For the crystalline temperature of BaSnO_(3)(BTO)was above 650℃,the transparent conductive BTO-based films were always deposited above this temperature on epitaxy substrates by pulsed laser deposition or molecular be...For the crystalline temperature of BaSnO_(3)(BTO)was above 650℃,the transparent conductive BTO-based films were always deposited above this temperature on epitaxy substrates by pulsed laser deposition or molecular beam epitaxy till now which limited there application in low temperature device process.In the article,the microstructure,optical and electrical of BTO and In_(2)O_(3) mixed transparent conductive BaInSnO_(x)(BITO)film deposited by filtered cathodic vacuum arc technique(FCVA)on glass substrate at room temperature were firstly reported.The BITO film with thickness of 300 nm had mainly In_(2)O_(3) polycrystalline phase,and minor polycrystalline BTO phase with(001),(011),(111),(002),(222)crystal faces which were first deposited at room temperature on amorphous glass.The transmittance was 70%–80%in the visible light region with linear refractive index of 1.94 and extinction coefficient of 0.004 at 550-nm wavelength.The basic optical properties included the real and imaginary parts,high frequency dielectric constants,the absorption coefficient,the Urbach energy,the indirect and direct band gaps,the oscillator and dispersion energies,the static refractive index and dielectric constant,the average oscillator wavelength,oscillator length strength,the linear and the third-order nonlinear optical susceptibilities,and the nonlinear refractive index were all calculated.The film was the n-type conductor with sheet resistance of 704.7Ω/□,resistivity of 0.02Ω⋅cm,mobility of 18.9 cm2/V⋅s,and carrier electron concentration of 1.6×10^(19) cm^(−3) at room temperature.The results suggested that the BITO film deposited by FCVA had potential application in transparent conductive films-based low temperature device process.展开更多
Highly conductive and transparent Al-doped ZnO (AZO) thin films were prepared from a zinc target containing Al (1.5 wt.%) by direct current (DC) and radio frequency (RF) reactive magnetron sputtering. The stru...Highly conductive and transparent Al-doped ZnO (AZO) thin films were prepared from a zinc target containing Al (1.5 wt.%) by direct current (DC) and radio frequency (RF) reactive magnetron sputtering. The structural, optical, and electrical properties of AZO films as-deposited and submitted to annealing treatment (at 300 and 400℃, respectively) were characterized using various techniques. The experimental results show that the properties of AZO thin films can be further improved by annealing treatment. The crystallinity of ZnO films improves after annealing treatment. The transmittances of the AZO thin films prepared by DC and RF reactive magnetron sputtering are up to 80% and 85% in the visible region, respectively. The electrical resistivity of AZO thin films prepared by DC reactive magnetron sputtering can be as low as 8.06 x 10-4 Ωcm after annealing treatment. It was also found that AZO thin films prepared by RF reactive magnetron sputtering have better structural and optical properties than that prepared by DC reactive magnetron sputtering.展开更多
Zinc oxide (ZnO) thin films were deposited on sapphire (0001) substrates at room temperature by radiofrequency (RF) magnetron sputtering at oxygen gas contents of 0%, 25%, 50% and 75%, respectively. The influenc...Zinc oxide (ZnO) thin films were deposited on sapphire (0001) substrates at room temperature by radiofrequency (RF) magnetron sputtering at oxygen gas contents of 0%, 25%, 50% and 75%, respectively. The influence of oxygen gas content on the structural and optical properties of ZnO thin films was studied by a surface profile measuring system, X-ray diffraction analysis, atomic force microscopy, and UV spectro- photometry. It is found that the size of ZnO crystalline grains increases first and then decreases with the increase of oxygen gas content, and the maximum grain size locates at the 25% oxygen gas content. The crystalline quality and average optical transmittance (〉90%) in the visi- ble-light region of the ZnO film prepared at an oxygen gas content of 25% are better than those of ZnO films at the other contents. The obtained results can be attributed to the resputtefing by energetic oxygen anions in the growing process.展开更多
