A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%,...A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.展开更多
NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material.Depending on the speci...NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material.Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure.Moreover it enables the determination of moisture transport properties and the(re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing.However,as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale(<10 mL)samples.This paper describes the capabilities of an NMR tomograph,which has been specifically optimized for the investigation of larger,heterogeneous building material samples(diameters of up to 72 mm,length of up to 700 mm)with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times(50-80 ms).展开更多
基金Funded by the National Natural Science Foundation of China(No.51878081).
文摘A high strength self-compacting pervious concrete(SCPC) with top-bottom interconnected pores was prepared in this paper. The frost-resisting durability of such SCPC in different deicing salt concentrations(0%, 3%, 5%, 10%, and 20%) was investigated. The mass-loss rate, relative dynamic modulus of elasticity, compressive strength, flexural strength and hydraulic conductivity of SCPC after 300 freeze-thaw cycles were measured to evaluate the frost-resisting durability. In addition, the microstructures of SCPC near the top-bottom interconnected pores after 300 freeze-thaw cycles were observed by SEM. The results show that the high strength SCPC possesses much better frost-resisting durability than traditional pervious concrete(TPC) after 300 freeze-thaw cycles, which can be used in heavy loading roads. The most serious freeze-thaw damage emerges in the SCPC immersed in the 3% of Na Cl solution, while there is no obvious damage in 20% of Na Cl solution. Furthermore, it can be deduced that the high strength SCPC can be used for 100 years in a cold environment.
文摘NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material.Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure.Moreover it enables the determination of moisture transport properties and the(re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing.However,as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale(<10 mL)samples.This paper describes the capabilities of an NMR tomograph,which has been specifically optimized for the investigation of larger,heterogeneous building material samples(diameters of up to 72 mm,length of up to 700 mm)with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times(50-80 ms).