In order to improve the performances of electroplating permanent magnetic films, neodymium is introduced into the electroplating CoNiMnP permanent magnetic films. The influences of the neodymium content are also inves...In order to improve the performances of electroplating permanent magnetic films, neodymium is introduced into the electroplating CoNiMnP permanent magnetic films. The influences of the neodymium content are also investigated by varying NdCl3 plating bath concentration. The neodymium-doped films are analyzed by energy dispersive spectrum (EDS), vibrating sample magnetometer (VSM) and magnetic force microscope (MFM). The experimental results show that high magnetic performances of CoNdNiMnP permanent magnetic films with vertical anisotropy could be fabricated with current density 5mA/cm2 at room temperature. With the increasing of neodymium contents, the magnetic properties of films were improved. However when neodymium contents exceeded 3.5wt%, the magnetic properties of films are not improved any more. The increase of film magnetic properties results from the ferromagnetic-coupling between light rare earth element-neodymium and transition metal element-cobalt.展开更多
Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30...Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30 nm exhibited two-phase behavior in the demagnetization process,the obvious kink was observed near zero.For the SmCo film of 50 nm,the kink was invisible,and a single phase like behavior was obtained in the demagnetization process.The reversal behavior became consistent in the thicker films.Moreover,the coercivity reduced and the saturated magnetization increased obviously with the increasing thickness.X-ray diffraction results indicated that the average grain size of SmCo 5 in the thicker films were almost 30 nm,but the quantity of SmCo 5 grains increased with the increasing thickness,which enhanced the intergrain exchange coupling（IEC） of the SmCo 5 hard phases.The increase of IEC improved the magnetic properties of SmCo films with increasing thickness.展开更多
文摘In order to improve the performances of electroplating permanent magnetic films, neodymium is introduced into the electroplating CoNiMnP permanent magnetic films. The influences of the neodymium content are also investigated by varying NdCl3 plating bath concentration. The neodymium-doped films are analyzed by energy dispersive spectrum (EDS), vibrating sample magnetometer (VSM) and magnetic force microscope (MFM). The experimental results show that high magnetic performances of CoNdNiMnP permanent magnetic films with vertical anisotropy could be fabricated with current density 5mA/cm2 at room temperature. With the increasing of neodymium contents, the magnetic properties of films were improved. However when neodymium contents exceeded 3.5wt%, the magnetic properties of films are not improved any more. The increase of film magnetic properties results from the ferromagnetic-coupling between light rare earth element-neodymium and transition metal element-cobalt.
基金Project supported by National Natural Science Foundation of China (50871014)New Teacher Foundation of Ministry of Education(200800081030)+1 种基金Funding Project for Academic Human Resources Development in Institutions of Higher Learning Under the Jurisdiction of Beijing Municipality (PHR201007122)Beijing Natural Science Foundation (2102014)
文摘Cr/SmCo/Cr films with different SmCo thickness were deposited on glass substrates by magnetron sputtering,followed by an annealing process at 550 °C for 20 min.Experimental results showed that the SmCo film of 30 nm exhibited two-phase behavior in the demagnetization process,the obvious kink was observed near zero.For the SmCo film of 50 nm,the kink was invisible,and a single phase like behavior was obtained in the demagnetization process.The reversal behavior became consistent in the thicker films.Moreover,the coercivity reduced and the saturated magnetization increased obviously with the increasing thickness.X-ray diffraction results indicated that the average grain size of SmCo 5 in the thicker films were almost 30 nm,but the quantity of SmCo 5 grains increased with the increasing thickness,which enhanced the intergrain exchange coupling（IEC） of the SmCo 5 hard phases.The increase of IEC improved the magnetic properties of SmCo films with increasing thickness.