The quantitative relationship between microstructure and properties of austenitic Fe-28Mn-xAl-1C(x=10 and 12 wt.%)low-density steels was evaluated using Rietveld method to refine X-ray diffraction(XRD)patterns.The res...The quantitative relationship between microstructure and properties of austenitic Fe-28Mn-xAl-1C(x=10 and 12 wt.%)low-density steels was evaluated using Rietveld method to refine X-ray diffraction(XRD)patterns.The results showed that a typical three-phase austenitic steel was obtained in the forged Mn28Al10(i.e.Fe-28Mn-10Al-1C)steel,which included about 92.85 wt.% γ-Fe(Mn,Al,C)(austenite),5.28 wt.%(Fe,Mn)_3AlC_(0.5)(κ-carbide),and 1.87 wt.% α-Fe(Al,Mn)(ferrite).For the forged Mn28Al12(i.e.Fe-28Mn-12Al-1C)steel,nevertheless,only about 76.64 wt.% austenite,9.63 wt.%κ-carbide,9.14 wt.%ferrite and 4.59 wt.% Fe_3Al(DO_3)could be obtained.Nanometerκ-carbide and DO_3 were mainly distributed in austenite grains and at the interface between austenite and ferrite,respectively.The forged Mn28Al10 steel had a better combination of strength,ductility and specific strength as compared with the forged Mn28Al12 steel.The ductility of the forged Mn28Al12 steel was far lower than that of the forged Mn28Al10 steel.The oxidation kinetics of Mn28Al10 steel oxidized at 1323 Kfor 5-25 h had two-stage linear rate laws,and the oxidation rate of the second stage was faster than that of the first stage.Although the oxidation kinetics of Mn28Al12 steel under this condition also had two-stage linear rate laws,the oxidation rate of the second stage was slower than that of the first stage.When the oxidation temperature increased to 1373K,the oxidation kinetics of the two steels at 5-25 hhad only onestage linear rate law,and the oxidation rates of the two steels were far faster than those at 1323K for5-25 h.The oxidation resistance of Mn28Al12 steel was much better than that of Mn28Al10 steel.Ferrite layer formed between the austenite matrix and the oxidation layer of the two Fe-Mn-Al-C steels oxidized at high temperature.展开更多
In this work, we focus on the optical super-resolution effect induced by strong nonlinear saturation absorption(NSA) of graphene oxide(GO) membranes. The third-order optical nonlinearities are characterized by the can...In this work, we focus on the optical super-resolution effect induced by strong nonlinear saturation absorption(NSA) of graphene oxide(GO) membranes. The third-order optical nonlinearities are characterized by the canonical Z-scan technique under femtosecond laser(wavelength: 800 nm, pulse width: 100 fs) excitation. Through controlling the applied femtosecond laser energy, NSA of the GO films can be tuned continuously. The GO film is placed at the focal plane as a unique amplitude filter to improve the resolution of the focused field. A multi-layer system model is proposed to present the generation of a deep sub-wavelength spot associated with the nonlinearity of GO films. Moreover, the parameter conditions to achieve the best resolution(~λ/6) are determined entirely. The demonstrated results here are useful for high density optical recoding and storage, nanolithography, and super-resolution optical imaging.展开更多
基金funded by the National Natural Science Foundation of China (Grant No.51674004)Education Department of Anhui Province of China (Grant Nos.KJ2016A104 and KJ2017A805)
文摘The quantitative relationship between microstructure and properties of austenitic Fe-28Mn-xAl-1C(x=10 and 12 wt.%)low-density steels was evaluated using Rietveld method to refine X-ray diffraction(XRD)patterns.The results showed that a typical three-phase austenitic steel was obtained in the forged Mn28Al10(i.e.Fe-28Mn-10Al-1C)steel,which included about 92.85 wt.% γ-Fe(Mn,Al,C)(austenite),5.28 wt.%(Fe,Mn)_3AlC_(0.5)(κ-carbide),and 1.87 wt.% α-Fe(Al,Mn)(ferrite).For the forged Mn28Al12(i.e.Fe-28Mn-12Al-1C)steel,nevertheless,only about 76.64 wt.% austenite,9.63 wt.%κ-carbide,9.14 wt.%ferrite and 4.59 wt.% Fe_3Al(DO_3)could be obtained.Nanometerκ-carbide and DO_3 were mainly distributed in austenite grains and at the interface between austenite and ferrite,respectively.The forged Mn28Al10 steel had a better combination of strength,ductility and specific strength as compared with the forged Mn28Al12 steel.The ductility of the forged Mn28Al12 steel was far lower than that of the forged Mn28Al10 steel.The oxidation kinetics of Mn28Al10 steel oxidized at 1323 Kfor 5-25 h had two-stage linear rate laws,and the oxidation rate of the second stage was faster than that of the first stage.Although the oxidation kinetics of Mn28Al12 steel under this condition also had two-stage linear rate laws,the oxidation rate of the second stage was slower than that of the first stage.When the oxidation temperature increased to 1373K,the oxidation kinetics of the two steels at 5-25 hhad only onestage linear rate law,and the oxidation rates of the two steels were far faster than those at 1323K for5-25 h.The oxidation resistance of Mn28Al12 steel was much better than that of Mn28Al10 steel.Ferrite layer formed between the austenite matrix and the oxidation layer of the two Fe-Mn-Al-C steels oxidized at high temperature.
基金supported by the National Natural Science Foundation of China(Nos.61575139,51602213 and 11604236)the Young Science Foundation of Taiyuan University of Technology(No.2015QN066)
文摘In this work, we focus on the optical super-resolution effect induced by strong nonlinear saturation absorption(NSA) of graphene oxide(GO) membranes. The third-order optical nonlinearities are characterized by the canonical Z-scan technique under femtosecond laser(wavelength: 800 nm, pulse width: 100 fs) excitation. Through controlling the applied femtosecond laser energy, NSA of the GO films can be tuned continuously. The GO film is placed at the focal plane as a unique amplitude filter to improve the resolution of the focused field. A multi-layer system model is proposed to present the generation of a deep sub-wavelength spot associated with the nonlinearity of GO films. Moreover, the parameter conditions to achieve the best resolution(~λ/6) are determined entirely. The demonstrated results here are useful for high density optical recoding and storage, nanolithography, and super-resolution optical imaging.