Due to high cost of aggregates, cement and steel in plain regions of Pakistan, low income people are unable to get their houses constructed using Reinforced Cement Concrete (RCC). In this study, potential of baked cla...Due to high cost of aggregates, cement and steel in plain regions of Pakistan, low income people are unable to get their houses constructed using Reinforced Cement Concrete (RCC). In this study, potential of baked clay as an economical material of building construction is investigated in order to replace normal concrete. For this purpose, compressive strength and tensile strength of baked clay fired at 1000℃ were determined. The results show that the compressive strength and tensile strength of baked clay are about 65%, and 80% more than those of corresponding values of normal concrete, respectively. This implies that by utilizing reinforced baked clay instead of RCC, saving of cement aggregates and reinforcing steel could be achieved.展开更多
Multiaxial compression tests were performed on 100 mm×100 mm×100 mm high-strength high-performance concrete (HSI-IPC) cubes and normal strength concrete (NSC) cubes. The failure modes of specimens were p...Multiaxial compression tests were performed on 100 mm×100 mm×100 mm high-strength high-performance concrete (HSI-IPC) cubes and normal strength concrete (NSC) cubes. The failure modes of specimens were presented, the static compressive strengths in principal directions were measured, the influence of the stress ratios was analyzed. The experimental results show that the ultimate strengths for HSHPC and NSC under multiaxial compression are greater than the uniaxial compressive strengths at all stress ratios, and the multiaxial strength is dependent on the brittleness and stiffness of concrete, the stress state and the stress ratios. In addition, the Kupfer-Gersfle and Ottosen's failure criteria for plain HSHPC and NSC under multiaxial compressive loading were modified.展开更多
Lightweight aggregate concrete cube specimens (100 mm×100 mm×100 mm) and plate specimens (100 mm×100 mm×50 mm) were tested under biaxial compression-compression (CC) and compression-tension (CT) lo...Lightweight aggregate concrete cube specimens (100 mm×100 mm×100 mm) and plate specimens (100 mm×100 mm×50 mm) were tested under biaxial compression-compression (CC) and compression-tension (CT) load combinations. For comparison, normal concrete plate specimens (100 mm×100 mm×50 mm) were tested under the same load combinations. Based on the test results, a two-level strength criterion of lightweight aggregate concrete in both octahedral stress coordinate and principal stress coordinate was suggested. The lightweight aggregate concrete cube specimens (100 mm×100 mm×100 mm) were then tested under triaxial compression-compression-compression (CCC) load combination with corresponding tests on normal concrete cube specimens (100 mm×100 mm×100 mm). The effect of intermediate principal stress on triaxial compressive strength is further examined. A "plastic flow plateau" area was apparent in principal compressive stress-strain relationships of lightweight aggregate concrete but not in normal concrete. A quadratic formula was suggested for the expression of strength criterion under triaxial compression.展开更多
文摘Due to high cost of aggregates, cement and steel in plain regions of Pakistan, low income people are unable to get their houses constructed using Reinforced Cement Concrete (RCC). In this study, potential of baked clay as an economical material of building construction is investigated in order to replace normal concrete. For this purpose, compressive strength and tensile strength of baked clay fired at 1000℃ were determined. The results show that the compressive strength and tensile strength of baked clay are about 65%, and 80% more than those of corresponding values of normal concrete, respectively. This implies that by utilizing reinforced baked clay instead of RCC, saving of cement aggregates and reinforcing steel could be achieved.
文摘Multiaxial compression tests were performed on 100 mm×100 mm×100 mm high-strength high-performance concrete (HSI-IPC) cubes and normal strength concrete (NSC) cubes. The failure modes of specimens were presented, the static compressive strengths in principal directions were measured, the influence of the stress ratios was analyzed. The experimental results show that the ultimate strengths for HSHPC and NSC under multiaxial compression are greater than the uniaxial compressive strengths at all stress ratios, and the multiaxial strength is dependent on the brittleness and stiffness of concrete, the stress state and the stress ratios. In addition, the Kupfer-Gersfle and Ottosen's failure criteria for plain HSHPC and NSC under multiaxial compressive loading were modified.
基金Project (No. 50679007) supported by the National Natural Science Foundation of China
文摘Lightweight aggregate concrete cube specimens (100 mm×100 mm×100 mm) and plate specimens (100 mm×100 mm×50 mm) were tested under biaxial compression-compression (CC) and compression-tension (CT) load combinations. For comparison, normal concrete plate specimens (100 mm×100 mm×50 mm) were tested under the same load combinations. Based on the test results, a two-level strength criterion of lightweight aggregate concrete in both octahedral stress coordinate and principal stress coordinate was suggested. The lightweight aggregate concrete cube specimens (100 mm×100 mm×100 mm) were then tested under triaxial compression-compression-compression (CCC) load combination with corresponding tests on normal concrete cube specimens (100 mm×100 mm×100 mm). The effect of intermediate principal stress on triaxial compressive strength is further examined. A "plastic flow plateau" area was apparent in principal compressive stress-strain relationships of lightweight aggregate concrete but not in normal concrete. A quadratic formula was suggested for the expression of strength criterion under triaxial compression.