The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The in...The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900～1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.展开更多
As the oxygen redox ability shows great effects on the catalytic performances of ceria-zirconia based materials,many strategies have been utilized to improve the oxygen storage capacity.Here in this study,we report a ...As the oxygen redox ability shows great effects on the catalytic performances of ceria-zirconia based materials,many strategies have been utilized to improve the oxygen storage capacity.Here in this study,we report a simple and facile approach to prepare a SO_(4)^(2-)-modified La,Y-doped ceria-zirconia material(SO/CZLY-f)with high oxygen storage capacity.Due to the additional redox process between SO_(4)^(2-)and S^(2-),oxygen storage capacity of SO/CZLY-f(745.3μmol O_(2)/g)is about 1.6 times higher than that of La,Ydoped ceria-zirconia material without SO_(4)^(2-)modification.Moreover,the catalytic activities and stability of the corresponding Pd-only three-way catalyst were measured.Compared to that of Pd@CZLY-f,the operation window of CO,full conversion temperature of HC and NO over Pd@SO/CZLY-f are obviously widened and lowered,respectively.After aging treatment at 1100℃for 4 h,the superiority of aged Pdloading composite is still maintained.展开更多
文摘The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900～1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.
基金Project supported by the Beijing Nova Program(Z181100006218030)Major State Research Development Program of Hebei province(20374202D)。
文摘As the oxygen redox ability shows great effects on the catalytic performances of ceria-zirconia based materials,many strategies have been utilized to improve the oxygen storage capacity.Here in this study,we report a simple and facile approach to prepare a SO_(4)^(2-)-modified La,Y-doped ceria-zirconia material(SO/CZLY-f)with high oxygen storage capacity.Due to the additional redox process between SO_(4)^(2-)and S^(2-),oxygen storage capacity of SO/CZLY-f(745.3μmol O_(2)/g)is about 1.6 times higher than that of La,Ydoped ceria-zirconia material without SO_(4)^(2-)modification.Moreover,the catalytic activities and stability of the corresponding Pd-only three-way catalyst were measured.Compared to that of Pd@CZLY-f,the operation window of CO,full conversion temperature of HC and NO over Pd@SO/CZLY-f are obviously widened and lowered,respectively.After aging treatment at 1100℃for 4 h,the superiority of aged Pdloading composite is still maintained.