A simple method to tune the optical properties of porous anodic alumina (PAA) films embedded with Co nanowires (PAA@Co nanocomposite films) is reported in this paper. The films exhibit vivid structural colors and ...A simple method to tune the optical properties of porous anodic alumina (PAA) films embedded with Co nanowires (PAA@Co nanocomposite films) is reported in this paper. The films exhibit vivid structural colors and magnetic properties. The optical properties of the films can be effectively tuned by adjusting the thickness of the PAA template. The deposition of Co nanowires greatly increases the color saturation of the PAA films. The theoretical results of the changes in structural color according to the Bragg-Snell formula are consistent with the experimental results. PAA@Co films can be used in many areas, including decoration, display, and multifunctional anti-counterfeiting applications.展开更多
TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, hi...TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, high dielectric constant, wide band gap, high wear resistance and stability, etc, for which make it being used in many fields. This paper aims to investigate the optical characterizatio n of thin film TiO2 on silicon wafer. The TiO2 thin films were prepared by DC re active magnetron sputtering process from Ti target. The reflectivity of the film s was measured by UV-3101PC, and the index of refraction (n) and extinction coef ficient (k) were measured by n & k Analyzer 1200.展开更多
Thin oxidized copper films in various thickness values are deposited onto quartz glass substrates by electron beam evaporation. The ellipsometry parameters and transmittance in a wavelength range of 300 nm-1000 nm are...Thin oxidized copper films in various thickness values are deposited onto quartz glass substrates by electron beam evaporation. The ellipsometry parameters and transmittance in a wavelength range of 300 nm-1000 nm are collected by a spectroscopic ellipsometer and a spectrophotometer respectively. The effective thickness and optical constants, i.e., refractive index n and extinction coefficient k, are accurately determined by using newly developed ellipsometry combined with transmittance iteration method. It is found that the effective thickness determined by this method is close to the physical thickness and has obvious difference from the mass thickness for very thin film due to variable density of film. Furthermore, the thickness dependence of optical constants of thin oxidized Cu films is analyzed.展开更多
The Al film reflectors can yield a high-reflectance over a broad wavelength region, and have been widely used in the spacecraft optical instruments for high quality optical applications. Under the irradiation of charg...The Al film reflectors can yield a high-reflectance over a broad wavelength region, and have been widely used in the spacecraft optical instruments for high quality optical applications. Under the irradiation of charged particles in the Earth radiation belt, the reflectors could be deteriorated. In order to reveal the deterioration mechanism, the change in optical constants of Al film reflector induced by proton radiation with 60 keV was studied in an environment of vacuum with heat sink. Experimental results showed that when the radiation damage primarily occurs in the Al reflecting film, the extinction coefficient k will gradually decrease with increasing radiation fluence, which results in the decrease of the energies of reflective light. Therefore, the proton radiation induced an obvious degradation of spectral reflectance in the wavelength region from 200 to 800nm on the Al film reflector.展开更多
The effect of different annealing temperatures on the structure, morphology,and optical properties of ZnO thin films prepared by the chelating sol-gel method was investigated.Zinc-oxide thin films were coated on quart...The effect of different annealing temperatures on the structure, morphology,and optical properties of ZnO thin films prepared by the chelating sol-gel method was investigated.Zinc-oxide thin films were coated on quartz glass substrates by dip coating. Zinc nitrate, absoluteethanol, and citric acid were used as precursor, solvent, and chelating agent, respectively. Theresults show that ZnO films derived from zinc-citrate have lower crystallization temperature (below400℃), and that the crystal structure is wurtzite. The films, treated over 500℃, consist ofnano-particles and show to be porous at 600℃. The particle size of the film increases with theincrease of the annealing temperature. The largest particle size is 60 nm at 600℃. The opticaltransmittances related to the annealing temperatures become 90% higher in the visible range. Thefilm shows a starting absorption at 380 nm, and the optical band-gap of the thin film (fired at500℃) is 3.25 eV and close to the intrinsic band-gap of ZnO (3.2 eV).展开更多
