Piezoresistivity in Carbon Fiber Reinforced Cement Based Composites

The results of some interesting investigation on the piezoresistivity of carbon fiber reinforced cement based composites (CFRC) are presented with the prospect of developing a new nondestructive testing method to assess the integrity of the composite. The addition of short carbon fibers to cement-based mortar or concrete improves the structural performance and at the same time significantly decreases the bulk electrical resistivity. This makes CFRC responsive to the smart behavior by measuring the resistance change with uniaxial pressure. The piezoresistivity of CFRC under different stress was studied, at the same time the damage occurring inner specimens was detected by acoustic emission as well. Test results show that there exists a marking pressure dependence of the conductivity in CFRC, in which the so-called negative pressure coefficient of resistive (NPCR) and positive pressure coefficient of resistive (PPCR) are observed under low and high pressure. Under constant pressures, time-dependent resistivity is an outstanding characteristic for the composites, which is defined as resistance creep. The breakdown and rebuild-up process of conductive network under pressure may be responsible for the pressure dependence of resistivity.

Influence of Water Content on Conductivity and Piezoresistivity of Cement-based Material with both Carbon Fiber and Carbon Black

The influence of water content on the conductivity and piezoresistivity of cement-based material with carbon fiber （CF） and carbon black （CB） was investigated. The piezoresistivity of cement-based material with both CF and CB was compared with that of cement-based material with CF only, and the changes in electrical resistivity of cement-based material with both CF and CB under static and loading conditions in different drying and soaking time were studied. It is found that the piezoresistivity of cement-based material with both CF and CB has better repeatability and linearity than that of cement-based material with CF only. The conductivity and the sensitivity of piezoresistive cement-based material with both CF and CB are enhanced as the water content in piezoresistive cement-based material increases.

Piezoresistivity of Carbon Fiber Graphite Cement-based Composites with CCCW

The electrical conductivity and piezoresistivity of carbon fiber graphite cement-matrix composites（CFGCC） with carbon fiber content（1% by the weight of cement）,graphite powder contents （0%-50% by the weight of cement） and CCCW（cementitious capillary crystalline waterproofing materials,4% by the weight of cement） were studied.The experimental results showed that the relationship between the resistivity of CFGCC and the concentration of graphite powders had typical features of percolation phenomena.The percolation threshold was about 20%.A clear piezoresistive effect was observed in CFGCC with 1wt% of carbon fibers,20wt% or 30wt% of graphite powders under uniaxial compressive tests,indicating that this type of smart composites was a promising candidate for strain sensing.The measured gage factor （defined as the fractional change in resistance per unit strain） of CFGCC with graphite content of 20wt% and 30wt% were 37 and 22,respectively.With the addition of CCCW,the mechanical properties of CFGCC were improved,which benefited CFGCC piezoresistivity of stability.

Enhanced piezoresistivity in Ni-silicone rubber composites

This paper reports that the nickel-silicone rubber composites with enhanced piezoresistivity were synthesized with much reduced nickel concentration. A large piezosensitivity of 0.716/kPa and a gauge factor of 600 have been obtained for a composite sample with filler-polymer ratio of 2.7：1 by weight. Measurements of resistance as a function of uniaxial force reveal that the piezoresistance arises predominantly from the internal heterogeneity of the material and the effect of geometrical changes of samples under pressure is negleetably small. The nonlinear current-voltage characteristic of the composite depends strongly on the filler content, the initial compression and the electrical current flowing in the sample. Ohmic behaviour has been observed only in the highly compressed samples. The breakdown strength decreases with increasing filler content of the composite. Both I - V and R - f characteristics indicates that the resistivity of the composites decreases with electrical field, suggesting that the composite may also be used to make voltage sensitive resistors for protecting circuits. All the experimental results favour a quantum tunnelling mechanism of conductivity. It finds that the concept ＇negative resistance＇, often used to describe the phenomena that current decreases with increasing voltage, is not appropriate and should be avoided.

