We studied the effects of nanoparticles of organo-silane(NOS) compounds in the size range of20–80 nm on physical and mechanical properties in medium density fiberboard,and used NOS at four consumption levels of 0,5...We studied the effects of nanoparticles of organo-silane(NOS) compounds in the size range of20–80 nm on physical and mechanical properties in medium density fiberboard,and used NOS at four consumption levels of 0,50,100,and 150 g kg-1dry wood fibers.Density of all treatments was kept constant at 0.67 g cm-3.The water-repellent property of organo-silane significantly reduced water absorption(WA) and thickness swelling but mechanical properties declined due to the reduced proportion of wood-fiber as organo-silane was added to the matrix:the compression ratio of MDF panels and the integrity among wood-fibers both declined,resulting in reduced mechanical properties.We recommend use of 50 g of NOS/kg wood-fiber to improve WA and thickness swelling while retaining acceptable mechanical properties.展开更多
The objective of this investigation was to introduce a cement-based composite of higher quality. For this purpose new hybrid nanocomposite from bagasse fiber,glass fiber and multi-wall carbon nanotubes(MWCNTs)were m...The objective of this investigation was to introduce a cement-based composite of higher quality. For this purpose new hybrid nanocomposite from bagasse fiber,glass fiber and multi-wall carbon nanotubes(MWCNTs)were manufactured. The physical and mechanical properties of the manufactured composites were measured according to standard methods. The properties of the manufactured hybrid nanocomposites were dramatically better than traditional composites. Also all the reinforced composites with carbon nanotube, glass fiber or bagasse fiber exhibited better properties rather than neat cement.The results indicated that bagasse fiber proved suitable for substitution of glass fiber as a reinforcing agent in the cement composites. The hybrid nanocomposite containing10 % glass fiber, 10 % bagasse fiber and 1.5 % MWCNTs was selected as the best compound.展开更多
The artificial afforestation of precious Phoebe bournei has been carried out in China.During the cultivation process,thinning wood will be produced.The properties of thinning wood might vary greatly with matured wood ...The artificial afforestation of precious Phoebe bournei has been carried out in China.During the cultivation process,thinning wood will be produced.The properties of thinning wood might vary greatly with matured wood and require evaluation for better utilization.The objective of the present study aims to determine the wood structure,fiber morphology,and physical and mechanical properties of the Phoebe bournei thinning wood to help us understand the wood properties and improve its utility value.Three 14-year-old Phoebe bournei were cut from Jindong Forestry Farm of Hunan Province,China.The wood structure and fiber morphology were observed and analyzed with a light microscope and scanning electron microscope.The physical and mechanical properties were tested according to the Chinese national standards.The results showed as follows:(1)The Phoebe bournei thinning wood has a beautiful wood figure and fine texture,whereas the heartwood has not yet formed.(2)It is a diffuse-porous hardwood with small and less pores as well as fine wood rays.(3)The wood fiber is medium length and extremely thin wall thickness.(4)It is low in density and has excellent dimensionally stability.(5)The wood mechanical properties belong to the low to medium class and the comprehensive strength of wood belongs to the medium-strength class.It is concluded that Phoebe bournei thinning wood is suitable for wood carving,handicraft,high-end furniture,and decorative furniture parts.展开更多
In deep-earth engineering,the high earth temperature can significantly affect the rock's mechanical properties,especially when the rock is cooled during the construction process.Accordingly,whether the cooling spe...In deep-earth engineering,the high earth temperature can significantly affect the rock's mechanical properties,especially when the rock is cooled during the construction process.Accordingly,whether the cooling speed affects the mechanical and physical properties of rocks is worth to be investigated.The present study explored the influence of the cooling rate on the physical and chemical properties of granite heated at 25–800°C.The mechanical and physical properties involved in this study included uniaxial compression strength,peak strain,modulus,P-wave velocity,mass and volume,the change of which could reflect the sensitivity of granite to the cooling rate.Acoustic emission(AE)monitoring,microscopic observation,and X-ray diffraction(XRD)are used to analyze the underlying damage mechanism.It is found that more AE signals and large-scale cracks are accounted for based on the b-value method when the specimens are cooled by water.Furthermore,the microscopic observation by polarized light microscopy indicates that the density,opening degree,and connectivity of the cracks under water cooling mode are higher than that under natural cooling mode.In addition,the XRD illustrates that there is no obvious change in mineral content and diffraction angle at different temperatures,which confirms that the change of mechanical properties is not related to the chemical properties.The present conclusion can provide a perspective to assess the damage caused by different cooling methods to hot rocks.展开更多
The use of agricultural waste in construction is an advantage favorable to environmental sanitation, the preservation of non-renewable resources but also to the execution of an ecological work. The objective of this w...The use of agricultural waste in construction is an advantage favorable to environmental sanitation, the preservation of non-renewable resources but also to the execution of an ecological work. The objective of this work is to study the influence of the addition of palm nut cockles ash as an adjuvant on the physico-mechanical properties of concrete. For this study, ordinary concretes and ash concretes were made and subjected to physical and mechanical characterization tests at different maturation periods. The results of the tests carried out indicate that the presence of ash reduces the workability and porosity of the concrete and then increases the density of the concrete to 6.3%. In addition, we found that incorporating the ash improves the mechanical strength of the concrete compared to the control concrete. Thus, the compressive strength of ash concrete is 32.07 MPa and that of splitting is 2.76 MPa at 28 days, which is satisfactory vis-à-vis the threshold of construction projects for ready concrete for use, which recommends a minimum of 25 MPa (compression) and 2.6 MPa (splitting) at 28 days. This improvement in mechanical performance can be attributed to the pozzolanic effect of the constituents of the ash. Therefore, the ash from palm nut shells can be used to improve the mechanical properties of concrete.展开更多
