A modified method for evaluation of materials containing volatile corrosion inhibitor

A systematic research on a modified method that was developed to evaluate the effectiveness of volatile corrosion inhibitor(VCI) materials was carried out. The metal specimen in size of 50mm×25mm×2mm was level mounted on the top of a beaker by transparent adhesive tape and the assembly was placed in a constant temperature water bath and kept at approximately 40℃ to accelerate the vaporization of VCI and distilled water, which was placed at the bottom of the beaker at the same time. The experimental results show that the reproducibility of rust appearance and corrosion rate calculated by specimen’s mass loss is perfect. The outstanding characteristic of the rust appearance based on different VCI formula is discovered that is very important in studying the mechanism of VCI and the synergism of chemical reagent. The accelerated ratio is increased greatly as compared with the traditional method and the value is approximately 15 as compared with Shijiazhuang atmospheric environment corrosion test. The modified method is suitable for formula screening test and quick effectiveness evaluation of VCI materials.

基于壬酸复配的绿色气相缓蚀剂及其性能研究

气相缓蚀技术在金属腐蚀防护中发挥着重要作用,研发新型环保且高效的气相缓蚀剂配方具有重要意义。以10钢为研究对象,开展壬酸与钼酸钠双组分复配,通过失重试验探究其气相缓蚀效果,采用电化学工作站、水接触角测试仪、白光干涉形貌仪、扫描电镜、能谱仪对电化学和失重试验后的金属表面腐蚀情况进行分析。结果表明:复配缓蚀剂是一种阳极缓蚀剂;与单组分比较,不同比例的壬酸与钼酸钠复配剂的缓蚀效果均得到提高;壬酸与钼酸钠复配优化能发挥协同作用,当复配比例(质量比)为7∶3条件下,其缓蚀效率达92.89%,试样金属表面水接触角为112.6°并形成了疏水保护层,显著抑制了Fe的溶解和氧化产物生成,有效降低了金属表面粗糙度。

绿色气相缓蚀剂的研究进展

近年来,随着人们对健康、环保和安全等方面意识的不断提升以及相关法律法规的落实,工业上对金属制品生产和应用过程中起防护作用的气相缓蚀剂提出了更高要求,一些毒性高、对环境有影响的气相缓蚀剂受到了使用限制。因此,研发和推广新一代环保、安全的气相缓蚀剂势在必行。此外,可再生资源的开发利用是人类社会可持续发展的重要措施。源自自然界动植物的可再生资源,特别是农作物、瓜果蔬菜和林木加工废弃物等资源中含有大量天然抗氧剂、防腐剂、抑菌剂等成分,作为气相缓蚀剂开发利用的潜力很大,目前国内外研究人员已经对这类新一代绿色气相缓蚀剂开展了重点研究。概述了气相缓蚀剂的发展历程,总结了氨基酸、聚天冬氨酸、植物源化合物、植物提取物等绿色气相缓蚀剂的研究现状,并对绿色气相缓蚀剂的发展趋势进行了展望,以为其产业化应用提供必要的支持。

碳钢用新型气相防锈包装膜的制备与性能研究

目的以正癸酸(CA)为缓蚀剂制备一种新型气相防锈包装膜,以期拓展中长链脂肪酸类缓蚀剂在防锈包装中的应用。方法利用挤出吹塑法制备了含不同质量分数(0、0.5%、1.0%、2.0%)CA的低密度聚乙烯(LDPE)基气相防锈包装膜,试验测定分析CA添加量对包装膜光学、力学、阻隔、缓蚀等性能的影响。结果CA的添加可改善LDPE包装膜的韧性,其质量分数为0.5%、1.0%、2.0%时,可使包装膜的水蒸气阻隔性能分别提高3.7%、17.9%、14.8%;CA质量分数为1.0%和2.0%的包装膜可使低碳钢在交变湿热环境下保持9周期无锈蚀,满足国标对气相防锈包装膜的相关性能要求。结论添加CA的气相防锈包装膜可有效延缓碳钢腐蚀,为该类新型气相防锈包装膜研制提供技术支撑。