A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichl...A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichloro ruthenium(II)hexahydrate(Ru(bpy)3Cl2)as the fluorescence indicator and iron(III)tetrasulfophthalocyanine(Fe(III)PcTs)as bionic enzyme.A lock-in amplifier was used for detecting the lifetime of the composite oxygen-sensitive film by measuring the phase delay of the sensor head.The different variables affecting the sensor performance were evaluated and optimized.Under the optimal conditions(i e,pH 6.0,25℃,Fe(III)PcTs concentration of 5.0×10^-5 mol/L),the linear detection range,detection limit and response time of the fiber optic sensor are 3.0×10^-7-9.0×10^-5 mol/L,4.8×10^-8 mol/L(S/N=3),and 220 s,respectively.The sensor displays high selectivity,good repeatability and stability,which have good potentials in analyzing DCP concentration in practical water samples.展开更多
γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films w...γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films were investigated.Scanning electron microscope(SEM) photos revealed that the shape and grain size of CuI grains were related to substrate temperature.X-ray diffraction results showed that substrate temperature affected the crystalline quality of CuI films.When the substrate temperature was 110°C,CuI thin films showed γ-phase zinkblende structure with(111) preferred orientation.The dimension of the globular CuI crystallite was approximately 35 nm,the energy band gap was 2.97 eV,the maximum transmittance was 87.3% in the part of the visible region,and the open circuit voltage was close to 380 mV.This opened a route for a cadmium-free buffer layer for CuInS2 solar cells.展开更多
Erbium doped BaTiO 3 optical-waveguide films on Pyrex substrate was elaborated successfully through sol-gel method. BaTiO 3 is well crystallized when the film is annealed at 650 ℃ in air circumstance. The so-prepar...Erbium doped BaTiO 3 optical-waveguide films on Pyrex substrate was elaborated successfully through sol-gel method. BaTiO 3 is well crystallized when the film is annealed at 650 ℃ in air circumstance. The so-prepared films with 13 layers have comparatively lower refractive index than bulk BaTiO 3, and it can support two TM and TE modes. Photoluminescence and up-conversion luminescence spectra proved the successful doping of rare earth ions.展开更多
Tungsten oxide thin films were deposited on glass substrates by the magnetron sputtering of WO3 bulk at room temperature. The deposited films were annealed at different temperatures in air. The structural measurements...Tungsten oxide thin films were deposited on glass substrates by the magnetron sputtering of WO3 bulk at room temperature. The deposited films were annealed at different temperatures in air. The structural measurements indicate that the films annealed below 300℃ were amorphous, while the films annealed at 400 ℃ were mixed crystalline with hexagonal and triclinic phases of WO3. It was observed that the crystallization of the annealed films becomes more and more distinct with an increase in the annealing temperature. At 400 ℃, nanorod-like structures were observed on the film surface when the annealing time was increased from 60 min to 180 min. The presence of W=O stretching, W-O-W stretching, W-O-W bending and various lattice vibration modes were observed in Raman measurements. The optical absorption behaviors of the films in the range of 450-800 nm are very different with changing annealing temperatures from the room temperature to 400 ℃. After annealing at 400 ℃, the film becomes almost transparent. Increasing annealing time at 400 ℃ can lead to a small blue shift of the optical gap of the film.展开更多
The optical properties of hexagonal boron nitride (h-BN) thin films were studied in this paper. The films were characterized by Fourier transform infrared spectroscopy, UV-visible transmittance and reflection spectr...The optical properties of hexagonal boron nitride (h-BN) thin films were studied in this paper. The films were characterized by Fourier transform infrared spectroscopy, UV-visible transmittance and reflection spectra, h-BN thin films with a wide optical band gap Eg (5.86 eV for the as-deposited film and 5.97 eV for the annealed film) approaching h-BN single crystal were successfully prepared by radio frequency (RF) bias magnetron sputtering and post-deposition annealing at 970 K. The optical absorption behaviour of h-BN films accords with the typical optical absorption characteristics of amorphous materials when fitting is made by the Urbach tail model. The annealed film shows satisfactory structure stability. However, high temperature still has a significant effect on the optical absorption properties, refractive index n, and optical conductivity σ of h-BN thin films. The blue-shift of the optical absorption edge and the increase of Eg probably result from stress relaxation in the film under high temperatures. In addition, it is found that the refractive index clearly exhibits different trends in the visible and ultraviolet regions. Previous calculational results of optical conductivity of h-BN films are confirmed in our experimental results.展开更多