To study the damage mechanisms of anhydrite rock under freeze-thaw cycles, the physicalmechanical properties and the microcracking activities of anhydrite rock were investigated through mass variation, nuclear magneti...To study the damage mechanisms of anhydrite rock under freeze-thaw cycles, the physicalmechanical properties and the microcracking activities of anhydrite rock were investigated through mass variation, nuclear magnetic resonance, scanning electron microscope tests, and uniaxial compression combined with acoustic emission(AE) tests. Results show that with the increase of freeze-thaw processes,the mass, uniaxial compression strength, and elastic modulus of the anhydrite specimens decrease while the porosity and plasticity characteristics increase.For example, after 120 cycles, the uniaxial compression strength and elastic modulus decrease by 46.54% and 60.16%, and the porosity increase by 75%. Combined with the evolution trend of stressstrain curves and the detected events, three stages were labeled to investigate the AE characteristics in freeze-thaw weathered anhydrite rock. It is found that with the increase of freeze-thaw cycles, the proportions of AE counts in stage Ⅰ and stage Ⅱ show a decaying exponential trend. Contrarily, the proportion of AE counts in stage Ⅲ displays an exponential ascending trend. Meanwhile, as the freeze-thaw cycles increase, the low-frequency AE signals increase while the intermediate-frequency AE signals decrease. After 120 cycles, the proportion of low-frequency AE signals increases by 168.95%, and the proportion of intermediate-frequency AE signals reduces by 81.14%. It is concluded that the microtensile cracking events occupy a dominant position during the loading process. With the increase of freeze-thaw cycles, the b value of samples decreases.After 120 cycles, b value decreases by 27.2%, which means that the proportion of cracking events in rocks with small amplitude decreases. Finally, it is proposed that the freeze-thaw damage mechanism of anhydrite is also characterized by the water chemical softening effect.展开更多
In order to improve the fire resistance,water resistance and wear resistance of ordinary plywood products in the wood processing industry,three composite structures of plywood products S1,S2 and S3 were designed in th...In order to improve the fire resistance,water resistance and wear resistance of ordinary plywood products in the wood processing industry,three composite structures of plywood products S1,S2 and S3 were designed in this paper,and a reasonable production process was proposed.Through the physical and mechanical properties and fire resistance testing and technical and economic analysis,the applicability of composite plywood was evaluated.The results of the study showed that the physical mechanics of the three kinds of composite structure plywood met the standard requirements,and their fire resistance was far better than that of ordinary plywood.Among them,the S1 structural board had the best overall physical and mechanical properties.The S3 structural board showed the best fire resistance,which was about 1.9 times more than that of ordinary plywood,and the added cost was the lowest.The thin cork board added to the S2 structural board had poor fire performance since the air in the cork board cavities had a certain combustion-supporting effect,which inhibited the fire resistance of high-pressure laminate(HPL)layer.Moreover,the additional cost of the S2 board was the highest,and its comprehensive performance was the worst.The S3 structural plywood product composed of HPL fireproof board with a thickness of about 1 mm in the surface layer and ordinary plywood with a thickness of about 12 mm in the core layer was the most cost-effective product,which could meet the needs of various fields such as construction,home furnishing,decoration and transportation.展开更多
Generally, ring spun yarns are manufactured from roving which is produced by roving frame. In this paper, an experiment has been done producing ring spun cotton yarn directly from finisher drawn sliver eliminatin...Generally, ring spun yarns are manufactured from roving which is produced by roving frame. In this paper, an experiment has been done producing ring spun cotton yarn directly from finisher drawn sliver eliminating the roving frame. Total 3 types of yarn with the various linear density of 8 Ne, 10 Ne & 12 Ne were produced using a roving frame and without using a roving frame. In the next step, physical and mechanical properties of those yarns including unevenness, imperfections, hairiness & tenacity were investigated. The result showed that ring spun cotton yarns produced from sliver exhibited inferior physical and mechanical properties compared with samples from the conventional ring spinning system.展开更多
In this paper, the authors aim to propose the use of waste plastics as a binder in a coconut shell reinforcement for the development of an 8/6 size composite rafter to replace the natural 8/6 size backbone in construc...In this paper, the authors aim to propose the use of waste plastics as a binder in a coconut shell reinforcement for the development of an 8/6 size composite rafter to replace the natural 8/6 size backbone in construction. Following a study into the choice of the best proportions, a total of 30 size 8/6 composite rafters with different proportions of 20%, 25%, 30%, 35%, 40% and 50% plastic content were developed. All the 8/6 composite rafters were subjected to mechanical (3-point bending strength and Monnin hardness) and physical (bulk density and water absorption) characterization analyses. The results show that flexural strength increases from 27.56 MPa to 33.30 MPa for proportions ranging from 20% to 35% plastic content. Above 35% plastic, the strength drops to 19.60 MPa for a 50% plastic content. Similarly, the Monnin hardness drops from 9 mm to 5 mm when the plastic content varies from 20 to 50%. As for the results of the physical characterisation, the values obtained for apparent density vary from 0.89 to 1 for proportions varying from 20% to 35% plastic content and drop to 0.94 for 50% plastic content. As for water absorption, values drop from 6.82% to 2.45% when the plastic content increases from 20% to 50%. These mechanical strengths stabilise at 35% plastic content. The development of an 8/6 chevron composite material based on plastic and coconut shell could therefore be a way of recovering waste and solving the problem of deforestation.展开更多
We investigated the hydration behavior and some physical/mechanical properties of cement-bonded particleboard (CBPB) containing particles of wheat straw and poplar wood at various usage ratios and bonded with Portla...We investigated the hydration behavior and some physical/mechanical properties of cement-bonded particleboard (CBPB) containing particles of wheat straw and poplar wood at various usage ratios and bonded with Portland cement mixed with different levels of inorganic additives. We determined the setting time and compression strength of cement pastes containing different additives and particles, and studied the effects of these additives and particles on thickness swelling, internal bond strength and modulus of rupture of CBPB by using RSM (Response Surface Methodology). The mathematical model equations (second-order response functions) were derived to optimize properties of CBPB by computer simulation programming. Predicted values were in agreement with experimental values (R2 values of 0.93, 0.96 and 0.96 for TS, IB and MOR, respectively). RSM can be efficiently applied to model panel properties. The variables can affect the properties of panels. The cement composites with bending strength 〉 12.5 MPa and internal bond strength 〉 0.28 MPa can be made by using wheat straw as a reinforcing material. Straw particle usage up to 11.5% in the mixture satisfies the minimum requirements of International Standard, EN 312 (2003) for IB and MOR. The dose of 4.95% calcium chloride, by weight of cement, can improve mechanical properties of the panels at the minimum requirement of EN 312. By increasing straw content from 0 to 30%, TS was reduced by increasing straw particle usage up to 1.5% and with 5.54% calcium chloride in the mixture, TS satisfied the EN 312 standard.展开更多