Effect of HPMC on the Piezoresistivity of Smart Concrete Aggregate with Z Shape

Cement mortar with carbon fiber(CFc)and resin-cement mortar with carbon fiber(CFrc)were used as inner and outer cores of smart aggregate with Z shape,respectively,which was used as the basic perception units to prepare smart concrete aggregate with a mosaic structure(SAMS).The hydroxpropyl methylcellulose(HPMC)was taken into consideration to improve the properties of mortar;by using HPMC,the structure of SAMS was optimized and its mechanical and electrical properties were evaluated.The experimental results show that the toughness of mortar could be improved by the complex that formed by epoxy resin,and the effect of HPMC on the flexibility of CFc was greater than that on the flexibility of CFrc;the feasible designing indicates that the CFc-Z core and CFrc-Z core could be used as inner and outer cores of SAMS.When the proposed dosages of HPMC in inner and outer cores are 0.35wt%and 0.2wt%,respectively,it could give an effective prediction for the damage of concrete during the loading process.

Recent advances of wearable and flexible piezoresistivity pressure sensor devices and its future prospects

The human skin inspired soft electronic devices have attracted broadly research attention in the past decades as the promising potential applications in health monitoring and diagnosis,robotics,and prosthetics.The soft wearable piezoresistivity pressure sensor is one of the most attractive candidates for the development of advanced electronic skin for its simple mechanism,compact structure,low cost and power energy consumption and ease of signal acquisition and transforms advantages.In this review,we will explore the recent progress and achievements in the field of piezoresistivity pressure sensor,focusing on the fundamentals of the piezoresistivity pressure sensor and the materials related to the devices,including active materials,substrate materials,and electrode materials.Subsequently,the challenges and outlook are discussed.We list several current challenges perspectives on the development of pressure sensors.Several critical topics for the optimization of the sensitivity and working range of sensing devices toward practical applications are discussed.Finally,perspectives on the slip and force vectors sensors,the developing technologies for multi-function and high-resolution sensor systems and signals process technologies are examined to highlight the near future development tendency in piezoresistivity pressure sensor research field.

Fully sprayed MXene-based high-performance flexible piezoresistive sensor for image recognition

High-performance flexible pressure sensors provide comprehensive tactile perception and are applied in human activity monitoring,soft robotics,medical treatment,and human-computer interface.However,these flexible pressure sensors require extensive nano-architectural design and complicated manufacturing and are timeconsuming.Herein,a highly sensitive,flexible piezoresistive tactile sensor is designed and fabricated,consisting of three main parts:the randomly distributed microstructure on T-ZnOw/PDMS film as a top substrate,multilayer Ti_(3)C_(2)-MXene film as an intermediate conductive filler,and the few-layer Ti_(3)C_(2)-MXene nanosheetbased interdigital electrodes as the bottom substrate.The MXene-based piezoresistive sensor with randomly distributed microstructure exhibits a high sensitivity over a broad pressure range(less than 10 kPa for 175 kPa^(-1))and possesses an out-standing permanence of up to 5000 cycles.Moreover,a 16-pixel sensor array is designed,and its potential applications in visualizing pressure distribution and an example of tactile feedback are demonstrated.This fully sprayed MXene-based pressure sensor,with high sensitivity and excellent durability,can be widely used in,electronic skin,intelligent robots,and many other emerging technologies.

Piezoresistivity studies of diamond films

Like natural diamond, diamond thin films prepared by chemical vapour deposition also have various unique properties. They possess a potential application for high temperature, high speed, high power and anti-radiation devices. Recently, it was found that polycrystaUine p-type diamond films can also have a much stronger piezoresistive ef-

Highly Ordered Thermoplastic Polyurethane/Aramid Nanofiber Conductive Foams Modulated by Kevlar Polyanion for Piezoresistive Sensing and Electromagnetic Interference Shielding

