Multiblock poly(ether-b-amide)copolymers comprised of PA1212 and PPO-PEO-PPO with specific moisture-responsive and antistatic properties

Functional multiblock poly(ether-b-amide)(PEBA)copolymers,comprised of PA1212(polyamide 1212)as hard segments and Jeffamine ED-2003 as soft segments,were successfully prepared via two-step melt polycondensation without any amidation catalyst.Here,using diamino-terminated poly(propylene oxide)-poly(ethylene oxide)-poly(propylene oxide)(PPO-PEO-PPO),Jeffamine ED-2003,enhances the compatibility between polyamide oligomer and polyether,which is better than the traditional route using hydroxyl-terminated polyether.The chemical structure of multiblock PEBAs,as well as the microphase separated structure with crystalline phase of polyamide and polyether,were confirmed by heteronuclear multiple-bond correlation spectrum,heteronuclear multiple quantum correlation spectrum,Fourier transform infrared spectroscopy(FT-IR),differential scanning calorimetry and dynamic mechanical analysis.The hydrophilic PEBA copolymers showed water adsorption ranging from 87.3%to 17.1%depending on the polyether content,and specially showed moisture responsive behavior within seconds when exposed to moisture.The corresponding mechanism was studied using time-resolved attenuated total reflectance FT-IR spectroscopy in the molecular level and the water diffusion coefficient was estimated to be 1.07×10^(–8)cm^(2)∙s^(-1).Two-dimensional correlation FT-IR spectra analysis was performed to confirm that the interaction between water and polyether phase was in preference to that between water and polyamide matrix,and water molecule only forms hydrogen bond with the polyether segment.Due to the incorporation of PEO segments,the PEBAs have the surface resistivity varying from 5.6×10^(9)to 6.5×10^(10)Ω,which makes PEBA potential candidate as permanent antistatic agent.

Characterization of 3D Printed Poly(3-Hydroxybutyric-Co-3-Hydroxyvalerate) by Fused Granular Fabrication through Thermal and Mechanical Analyses

Poly[R-3-hydroxybutyrate-co-(R-3-hydroxyvalerate)] (PHBVs) copolymers are promising biopolymers, which could substitute petroleum-based plastics for various applications. PHB and PHBV pellets were processed on a customized 3D printer via Fused Granular Manufacturing (FGM) approach modified with a Mahor screw extruder. To anticipate the behaviour of PHBVs when transformed using conventional thermo-mechanical shaping processes, thermal and mechanical analyses were carried out in order to better understand the effect of annealing temperature on their crystallization behaviour and mechanical properties of PHB polymer and PHBV copolymer. The objectives of the present work were to propose an experimental strategy to study the melting and crystallization events, crystalline structure changes, and mechanical performances of both PHB homopolymer and PHBV copolymer according to identical thermal annealing treatments. A monitoring of 3D printed PHB and PHBV structures was achieved by coupling Differential Scanning Calorimetry (DSC) and tensile tests. .

Poly3D软件及其在地学中的应用

免费的Poly3D边界元软件基于位移不连续性方法,它不仅能够模拟断层或裂缝的静态生长,而且所采用的多边形单元可以很好地表示出复杂多边的不连续界面。该软件在地学中的应用较为广泛,诸如裂缝形成、由断层互相作用造成的应力扰动和滑移量分布、地下断层形态的确定、低于地震识别精度的断层的预测、地震触发等等。

