Functionalized PS/SiO_2 composite nanoparticles bearing sulfonic groups on the surface were successfully synthesized via emulsion copolymerization using a polymerizable emulsifierαolefin solfonate(AOS).As demonstrate...Functionalized PS/SiO_2 composite nanoparticles bearing sulfonic groups on the surface were successfully synthesized via emulsion copolymerization using a polymerizable emulsifierαolefin solfonate(AOS).As demonstrated by transmission electron microscopy and atomic force microscopy,well-defined core-shell PS/SiO_2 composite nanoparticles with a diameter of 50 nm were obtained.Sulfonic groups introduced onto the surface of the composite nanoparticles were quantified by FTIR,and can be controlled to some exten...展开更多
In this paper, the optimum process parameters were obtained through treating phenol of simulated semi-coking wastewater using heat, Fe2＋, Fe^0 and semi-coke to catalyze persulfate. The results of phenol decomposition...In this paper, the optimum process parameters were obtained through treating phenol of simulated semi-coking wastewater using heat, Fe2＋, Fe^0 and semi-coke to catalyze persulfate. The results of phenol decomposition using PS catalyzed by heating, Fe2＋, Fe^0 and semi-coke were compared for selecting a better activating way. The article investigated the effects of temperature, catalyzer dosage, pH value and reaction time. The experiment showed the four methods can all catalyzed the process. Under the experimental conditions of heating, Fe2＋, Fe^0 and semi-coke degradation rate could reach to 20.7%, 75.1%, 94.5% and 40.0%, respectively. On this basis, this study established an Lt6（45） table to analyze the main influencing factors in semi-coke/Fe^0 catalyzing system. Under the optimum conditions, the degradation rate of Phenol reached to 93.6%. However, the PS dosage was reduced by 14.4%.展开更多
Silica-bonded S-sulfonic acid （SBSSA） was prepared by the reaction of 3-mercaptopropylsilica （MPS） and chlorosulfonic acid in chloroform. This solid acid has been employed as a recyclable catalyst for the synthesi...Silica-bonded S-sulfonic acid （SBSSA） was prepared by the reaction of 3-mercaptopropylsilica （MPS） and chlorosulfonic acid in chloroform. This solid acid has been employed as a recyclable catalyst for the synthesis of coumarins from phenols and β-keto- esters at 80 ℃ under solvent-free conditions.展开更多
The effect of different sulfonation degree on properties of sulfonated syndiotactic polystyrene(S s PS) was investigated by 1H NMR, 13 C NMR,FTIR,DSC and WAXD.The results of 13 C NMR showed that a peak at δ =145 5 ap...The effect of different sulfonation degree on properties of sulfonated syndiotactic polystyrene(S s PS) was investigated by 1H NMR, 13 C NMR,FTIR,DSC and WAXD.The results of 13 C NMR showed that a peak at δ =145 5 appeared in all S s PS spectra,which proved that the syndiotactic structure of syndiotactic polystyrene( s PS) still existed in S s PS.With increasing degree of sulfonition,the chemical shifts of C 1 and C\|3 for sulfonated benzene ring turned out to be wider. 1 H NMR spectra showed that C\|3 for sulfonated benzene ring had a chemical shift of 7 66.FTIR spectra showed that sulfonic acid groups were introduced on the para position of benzene rings and with increasing sulfonation degree,the absorption strength of 612/1600 cm 1 ,834/1600cm -1 increased,but the absorption strength of 1078/1600cm -1 decreased.The absorption of ～1030cm -1 ,～1179cm -1 ,～1217cm -1 appeared when the sulfonation degree was higher that 6%. s PS and S s PS H 2 2 had absorption at 975 and 943cm -1 and also had double peaks around ～1175cm -1 ;DSC showed that with increasing sulfonation degree, the glass transition temperature increased, the melt temperature,crystallization temperature and crystallization degree decreased;S s PS couldn’t crystallize when sulfonation degree was higher that 6mol%;WAXD proved that s PS had the α and β crystal types, however,S s PS with 2 2% sulfonation degree only had the β crystal type, and S s PS with 6 1% sulfonation degree didn’t crystallize.展开更多
基金supported by the Hi-Tech Research and Development Program of China(863,No2006AA03Z562)
文摘Functionalized PS/SiO_2 composite nanoparticles bearing sulfonic groups on the surface were successfully synthesized via emulsion copolymerization using a polymerizable emulsifierαolefin solfonate(AOS).As demonstrated by transmission electron microscopy and atomic force microscopy,well-defined core-shell PS/SiO_2 composite nanoparticles with a diameter of 50 nm were obtained.Sulfonic groups introduced onto the surface of the composite nanoparticles were quantified by FTIR,and can be controlled to some exten...
文摘In this paper, the optimum process parameters were obtained through treating phenol of simulated semi-coking wastewater using heat, Fe2＋, Fe^0 and semi-coke to catalyze persulfate. The results of phenol decomposition using PS catalyzed by heating, Fe2＋, Fe^0 and semi-coke were compared for selecting a better activating way. The article investigated the effects of temperature, catalyzer dosage, pH value and reaction time. The experiment showed the four methods can all catalyzed the process. Under the experimental conditions of heating, Fe2＋, Fe^0 and semi-coke degradation rate could reach to 20.7%, 75.1%, 94.5% and 40.0%, respectively. On this basis, this study established an Lt6（45） table to analyze the main influencing factors in semi-coke/Fe^0 catalyzing system. Under the optimum conditions, the degradation rate of Phenol reached to 93.6%. However, the PS dosage was reduced by 14.4%.
文摘Silica-bonded S-sulfonic acid （SBSSA） was prepared by the reaction of 3-mercaptopropylsilica （MPS） and chlorosulfonic acid in chloroform. This solid acid has been employed as a recyclable catalyst for the synthesis of coumarins from phenols and β-keto- esters at 80 ℃ under solvent-free conditions.
文摘The effect of different sulfonation degree on properties of sulfonated syndiotactic polystyrene(S s PS) was investigated by 1H NMR, 13 C NMR,FTIR,DSC and WAXD.The results of 13 C NMR showed that a peak at δ =145 5 appeared in all S s PS spectra,which proved that the syndiotactic structure of syndiotactic polystyrene( s PS) still existed in S s PS.With increasing degree of sulfonition,the chemical shifts of C 1 and C\|3 for sulfonated benzene ring turned out to be wider. 1 H NMR spectra showed that C\|3 for sulfonated benzene ring had a chemical shift of 7 66.FTIR spectra showed that sulfonic acid groups were introduced on the para position of benzene rings and with increasing sulfonation degree,the absorption strength of 612/1600 cm 1 ,834/1600cm -1 increased,but the absorption strength of 1078/1600cm -1 decreased.The absorption of ～1030cm -1 ,～1179cm -1 ,～1217cm -1 appeared when the sulfonation degree was higher that 6%. s PS and S s PS H 2 2 had absorption at 975 and 943cm -1 and also had double peaks around ～1175cm -1 ;DSC showed that with increasing sulfonation degree, the glass transition temperature increased, the melt temperature,crystallization temperature and crystallization degree decreased;S s PS couldn’t crystallize when sulfonation degree was higher that 6mol%;WAXD proved that s PS had the α and β crystal types, however,S s PS with 2 2% sulfonation degree only had the β crystal type, and S s PS with 6 1% sulfonation degree didn’t crystallize.