Highly ordered and uniformly porous structure of conductive foams is a vital issue for various functional purposes such as piezoresistive sensing and electromagnetic interference(EMI) shielding. With the aids of Kevlar polyanionic chains, thermoplastic polyurethane(TPU) foams reinforced by aramid nanofibers(ANF) with adjustable pore-size distribution were successfully obtained via a nonsolvent-induced phase separation. In this regard, the most outstanding result is the in situ formation of ANF in TPU foams after protonation of Kevlar polyanion during the NIPS process. Furthermore, in situ growth of copper nanoparticles(Cu NPs) on TPU/ANF foams was performed according to the electroless deposition by using the tiny amount of pre-blended Ti_(3)C_(2)T_(x) MXene as reducing agents. Particularly, the existence of Cu NPs layers significantly promoted the storage modulus in 2,932% increments, and the well-designed TPU/ANF/Ti_(3)C_(2)T_(x) MXene(PAM-Cu) composite foams showed distinguished compressive cycle stability. Taking virtues of the highly ordered and elastic porous architectures, the PAM-Cu foams were utilized as piezoresistive sensor exhibiting board compressive interval of 0–344.5 kPa(50% strain) with good sensitivity at 0.46 kPa^(-1). Meanwhile,the PAM-Cu foams displayed remarkable EMI shielding effectiveness at 79.09 dB in X band. This work provides an ideal strategy to fabricate highly ordered TPU foams with outstanding elastic recovery and excellent EMI shielding performance, which can be used as a promising candidate in integration of satisfactory piezoresistive sensor and EMI shielding applications for human–machine interfaces.

Bioinspired flexible piezoresistive sensor for high-sensitivity detection of broad pressure range

The human skin has the ability to sense tactile touch and a great range of pressures.Therefore,in prosthetic or robotic systems,it is necessary to prepare pressure sensors with high sensitivity in a wide measurement range to provide human-like tactile sensation.Herein,we developed a flexible piezoresistive pressure sensor that is highly sensitive in a broad pressure range by using lotus leaf micropatterned polydimethylsiloxane and multilayer superposition.By superposing four layers of micropatterned constructive substrates,the multilayer piezoresistive pressure sensor achieves a broad pressure range of 312 kPa,a high sensitivity of 2.525 kPa^(−1),a low limit of detection(LOD)of<12 Pa,and a fast response time of 45 ms.Compared with the traditional flexible pressure sensor,the pressure range of this sensor can be increased by at least an order of magnitude.The flexible piezoresistive pressure sensor also shows high robustness:after testing for at least 1000 cycles,it shows no sign of fatigue.More importantly,these sensors can be potentially applied in various human motion detection scenarios,including tiny pulse monitoring,throat vibration detection,and large under-feet pressure sensing.The proposed fabrication strategy may guide the design of other kinds of multifunctional sensors to improve the detection performance.

Recent progress in graphene-based wearable piezoresistive sensors:From 1D to 3D device geometries

Electronic skin and flexible wearable devices have attracted tremendous attention in the fields of human-machine interaction,energy storage,and intelligent robots.As a prevailing flexible pressure sensor with high performance,the piezoresistive sensor is believed to be one of the fundamental components of intelligent tactile skin.Furthermore,graphene can be used as a building block for highly flexible and wearable piezoresistive sensors owing to its light weight,high electrical conductivity,and excellent mechanical.This review provides a comprehensive summary of recent advances in graphene-based piezoresistive sensors,which we systematically classify as various configurations including one-dimensional fiber,two-dimensional thin film,and threedimensional foam geometries,followed by examples of practical applications for health monitoring,human motion sensing,multifunctional sensing,and system integration.We also present the sensing mechanisms and evaluation parameters of piezoresistive sensors.This review delivers broad insights on existing graphene-based piezoresistive sensors and challenges for the future generation of high-performance,multifunctional sensors in various applications.

MXene-based flexible pressure sensor with piezoresistive properties significantly enhanced by atomic layer infiltration

The flexible pressure sensor has been credited for leading performance including higher sensitivity,faster response/recovery,wider detection range and higher mechanical durability,thus driving the development of novel sensing materials enabled by new processing technologies.Using atomic layer infiltration,Pt nanocrystals with dimensions on the order of a few nanometers can be infiltrated into the compressible lamellar structure of Ti3C2Tx MXene,allowing a modulation of its interlayer spacing,electrical conductivity and piezoresistive property.The flexible piezoresistive sensor is further developed from the Pt-infiltrated MXene on a paper substrate.It is demonstrated that Pt infiltration leads to a significant enhancement of the pressure-sensing performance of the sensor,including increase of sensitivity from 0.08 kPa^(-1)to 0.5 kPa^(-1),extension of detection limit from 5 kPa to 9 kPa,decrease of response time from 200 ms to 20 ms,and reduction of recovery time from 230 ms to 50 ms.The mechanical durability of the flexible sensor is also improved,with the piezoresistive performance stable over 1000 cycles of flexure fatigue.The atomic layer infiltration process offers new possibilities for the structure modification of MXene for advanced sensor applications.