Poly d(GC)在负超螺旋下形成的Z-DNA

为建立一个生理状态下的左旋DNA(Z-DNA)模型,本文以pMD18-T质粒为母本质粒,将含有d(GC)_6、d(GC)_8、d(GC)_(10)、d(GC)_(13)等poly d(GC)片段的特殊序列插入到pMD18-T质粒中,构建了poly d(GC)重组质粒。这些poly d(GC)重组质粒处于负超螺旋状态。甲基化抑制实验证实,这些插入到质粒中的poly d(GC)能够形成潜在的Z-DNA构象。同时,为进一步验证poly d(GC)重复的长度与形成Z-DNA效率的关系,原核表达并亲和层析纯化了鲫鱼PKZZα多肽(P★)。凝胶阻滞实验分析了d(GC)_6、d(GC)_8、d(GC)_(10)、d(GC)_(13)4种重组质粒与P_(Zα)的亲和性。结果显示,P_(Zα)对这4种重组质粒的迁移都能产生阻滞效应,并且随着GC的增多,阻滞效应越明显。说明d(GC)越多,poly d(GC)形成Z-DNA的能力越强。

调节性T细胞在poly I:C/D-GalN诱发的肝脏损伤中的免疫调节作用

目的:探讨调节性T细胞在Polyinosinic-polycytidylic acid(poly I:C)/D-galactosamine(D-GalN)诱发的急性肝脏损伤中的作用及其机制。方法:建立poly I:C/D-GalN诱发的爆发性肝炎小鼠模型,观察比较野生型C57BL/6小鼠、Rag1-/-小鼠(C57BL/6背景)和过继转输调节性T细胞的Rag1-/-小鼠的血清转氨酶活性;肝脏HE染色评价小鼠肝组织病理形态学改变;实时荧光定量PCR检测肝脏TNF-α和IFN-γmRNA水平;ELISA检测血清IFN-γ和TNF-α蛋白水平。结果:poly I:C/D-GalN联合注射后,与野生型小鼠相比,Rag1-/-小鼠血清转氨酶水平明显增高,肝脏损伤更加严重,炎性因子mRNA水平和蛋白水平都显著增加。给Rag1-/-小鼠过继转输CD25+细胞后能明显降低poly I:C/D-GalN诱导的肝脏损伤。结论:调节性T细胞对poly I:C/D-GalN诱发的肝脏损伤有抑制作用,提示调节性T细胞可以负向调节天然免疫细胞。

Synthesis of the Biomimetic Polymer: Aliphatic Diamine and RGDS Modified Poly(d,l-lactic acid)

A novel poly（d, /-lactic acid） （PDLLA） based biomimetic polymer was synthesized by grafting maleic anhydride, butanediamine and arg-gly-asp-ser （RGDS） peptides onto the backbone of PDLLA, aiming to overcome the acidity and auto-accelerating degradation of PDLLA during degradation and to improve its biospecificity and biocompatibility. The synthetic copolymer was characterized by FTIR, ^13C NMR and amino acid analyzer （AAA）.

Microwave-assisted Polymerization of D,L-Lactide with Stannous Octanoate as Catalyst

Poly (lactic acid) (PLA) was synthesized by microwave-assisted ring-opening polymerization of D, L-lactide with stannous octanoate (SnOct(2)) as catalyst. Its weight-average molar mass (M-w) ranged from 39000 to 67000 and the polydispersity index from 1.3 to 1.7. The polymerization rate was much faster than that of the conventional thermal polymerization. A degradation of newly formed PLA in reaction mixture by microwave irradiation was observed.

Transplantation of Nogo-66 receptor gene-silenced cells in a poly(D,L-lactic-co-glycolic acid) scaffold for the treatment of spinal cord injury

Inhibition of neurite growth, which is in large part mediated by the Nogo-66 receptor, affects neural regeneration following bone marrow mesenchymal stem cell transplantation. The tissue engineering scaffold poly（D,L-lactide-co-glycolic acid） has good histocompatibility and can promote the growth of regenerating nerve fibers. The present study used small interfering RNA to silence Nogo-66 receptor gene expression in bone marrow mesenchymal stem cells and Schwann cells, which were subsequently transplanted with poly（D,L-lactide-co-glycolic acid） into the spinal cord lesion regions in rats. Simultaneously, rats treated with scaffold only were taken as the control group. Hematoxylin-eosin staining and immunohistochemistry revealed that at 4 weeks after transplantation, rats had good motor function of the hind limb after treatment with Nogo-66 receptor gene-silenced ceils prus the poly（O,L-lactide-co-glycolic acid） scaffold compared with rats treated with scaffold only, and the number of bone marrow mesenchymal stem cells and neuron-like cells was also increased. At 8 weeks after transplantation, horseradish peroxidase tracing and transmission electron microscopy showed a large number of unmyelinated and myelinated nerve fibers, as well as intact regenerating axonal myelin sheath following spinal cord hemisection injury. These experimental findings indicate that transplantation of Nogo-66 receptor gene-silenced bone marrow mesenchymal stem cells and Schwann cells plus a poly（D,L-lactide-co-glycolic acid） scaffold can significantly enhance axonal regeneration of spinal cord neurons and improve motor function of the extremities in rats following spinal cord injury.

