The corrosion morphologies of aged magnesium alloy AZ80 were investigated by immersion corrosion tests, scanning electron microscopy （SEM）, electrochemical measurement. The T5 heat treatment was carried out in a vac...The corrosion morphologies of aged magnesium alloy AZ80 were investigated by immersion corrosion tests, scanning electron microscopy （SEM）, electrochemical measurement. The T5 heat treatment was carried out in a vacuum furnace, holding for 16 h at 177℃, and then cooling in air. The results showed intergranular corrosion （IGC） occurred as an aged AZ80 sample was immersed in 3.5 wt pct NaCI aqueous solution for 1 h and the narrow path attack progressed predominantly along the bulk β phase in the grain boundaries or took place in the eutectic areas. IGC was attributed to the network distribution of β phase along the grain boundaries, the depleted aluminium in the precipitation areas and the breakdown potential.展开更多
Variation and degradation of P-110 casing steel mechanical properties, due to sulfide stress cracking （SSC） in sour environments, was investigated using tensile and impact tests. These tests were carried out on spec...Variation and degradation of P-110 casing steel mechanical properties, due to sulfide stress cracking （SSC） in sour environments, was investigated using tensile and impact tests. These tests were carried out on specimens, which were pretreated under the following conditions for 168 hours： temperature, 60 ℃; pressure, 10 MPa; H2S partial pressure, 1 MPa and CO2 partial pressure, 1 MPa; preload stress, 80% of the yield strength （os）; medium, simulated formation water. The reduction in tensile and impact strengths for P-110 casing specimens in corrosive environments were 28% and 54%, respectively. The surface morphology analysis indicated that surface damage and uniform plastic deformation occurred as a result of strain aging. Impact toughness of the casing decreased significantly and intergranular cracking occurred when specimens were maintained at a high stress level of 85% %.展开更多
基金the National HiTech R. ＆ D. Program under grant No. 2001AA331050 Key Natural Science Foundation of Chongqing Science and Technology Commission under grant No. 200413A4002 Science ＆ Technology Research Project of Chongqing Education Commission under grant No. KJ050604.
文摘The corrosion morphologies of aged magnesium alloy AZ80 were investigated by immersion corrosion tests, scanning electron microscopy （SEM）, electrochemical measurement. The T5 heat treatment was carried out in a vacuum furnace, holding for 16 h at 177℃, and then cooling in air. The results showed intergranular corrosion （IGC） occurred as an aged AZ80 sample was immersed in 3.5 wt pct NaCI aqueous solution for 1 h and the narrow path attack progressed predominantly along the bulk β phase in the grain boundaries or took place in the eutectic areas. IGC was attributed to the network distribution of β phase along the grain boundaries, the depleted aluminium in the precipitation areas and the breakdown potential.
基金support of the State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation,Southwest Petroleum University in Chinathe National Natural Science Foundation of China (Grant No.51004084)
文摘Variation and degradation of P-110 casing steel mechanical properties, due to sulfide stress cracking （SSC） in sour environments, was investigated using tensile and impact tests. These tests were carried out on specimens, which were pretreated under the following conditions for 168 hours： temperature, 60 ℃; pressure, 10 MPa; H2S partial pressure, 1 MPa and CO2 partial pressure, 1 MPa; preload stress, 80% of the yield strength （os）; medium, simulated formation water. The reduction in tensile and impact strengths for P-110 casing specimens in corrosive environments were 28% and 54%, respectively. The surface morphology analysis indicated that surface damage and uniform plastic deformation occurred as a result of strain aging. Impact toughness of the casing decreased significantly and intergranular cracking occurred when specimens were maintained at a high stress level of 85% %.