In order to produce the hear-resistant inner layer of hot-forging die, the plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% tungst...In order to produce the hear-resistant inner layer of hot-forging die, the plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% tungsten carbide （WC） ceramic powder used as coating material to obtain different Nickel-based WC alloys coating. Micro-structure and micro-hardness analysis of the coating layer are conducted, as well as thermophysical properties for the coating layer were measured. The experimental results show that the coating prepared with 70%Ni60, 30%WC powder has the best properties with plasma spray welding, in which the micro-hardness can achieve 900HV, meanwhile it can improve the thermal property of hot-forging die dramatically.展开更多
In order to produce the hear-resistant inner layer of hot-forging die, plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% SiC cerami...In order to produce the hear-resistant inner layer of hot-forging die, plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% SiC ceramic powder used as coating material to obtain different Ni-based SiC alloys coating. Micro-structure and micro-hardness analysis of the coating layer were followed, as well as thermophysical properties for the coating layer were measured. The experimental results show that the coating prepared with 70% Ni60, 30% SiC powder has best properties with plasma spray welding, in which the micro-hardness can achieve 1100 HV, meanwhile can improve the thermal property of hot-forging die dramatically.展开更多
In order to prepare heatresistant inner layer of hot-forging die, plasma spraying, plasma re- melting and plasma spray welding were adopted. Cr3C2 coatings of Ni-Based were prepared respectively with 10%, 20% and 30% ...In order to prepare heatresistant inner layer of hot-forging die, plasma spraying, plasma re- melting and plasma spray welding were adopted. Cr3C2 coatings of Ni-Based were prepared respectively with 10%, 20% and 30% Cr3C2 powder and W6Mo5Cr4V2 substrate. The coating microstructure analysis, the micro-hardness test, and the measurement of thermal parameters of coating were conducted. The experimental results show that the coating has the better thermo-physical property by using plasma spray welding method with the powder ratio of 90% Ni60 and 10% Cr3C2, and by this way the micro-hardness of coating can achieve 1100 HV.展开更多
A multi-functional micro-arc plasma spraying system was developed according to aerodynamics and plasma spray theory. The soft switch IGBT （Insulated Gate Bipolar Transistor） invert technique, micro-computer control ...A multi-functional micro-arc plasma spraying system was developed according to aerodynamics and plasma spray theory. The soft switch IGBT （Insulated Gate Bipolar Transistor） invert technique, micro-computer control technique, convergent-divergent nozzle structure and axial powder feeding techniques have been adopted in the design of the micro-arc plasma spraying system. It is not only characterized by a small volume, a light weight, highly accurate control, high deposition efficiency and high reliability, but also has multi-functions in plasma spraying, welding and quenching. The experimental results showed that the system can produce a supersonic flame at a low power, spray Al2O3 particles at an average speed up to 430 m/s, and make nanostructured AT13 coatings with an average bonding strength of 42.7 MPa. Compared to conventional 9M plasma spraying with a higher power, the coatings with almost the same properties as those by conventional plasma spray can be deposited by multi-functional micro-arc plasma spraying with a lower power plasma arc due to an improved power supply design, spray gun structure and powder feeding method. Moreover, this system is suitable for working with thin parts and undertaking on site repairs, and as a result, the application of plasma spraying will be greatly extended.展开更多
The NiCrBSi/WC biomimetic coatings were prepared on the low carbon steel substrate by plasma spray welding with mixed powders （WC-Col2＋NiCrBSi） based on the bionic principles, and the coating characteristics were i...The NiCrBSi/WC biomimetic coatings were prepared on the low carbon steel substrate by plasma spray welding with mixed powders （WC-Col2＋NiCrBSi） based on the bionic principles, and the coating characteristics were investigated. The results indicate that the coatings have a full metallurgical bond in coating/substrate interface, and consist mainly ofy-Ni, WC, Cr23C6, Cr7C3, Ni3Si, CrsB3, and FeNi3 phases. The powder composition influences the microstructures and properties of the coatings. The WC content and the hardness of coatings increase with the mass fraction of WC-Co 12 powder. The biomimetic coatings have much higher wear resistance compared with the low carbon steel, which is attributed to the combination of hard WC and chromium carbide particles （bionic units） and soft y-Ni matrix in the coatings. It is favorable to prepare the biomimetic coating by plasma spray welding with the mixed powders （20wt%WC-Col2＋80wt%NiCrBSi） for improving the wear resis- tance of the coating.展开更多
基金Funded by the National Natural Science Foundation of China(No.50675165)the National Key Technology R&D Program(No.2006BAF02A29)
文摘In order to produce the hear-resistant inner layer of hot-forging die, the plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% tungsten carbide （WC） ceramic powder used as coating material to obtain different Nickel-based WC alloys coating. Micro-structure and micro-hardness analysis of the coating layer are conducted, as well as thermophysical properties for the coating layer were measured. The experimental results show that the coating prepared with 70%Ni60, 30%WC powder has the best properties with plasma spray welding, in which the micro-hardness can achieve 900HV, meanwhile it can improve the thermal property of hot-forging die dramatically.