Indium-doped ZnO thin films are deposited on quartz glass slides by RF magnetron sputtering at ambient temperature. The as-deposited films are annealed at different temperatures from 400℃ to 800 ℃ in air for 1 h. Tr...Indium-doped ZnO thin films are deposited on quartz glass slides by RF magnetron sputtering at ambient temperature. The as-deposited films are annealed at different temperatures from 400℃ to 800 ℃ in air for 1 h. Transmittance spectra are used to determine the optical parameters and the thicknesses of the films before and after annealing using a nonlinear programming method, and the effects of the annealing temperatures on the optical parameters and the thickness are investigated. The optical band gap is determined from the absorption coefficient. The calculated results show that the film thickness and optical parameters both increase first and then decrease with increasing annealing temperature from 400℃ to 800℃. The band gap of the as-deposited ZnO:In thin film is 3.28 eV, and it decreases to 3.17 eV after annealing at 400℃. Then the band gap increases from 3.17 eV to 3.23 eV with increasing annealing temperature from 400℃ to 800℃.展开更多
Cadmium sulphide (CdS) thin films were deposited on glass substrates by the chemical bath deposition (CBD) method, using anhydrous cadmium chloride (CdCl2) and thiourea (CS(NH2)2) as sources of cadmium and sulphur ion...Cadmium sulphide (CdS) thin films were deposited on glass substrates by the chemical bath deposition (CBD) method, using anhydrous cadmium chloride (CdCl2) and thiourea (CS(NH2)2) as sources of cadmium and sulphur ions respectively. The influence of bath temperature (Tb), deposition time (td) aSnd [S]/[Cd] ratio in the solution on the structural, morphological, chemical composition and optical properties of these films were investigated. XRD studies revealed that all the deposited films were polycrystalline with hexagonal structure and exhibited (002) preferential orientation. The films deposited under optimum conditions (Tb = 75?C, td = 60 min and [S]/[Cd] ratio = 2.5) were relatively well crystallized. These films showed large final thickness and their surface morphologies were composed of small grains with an approximate size of 20 to 30 nm and grains grouped together to form large clusters. EDAX analysis revealed that these films were nonstoichiometric with a slight sulphur deficiency. These films exhibited also a transmittance value about 80% in the visible and infra red range.展开更多
We investigated the effect of annealing process on microstructures and optical properties of the sol-gel derived Ba0.9Sr0.1TiO3 (BST) films. The BST films, fabricated by layer-by-layer high-temperature (≥ 650 ℃)...We investigated the effect of annealing process on microstructures and optical properties of the sol-gel derived Ba0.9Sr0.1TiO3 (BST) films. The BST films, fabricated by layer-by-layer high-temperature (≥ 650 ℃) annealing process, had laminated structures consisting of alternating dense and porous BST layers, and exhibited excellent optical performance as Bragg reflectors. The Bragg reflection characteristic can be enhanced with increasing annealing temperature. Those BST films fabricated at temperatures lower than 650 ℃ displayed uniform cross-sectional morphologies even treated at a higher temperature. The difference in the microstructures of the BST thin films was also discussed.展开更多
Na-doped ZnO thin films were deposited on the glass substrates using sol-gel method. The effect of Na concentrations on the structural and optical properties of ZnO films was studied. As Na concentration increases fro...Na-doped ZnO thin films were deposited on the glass substrates using sol-gel method. The effect of Na concentrations on the structural and optical properties of ZnO films was studied. As Na concentration increases from 0.0 at% to 16.0 at%, preferential c-axis orientation becomes more and more obvious, and the intensity of the diffraction peaks from (103) increases. The optical band gap Eg value increases from 3.261 to 3.286 eV first and then decreases as Na concentration increases from 0.0 to 2.0 at% and then beyond 2.0 at%. The intensity of all the emissions increases with increasing Na concentration and the origins of the violet emission (wavelength in the 400-407 nm) and the blue emission (wavelength at 473 nm) were discussed in detail.展开更多
