YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering m...YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering method. The structures and phaseevolution of the coatings were studied with X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersivespectrometry （EDS）. The relation between microstructures and properties of the BPs-coated samples was discussed. The results showthat the adhesion strength and gain mass of the BPs-coated samples with isothermal oxidation at 1100℃ for 100 h are 3.3 N and0.00817 mg/cm^2, respectively, while those of the non-BPs-coated sample are 2.6 N and 0.00559 mg/cm^2, respectively. The EDSmapping analysis indicates that an obvious outward diffusion of Cr from the substrate to BPs coated samples occurs after isothermaloxidation. The BPs-coated sample shows the superior adhesion and oxidation resistance compared with non-BPs-coated samples.展开更多
基金Project(51271111)supported by the National Natural Science Foundation of ChinaProject(14KY0515)support by Graduate Research and Innovation Special Projects of Shanghai University of Engineering Science,China
文摘YSZ/（Ni, Al） composite coatings were deposited on Inconel600 superalloy with ball peening （BP） and without （non BP）treatment using the electrophoretic deposition （EPD） technique, followed by vacuum sintering method. The structures and phaseevolution of the coatings were studied with X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersivespectrometry （EDS）. The relation between microstructures and properties of the BPs-coated samples was discussed. The results showthat the adhesion strength and gain mass of the BPs-coated samples with isothermal oxidation at 1100℃ for 100 h are 3.3 N and0.00817 mg/cm^2, respectively, while those of the non-BPs-coated sample are 2.6 N and 0.00559 mg/cm^2, respectively. The EDSmapping analysis indicates that an obvious outward diffusion of Cr from the substrate to BPs coated samples occurs after isothermaloxidation. The BPs-coated sample shows the superior adhesion and oxidation resistance compared with non-BPs-coated samples.