Eight complexes of rare earth with 2 mercaptobenthiazole, RELCl 2·RE(OH) 3· x H 2O (L=2 mercaptobenthiazole, RE= La~Gd, Y, except for Pm, x =0, 2~4), were synthesized in unhydrous ethanol and char...Eight complexes of rare earth with 2 mercaptobenthiazole, RELCl 2·RE(OH) 3· x H 2O (L=2 mercaptobenthiazole, RE= La~Gd, Y, except for Pm, x =0, 2~4), were synthesized in unhydrous ethanol and characterized by elemental analyses, IR spectra and thermal analyses. The results show that the ligand is coordinated to the RE ion through both the exocyclic sulfur and the thiazole nitrogen. The vulcanizing properties of the La complex as accelerator were studied in the traditional tire rubber, which indicate that the cross linked rubber accelerated by the rare earth complex has good physical and dynamic mechanical properties by comparison.展开更多
Under the condition of freeze-thaw cycles, two types of rocks (granite and andesite), used as slope protection for the Qinghai-Tibet Railway, were tested according to the special climatic conditions in the Tibetan P...Under the condition of freeze-thaw cycles, two types of rocks (granite and andesite), used as slope protection for the Qinghai-Tibet Railway, were tested according to the special climatic conditions in the Tibetan Plateau, and their various damage processes in ap- pearance were carefully observed. Observation results show that damage of andesite was more serious than that of granite. Using an acoustic instrument, ultrasonic velocity was tested. The changing trends of velocity with the number of freeze-thaw cycles were analyzed, and the freeze-thaw cycle damaging the physical and mechanical properties of rocks can be seen. According to the changing trends of ultrasonic velocity with the number of freeze-thaw cycles, mechanical parameters of rocks, such as dynamic elasticity modulus, Poisson's ratio, and dynamic bulk modulus were analyzed. It is found that they all have declining trends as the number of fi'eeze-thaw cycles increases, and in particular, when the cycle number reaches a certain extent, the Poisson's ratio of rocks begins to become negative.展开更多
For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde (UF) resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the forma...For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde (UF) resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the formaldehyde emission, physical and mechanical properties of the manufactured particleboard. Wheat straws were treated at three levels of urea concentration (5%, 10%, 15%) and 95℃ as holding temperature. Wheat straw particleboards were manufactured using hot press at 180℃ and 3 MPa with two types of UF adhesive (UF-45, UF-91). Then the formaldehyde emission values, physical properties and mechanical properties were considered. The results show that the for- maldehyde emission value was decreased by increasing urea concentration. Furthermore, the results indicate that the specimens under urea treatment have better mechanical and physical properties compared with control specimens. Also specimens under urea treatment at 10% concentration and UF-91 type adhesive have the most optimum physical and mechanical strength.展开更多
China began to build its national shale gas demonstration area in 2012.The central exploration,drilling,and development technologies for medium and shallow marine shale reservoirs with less than 3,500m of buried depth...China began to build its national shale gas demonstration area in 2012.The central exploration,drilling,and development technologies for medium and shallow marine shale reservoirs with less than 3,500m of buried depth in Changning-Weiyuan,Zhaotong,and other regions had matured.In this study,we macroscopically investigated the development history of shale gas in the United States and China and compared the physical and mechanical conditions of deep and shallow reservoirs.The comparative results revealed that themain reasons for the order-ofmagnitude difference between China’s annual shale gas output and the United States could be attributed to three aspects:reservoir buried depth,reservoir physical and mechanical properties,and engineering technology level.The current engineering technology level of China could not meet the requirements of increasing production and reducing costs for deep shale gas reservoirs;they had reached the beneficial threshold development stage and lacked the capacity for large-scale commercial production.We identified several physical and mechanical reasons for this threshold development stage.Deep shale reservoirs were affected by the bedding fracture,low brittleness index,low clay mineral content,and significant areal differences,as well as by the transformation from elasticity to plasticity,difficulty in sanding,and high mechanical and strength parameters.Simultaneously,they were accompanied by six high values of formation temperature,horizontal principal stress difference,pore pressure,fracture pressure,extension pressure,and closure pressure.The key to deep shale gas horizontal well fracturing was to improve the complexity of the hydraulic fracture network,formadequate proppant support of fracture surface,and increase the practical stimulated reservoir volume(SRV),which accompanied visual hydraulic discrete network monitoring.On this basis,we proposed several ideas to improve China’s deep shale gas development involving advanced technology systems,developing tools,and supporting technologies in shale gas exploration and development in the United States.These ideas primarily involved stimulation technologies,such as vertically integrated dessert identification and optimization,horizontal well multistage/multicluster fracturing,staged tools development for horizontal wells,fractures network morphology monitoring by microseismic and distributed optical fiber,shale hydration expansion,soak well,and fracturing fluid flow back.China initially developed the critical technology of horizontal well large-scale and high-strength volume fracturing with a core of“staged fracturing with dense cutting+shorter cluster spacing+fracture reorientation by pitching+forced-sand addition+increasing diameter perforating+proppant combination by high strength and small particle size particles”.We concluded that China should continue to conduct critical research on theories and technical methods of horizontal well fracturing,suitable for domestic deep and ultra-deep marine and marine-continental sedimentary shale,to support and promote the efficient development of shale gas in China in the future.It is essential to balance the relationship between the overall utilization degree of the gas reservoir and associated economic benefits and to localize some essential tools and supporting technologies.These findings can contribute to the flourishing developments of China’s deep shale gas.展开更多