适用于岛礁环境下电器设备防护的气相缓蚀剂研究

针对岛礁环境下电器设备防护的需求,调研筛选出8种气相缓蚀剂,通过对气相缓蚀剂进行挥发减量试验、气相缓蚀能力试验、电化学试验、盐雾试验,评价气相缓蚀剂的防护性能。挥发减量试验结果表明CORTEC VPCI-609、RTFD VCI 、SF/D-331兼具高挥发性成分与低挥发性成分,具有挥发持久性;气相缓蚀能力试验结果表明RTFD VCI和VCIrus-505 VCI P对四种金属均具有缓蚀作用;电化学结果说明RTFD VCI和SF/D-331对四种金属均具有正向缓蚀效果;盐雾试验证明RTFD VCI和SF/D-331对电脑主板具有长效保护作用,对其电性能没有影响。综上所述,RTFD VCI与SF/D-331对四种金属(铜、铝、钢、镁)均具有正向防护能力,对电脑主板具有较好的防护效果,且不影响其电性能,适用于电器设备、各种元器件及各种金属零部件的防锈。

VCI材料在汽车零部件包装上的应用

本文介绍了气相防锈包装材料技术,详细阐述了气相缓蚀剂的定义、工作原理与技术特点、气相防锈包装材料的分类,着重总结了气相防锈包装材料在汽车零部件包装上的应用,揭露了当前气相防锈包装材料存在的不足;展望了未来气相防锈包装材料的发展方向,为其在汽车零部件包装上的应用提供一定的理论指导。

绿色气相缓蚀剂的复配及其缓蚀性能研究

目的 为解决单组分绿色气相缓蚀剂缓蚀性能差的问题,复配一种绿色复合气相缓蚀剂,探究其对碳钢和黄铜金属试样的缓蚀作用。方法 采用腐蚀质量损失、接触角、电化学等试验测试分析复合气相缓蚀剂对碳钢、黄铜的缓蚀效果与成膜耐久性。结果 复合气相缓蚀剂对10号钢、H62黄铜的缓蚀效率分别为84.71%、91.67%,缓蚀性能显著优于单组分气相缓蚀剂;复合气相缓蚀剂在10号钢、H62黄铜表面均形成了缓蚀膜,H62黄铜表面形成的缓蚀膜较10号钢的更具耐久性。结论 与单组分气相缓蚀剂相比,该复合气相缓蚀剂对碳钢、黄铜均具备良好的缓蚀作用,为绿色气相缓蚀剂的防锈包装应用提供支撑。

环保型金属包装用气相防锈纸的研究

通过研究气相缓蚀剂钨酸钠、乌洛托品与尿素3者之间的最佳配比关系,开发了一种新型无毒的环境友好型气相防锈纸。通过快速气相防锈甄别试验,与市售气相防锈纸作对比,结果表明该防锈纸防锈效果良好,能够对所包装的金属产品进行较长期的防锈保护。

炼油厂闲置设备保护用气相缓蚀剂的研制

在实验室制得了V2复合型气相缓蚀剂 ,采用静态、动态粉末法、密闭空间挥发减量试验、现场保护试验等方法进行了性能评价 ,并采用模拟大气腐蚀状态的电化学测试技术对其缓蚀机理进行了初步研究。结果表明 ,V2是一种性能优良。

新型吗啉类气相缓蚀剂的电化学阻抗研究

采用电化学阻抗(EIS)技术,通过双电极叠片ACM电池,考察了新型吗啉类气相缓蚀剂HJ-20-2的吸附行为和成膜方式。结果表明,经HJ-20-2气相缓蚀剂预膜的电极,电荷转移电阻力5.88kΩ/cm^2,表观双电层电容为190.1μF/cm^2。HJ-20-2气相缓蚀剂和吗啉相比,在电极表面具有较大的吸附能力和覆盖面积,从而具有较好的缓蚀能力。

一种新型气相防锈纸的研制

一般的气相防锈纸具有防锈期短、强度低、易破裂、不防潮、不耐水等缺点。作者研制的新型气相防锈纸,不仅防锈期长,还提高了纸的柔韧性能和强度,另外还防潮、防水等。通过静态纸上不接触法进行了防锈试验,结果表明该防锈纸防锈效果良好,能够对所包装的金属产品进行长期的防锈。

吗啉衍生物气相缓蚀剂的分子设计和缓蚀协同作用研究

采用Pcmodel分子力学程序和PM3半经验量子化学计算法,对新型吗啉衍生物气相缓蚀的分子设计过程进行了讨论.结果表明:通过分子内的亚甲基链把吗啉和二环己胺分子连接起来,合成吗啉Mannish碱衍生物N,N-二环己基胺甲基吗啉,可以在碳钢表面形成多中心的吸附,具有较高的EHOMO和较低的ELUMO,提高了N,N-二环己基胺甲基吗啉在金属表面的覆盖程度以及与金属的键合强度.当向N,N-二环己基胺甲基吗啉引入苯甲酸根阴离子后,整个体系的EHOMO进一步升高,ELUMO进一步降低,该复配体系和钢铁成键更稳定,从而使其气相缓蚀能力得到进一步的增强.