Multifunctional characteristics of 3D printed polymer nanocomposites under monotonic and cyclic compression

This study presents the multifunctional characteristics of multi-walled carbon nanotube(MWCNT)/polypropylene random copolymer(PPR) composites enabled via fused filament fabrication(FFF) under monotonic and quasi-static cyclic compression. Utilizing in-house MWCNT-engineered PPR filament feedstocks, both bulk and cellular composites were realized. The morphological features of nanocomposites were examined via scanning electron microscopy, which reveals that MWCNTs are uniformly dispersed. The uniformly dispersed MWCNTs forms an electrically conductive network within the PPR matrix, and the resulting nanocomposite shows good electrical conductivity(~10^(-1)S/cm), improved mechanical performance(modulus increases by 125% and compressive strength increases by 25% for 8 wt% MWCNT loading) and pronounced piezoresistive response(gauge factor of 27.9-8.5 for bulk samples)under compression. The influence of strain rate on the piezoresistive response of bulk samples(4 wt% of MWCNT) under compression was also measured. Under repeated cyclic compression(2% constant strain amplitude), the nanocomposite exhibited stable piezoresistive performance up to 100 cycles. The piezoresistive response under repeated cyclic loading with increasing strain amplitude of was also assessed.The gauge factor of BCC and FCC cellular composites(4 wt% of MWCNT) with a relative density of 30%was observed to be 46.4 and 30.2 respectively, under compression. The higher sensitivity of the BCC plate-lattice could be attributed to its higher degree of stretching-dominated deformation behavior than the FCC plate-lattice, which exhibits bending-dominated behavior. The 3D printed cellular PPR/MWCNT composites structures were found to show excellent piezoresistive self-sensing characteristics and open new avenues for in situ structural health monitoring in various applications.

正交异性材料的压阻特性(英文)

阐述和证明了正交异性材料主方向的压阻特性：（１）压阻效应只与正应变／正应力有关，而与剪切应变／剪切应力无关；（２）压导系数与压阻系数间存在下列关系ηｉｋｋ＝－（γｉ）－２ξｉｋｋ＝－（ρｉ）２ξｉｋｋλｉｋｋ＝－（γｉ）－２χｉｋｋ＝－（ρｉｉ）２χｉｉｋｋ（３）由正交异性单层构成的层合板的电特性呈整体正交异性。

Self-monitoring Application of Asphalt Concrete Containing Graphite and Carbon Fibers

The self-monitoring application of asphalt concrete containing graphite and carbon fibers using indirect tensile test and wheel rolling test were introduced. The experiment results indicate that this kind of pitch-based composite is effective for strain/stress self-monitoring. In the indirect tensile test, for a completely conductive asphalt concrete specimen, the piezoresistivity was very weak and slightly positive, which meant the resistivity increase with the increment of tensile strain at all stress/strain amplitudes, with the gage factor as high as 6. The strain self-sensing ability was superior in the case of higher graphite content. However, when the conductive concrete was embedded into common asphalt concrete specimen as a partial structure function, the piezoresistivity was positive at all stress/strain amplitudes and with the gage factor of 13, which was much higher than that of completely conductive specimen. Thus, the strain self-sensing ability was superior when conductive asphalt concrete was taken in as a partial structure function. In the wheel-rolling test, the piezoresistivity was highly positive. At any stress amplitude, the piezoresistivity was strong, with the gage factor as high as 100, which was higher for a stress amplitude of 0.7 MPa than that of 0.5 MPa.