基金Project supported by the Enterprise Science and Technology Correspondent for Guangdong Province,China (Grant No.GDKTP2021015200)。
文摘For the crystalline temperature of BaSnO_(3)(BTO)was above 650℃,the transparent conductive BTO-based films were always deposited above this temperature on epitaxy substrates by pulsed laser deposition or molecular beam epitaxy till now which limited there application in low temperature device process.In the article,the microstructure,optical and electrical of BTO and In_(2)O_(3) mixed transparent conductive BaInSnO_(x)(BITO)film deposited by filtered cathodic vacuum arc technique(FCVA)on glass substrate at room temperature were firstly reported.The BITO film with thickness of 300 nm had mainly In_(2)O_(3) polycrystalline phase,and minor polycrystalline BTO phase with(001),(011),(111),(002),(222)crystal faces which were first deposited at room temperature on amorphous glass.The transmittance was 70%–80%in the visible light region with linear refractive index of 1.94 and extinction coefficient of 0.004 at 550-nm wavelength.The basic optical properties included the real and imaginary parts,high frequency dielectric constants,the absorption coefficient,the Urbach energy,the indirect and direct band gaps,the oscillator and dispersion energies,the static refractive index and dielectric constant,the average oscillator wavelength,oscillator length strength,the linear and the third-order nonlinear optical susceptibilities,and the nonlinear refractive index were all calculated.The film was the n-type conductor with sheet resistance of 704.7Ω/□,resistivity of 0.02Ω⋅cm,mobility of 18.9 cm2/V⋅s,and carrier electron concentration of 1.6×10^(19) cm^(−3) at room temperature.The results suggested that the BITO film deposited by FCVA had potential application in transparent conductive films-based low temperature device process.
基金the Program for New Century Excellent Talents in Universities, MOE, China (No. NCET-05-0764)the Tackle Key Problems on Scientific Technology Foundation of Chongqing Municipality (Nos. CSTC2005AA4006-A6 and CSTC2004AC4034)+2 种基金the Natural Science Foundation of Chongqing Municipality (No. CSTC2005BA4016)China Postdoctoral Science Foundation (No. 2005037544)the Inno-base for Graduates of Chongqing University (No. 200506Y1B0240131).
文摘Highly conductive and transparent Al-doped ZnO (AZO) thin films were prepared from a zinc target containing Al (1.5 wt.%) by direct current (DC) and radio frequency (RF) reactive magnetron sputtering. The structural, optical, and electrical properties of AZO films as-deposited and submitted to annealing treatment (at 300 and 400℃, respectively) were characterized using various techniques. The experimental results show that the properties of AZO thin films can be further improved by annealing treatment. The crystallinity of ZnO films improves after annealing treatment. The transmittances of the AZO thin films prepared by DC and RF reactive magnetron sputtering are up to 80% and 85% in the visible region, respectively. The electrical resistivity of AZO thin films prepared by DC reactive magnetron sputtering can be as low as 8.06 x 10-4 Ωcm after annealing treatment. It was also found that AZO thin films prepared by RF reactive magnetron sputtering have better structural and optical properties than that prepared by DC reactive magnetron sputtering.
基金supported by the National Natural Science Foundation of China (Nos. 60876055 and11074063)the Natural Science foundation of Hebei Province,China (Nos. E2008000620 and E2009000207)+1 种基金the Specialized Research Fund for the Doctoral Program of Higher Education of China (No. 20091301110002)the Key Basic Research Program of Hebei Provincial Applied Basic Research Plan (No. 10963525D)
文摘Zinc oxide (ZnO) thin films were deposited on sapphire (0001) substrates at room temperature by radiofrequency (RF) magnetron sputtering at oxygen gas contents of 0%, 25%, 50% and 75%, respectively. The influence of oxygen gas content on the structural and optical properties of ZnO thin films was studied by a surface profile measuring system, X-ray diffraction analysis, atomic force microscopy, and UV spectro- photometry. It is found that the size of ZnO crystalline grains increases first and then decreases with the increase of oxygen gas content, and the maximum grain size locates at the 25% oxygen gas content. The crystalline quality and average optical transmittance (〉90%) in the visi- ble-light region of the ZnO film prepared at an oxygen gas content of 25% are better than those of ZnO films at the other contents. The obtained results can be attributed to the resputtefing by energetic oxygen anions in the growing process.