The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber compo...The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber composite material will be influenced by the die different structures. The effects of radial-orientation-die structure parameters on properties of short fiber and rubber composite were studied experimentally by different structure parameters, including expansion ratio, expansion angle, dam clearance, molding channel length, convergence angle, and transition channel length. The experimental results indicated that short fiber and rubber composite could get good properties with optimized radial-orientation-die structure parameter. And the optimized structure parameters are that expansion ratio is about 5with an expansion angle of 150°,dam clearance is about 4 mm,molding channel length is about 50 mm,convergence angle is about120°,and transition channel length is about 30 mm. Accordingly,the physical and mechanical properties of the composite can be remarkably improved,which give an obvious anisotropy.展开更多
The demand for alternative cementitious materials is on the rise,as the cement causes huge energy consumption and produces greenhouse gas emission.Additionally,there is economic potential for the construction industry...The demand for alternative cementitious materials is on the rise,as the cement causes huge energy consumption and produces greenhouse gas emission.Additionally,there is economic potential for the construction industry to reuse wastes as supplementary building materials.The purpose of this study is to evaluate the potential of utilizing ferrochrome slag wastes in mortar as supplementary cementitious materials (SCMs),thereby achieving this double-sided goal.Thus,the mechanical and physical properties of ferrochrome slag wastes were investigated to be used as admixtures in concrete production.Three different cement mortar specimens were prepared by replacing cement with ferrochrome slag in ratios of 0,30%,and 60% by mass and flexural and compressive strengths of the specimens were determined at the ages of 7,28,56,90,and 180 days.Also,the effects of the ferrochrome slag replacement ratio on workability,setting time and volume expansion were revealed.Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were also investigated to study the microstructural properties of the specimens containing ferrochrome slag.Based on the results,it is concluded that ferrochrome slag wastes have pozzolanic activity,therefore reusing them as SCMs in the cement and concrete industry is convenient.展开更多
Freeze-thaw hazard is one of the main problems in cold regions engineering and artificial ground freezing engineering.To mitigate freeze-thaw hazards,it is essential to investigate the effects of freeze-thaw on soils ...Freeze-thaw hazard is one of the main problems in cold regions engineering and artificial ground freezing engineering.To mitigate freeze-thaw hazards,it is essential to investigate the effects of freeze-thaw on soils engineering properties.This paper summarizes the effects of freeze-thaw on the physical and mechanical properties of soils reported in recent studies.The differences of freeze-thaw conditions between freezing shaft sinking and cold regions engineering are discussed.Based on the technological characteristics of freezing shaft sinking in deep alluvium,we further attempt to identify key research needs regarding the freeze-thaw effects on the engineering properties of deep soils.展开更多
In this work, we review the developing progress of two-dimensional terahertz time-domain spectroscopy(THz-TDS) and its diverse applications, including analyzing the polarization of THz radiation from a laser-induced...In this work, we review the developing progress of two-dimensional terahertz time-domain spectroscopy(THz-TDS) and its diverse applications, including analyzing the polarization of THz radiation from a laser-induced plasma source and studying the corresponding physical mechanism, and characterizing the optical properties of crystals, etc.展开更多
Current industrial methods for dissolution of cellulose in making regenerated cellulose products are relatively expensive,toxic and dangerous and have environmental problems coming with the hazard chemical wastes.To s...Current industrial methods for dissolution of cellulose in making regenerated cellulose products are relatively expensive,toxic and dangerous and have environmental problems coming with the hazard chemical wastes.To solve these problems,a novel ethylenediamine and potassium thiocyanate(ED/KSCN)solvent system was developed,that is economical,ecofriendly,and highly efficient.The ED/KSCN solvent system was proven to be a suitable solvent for fabricating cellulose(blended with other polymers)membranes.In this study,gluten was used to develop nonporous membranes with cellulose.The method of casting these membranes provided better ones than the former researchers’techniques.These composite membranes’physical and mechanical properties were studied by analysis of morphology,viscosity,crystallinity,thermal behaviors,tensile properties and water absorption of membranes.Results showed that membranes are nonporous,uniform,strong,flexible,ecofriendly and renewable.Mechanical and physical properties were influenced by the ratio of cellulose/gluten.By blending 40% gluten,the tensile strength of cellulose membrane dropped to 15.89 MPa from 35.11 MPa.However,its elongation at break increased from 35.3% to 57.02% accordingly.展开更多
In this research,some practical aspects of densified wood glulam were investigated.For this aim,poplar wood specimens were densified by hygro-thermo-mechanical technique.Glulam specimens were produced by finger joint ...In this research,some practical aspects of densified wood glulam were investigated.For this aim,poplar wood specimens were densified by hygro-thermo-mechanical technique.Glulam specimens were produced by finger joint technique and polyurethane glue was used as resin.Physical and mechanical properties of glulams were investigated according to ASTM D 143-09,ASTM D 905-03 and ISO 8375 standards.Based on obtained results,using this process(steam and pressurize compaction)resulted in improvement of physical and mechanical prop-erties of glulam specimens.Optical microscopic and scanning electron microscopic(SEM)pictures were proved structural changes on wood material during of applied technique.Generally,the increase of wood density and hygrothermal treatment has a positive role on the glulam properties especially its dimensional stability.This tech-nique showed a significant effect on water absorption;the steaming temperature and holding time significantly decreased water absorption but densification process increased this parameter.Also,delamination of specimens was decreased by hygrothermal treatment while densification showed negative effect on delamination.Moreover,modulus of rupture,modulus of elasticity,shear strength and compression strength parallel to grain were decreased by this technique but it is depend to treatment temperature and holding time.Higher temperature and holding time cause to higher decrease in the glulam mechanical strength.展开更多
基金conducted as a joint research projectfinanced by SRTTU(Iran)UPM(Malaysia)
文摘We studied the effects of nanoparticles of organo-silane(NOS) compounds in the size range of20–80 nm on physical and mechanical properties in medium density fiberboard,and used NOS at four consumption levels of 0,50,100,and 150 g kg-1dry wood fibers.Density of all treatments was kept constant at 0.67 g cm-3.The water-repellent property of organo-silane significantly reduced water absorption(WA) and thickness swelling but mechanical properties declined due to the reduced proportion of wood-fiber as organo-silane was added to the matrix:the compression ratio of MDF panels and the integrity among wood-fibers both declined,resulting in reduced mechanical properties.We recommend use of 50 g of NOS/kg wood-fiber to improve WA and thickness swelling while retaining acceptable mechanical properties.
