O octahedra,with the temperature coefficient of the resonant frequency(τ_(f))of the ceramic increasing with Y_(2)-O octahedral distortion.The ceramic comprises uniform grains with a homogeneous elemental distribution,clear grain boundaries,and no obvious cavities at x=0.02.The Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics exhibited good microwave dielectric properties,with optimal performance observed at x=0.02(dielectric constant(εr)=15.41,Q×f=112,375 GHz,and τ_(f)=-17.44 ppm/℃).The τ_(f) value was reduced to meet the temperaturestability requirements of 5G/6G communication systems by adding CaTiO_(3),with Sr_(1.02)Y_(2)O_(4.02)+2wt% CaTiO_(3) exhibiting ε_(r)=16.14,Q×f=51,004 GHz,andτf=0 ppm/℃.A dielectric resonator antenna prepared using Sr_(1.02)Y_(2)O_(4.02)+2wt%CaTiO_(3) exhibited a central frequency of 26.6 GHz,with a corresponding gain and efficiency of 3.66 dBi and 83.14%,respectively.Consequently,Sr_(1.02)Y_(2)O_(4).02-based dielectric resonator antennas are suitable for use in 5G millimeter-wave band(24.5-27.5 GHz)applications.展开更多
基金supported by the National Natural Science Foundation of China(Nos.61761015 and 11664008)the Natural Science Foundation of Guangxi(No.2018GXNSFFA050001)the High Level Innovation Team and Outstanding Scholar Program of Guangxi Institutes.
文摘Microwave dielectric ceramics should be improved to advance mobile communication technologies further.In this study,we prepared Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics with nonstoichiometric Sr^(2+)ratios based on our previously reported SrY_(2)O_(4) microwave dielectric ceramic,which has a low dielectric constant and an ultrahigh quality factor(Q value).The ceramic exhibited a 33.6% higher Q-by-frequency(Q×f)value(Q≈12,500)at x=0.02 than SrY_(2)O_(4).All Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics exhibited pure phase structures,although variations in crystal-plane spacings were observed.The ceramics are mainly composed of Sr-O,Y1-O,and Y_(2)-O octahedra,with the temperature coefficient of the resonant frequency(τ_(f))of the ceramic increasing with Y_(2)-O octahedral distortion.The ceramic comprises uniform grains with a homogeneous elemental distribution,clear grain boundaries,and no obvious cavities at x=0.02.The Sr_(1+x)Y_(2)O_(4+x)(x=0-0.04)ceramics exhibited good microwave dielectric properties,with optimal performance observed at x=0.02(dielectric constant(εr)=15.41,Q×f=112,375 GHz,and τ_(f)=-17.44 ppm/℃).The τ_(f) value was reduced to meet the temperaturestability requirements of 5G/6G communication systems by adding CaTiO_(3),with Sr_(1.02)Y_(2)O_(4.02)+2wt% CaTiO_(3) exhibiting ε_(r)=16.14,Q×f=51,004 GHz,andτf=0 ppm/℃.A dielectric resonator antenna prepared using Sr_(1.02)Y_(2)O_(4.02)+2wt%CaTiO_(3) exhibited a central frequency of 26.6 GHz,with a corresponding gain and efficiency of 3.66 dBi and 83.14%,respectively.Consequently,Sr_(1.02)Y_(2)O_(4).02-based dielectric resonator antennas are suitable for use in 5G millimeter-wave band(24.5-27.5 GHz)applications.