基金supported by the Natural Science Foundation of Hebei Province,China(Grant No.A2012205038)
文摘A simple method to tune the optical properties of porous anodic alumina (PAA) films embedded with Co nanowires (PAA@Co nanocomposite films) is reported in this paper. The films exhibit vivid structural colors and magnetic properties. The optical properties of the films can be effectively tuned by adjusting the thickness of the PAA template. The deposition of Co nanowires greatly increases the color saturation of the PAA films. The theoretical results of the changes in structural color according to the Bragg-Snell formula are consistent with the experimental results. PAA@Co films can be used in many areas, including decoration, display, and multifunctional anti-counterfeiting applications.
基金This work was supported by the National Natural Science Foundation of China(No,50376067)the Plan for Science&Technology Development of Guangzhou(2001-Z-117-01).
文摘TiO2 thin film has attracted considerable attention in recent years, due to its different refractive index and transparency with amorphous and different crysta ls in the visible and near-infrared wavelength region, high dielectric constant, wide band gap, high wear resistance and stability, etc, for which make it being used in many fields. This paper aims to investigate the optical characterizatio n of thin film TiO2 on silicon wafer. The TiO2 thin films were prepared by DC re active magnetron sputtering process from Ti target. The reflectivity of the film s was measured by UV-3101PC, and the index of refraction (n) and extinction coef ficient (k) were measured by n & k Analyzer 1200.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11074232,10874160,and 21002097)the National Basic Research Program of China(Grant Nos.2011CB932801 and 2012CB933702)
文摘Thin oxidized copper films in various thickness values are deposited onto quartz glass substrates by electron beam evaporation. The ellipsometry parameters and transmittance in a wavelength range of 300 nm-1000 nm are collected by a spectroscopic ellipsometer and a spectrophotometer respectively. The effective thickness and optical constants, i.e., refractive index n and extinction coefficient k, are accurately determined by using newly developed ellipsometry combined with transmittance iteration method. It is found that the effective thickness determined by this method is close to the physical thickness and has obvious difference from the mass thickness for very thin film due to variable density of film. Furthermore, the thickness dependence of optical constants of thin oxidized Cu films is analyzed.
基金financially supported by the National Natural Science Foundation of China (No. 50902006)the National High Technology Development 863 Program of China (No. 2009AA03Z428)National Student Innovative Experiment Plan
文摘The Al film reflectors can yield a high-reflectance over a broad wavelength region, and have been widely used in the spacecraft optical instruments for high quality optical applications. Under the irradiation of charged particles in the Earth radiation belt, the reflectors could be deteriorated. In order to reveal the deterioration mechanism, the change in optical constants of Al film reflector induced by proton radiation with 60 keV was studied in an environment of vacuum with heat sink. Experimental results showed that when the radiation damage primarily occurs in the Al reflecting film, the extinction coefficient k will gradually decrease with increasing radiation fluence, which results in the decrease of the energies of reflective light. Therefore, the proton radiation induced an obvious degradation of spectral reflectance in the wavelength region from 200 to 800nm on the Al film reflector.
基金This work was financially supported by the Natural Science Foundation of Tianjin (No. 33802311)
文摘The effect of different annealing temperatures on the structure, morphology,and optical properties of ZnO thin films prepared by the chelating sol-gel method was investigated.Zinc-oxide thin films were coated on quartz glass substrates by dip coating. Zinc nitrate, absoluteethanol, and citric acid were used as precursor, solvent, and chelating agent, respectively. Theresults show that ZnO films derived from zinc-citrate have lower crystallization temperature (below400℃), and that the crystal structure is wurtzite. The films, treated over 500℃, consist ofnano-particles and show to be porous at 600℃. The particle size of the film increases with theincrease of the annealing temperature. The largest particle size is 60 nm at 600℃. The opticaltransmittances related to the annealing temperatures become 90% higher in the visible range. Thefilm shows a starting absorption at 380 nm, and the optical band-gap of the thin film (fired at500℃) is 3.25 eV and close to the intrinsic band-gap of ZnO (3.2 eV).
