Al-Ti-C grain refiner was prepared by SHS （self-propagating high-temperature synthesis ）-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The exp...Al-Ti-C grain refiner was prepared by SHS （self-propagating high-temperature synthesis ）-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The experimental results indicate that La can improve the wettability between liquid aluminum and graphite ; the addition of La results in dispersive distribution of TiAl3 and TiC particles in the matrix. An excellent grain refining performance of Al-Ti-C grain refiner on commercially pure Al was obtained.展开更多
An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The ...An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The results show that sound pressure node in which graphite suspends is formed in the melt between radiation block and reflecting board by ultrasonic and TiAl3 particles congregate around C powder. Meanwhile, due to ultrasonic cavitation, dissolved TiAl3 provides better surface condition for the synthesis reaction of TiC. The reaction route is that C and dissolved Ti react to form TiC. Ultrasonic cavitation has a thermal activation effect on TiC particles and Al-3Ti-0.15C refiner has excellent microstructural refining effect on α-Al.展开更多
基金Project supported by the Natural Science Foundation of Shanxi Province (20011047)Patent Generalization Project ofShanxi Province (051025)
文摘Al-Ti-C grain refiner was prepared by SHS （self-propagating high-temperature synthesis ）-melting technique. The effect of La on the microstructures of grain refiner was studied by OM, TEM, SEM, XRD, and EDS. The experimental results indicate that La can improve the wettability between liquid aluminum and graphite ; the addition of La results in dispersive distribution of TiAl3 and TiC particles in the matrix. An excellent grain refining performance of Al-Ti-C grain refiner on commercially pure Al was obtained.
基金Funded by National Natural Science Foundation of China(No.50774023)
文摘An electrostrictive uniaxial ultrasonic levitation reaction system was designed to perform TiC synthesis reaction by suspending graphite powder in Al-3Ti melt and an Al-3Ti-0.15C grain refiner alloy was obtained. The results show that sound pressure node in which graphite suspends is formed in the melt between radiation block and reflecting board by ultrasonic and TiAl3 particles congregate around C powder. Meanwhile, due to ultrasonic cavitation, dissolved TiAl3 provides better surface condition for the synthesis reaction of TiC. The reaction route is that C and dissolved Ti react to form TiC. Ultrasonic cavitation has a thermal activation effect on TiC particles and Al-3Ti-0.15C refiner has excellent microstructural refining effect on α-Al.