文摘The objective of this investigation was to introduce a cement-based composite of higher quality. For this purpose new hybrid nanocomposite from bagasse fiber,glass fiber and multi-wall carbon nanotubes(MWCNTs)were manufactured. The physical and mechanical properties of the manufactured composites were measured according to standard methods. The properties of the manufactured hybrid nanocomposites were dramatically better than traditional composites. Also all the reinforced composites with carbon nanotube, glass fiber or bagasse fiber exhibited better properties rather than neat cement.The results indicated that bagasse fiber proved suitable for substitution of glass fiber as a reinforcing agent in the cement composites. The hybrid nanocomposite containing10 % glass fiber, 10 % bagasse fiber and 1.5 % MWCNTs was selected as the best compound.
基金the Postgraduate Scientific Research Innovation Project of Hunan Province(No.CX20210867)the Scientific Innovation Fund for Postgraduates of Central South University of Forestry and Technology(No.CX202102030).
文摘The artificial afforestation of precious Phoebe bournei has been carried out in China.During the cultivation process,thinning wood will be produced.The properties of thinning wood might vary greatly with matured wood and require evaluation for better utilization.The objective of the present study aims to determine the wood structure,fiber morphology,and physical and mechanical properties of the Phoebe bournei thinning wood to help us understand the wood properties and improve its utility value.Three 14-year-old Phoebe bournei were cut from Jindong Forestry Farm of Hunan Province,China.The wood structure and fiber morphology were observed and analyzed with a light microscope and scanning electron microscope.The physical and mechanical properties were tested according to the Chinese national standards.The results showed as follows:(1)The Phoebe bournei thinning wood has a beautiful wood figure and fine texture,whereas the heartwood has not yet formed.(2)It is a diffuse-porous hardwood with small and less pores as well as fine wood rays.(3)The wood fiber is medium length and extremely thin wall thickness.(4)It is low in density and has excellent dimensionally stability.(5)The wood mechanical properties belong to the low to medium class and the comprehensive strength of wood belongs to the medium-strength class.It is concluded that Phoebe bournei thinning wood is suitable for wood carving,handicraft,high-end furniture,and decorative furniture parts.
基金The National Natural Science Foundation of China,Grant/Award Number:41702326the Innovative Experts,Long-term Program of Jiangxi Province,Grant/Award Number:jxsq2018106049+1 种基金the Natural Science Foundation of Jiangxi Province,Grant/Award Number:20202ACB214006the Supported by Program of Qingjiang Excellent Young Talents,Jiangxi University of Science and Technology。
文摘In deep-earth engineering,the high earth temperature can significantly affect the rock's mechanical properties,especially when the rock is cooled during the construction process.Accordingly,whether the cooling speed affects the mechanical and physical properties of rocks is worth to be investigated.The present study explored the influence of the cooling rate on the physical and chemical properties of granite heated at 25–800°C.The mechanical and physical properties involved in this study included uniaxial compression strength,peak strain,modulus,P-wave velocity,mass and volume,the change of which could reflect the sensitivity of granite to the cooling rate.Acoustic emission(AE)monitoring,microscopic observation,and X-ray diffraction(XRD)are used to analyze the underlying damage mechanism.It is found that more AE signals and large-scale cracks are accounted for based on the b-value method when the specimens are cooled by water.Furthermore,the microscopic observation by polarized light microscopy indicates that the density,opening degree,and connectivity of the cracks under water cooling mode are higher than that under natural cooling mode.In addition,the XRD illustrates that there is no obvious change in mineral content and diffraction angle at different temperatures,which confirms that the change of mechanical properties is not related to the chemical properties.The present conclusion can provide a perspective to assess the damage caused by different cooling methods to hot rocks.
文摘The use of agricultural waste in construction is an advantage favorable to environmental sanitation, the preservation of non-renewable resources but also to the execution of an ecological work. The objective of this work is to study the influence of the addition of palm nut cockles ash as an adjuvant on the physico-mechanical properties of concrete. For this study, ordinary concretes and ash concretes were made and subjected to physical and mechanical characterization tests at different maturation periods. The results of the tests carried out indicate that the presence of ash reduces the workability and porosity of the concrete and then increases the density of the concrete to 6.3%. In addition, we found that incorporating the ash improves the mechanical strength of the concrete compared to the control concrete. Thus, the compressive strength of ash concrete is 32.07 MPa and that of splitting is 2.76 MPa at 28 days, which is satisfactory vis-à-vis the threshold of construction projects for ready concrete for use, which recommends a minimum of 25 MPa (compression) and 2.6 MPa (splitting) at 28 days. This improvement in mechanical performance can be attributed to the pozzolanic effect of the constituents of the ash. Therefore, the ash from palm nut shells can be used to improve the mechanical properties of concrete.