蒙脱土改性气相缓蚀剂的制备及性能研究

采用蒙脱土对吗啉类气相缓蚀剂进行改性,通过气相防锈甄别试验和气相缓蚀能力试验,对改性气相缓蚀剂进行了防锈性能评定,结果表明,蒙脱土的引入增强了气相缓蚀剂的缓蚀能力。密闭空间挥发减重试验表明,改性气相缓蚀剂的挥发能力有所提高。模拟大气腐蚀水的电化学极化曲线表明,蒙脱土的引入进一步增大了对阳极和阴极电化学过程的抑制作用。

金属气相防锈技术的应用进展

综述了金属气相防锈技术的发展过程、应用类型和应用状况,对其技术发展前景进行了展望。

有机蒙脱土的制备及对气相缓蚀剂的改性

用十六烷基三甲基溴化铵(CTAB)、蒙脱土为原料,在80℃搅拌混合1 h,制备了有机蒙脱土。在吗啉类气相缓蚀剂合成过程中,通过添加有机蒙脱土对其进行改性,有机蒙脱土和吗啉的质量比为0.9∶20,反应时间为5h,反应温度为50℃。用密闭空间挥发减重实验、气相防锈甄别实验和气相缓蚀能力实验对改性气相缓蚀剂的性能进行了测定,结果表明,有机蒙脱土改性气相缓蚀剂的72 h密闭空间挥发失重率增加到2.5%,对碳钢的缓蚀率为94.3%。模拟大气腐蚀水的电化学极化曲线表明,当有机蒙脱土改性气相缓蚀剂的质量分数为0.5%时,将导致碳钢电极腐蚀电位正移至-0.547 8 V,腐蚀电流密度降低为4.475μA.cm-2,有机蒙脱土改善了吗啉类气相缓蚀剂的挥发能力和缓蚀性能。

气相缓蚀剂的研究现状及发展趋势

综述了国内外气相缓蚀剂的发展历程,阐述了气相缓蚀剂的作用原理、应用形式及评价方法,对气相缓蚀剂的发展趋势进行了展望。

一种可喷涂于包装材料上水性气相防锈涂料的研制

介绍了一种应用于包装材料上水性气相防锈涂料的研制 ,提出了该涂料的最佳配方 ,对该涂料的防锈效果进行了加速试验、实地试验 ,结果表明本水性气相防锈涂料的防锈效果优良 ,应用于包装材料上 。

复合气相缓蚀剂对纯铜缓蚀的研究

铜应用广泛,但在湿度较高的腐蚀性介质中其易被腐蚀,采用苯骈三氮唑(BTA)和酚类W制成一种新型复合气相缓蚀剂,采用原子分光光度计和电化学测试方法、扫描电镜和激光拉曼显微镜研究了该复合气相缓蚀剂对纯铜的缓蚀性能及其缓蚀机理。结果表明,该复合气相缓蚀剂在铜表面形成的膜是一种自组装缓蚀膜,具有很好的防蚀和拒水性能。

薄层电解液中气相缓蚀剂对碳钢腐蚀和缓蚀行为的影响

采用电化学极化曲线和电化学阻抗技术,研究了薄层电解液中碳钢的腐蚀行为和吗啉缓蚀剂对它的缓蚀作用.结果表明,300μm的薄层电解液下碳钢电极的阳极极化曲线和阴极极化曲线呈现扩散控制特征,其腐蚀速度比溶液中碳钢电极的腐蚀速度增加.薄层电解液中缓蚀剂的加入,降低了碳钢电极的电化学极化曲线上的阴极和阳极的扩散电流密度,使碳钢电极的电化学阻抗谱上出现感抗弧,表明缓蚀剂在碳钢表面发生了吸附,阻止了阴极还原的氧扩散以及阳极腐蚀产物的迁移.

一种新型气相防锈吸湿剂

气相防锈技术是近年来应用于金属防锈方面的一项新技术。采用气相缓蚀剂、膨润土和氯化钙制备了一种气相防锈吸湿剂。通过防锈和吸湿性能试验,表明本产品不仅具有气相防锈的性能,还具有良好的吸湿性能,可以广泛应用于湿度比较大的环境中金属产品的防锈。