Electroreduction Kinetics for Molten Oxide Slags

The oxygen-ion conductor, the reducing agent, and the molten oxide slag containing electroactive matter were used as constituent of a galvanic cell. Metal was directly electroreduced from molten slag using a short-circuit galvanic cell. The following galvanic cell was assembled in the present experiment： graphite rod, [-O]Fe-C saturated ｜ZrO2 （MgO） ｜ Cu（1） ＋ （FeO）（slag） , and molybdenum wire. The FeO electroreduction reaction was studied through measuring short circuit current by controlling factors such as temperature, the FeO content in molten slags, and the external circuit resistance. An overall kinetics model was developed to describe the process of FeO electroreductiono It was found that the modeled curves were in good agreement with the experimental values. The new oxide reduction method in the metallurgy with controlled oxygen flow was proposed and the metallurgical theory with controlled oxygen flow was developed.

Effect of the CaO/SiO2 mass ratio and FeO content on the viscosity of CaO–SiO2–“FeO”–12wt%ZnO–3wt%Al2O3 slags

An effective process for recycling lead from hazardous waste cathode ray tubes（CRTs） funnel glass through traditional lead smelting has been presented previously. The viscous behavior of the molten high lead slag, which is affected by the addition of funnel glass, plays a critical role in determining the production efficiency. Therefore, the viscosities of the CaO–SiO_2–＂FeO＂–12wt%ZnO–3wt%Al_2O_3 slags were measured in the current study using the rotating spindle method. The slag viscosity decreases as the CaO/SiO_2 mass ratio is increased from 0.8 to 1.2 and also as the FeO content is increased from 8wt% to 20wt%. The breaking temperature of the slag is lowered substantially by the addition of FeO, whereas the influence of the CaO/SiO_2 mass ratio on the breaking temperature is complex. The structural analysis of quenched slags using Fourier transform infrared（FTIR） spectroscopy and Raman spectroscopy reveals that the silicate network structure is depolymerized with increasing CaO/SiO_2 mass ratio or increasing FeO content. The [FeO_6]-octahedra in the slag melt increase as the CaO/SiO_2 mass ratio or the FeO content increases. This increase can further decrease the degree of polymerization（DOP） of the slag. Furthermore, the activation energy for viscous flow decreases both with increasing CaO/SiO_2 mass ratio and increasing FeO content.

Effects of MgO and TiO_2 on the viscous behaviors and phase compositions of titanium-bearing slag

The effects of MgO and TiO_2 on the viscosity, activation energy for viscous flow, and break-point temperature of titanium-bearing slag were studied. The correlation between viscosity and slag structure was analyzed by Fourier transform infrared（FTIR） spectroscopy. Subsequently, main phases in the slag and their content changes were investigated by X-ray diffraction and Factsage 6.4 software package. The results show that the viscosity decreases when the MgO content increases from 10.00wt% to 14.00wt%. Moreover, the break-point temperature increases, and the activation energy for viscous flow initially increases and subsequently decreases. In addition, with increasing TiO_2 content from 5.00wt% to 9.00wt%, the viscosity decreases, and the break-point temperature and activation energy for viscous flow initially decrease and subsequently increase. FTIR analyses reveal that the polymerization degree of complex viscous units in titanium-bearing slag decreases with increasing MgO and TiO_2 contents. The mechanism of viscosity variation was elucidated. The basic phase in experimental slags is melilite. Besides, as the MgO content increases, the amount of magnesia–alumina spinel in the slag increases. Similarly, the sum of pyroxene and perovskite phases in the slag increases with increasing TiO_2 content.

Thermodynamic Modeling of Deoxidation Products and Inclusion Chemistry in Mn/Si Killed Tire-Cord Steel

The present work deals with thermodynamic modeling of oxide systems, in the context of slags and inclusions in steelmaking. The work has emphasis on oxides encountered during the production of tire – cord steel. Control of inclusion chemistry and variation in eutectic temperature and eutectic composition of MnO-Al2O3-SiO2 slag system have been studied, using Thermo-CalcR software. Relatively low liquidus temperatures are obtained for ratio of MnO / SiO2 = 0.5 - 1.5 and Al2O3 content from 10 - 20 mass%. It has been observed that the addition of Alumina leads to further increase in the liquidus temperature. The stability of inclusions is analyzed in terms of free energy values of related slag systems; and an appropriate minimum of Gibbs free energy value of slag phase observed at around 50 ppm of Oxygen. The observations could not be verified using thermodynamic experiments, but have been compared with findings in the open literature.