基金the Fundamental Research Funds for the Central Universities(Project No.2022CDJKYJH037)the National Key R&D Program of China(Grant No.2021YFB3901402)。
文摘To study the damage mechanisms of anhydrite rock under freeze-thaw cycles, the physicalmechanical properties and the microcracking activities of anhydrite rock were investigated through mass variation, nuclear magnetic resonance, scanning electron microscope tests, and uniaxial compression combined with acoustic emission(AE) tests. Results show that with the increase of freeze-thaw processes,the mass, uniaxial compression strength, and elastic modulus of the anhydrite specimens decrease while the porosity and plasticity characteristics increase.For example, after 120 cycles, the uniaxial compression strength and elastic modulus decrease by 46.54% and 60.16%, and the porosity increase by 75%. Combined with the evolution trend of stressstrain curves and the detected events, three stages were labeled to investigate the AE characteristics in freeze-thaw weathered anhydrite rock. It is found that with the increase of freeze-thaw cycles, the proportions of AE counts in stage Ⅰ and stage Ⅱ show a decaying exponential trend. Contrarily, the proportion of AE counts in stage Ⅲ displays an exponential ascending trend. Meanwhile, as the freeze-thaw cycles increase, the low-frequency AE signals increase while the intermediate-frequency AE signals decrease. After 120 cycles, the proportion of low-frequency AE signals increases by 168.95%, and the proportion of intermediate-frequency AE signals reduces by 81.14%. It is concluded that the microtensile cracking events occupy a dominant position during the loading process. With the increase of freeze-thaw cycles, the b value of samples decreases.After 120 cycles, b value decreases by 27.2%, which means that the proportion of cracking events in rocks with small amplitude decreases. Finally, it is proposed that the freeze-thaw damage mechanism of anhydrite is also characterized by the water chemical softening effect.
基金This work was supported by the 2020 Jiangsu Provincial Department of Science and Technology Policy Guidance Category(North Jiangsu Science and Technology Special SZ-L YG202014).
文摘In order to improve the fire resistance,water resistance and wear resistance of ordinary plywood products in the wood processing industry,three composite structures of plywood products S1,S2 and S3 were designed in this paper,and a reasonable production process was proposed.Through the physical and mechanical properties and fire resistance testing and technical and economic analysis,the applicability of composite plywood was evaluated.The results of the study showed that the physical mechanics of the three kinds of composite structure plywood met the standard requirements,and their fire resistance was far better than that of ordinary plywood.Among them,the S1 structural board had the best overall physical and mechanical properties.The S3 structural board showed the best fire resistance,which was about 1.9 times more than that of ordinary plywood,and the added cost was the lowest.The thin cork board added to the S2 structural board had poor fire performance since the air in the cork board cavities had a certain combustion-supporting effect,which inhibited the fire resistance of high-pressure laminate(HPL)layer.Moreover,the additional cost of the S2 board was the highest,and its comprehensive performance was the worst.The S3 structural plywood product composed of HPL fireproof board with a thickness of about 1 mm in the surface layer and ordinary plywood with a thickness of about 12 mm in the core layer was the most cost-effective product,which could meet the needs of various fields such as construction,home furnishing,decoration and transportation.
文摘Generally, ring spun yarns are manufactured from roving which is produced by roving frame. In this paper, an experiment has been done producing ring spun cotton yarn directly from finisher drawn sliver eliminating the roving frame. Total 3 types of yarn with the various linear density of 8 Ne, 10 Ne & 12 Ne were produced using a roving frame and without using a roving frame. In the next step, physical and mechanical properties of those yarns including unevenness, imperfections, hairiness & tenacity were investigated. The result showed that ring spun cotton yarns produced from sliver exhibited inferior physical and mechanical properties compared with samples from the conventional ring spinning system.
文摘In this paper, the authors aim to propose the use of waste plastics as a binder in a coconut shell reinforcement for the development of an 8/6 size composite rafter to replace the natural 8/6 size backbone in construction. Following a study into the choice of the best proportions, a total of 30 size 8/6 composite rafters with different proportions of 20%, 25%, 30%, 35%, 40% and 50% plastic content were developed. All the 8/6 composite rafters were subjected to mechanical (3-point bending strength and Monnin hardness) and physical (bulk density and water absorption) characterization analyses. The results show that flexural strength increases from 27.56 MPa to 33.30 MPa for proportions ranging from 20% to 35% plastic content. Above 35% plastic, the strength drops to 19.60 MPa for a 50% plastic content. Similarly, the Monnin hardness drops from 9 mm to 5 mm when the plastic content varies from 20 to 50%. As for the results of the physical characterisation, the values obtained for apparent density vary from 0.89 to 1 for proportions varying from 20% to 35% plastic content and drop to 0.94 for 50% plastic content. As for water absorption, values drop from 6.82% to 2.45% when the plastic content increases from 20% to 50%. These mechanical strengths stabilise at 35% plastic content. The development of an 8/6 chevron composite material based on plastic and coconut shell could therefore be a way of recovering waste and solving the problem of deforestation.
