Structure and corrosion behavior of FeCoCrNiMo high-entropy alloy coatings prepared by mechanical alloying and plasma spraying

FeCoCrNiMox composite powders were prepared using the mechanical alloying technique and made into high-entropy alloy(HEA)coatings with the face-centered cubic phase using plasma spraying to address the element segregation problem in HEAs and pre-pare uniform HEA coatings.Scanning electron microscopy,transmission electron microscopy,and X-ray diffractometry were employed to characterize these coatings’microstructure and phase composition.The hardness,elastic modulus,and fracture toughness of coatings were tested,and the corrosion resistance was analyzed in simulated seawater.Results show that the hardness of the coating is HV0.1606.15,the modulus of elasticity is 128.42 GPa,and the fracture toughness is 43.98 MPa·m^(1/2).The corrosion potential of the coating in 3.5wt%NaCl solution is-0.49 V,and the corrosion current density is 1.2×10^(−6)A/cm^(2).The electrochemical system comprises three parts:the electrolyte,the adsorption and metallic oxide films produced during immersion,and the FeCoNiCrMo HEA coating.Over in-creasingly long periods,the corrosion reaction rate increases first and then decreases,the corrosion product film comprising metal oxides reaches a dynamic balance between formation and dissolution,and the internal reaction of the coating declines.

Different bactericidal abilities of plasma-activated saline with various reactive species prepared by surface plasma-activated air and plasma jet combinations

Plasma-activated water(PAW),as an extended form of cold atmospheric-pressure plasma,greatly expands the application of plasma-based technology.The biological effects of PAW are closely related to the aqueous reactive species,which can be regulated by the activation process.In this study,surface plasma-activated air(SAA)and a He+O_(2)plasma jet(Jet)were parallelly combined(the SAA+Jet combination)or sequentially combined(the SAA→Jet combination and the Jet→SAA combination)to prepare plasma-activated saline(PAS).The PAS activated by the combinations exhibited stronger bactericidal effects than that activated by the SAA or the Jet alone.The concentrations of H_(2)O_(2)and NO_(2)^(-)were higher in the PAS activated by the Jet→SAA combination,while ONOO^(-)concentrations were close in the three kinds of PAS and^(1)O_(2)concentrations were higher in the PAS activated by the SAA+Jet combination.The analysis of scavengers also demonstrated that H_(2)O_(2),^(1)O_(2),and ONOO^(-)in the PAS activated by the SAA+Jet combination,and^(1)O_(2)in the PAS activated by the Jet→SAA combination played critical roles in bactericidal effects.Further,the effective placement time of the three PAS varied,and the PAS activated by the Jet→SAA combination could also inactivate 2.6-log_(10)of MRSA cells after placement for more than 60 min.The regulation of reactive species in plasma-activated water via different combinations of plasma devices could improve the directional application of plasma-activated water in the biomedical field.

Ultra wear resistant TiC-Fe coating prepared by high efficient and economic plasma cladding method

The key components of engineering machinery frequently failed due to working in the high load and high wear operating envir-onment.And the performance of the Fe-based alloy coatings typically employed need to be improved for fulfilling the service requirements.Herein,a TiC strengthened Fe-based alloy cladding layer,named TiC-Fe coating,was designed and prepared by plasma cladding technology.The frictional wear performance of coating under various loads was tested.The wear morphology of the coating was observed,and its wear mechanism was examined.The results indicated that the TiC-Fe coating was well formed and metallurgically bonded to the Q345C substrate.Its microstructure mainly consisted of Fe-Cr solid solution,α-Fe phase,(Fe,Cr)_(7)C_(3) phase and TiC phase.The coating exhibited an average microhardness of 980 HV0.2,which was about 5.4 times that of the Q345C substrate.The wear mass loss of the TiC-Fe coatings was much smaller than that of the Q345C substrate,which indicated that the wear resistance of the Q345C coating was superior to the substrate,and the wear mechanism of the coating was mainly attributed to the abrasive wear.