基金Funded by the National Natural Science Foundation of China (No. 50675165)
文摘In order to produce the hear-resistant inner layer of hot-forging die, plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% SiC ceramic powder used as coating material to obtain different Ni-based SiC alloys coating. Micro-structure and micro-hardness analysis of the coating layer were followed, as well as thermophysical properties for the coating layer were measured. The experimental results show that the coating prepared with 70% Ni60, 30% SiC powder has best properties with plasma spray welding, in which the micro-hardness can achieve 1100 HV, meanwhile can improve the thermal property of hot-forging die dramatically.
文摘In order to prepare heatresistant inner layer of hot-forging die, plasma spraying, plasma re- melting and plasma spray welding were adopted. Cr3C2 coatings of Ni-Based were prepared respectively with 10%, 20% and 30% Cr3C2 powder and W6Mo5Cr4V2 substrate. The coating microstructure analysis, the micro-hardness test, and the measurement of thermal parameters of coating were conducted. The experimental results show that the coating has the better thermo-physical property by using plasma spray welding method with the powder ratio of 90% Ni60 and 10% Cr3C2, and by this way the micro-hardness of coating can achieve 1100 HV.
文摘A multi-functional micro-arc plasma spraying system was developed according to aerodynamics and plasma spray theory. The soft switch IGBT （Insulated Gate Bipolar Transistor） invert technique, micro-computer control technique, convergent-divergent nozzle structure and axial powder feeding techniques have been adopted in the design of the micro-arc plasma spraying system. It is not only characterized by a small volume, a light weight, highly accurate control, high deposition efficiency and high reliability, but also has multi-functions in plasma spraying, welding and quenching. The experimental results showed that the system can produce a supersonic flame at a low power, spray Al2O3 particles at an average speed up to 430 m/s, and make nanostructured AT13 coatings with an average bonding strength of 42.7 MPa. Compared to conventional 9M plasma spraying with a higher power, the coatings with almost the same properties as those by conventional plasma spray can be deposited by multi-functional micro-arc plasma spraying with a lower power plasma arc due to an improved power supply design, spray gun structure and powder feeding method. Moreover, this system is suitable for working with thin parts and undertaking on site repairs, and as a result, the application of plasma spraying will be greatly extended.
文摘The NiCrBSi/WC biomimetic coatings were prepared on the low carbon steel substrate by plasma spray welding with mixed powders （WC-Col2＋NiCrBSi） based on the bionic principles, and the coating characteristics were investigated. The results indicate that the coatings have a full metallurgical bond in coating/substrate interface, and consist mainly ofy-Ni, WC, Cr23C6, Cr7C3, Ni3Si, CrsB3, and FeNi3 phases. The powder composition influences the microstructures and properties of the coatings. The WC content and the hardness of coatings increase with the mass fraction of WC-Co 12 powder. The biomimetic coatings have much higher wear resistance compared with the low carbon steel, which is attributed to the combination of hard WC and chromium carbide particles （bionic units） and soft y-Ni matrix in the coatings. It is favorable to prepare the biomimetic coating by plasma spray welding with the mixed powders （20wt%WC-Col2＋80wt%NiCrBSi） for improving the wear resis- tance of the coating.