基金supported by Department of Wood and Paper Science and Technology,University of Zabol
文摘We investigated the hydration behavior and some physical/mechanical properties of cement-bonded particleboard (CBPB) containing particles of wheat straw and poplar wood at various usage ratios and bonded with Portland cement mixed with different levels of inorganic additives. We determined the setting time and compression strength of cement pastes containing different additives and particles, and studied the effects of these additives and particles on thickness swelling, internal bond strength and modulus of rupture of CBPB by using RSM (Response Surface Methodology). The mathematical model equations (second-order response functions) were derived to optimize properties of CBPB by computer simulation programming. Predicted values were in agreement with experimental values (R2 values of 0.93, 0.96 and 0.96 for TS, IB and MOR, respectively). RSM can be efficiently applied to model panel properties. The variables can affect the properties of panels. The cement composites with bending strength 〉 12.5 MPa and internal bond strength 〉 0.28 MPa can be made by using wheat straw as a reinforcing material. Straw particle usage up to 11.5% in the mixture satisfies the minimum requirements of International Standard, EN 312 (2003) for IB and MOR. The dose of 4.95% calcium chloride, by weight of cement, can improve mechanical properties of the panels at the minimum requirement of EN 312. By increasing straw content from 0 to 30%, TS was reduced by increasing straw particle usage up to 1.5% and with 5.54% calcium chloride in the mixture, TS satisfied the EN 312 standard.
文摘Eight complexes of rare earth with 2 mercaptobenthiazole, RELCl 2·RE(OH) 3· x H 2O (L=2 mercaptobenthiazole, RE= La~Gd, Y, except for Pm, x =0, 2~4), were synthesized in unhydrous ethanol and characterized by elemental analyses, IR spectra and thermal analyses. The results show that the ligand is coordinated to the RE ion through both the exocyclic sulfur and the thiazole nitrogen. The vulcanizing properties of the La complex as accelerator were studied in the traditional tire rubber, which indicate that the cross linked rubber accelerated by the rare earth complex has good physical and dynamic mechanical properties by comparison.
基金supported in part by the Important Orientation Projects of the CAS (KZCX2-YW-Q03-04)the Grant of the Western Project Program of the Chinese Academy of Sciences (KZCX2-XB2-10)Natural Science Foundation of China (Grant No. 40625004,40821001)
文摘Under the condition of freeze-thaw cycles, two types of rocks (granite and andesite), used as slope protection for the Qinghai-Tibet Railway, were tested according to the special climatic conditions in the Tibetan Plateau, and their various damage processes in ap- pearance were carefully observed. Observation results show that damage of andesite was more serious than that of granite. Using an acoustic instrument, ultrasonic velocity was tested. The changing trends of velocity with the number of freeze-thaw cycles were analyzed, and the freeze-thaw cycle damaging the physical and mechanical properties of rocks can be seen. According to the changing trends of ultrasonic velocity with the number of freeze-thaw cycles, mechanical parameters of rocks, such as dynamic elasticity modulus, Poisson's ratio, and dynamic bulk modulus were analyzed. It is found that they all have declining trends as the number of fi'eeze-thaw cycles increases, and in particular, when the cycle number reaches a certain extent, the Poisson's ratio of rocks begins to become negative.
文摘For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde (UF) resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the formaldehyde emission, physical and mechanical properties of the manufactured particleboard. Wheat straws were treated at three levels of urea concentration (5%, 10%, 15%) and 95℃ as holding temperature. Wheat straw particleboards were manufactured using hot press at 180℃ and 3 MPa with two types of UF adhesive (UF-45, UF-91). Then the formaldehyde emission values, physical properties and mechanical properties were considered. The results show that the for- maldehyde emission value was decreased by increasing urea concentration. Furthermore, the results indicate that the specimens under urea treatment have better mechanical and physical properties compared with control specimens. Also specimens under urea treatment at 10% concentration and UF-91 type adhesive have the most optimum physical and mechanical strength.
基金funded by the National Key Research and Development Program of China under Grant No.2020YFC1808102the National Natural Science Foundation of China(Grant Nos.51874328,U1762215)the Strategic Cooperation Technology Projects of CNPC and CUPB(Grant No.ZLZX2020-02).
文摘China began to build its national shale gas demonstration area in 2012.The central exploration,drilling,and development technologies for medium and shallow marine shale reservoirs with less than 3,500m of buried depth in Changning-Weiyuan,Zhaotong,and other regions had matured.In this study,we macroscopically investigated the development history of shale gas in the United States and China and compared the physical and mechanical conditions of deep and shallow reservoirs.The comparative results revealed that themain reasons for the order-ofmagnitude difference between China’s annual shale gas output and the United States could be attributed to three aspects:reservoir buried depth,reservoir physical and mechanical properties,and engineering technology level.The current engineering technology level of China could not meet the requirements of increasing production and reducing costs for deep shale gas reservoirs;they had reached the beneficial threshold development stage and lacked the capacity for large-scale commercial production.We identified several physical and mechanical reasons for this threshold development stage.Deep shale reservoirs were affected by the bedding fracture,low brittleness index,low clay mineral content,and significant areal differences,as well as by the transformation from elasticity to plasticity,difficulty in sanding,and high mechanical and strength parameters.Simultaneously,they were accompanied by six high values of formation temperature,horizontal principal stress difference,pore pressure,fracture pressure,extension pressure,and closure pressure.The key to deep shale gas horizontal well fracturing was to improve the complexity of the hydraulic fracture network,formadequate proppant support of fracture surface,and increase the practical stimulated reservoir volume(SRV),which accompanied visual hydraulic discrete network monitoring.On this basis,we proposed several ideas to improve China’s deep shale gas development involving advanced technology systems,developing tools,and supporting technologies in shale gas exploration and development in the United States.These ideas primarily involved stimulation technologies,such as vertically integrated dessert identification and optimization,horizontal well multistage/multicluster fracturing,staged tools development for horizontal wells,fractures network morphology monitoring by microseismic and distributed optical fiber,shale hydration expansion,soak well,and fracturing fluid flow back.China initially developed the critical technology of horizontal well large-scale and high-strength volume fracturing with a core of“staged fracturing with dense cutting+shorter cluster spacing+fracture reorientation by pitching+forced-sand addition+increasing diameter perforating+proppant combination by high strength and small particle size particles”.We concluded that China should continue to conduct critical research on theories and technical methods of horizontal well fracturing,suitable for domestic deep and ultra-deep marine and marine-continental sedimentary shale,to support and promote the efficient development of shale gas in China in the future.It is essential to balance the relationship between the overall utilization degree of the gas reservoir and associated economic benefits and to localize some essential tools and supporting technologies.These findings can contribute to the flourishing developments of China’s deep shale gas.