基金Funded by the National Natural Science Foundation of China(No.61205062)the Scientific Research Foundation for Doctor of University(No.2019Y02)。
文摘A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichloro ruthenium(II)hexahydrate(Ru(bpy)3Cl2)as the fluorescence indicator and iron(III)tetrasulfophthalocyanine(Fe(III)PcTs)as bionic enzyme.A lock-in amplifier was used for detecting the lifetime of the composite oxygen-sensitive film by measuring the phase delay of the sensor head.The different variables affecting the sensor performance were evaluated and optimized.Under the optimal conditions(i e,pH 6.0,25℃,Fe(III)PcTs concentration of 5.0×10^-5 mol/L),the linear detection range,detection limit and response time of the fiber optic sensor are 3.0×10^-7-9.0×10^-5 mol/L,4.8×10^-8 mol/L(S/N=3),and 220 s,respectively.The sensor displays high selectivity,good repeatability and stability,which have good potentials in analyzing DCP concentration in practical water samples.
基金supported by Beijing Municipal Natural Science Foundation (No.2091003)
文摘γ-CuI thin films were prepared by a spraying method using acetonitrile as a solvent,CuI and iodine as reagents.The influences of substrate temperature on the structure,topography,and optical properties of CuI films were investigated.Scanning electron microscope(SEM) photos revealed that the shape and grain size of CuI grains were related to substrate temperature.X-ray diffraction results showed that substrate temperature affected the crystalline quality of CuI films.When the substrate temperature was 110°C,CuI thin films showed γ-phase zinkblende structure with(111) preferred orientation.The dimension of the globular CuI crystallite was approximately 35 nm,the energy band gap was 2.97 eV,the maximum transmittance was 87.3% in the part of the visible region,and the open circuit voltage was close to 380 mV.This opened a route for a cadmium-free buffer layer for CuInS2 solar cells.
文摘Erbium doped BaTiO 3 optical-waveguide films on Pyrex substrate was elaborated successfully through sol-gel method. BaTiO 3 is well crystallized when the film is annealed at 650 ℃ in air circumstance. The so-prepared films with 13 layers have comparatively lower refractive index than bulk BaTiO 3, and it can support two TM and TE modes. Photoluminescence and up-conversion luminescence spectra proved the successful doping of rare earth ions.
基金supported by the Major State Basic Research Development Program of China(No.2007CB613301)the National Natural Science Foundation of China(Nos.50842028 and 50972012)
基金supported by the Young Scientists Fund of the National Natural Science Foundation of China(Grant Nos.11104365 and 11104366)the Hubei Key Laboratory of Low Dimensional Optoelectronic Material and Devices,China(Grant No.13XKL02002)
文摘Tungsten oxide thin films were deposited on glass substrates by the magnetron sputtering of WO3 bulk at room temperature. The deposited films were annealed at different temperatures in air. The structural measurements indicate that the films annealed below 300℃ were amorphous, while the films annealed at 400 ℃ were mixed crystalline with hexagonal and triclinic phases of WO3. It was observed that the crystallization of the annealed films becomes more and more distinct with an increase in the annealing temperature. At 400 ℃, nanorod-like structures were observed on the film surface when the annealing time was increased from 60 min to 180 min. The presence of W=O stretching, W-O-W stretching, W-O-W bending and various lattice vibration modes were observed in Raman measurements. The optical absorption behaviors of the films in the range of 450-800 nm are very different with changing annealing temperatures from the room temperature to 400 ℃. After annealing at 400 ℃, the film becomes almost transparent. Increasing annealing time at 400 ℃ can lead to a small blue shift of the optical gap of the film.