Piezoresistive Response Extraction for Smart Cement-based Composites/Sensors

A kind of piezoresistive response extraction method for smart cement-based composites/sensors was proposed.Two kinds of typical piezoresistive cement-based composites/sensors were fabricated by respectively adding carbon nanotubes and nickel powders as conductive fillers into cement paste or cement mortar.The variation in measured electrical resistance of such cement-based composites/sensors was explored without loading and under repeated compressive loading and impulsive loading.The experimental results indicate that the measured electrical resistance of piezoresistive cement-based composites/sensors exhibits a two-stage variation trend of fast increase and steady increase with measurement time without loading,and an irreversible increase after loading.This results from polarization caused by ionic conduction in these composites/sensors.After reaching a plateau,the measured electrical resistance can be divided into an electrical resistance part and an electrical capacity part.The piezoresistive responses of electrical resistance part in measured electrical resistance to loading can be extracted by eliminating the linear electrical capacity part in measured electrical resistance.

Field Sensing Characteristic Research of Carbon Fiber Smart Material

In order to research the field sensing characteristic of the carbon fiber smart material, the Tikhonov regularization principle and the modified Newton-Raphson(MNR) algorithm were adopted to solve the inverse problem of the electrical resistance tomography(ERT). An ERT system of carbon fiber smart material was developed. Field sensing characteristic was researched with the experiment. The experimental results show that the specific resistance distribution of carbon fiber smart material is highly consistent with the distribution of structural strain. High resistance zone responds to high strain area, and the specific resistance distribution of carbon fiber smart material reflects the distribution of sample strain in covering area. Monitoring by carbon fiber smart material on complicated strain status in sample field domain is realized through theoretical and experimental study.

Electrical and Piezoresistive Properties of Steel Fiber Cement-based Composites Aligned by a Magnetic Field

Directionally distributed steel fiber cement-based composites(SFCCs)were prepared by magnetic field(MF)induction technology.The orientation factor of steel fibers in the as-obtained SFCCs was determined.Besides,the electrical resistivity and piezoresistive responses in two directions of aligned steel fiber cement-based composites,i e,parallel and perpendicular to MF,were measured.The effects of several variables,eg,steel fiber content,curing age,humidity,and temperature,on anisotropic electrical property were studied.The cyclic and failure piezoresistive responses in different directions were tested.It is found that the aligned steel fibers in the as-obtained SFCCs have a high orientation factor more than 0.88.Besides,SFCCs with aligned steel fibers exhibit an obvious anisotropic conductivity and piezoelectric sensitivity.The electrical conductivity of SFCCs with aligned steel fibers is less affected by temperature and humidity.At the steel fiber content of 2.5wt%,the piezoelectric sensitivity coefficient of SFCCs in the direction parallel to MF has the highest value of 324.14.In addition,the piezoresistive properties of SFCCs with aligned steel fibers in the direction parallel to MF indicate excellent sensitivity and stability under cyclic loading and monotonic loading.

DESIGN,FABRICATION,TESTING AND MECHANICAL ANALYSIS OF BULK-MICROMACHINED FLOWMETERS

Micromachined piezoresistive flowmeters with four different types of sensing struc- tures have been designed,fabricated and tested.Piezoresistors were defined at the end of the sensors through p-diffusion,and their values were about 3.5kΩ.Wheatstone bridge was configured with the piezoresistors in order to measure the output response.The output voltage increases with increasing flow rate of air,obeying determined relationships.The testing results show that the sensors that are designed for measuring 10L/M in full operational range have desired sensitivities.The sensor chip is manufactured with bulk-micromachining technologies,requiring a set of seven masks.

The Effect of Temperature and Doping Level on the Characteristics of Piezoresistive Pressure Sensor

Piezoresistive pressure sensors based on silicon have a large thermal drift because of their high sensitivity to temperature. The study of the effect of the temperature and doping level on characteristics of these sensors is essential to define the parameters that cause the output characteristics drift. In this study, we adopted the model of Kanda to determine the effect of the temperature and of doping level on the piezoresistivity of the Silicon monocrystal. This is to represent P(N,T) and for p-type silicon as functions of impurity concentration for different temperatures. This allows us to see the effect of temperature and doping concentration on the output characteristics of the sensor. Finally, we study the geometric influence parameters and doping on these characteristics to optimize the sensor performance. This study allows us to predict the sensor behavior against temperature and to minimize this effect by optimizing the doping concentration.