Effect of Crystallographic Orientation on Quenching Stress during Martensitic Phase Transformation of Carbon Steel Plate

During quenching, the residual stresses are affected by the crystallographic orientation of martensite, because the nonuniform thermal stresses affect the crystallographic orientation of the lathshaped martensite and induce the anisotropic expansion. To simulate this process, the model of anisotropic transformation induced plasticity（TRIP） was built using the WLR-BM phenomenological theory. The equivalent expansion coefficient was introduced considering the thermal and plastic strains, which simplified the numerical simulation. Furthermore, the quenching residual stresses in carbon steel plates were calculated using the finite element method under ANSYS Workbench simulation environment. To evaluate the simulative results, distributions of residual stresses from the surface to the interior at the center of specimen were measured using the layer-by-layer hole-drilling method. Compared to the measured results, the simulative results considering the anisotropic expansion induced by the crystallographic orientation of martenstic laths were found to be more accurate than those without considering it.

Opposite Relationship between Orientation Selection and Texture Memory in the Deformed Electrical Steel Sheets during α→γ→α Transformation

The undesired {111} texture component for the magnetic properties mainly exists in the sheets of electrical steels by the conventional process, whereas the sheets with the non-{111} texture can be obtained by α→γ→α transformation. In this paper, we mainly investigate the opposite relationship between orientation selection and texture memory in the deformed ultra-low carbon steel sheet during →→ transformation annealing. A 0.5 mm thick hot-rolled sheet is directly subjected to transformation. The result shows that the specific transformation textures are not possible to generate in the sheets without deformation. Besides, transformation annealing is conducted on the recrystallized sheets in hydrogen and vacuum, respectively. The near {100} and {110} grains have the growth advantage at the atmosphere/metal interface, and the initial ferrite textures are retained in vacuum. Cold-rolled sheets with different thicknesses are annealed for transformation in vacuum, hydrogen and nitrogen, respectively.The near {100} and {110} textures are still the preferential orientations at the atmosphere/metal interface. When the surface grains have sufficiently large growth advantage, the {111} grains developed by texture memory effect will be annexed. Otherwise, the {111} grains at the center layer of the sheets are hard to be replaced, and they are retained after α→γ→α transformation cycle. The results of deformed sheets annealed with different heating rates in hydrogen show that the growth of initial recrystallization grains has a great effect on variant selection.

The Change of Orientation Relationships Between Austenite and α'-Martensite During Deformation in High Manganese TRIP Steel

In situ observation of electron backscattering diffraction technique was used to evaluate the orientation relationships between austenite and α′-martensite（α′-M） for high manganese transformation-induced plasticity steel.It was noted that different from the thermal martensite,which well obeyed K-S relationship with austenite,the orientation relationship between deformation-induced α′-M with austenite changed during deformation,namely K-S and N-W relations coexisted.No clear differences existed between α′-M variants with two kinds of relationships in terms of martensitic orientation,shape and the misorientation between α′-M variants.And this phenomenon happened in almost all austenitic grains with different orientations investigated in this study.An atom displacement mechanism through conjugate complex slips of partial dislocations in the distorted fcc lattice was applied in this article to interpret the coexistence of K-S and N-W relationships.

Quantitative Analysis of the Crystallographic Orientation Relationship Between the Martensite and Austenite in Quenching–Partitioning–Tempering Steels

The orientation relationships（ORs）between the martensite and the retained austenite in low-and medium-carbon steels after quenching–partitioning–tempering process were studied in this work.The ORs in the studied steels are identified by selected-area electron diffraction（SAED）as either K–S or N–W ORs.Meanwhile,the ORs were also studied based on numerical fitting of electron backscatter diffraction data method suggested by Miyamoto.The simulated K–S and N–W ORs in the low-index directions generally do not well coincide with the experimental pole figure,which may be attributed to both the orientation spread from the ideal variant orientations and high symmetry of the low-index directions.However,the simulated results coincide well with experimental pole figures in the high-index directions{123}_（bcc）.A modified method with simplicity based on Miyamoto’s work was proposed.The results indicate that the ORs determined by modified method are similar to those determined by Miyamoto’method,that is,the OR is near K–S OR for the low-carbon Q–P–T steel,and with the increase of carbon content,the OR is closer to N–W OR in medium-carbon Q–P–T steel.