Storage time affects the level and diagnostic efficacy of plasma biomarkers for neurodegenerative diseases

Several promising plasma biomarker proteins,such as amyloid-β(Aβ),tau,neurofilament light chain,and glial fibrillary acidic protein,are widely used for the diagnosis of neurodegenerative diseases.However,little is known about the long-term stability of these biomarker proteins in plasma samples stored at-80°C.We aimed to explore how storage time would affect the diagnostic accuracy of these biomarkers using a large cohort.Plasma samples from 229 cognitively unimpaired individuals,encompassing healthy controls and those experiencing subjective cognitive decline,as well as 99 patients with cognitive impairment,comprising those with mild cognitive impairment and dementia,were acquired from the Sino Longitudinal Study on Cognitive Decline project.These samples were stored at-80°C for up to 6 years before being used in this study.Our results showed that plasma levels of Aβ42,Aβ40,neurofilament light chain,and glial fibrillary acidic protein were not significantly correlated with sample storage time.However,the level of total tau showed a negative correlation with sample storage time.Notably,in individuals without cognitive impairment,plasma levels of total protein and tau phosphorylated protein threonine 181(p-tau181)also showed a negative correlation with sample storage time.This was not observed in individuals with cognitive impairment.Consequently,we speculate that the diagnostic accuracy of plasma p-tau181 and the p-tau181 to total tau ratio may be influenced by sample storage time.Therefore,caution is advised when using these plasma biomarkers for the identification of neurodegenerative diseases,such as Alzheimer's disease.Furthermore,in cohort studies,it is important to consider the impact of storage time on the overall results.

Properties and microstructure of Cu/diamond composites prepared by spark plasma sintering method

Cu/diamond composites have been considered as the next generation of thermal management material for electronic packages and heat sinks applications. Cu/diamond composites with different volume fractions of diamond were successfully prepared by spark plasma sintering（SPS） method. The sintering temperatures and volume fractions（50%, 60% and 70%） of diamond were changed to investigate their effects on the relative density, homogeneity of the microstructure and thermal conductivity of the composites. The results show that the relative density, homogeneity of the microstructure and thermal conductivity of the composites increase with decreasing the diamond volume fraction; the relative density and thermal conductivity of the composites increase with increasing the sintering temperature. The thermal conductivity of the composites is a result of the combined effect of the volume fraction of diamond, the homogeneity and relative density of the composites.

Microstructure and magnetic properties of anisotropic Nd-Fe-B magnets prepared by spark plasma sintering and hot deformation

Bulk anisotropic Nd-Fe-B magnets were prepared from hydrogen-disproportionation-desorption-recombination（HDDR） powders via spark plasma sintering（SPS） and subsequent hot deformation. The influence of sintering temperature on the structure and magnetic properties of the spark plasma sintered Nd-Fe-B magnets were studied. The remanence Br, intrinsic coercivity Hcj, and the maximum energy product（BH）max, of sintered Nd-Fe-B magnets first increase and then decrease with the increase of sintering temperature, TSPS, from 650 °C to 900 °C. The optimal magnetic properties can be obtained when TSPS is 800 °C. The Nd-Fe-B magnet sinter treated at 800 °C was subjected to further hot deformation. Compared with the starting HDDR powders or the SPS treated magnets, the hot-deformed magnets present more obvious anisotropy and possess much better magnetic properties due to the good c-axis texture formed in the deformation process. The anisotropic magnet deformed at 800 °C with 50% compression ratio has a microstructure consisting of well aligned and platelet-shaped Nd2Fe14 B grains without abnormal grain growth and exhibits excellent magnetic properties parallel to the pressing axis.

Microstructure and mechanical properties of TiAl-based alloy prepared by double mechanical milling and spark plasma sintering

A fine-grained TiAl alloy with a composition of Ti-45Al-2Cr-2Nb-1B-0.5Ta-0.225Y （mole fraction, %） was prepared by double mechanical milling（DMM） and spark plasma sintering（SPS）. The relationship among sintering temperature, microstructure and mechanical properties was studied. The results show that the morphology of double mechanical milled powder is regular with size in the range of 20-40 μm and mainly composed of TiAl and Ti3Al phases. The main phase TiAl and few phases Ti3Al, Ti2Al and TiB2 were observed in the SPSed alloys. For samples sintered at 900 ℃ the equiaxed crystal grain microstructure is achieved with size in the range of 100-200 nm. With increasing the SPS temperature from 900 ℃to 1000 ℃ the size of equiaxed crystal grain obviously increases, the microhardness decreases from HV658 to HV616, and the bending strength decreases from 781 MPa to 652 MPa. In the meantime, the compression fracture strength also decreases from 2769 MPa to 2669 MPa, and the strain to fracture in compression increases from 11.69% to 17.76%. On the base of analysis of fractographies, it shows that the compression fracture transform of the SPSed alloys is intergranular rupture.

