Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were opt...Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were optimized by orthogonal tests.The PTA welding parameters including welding current,powder feed rate and welding speed have significant influence on the tungsten carbide degradation.The values for the optimum welding current,powder feed rate and welding speed were determined to be100A,25g/min and40mm/min,respectively.The produced WC/Ni-based composite coatings were crack-and degradation-free.The microstructure of deposited layers,as well as the microstructure and microhardness of the optimal coating were further analyzed.展开更多
The application of response surface methodology was highlighted to predict and optimize the percentage of dilution of iron-based hardfaced surface produced by the PTA （plasma tratisferred arc welding） process. The e...The application of response surface methodology was highlighted to predict and optimize the percentage of dilution of iron-based hardfaced surface produced by the PTA （plasma tratisferred arc welding） process. The experiments were conducted based on five-factor five-level central composite rotatable design with full replication technique and a mathematical model was developed using response surface methodology. Furthermore, the response surface methodology was also used to optimize the process parameters that yielded the lowest percentage of dilution.展开更多
The effects of different experimental conditions on the dry sliding wear behavior of stainless steel surface produced by plasma transferred arc （PTA） hardfacing process were studied. The wear test was conducted in a...The effects of different experimental conditions on the dry sliding wear behavior of stainless steel surface produced by plasma transferred arc （PTA） hardfacing process were studied. The wear test was conducted in a pinon-roller wear testing machine, at constant sliding distance of 1 kin. Mathematical models were developed to estimate wear rate incorporating with rotational speed, applied load and roller hardness using statistical tools such as design of experiments, regression analysis and analysis of variance. It is found that the wear resistance of the PTA hardfaced stainless steel surface is better than that of the carbon steel substrate.展开更多
基金Project (2016YFB0300502) supported by the National Key Research and Development Program of ChinaProjects (51601129,51775386) supported by the National Natural Science Foundation of China+2 种基金Project (16PJ1410000) supported by Shanghai Pujiang Program,ChinaProject (16ZR1438700) supported by the Natural Science Foundation of Shanghai,ChinaProject (TPL1706) supported by Traction Power State Key Laboratory of Southwest Jiaotong University,China
文摘Ni-based composite coatings with a high content of tungsten carbides(Stelcar65composite coatings)were synthesized by plasma transferred arc(PTA)hardfacing.The welding parameters of Stelcar65composite coatings were optimized by orthogonal tests.The PTA welding parameters including welding current,powder feed rate and welding speed have significant influence on the tungsten carbide degradation.The values for the optimum welding current,powder feed rate and welding speed were determined to be100A,25g/min and40mm/min,respectively.The produced WC/Ni-based composite coatings were crack-and degradation-free.The microstructure of deposited layers,as well as the microstructure and microhardness of the optimal coating were further analyzed.
基金the financial support to carry out this investigation through sponsored research and development project No.2003/20/36/1-BRNS.
文摘The application of response surface methodology was highlighted to predict and optimize the percentage of dilution of iron-based hardfaced surface produced by the PTA （plasma tratisferred arc welding） process. The experiments were conducted based on five-factor five-level central composite rotatable design with full replication technique and a mathematical model was developed using response surface methodology. Furthermore, the response surface methodology was also used to optimize the process parameters that yielded the lowest percentage of dilution.
文摘The effects of different experimental conditions on the dry sliding wear behavior of stainless steel surface produced by plasma transferred arc （PTA） hardfacing process were studied. The wear test was conducted in a pinon-roller wear testing machine, at constant sliding distance of 1 kin. Mathematical models were developed to estimate wear rate incorporating with rotational speed, applied load and roller hardness using statistical tools such as design of experiments, regression analysis and analysis of variance. It is found that the wear resistance of the PTA hardfaced stainless steel surface is better than that of the carbon steel substrate.