基金supported by the National Natural Science Foundation of China (Grants Nos 60876006 and 60376007)the Natural Science Foundation of Beijing (Grants No 4072007)
文摘The optical properties of hexagonal boron nitride (h-BN) thin films were studied in this paper. The films were characterized by Fourier transform infrared spectroscopy, UV-visible transmittance and reflection spectra, h-BN thin films with a wide optical band gap Eg (5.86 eV for the as-deposited film and 5.97 eV for the annealed film) approaching h-BN single crystal were successfully prepared by radio frequency (RF) bias magnetron sputtering and post-deposition annealing at 970 K. The optical absorption behaviour of h-BN films accords with the typical optical absorption characteristics of amorphous materials when fitting is made by the Urbach tail model. The annealed film shows satisfactory structure stability. However, high temperature still has a significant effect on the optical absorption properties, refractive index n, and optical conductivity σ of h-BN thin films. The blue-shift of the optical absorption edge and the increase of Eg probably result from stress relaxation in the film under high temperatures. In addition, it is found that the refractive index clearly exhibits different trends in the visible and ultraviolet regions. Previous calculational results of optical conductivity of h-BN films are confirmed in our experimental results.
基金supported by the National Natural Science Foundation of China (Grant Nos. 50942021 and 11075314)the Fundamental Research Fund for the Central Universities (Grant No. CDJXS10102207)
文摘Indium-doped ZnO thin films are deposited on quartz glass slides by RF magnetron sputtering at ambient temperature. The as-deposited films are annealed at different temperatures from 400℃ to 800 ℃ in air for 1 h. Transmittance spectra are used to determine the optical parameters and the thicknesses of the films before and after annealing using a nonlinear programming method, and the effects of the annealing temperatures on the optical parameters and the thickness are investigated. The optical band gap is determined from the absorption coefficient. The calculated results show that the film thickness and optical parameters both increase first and then decrease with increasing annealing temperature from 400℃ to 800℃. The band gap of the as-deposited ZnO:In thin film is 3.28 eV, and it decreases to 3.17 eV after annealing at 400℃. Then the band gap increases from 3.17 eV to 3.23 eV with increasing annealing temperature from 400℃ to 800℃.
文摘Cadmium sulphide (CdS) thin films were deposited on glass substrates by the chemical bath deposition (CBD) method, using anhydrous cadmium chloride (CdCl2) and thiourea (CS(NH2)2) as sources of cadmium and sulphur ions respectively. The influence of bath temperature (Tb), deposition time (td) aSnd [S]/[Cd] ratio in the solution on the structural, morphological, chemical composition and optical properties of these films were investigated. XRD studies revealed that all the deposited films were polycrystalline with hexagonal structure and exhibited (002) preferential orientation. The films deposited under optimum conditions (Tb = 75?C, td = 60 min and [S]/[Cd] ratio = 2.5) were relatively well crystallized. These films showed large final thickness and their surface morphologies were composed of small grains with an approximate size of 20 to 30 nm and grains grouped together to form large clusters. EDAX analysis revealed that these films were nonstoichiometric with a slight sulphur deficiency. These films exhibited also a transmittance value about 80% in the visible and infra red range.
基金Funded by the National Natural Science Foundation of China(No.61106126)
文摘We investigated the effect of annealing process on microstructures and optical properties of the sol-gel derived Ba0.9Sr0.1TiO3 (BST) films. The BST films, fabricated by layer-by-layer high-temperature (≥ 650 ℃) annealing process, had laminated structures consisting of alternating dense and porous BST layers, and exhibited excellent optical performance as Bragg reflectors. The Bragg reflection characteristic can be enhanced with increasing annealing temperature. Those BST films fabricated at temperatures lower than 650 ℃ displayed uniform cross-sectional morphologies even treated at a higher temperature. The difference in the microstructures of the BST thin films was also discussed.
基金Funded by the National Natural Science Foundation of China (No.50872001)Research Fund for the Doctoral Program of Higher Education ofChina (No. 20060357003)Talent Foundation of Anhui Province (No.2004Z029)
文摘Na-doped ZnO thin films were deposited on the glass substrates using sol-gel method. The effect of Na concentrations on the structural and optical properties of ZnO films was studied. As Na concentration increases from 0.0 at% to 16.0 at%, preferential c-axis orientation becomes more and more obvious, and the intensity of the diffraction peaks from (103) increases. The optical band gap Eg value increases from 3.261 to 3.286 eV first and then decreases as Na concentration increases from 0.0 to 2.0 at% and then beyond 2.0 at%. The intensity of all the emissions increases with increasing Na concentration and the origins of the violet emission (wavelength in the 400-407 nm) and the blue emission (wavelength at 473 nm) were discussed in detail.