Fe_(75)Zr_3Si_(13)B_9 magnetic materials prepared by spark plasma sintering

Fe75Zr3Si13B9 magnetic amorphous powders were fabricated by mechanical alloying. Bulk amorphous and nanocrystalline alloys with 20 mm in diameter and 7 mm in height were fabricated by the spark plasma sintering technology at different sintering temperatures. The phase composition, glass transition temperature （Tg）, onset crystallization temperature （Tx）, peak temperature （Tp） and super-cooled liquid region （ΔTx） of Fe75Zr3Si13B9 amorphous powders were analyzed by X-ray diffraction （XRD） and differential scanning calorimetry （DSC）. The phase transition, microstructure, mechanical properties and magnetic performance of the bulk alloys were discussed with X-ray diffractometer, scanning electron microscope （SEM）, Gleeble 3500 and vibration sample magnetometer （VSM）, respectively. It is found that with the increase in the sintering temperature at the pressure of 500 MPa, the density, compressive strength, micro-hardness and saturation magnetization of the sintering samples improved significantly, the amorphous phase began to crystallize gradually. Finally, the desirable amorphous and nanocrystalline magnetic materials at the sintering temperature of 863.15 K and the pressure of 500 MPa have a density of 6.9325 g/cm3, a compressive strength of 1140.28 MPa and a saturation magnetization of 1.28 T.

Characterization of carbon encapsulated Fe-nanoparticles prepared by confined arc plasma

Carbon encapsulated Fe nanoparticles were successfully prepared via confined arc plasma method. The composition, morphology, microstructure, specific surface area and particle size of the product were characterized via X-ray diffraction, transmission electron microscopy, high resolution transmission electron microscopy, energy dispersive X-ray spectrometry and Brunauer-Emmett-Teller N2 adsorption. The experiment results show that the carbon encapsulated Fe nanoparticles have clear core-shell structure. The core of the particles is body centered cubic Fe, and the shell is disorder carbons. The particles are in spherical or ellipsoidal shapes. The particle size of the nanocapsules ranges from 15 to 40 nm, with the average value of about 30 nm. The particle diameter of the core is 18 nm, the thickness of the shells is 6-8 nm, and the specific surface area is 24 m2/g.

Hydrogen storage properties of Mg-TiO_2 composite powder prepared by arc plasma method

Mg-based Mg-TiO2 composite powder was prepared by arc plasma evaporation of the Mg＋5%TiO2 mixture followed by passivation in air. ICP, XRD and SEM techniques were used to characterize the composition, phase components and microstructure of the composite powder. The hydrogen sorption properties of the composite powder were investigated by DSC and PCT techniques. According to the data from PCT measurements, the hydrogenation enthalpy and entropy changes of the composite powder are calculated to be-71.5 kJ/mol and-130.1 J/（K·mol）, respectively. Besides, the hydrogenation activation energy is determined to be 77.2 kJ/ mol. The results indicate that TiO2 added into Mg by arc plasma method can act as a catalyst to improve the hydrogen sorption kinetic properties of Mg.

Effect of sintering temperature on the microstructure and thermal conductivity of Al/diamond composites prepared by spark plasma sintering

Spark plasma sintering was used to fabricate Al/diamond composites.The effect of sintering temperature on the microstructure and thermal conductivity（TC） of the composites was investigated with the combination of experimental results and theoretical analysis.The composite sintered at 550℃shows high relative density and strong interfacial bonding,whereas the composites sintered at lower（520CC） and higher（580-600℃） temperatures indicate no interfacial bonding and poor interfacial bonding,respectively.High relative density and strong interfacial bonding can maximize the thermal conductivity of Al/diamond composites,and taking both effects of particle shape and inhomogeneous interfacial thermal conductance into consideration can give a fairly good prediction of composites＇ thermal conduction properties.