基金National Natural Science Foundation of China(No.511576)Doctoral Research Foundation of Education Ministry,China(No.20103719110003)Science&Technology Development Planning of Shandong Province,China(No.2013TD16006)
文摘The radial-orientation-die has special structure to make short fibers get radial orientation in rubber matrix during extrusion process,which means the physical and mechanical properties of short fiber and rubber composite material will be influenced by the die different structures. The effects of radial-orientation-die structure parameters on properties of short fiber and rubber composite were studied experimentally by different structure parameters, including expansion ratio, expansion angle, dam clearance, molding channel length, convergence angle, and transition channel length. The experimental results indicated that short fiber and rubber composite could get good properties with optimized radial-orientation-die structure parameter. And the optimized structure parameters are that expansion ratio is about 5with an expansion angle of 150°,dam clearance is about 4 mm,molding channel length is about 50 mm,convergence angle is about120°,and transition channel length is about 30 mm. Accordingly,the physical and mechanical properties of the composite can be remarkably improved,which give an obvious anisotropy.
文摘The demand for alternative cementitious materials is on the rise,as the cement causes huge energy consumption and produces greenhouse gas emission.Additionally,there is economic potential for the construction industry to reuse wastes as supplementary building materials.The purpose of this study is to evaluate the potential of utilizing ferrochrome slag wastes in mortar as supplementary cementitious materials (SCMs),thereby achieving this double-sided goal.Thus,the mechanical and physical properties of ferrochrome slag wastes were investigated to be used as admixtures in concrete production.Three different cement mortar specimens were prepared by replacing cement with ferrochrome slag in ratios of 0,30%,and 60% by mass and flexural and compressive strengths of the specimens were determined at the ages of 7,28,56,90,and 180 days.Also,the effects of the ferrochrome slag replacement ratio on workability,setting time and volume expansion were revealed.Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were also investigated to study the microstructural properties of the specimens containing ferrochrome slag.Based on the results,it is concluded that ferrochrome slag wastes have pozzolanic activity,therefore reusing them as SCMs in the cement and concrete industry is convenient.
基金supported by the National Natural Science Foundation of China(Grant No.41771072)Jiangsu Province Innovation and Entrepreneurship Training program for University Students(Grant No.202010290171H).
文摘Freeze-thaw hazard is one of the main problems in cold regions engineering and artificial ground freezing engineering.To mitigate freeze-thaw hazards,it is essential to investigate the effects of freeze-thaw on soils engineering properties.This paper summarizes the effects of freeze-thaw on the physical and mechanical properties of soils reported in recent studies.The differences of freeze-thaw conditions between freezing shaft sinking and cold regions engineering are discussed.Based on the technological characteristics of freezing shaft sinking in deep alluvium,we further attempt to identify key research needs regarding the freeze-thaw effects on the engineering properties of deep soils.
基金supported by the National Basic Research Program of China under Grant No.2014CB339802,No.2011CB808100the National Natural Science Foundation of China under Grant No.11174156
文摘In this work, we review the developing progress of two-dimensional terahertz time-domain spectroscopy(THz-TDS) and its diverse applications, including analyzing the polarization of THz radiation from a laser-induced plasma source and studying the corresponding physical mechanism, and characterizing the optical properties of crystals, etc.
文摘Current industrial methods for dissolution of cellulose in making regenerated cellulose products are relatively expensive,toxic and dangerous and have environmental problems coming with the hazard chemical wastes.To solve these problems,a novel ethylenediamine and potassium thiocyanate(ED/KSCN)solvent system was developed,that is economical,ecofriendly,and highly efficient.The ED/KSCN solvent system was proven to be a suitable solvent for fabricating cellulose(blended with other polymers)membranes.In this study,gluten was used to develop nonporous membranes with cellulose.The method of casting these membranes provided better ones than the former researchers’techniques.These composite membranes’physical and mechanical properties were studied by analysis of morphology,viscosity,crystallinity,thermal behaviors,tensile properties and water absorption of membranes.Results showed that membranes are nonporous,uniform,strong,flexible,ecofriendly and renewable.Mechanical and physical properties were influenced by the ratio of cellulose/gluten.By blending 40% gluten,the tensile strength of cellulose membrane dropped to 15.89 MPa from 35.11 MPa.However,its elongation at break increased from 35.3% to 57.02% accordingly.
文摘In this research,some practical aspects of densified wood glulam were investigated.For this aim,poplar wood specimens were densified by hygro-thermo-mechanical technique.Glulam specimens were produced by finger joint technique and polyurethane glue was used as resin.Physical and mechanical properties of glulams were investigated according to ASTM D 143-09,ASTM D 905-03 and ISO 8375 standards.Based on obtained results,using this process(steam and pressurize compaction)resulted in improvement of physical and mechanical prop-erties of glulam specimens.Optical microscopic and scanning electron microscopic(SEM)pictures were proved structural changes on wood material during of applied technique.Generally,the increase of wood density and hygrothermal treatment has a positive role on the glulam properties especially its dimensional stability.This tech-nique showed a significant effect on water absorption;the steaming temperature and holding time significantly decreased water absorption but densification process increased this parameter.Also,delamination of specimens was decreased by hygrothermal treatment while densification showed negative effect on delamination.Moreover,modulus of rupture,modulus of elasticity,shear strength and compression strength parallel to grain were decreased by this technique but it is depend to treatment temperature and holding time.Higher temperature and holding time cause to higher decrease in the glulam mechanical strength.