The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding...The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding parameters on the tensile strength of welds,based on an orthogonal test and analysis method.The welding parameters include beam current,welding speed,scanning figure,scanning frequency,figure size,beam offset and focus current.The optimum parameters for3 mm 5A06 Al alloy and 2 mm TC4 alloy were as follows：acceleration voltage was 60 kV,beam current was 11 mA,welding speed was 600 mm/min,focus current was 0 mA,scan figure was O,scanning frequency was 1 000 Hz and beam offset was 0.5 mm.The results show that the joints were with good appearance and quality welded by the optimum parameters.The successful joints could be gained and the maximum tensile strength of Al/Ti dissimilar alloy joints could be up to 222.61 MPa using electron beam welding-brazing.展开更多
Experimental investigations on the DC spot welding of Mg alloy AZ31B are presented. Experiments are carried out to study the influence of spot welding parameters （ electrode force, welding heat input and welding time...Experimental investigations on the DC spot welding of Mg alloy AZ31B are presented. Experiments are carried out to study the influence of spot welding parameters （ electrode force, welding heat input and welding time） on the tensile shear load and the diameter of nugget, based on an orthogonal test and analysis method. The optimum parameters are as follows： electrode force is 2 000 N, welding heat input is 80% and welding time is 6 cycles. The microstrueture of spot weld is single fine equiaxed crystals in the nugget, of which the structure is β-Mg17Al12 precipitated on α-Mg boundaries induced by nonequilibrium freezing. And the surface condition of the workpiece has great influence on the joint quality.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51105346)
文摘The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding parameters on the tensile strength of welds,based on an orthogonal test and analysis method.The welding parameters include beam current,welding speed,scanning figure,scanning frequency,figure size,beam offset and focus current.The optimum parameters for3 mm 5A06 Al alloy and 2 mm TC4 alloy were as follows：acceleration voltage was 60 kV,beam current was 11 mA,welding speed was 600 mm/min,focus current was 0 mA,scan figure was O,scanning frequency was 1 000 Hz and beam offset was 0.5 mm.The results show that the joints were with good appearance and quality welded by the optimum parameters.The successful joints could be gained and the maximum tensile strength of Al/Ti dissimilar alloy joints could be up to 222.61 MPa using electron beam welding-brazing.
文摘Experimental investigations on the DC spot welding of Mg alloy AZ31B are presented. Experiments are carried out to study the influence of spot welding parameters （ electrode force, welding heat input and welding time） on the tensile shear load and the diameter of nugget, based on an orthogonal test and analysis method. The optimum parameters are as follows： electrode force is 2 000 N, welding heat input is 80% and welding time is 6 cycles. The microstrueture of spot weld is single fine equiaxed crystals in the nugget, of which the structure is β-Mg17Al12 precipitated on α-Mg boundaries induced by nonequilibrium freezing. And the surface condition of the workpiece has great influence on the joint quality.