Microstructure and corrosion resistance of Fe/Mo composite amorphous coatings prepared by air plasma spraying

Fe/Mo composite coatings were prepared by air plasma spraying （APS） using Fe-based and Mo-based amorphous and nanocrys- talline mixed powders. Microstructural studies show that the composite coatings present a layered structure with low porosity due to adding the self-bonded Mo-based alloy. Corrosion behaviors of the composite coatings, the Fe-based coatings and the Mo-based coatings were in- vestigated by electrochemical measurements and salt spray tests. Electrochemical results show that the composite coatings exhibit a lower polarization current density and higher corrosion potentials than the Fe-based coating when tested in 3.5wt% NaC1 solutions, indicating supe- rior corrosion resistance compared with the Fe-based coating. Also with the increase in addition of the Mo-based alloy, a raised corrosion re- sistance, inferred by an increase in corrosion potential and a decrease in polarization current density, can be found. The results of salt spray tests again show that the corrosion resistance is enhanced by adding the Mo-based alloy, which helps to reduce the porosity of the composite coatings and enhance the stability of the passive films.

Effect of Thermal Treatment on the Grain Growth of Nanostructured YSZ Thermal Barrier Coating Prepared by Air Plasma Spraying

A nanostructured thermal barrier coating is prepared by air plasma spraying using the 8wt% Y_2O_3 partially stabilized zirconia nano-powder with an average grain size of 40 nm. The microstructure and phase composition of feedstock nano-powder and coating are investigated using SEM, TEM and XRD. It is found that the as-sprayed zirconia coating has an average grain size of 67 nm and mainly consistes of metastable tetragonal phase, together with some monoclinic phase and tetragonal phase. Thermal treatment results show that the grains of the nanostructured coating grow slightly below 900℃, whereas over 1000℃ the gains grow rapidly and monoclinic phase noticeably appeares.

Tribological behavior of different films on Ti-6Al-4V alloy prepared by plasma-based ion implantation

The tribological behaviors of TiN coating and TiN+TiC+Ti(C, N)/diamond like carbon (DLC), TiN/DLC, TiC/DLC multilayers on Ti 6Al 4V alloy prepared by plasma based ion implantation (PBII) were compared. Under the test conditions of counterbody AISI 52100, load 1 N and speed 0.05 m/s, the tribological properties of the alloy are improved by these films in the order of TiN, TiC/DLC, TiN/DLC and TiN+TiC+Ti(C,N)/DLC. Tribological behavior is affected by the conditions of surface modification and triboexperiments. The appearance of “peaks” in the wear dynamic resistance profiles may be due or correspond to the process of formation and breaking apart of transition films. The breakthrough of the DLC coated samples may start from partially wearing out, and end with joining piece dilamination. There are transition films on all counterbodies AISI 52100. When AISI 52100 counterbody is changed to Ti 6Al 4V, the wear of most modified samples is changed from only disc to both disc and ball abrasive dominated.

Ni-Co/Mg-Al catalyst derived from hydrotalcite-like compound prepared by plasma for dry reforming of methane

Ni-Co bimetallic catalysts with different Ni/Co content were derived from cold plasma jet decomposition and reduction of hydrotalcite-like compounds containing Ni,Co,Mg and Al,and their catalytic performance was investigated with dry reforming of methane.Experimental results showed that the hydrotalcite-like precursors could be completely decomposed and partly reduced by cold plasma jet,and the Nicontained catalysts exhibited much higher activity than the catalyst without Ni.Especially,the catalyst with Ni/Co ratio of 8/2 achieved not only the highest conversions of 80.3%and 69.3%for CH4 and CO2,respectively,but also the best stability in 100 h testing.The catalysts were characterized by XRD,XPS,TEM and N2 adsorption techniques,and the results showed that the better performance of the 8Ni2Co bimetallic catalyst was attributed to its higher metal dispersion,smaller metal particle size,as well as the interaction effect between Ni and Co,which were brought by the special catalyst preparation method.

Effect of rare earths on mechanical properties of plasma nitrocarburized surface layer of 17-4PH steel

The aim of this investigation is to reveal the influence of rare earths(RE) addition on mechanical properties of plasma nitrocarburized 17-4PH steel.The nitrocarburized layers were characterized by optical microscope,scanning electron microscope equipped with energy dispersive X-ray analyzer,X-ray diffractometer,microhardness tester and pin-on-disc tribometer.The results showed that RE atoms could diffuse into the surface layer of 17-4PH steel plasma nitrocarburized at 500 °C for 4 h and did not change the ...

Examination of Plasma Nitriding Microstructure with Addition of Rare Earths

Medium-carbon alloy steel was plasma nitrided with rare earths La, Ce and Nd into the nitriding chamber respectively. The nitriding layer microstructures with and without rare earths were compared using optical microscope,normal SEM and high resolution SEM, as well as TEM. It was found that the extent of the influence on plasma nitriding varies with different contents of rare earth. The effect of plasma nitriding is benefit from adding of Ce or Nd. The formation of hard and brittle phase Fe_(2-3)N can be prevented and the butterfly-like structure can be improved by adding Ce or Nd. However, pure La may prevent the diffusion of nitrogen and the formation of iron nitride, and reduce the depth of diffusion layer.

Effects of silver powder particle size on the microstructure and properties of Ag-Yb_2O_3 electrical contact materials prepared by spark plasma sintering

mg-Yb203 electrical contact materials were fabricated by spark plasma sintefing （SPS）. The effects of silver powder particle size on the microstructure and properties of the samples were investigated. The surface morphologies of the sintered samples were examined by optical microscope （OM）, and the fracture morphologies were observed by scanning electron microscopy （SEM）. The physical and mechanical properties such as density, electrical resistivity, microhardness, and tensile strength were also tested. The results show that the silver powder particle size has evident effects on the sintered materials. Comparing with coarse silver powder （5 ktm）, homogeneous and fme microstmcture was obtained by fine silver powder （_〈0.5-1am）. At the same time, the electrical conductivity, microhardness, and tensile strength of the sin- tered samples with fine silver powder were higher than those of the samples with coarse silver powder. However, silver powder particle size has little influence on the relative densities, which of all samples （both by free and coarse silver powders） is more than 95%. The fracture characteristics are ductile.

Ni60-SiC Coating Prepared by Plasma Spraying, Plasma Re-melting and Plasma Spray Welding on Surface of Hot Forging Die

In order to produce the hear-resistant inner layer of hot-forging die, plasma spraying and plasma re-melting and plasma spray welding were adopted. Substrate material was W6Mo5Cr4V2, including 10%, 20%, 30% SiC ceramic powder used as coating material to obtain different Ni-based SiC alloys coating. Micro-structure and micro-hardness analysis of the coating layer were followed, as well as thermophysical properties for the coating layer were measured. The experimental results show that the coating prepared with 70% Ni60, 30% SiC powder has best properties with plasma spray welding, in which the micro-hardness can achieve 1100 HV, meanwhile can improve the thermal property of hot-forging die dramatically.

Synthesis and Characterization of Nano-sized Boron Powder Prepared by Plasma Torch

Hydrogen thermal plasma jet was employed to prepare nano-sized boron powder with hydrogen reduction of BCI3. The maximum yield of nano-sized boron powders was about 50% with the operational conditions of H2/BCl3 of 4.5：1, total feed of 4.9 m3/h, and plasma power of 25 kW. The samples were analyzed by X-ray diffraction （XRD）, field emission scanning electron microscopy （FE-SEM）, and inductively coupled plasma - mass spectrometry （ICP-MS）, inductively coupled plasma - atomic emission spectrometry （ICP-AES）, inductive combustion infrared absorption （ICIA） and infrared thermal conductivity of oxygen and nitrogen analyzer （ITCA）. The results show that the boron powders have different crystal structures with higher dispersion and purity. The average diameter is about 50 nm, and the purity is 90.29% or so. This new technology can use simple process to produce high quality boron powders, and is feasible for industrial production.