Co-delivery of resveratrol and docetaxel via polymeric micelles to improve the treatment of drug-resistant tumors

Co-delivery of anti-cancer drugs is promising to improve the efficacy of cancer treatment.This study was aiming to investigate the potential of concurrent delivery of resveratrol(RES)and docetaxel(DTX)via polymeric nanocarriers to treat breast cancer.To this end,methoxyl poly(ethylene glycol)-poly(D,L-lactide)copolymer(mPEG-PDLA)was prepared and characterized using FTIR and 1H NMR,and their molecular weights were determined by GPC.Isobologram analysis and combination index calculation were performed to find the optimal ratio between RES and DTX to against human breast adenocarcinoma cell line(MCF-7 cells).Subsequently,RES and DTX were loaded in the mPEG-PDLA micelles simultaneously,and the morphology,particle size distribution,in vitro release,pharmacokinetic profiles,as well as cytotoxicity to the MCF-7 cells were characterized.IC50 of RES and DTX in MCF-7 cells were determined to be 23.0μg/ml and 10.4μg/ml,respectively,while a lower IC50 of 4.8μg/ml of the combination of RES and DTX was obtained.The combination of RES and DTX at a ratio of 1:1(w/w)generated stronger synergistic effect than other ratios in the MCF-7 cells.RES and DTX loaded mPEG-PDLA micelles exhibited prolonged release profiles,and enhanced cytotoxicity in vitro against MCF-7 cells.The AUC(0→t)of DTX and RES in mPEG-PDLA micelles after i.v.administration to rats were 3.0-fold and 1.6-fold higher than that of i.v.injections of the individual drugs.These findings indicated that the co-delivery of RES and DTX using mPEG-PDLA micelles could have better treatment of tumors.

Synthesis and Characterization of Chitosan-g-poly- (D, L-lactic acid) Copolymer

Biodegradable chitosan-g-poly (D, L-lactic acid) copolymers were prepared via two methods. (1) The lactide was grafted onto hydroxyl groups of chitosan by using macromolecular initiator sodium of trimethylsilyl-chitosan, (2) poly (D,L-lactic acid)(PLA) with low molecular weight can be linked to the amino group by coupling activated PLA to trimethylsilyl-chitosan. Two graft copolymers had hydrophilic-hydrophobic character and can be applied as carriers for drug delivery.

Different crystallinity of poly(d,l-lactide-co-p-dioxanone) copolymers acquired by control of chain microstructure

Poly（d,l-lactide-co-p-dioxanone） （P（LA-co-PDO）） copolymers with different chain microstructures were synthesized by onestep or two-step bulk ring-opening polymerizations of d,l-lactide （LA） and p-dioxanone （PDO） monomers using stannous octoate [Sn（Oct）2]/n-dodecanol as the initiating system. The average sequence lengths of the lactidyl （LLA） and dioxanyl （LpDo） units were calculated from the ^1H NMR spectra. It was found that both LLA and Lpoo values from the two-step syntheses were significantly longer than those from the corresponding one-step syntheses, indicating more blocky structure achieved for the twostep copolymers. Corresponding to this difference in microstructure, the two-step copolymers were semi-crystalline, while the one-step copolymers were completely amorphous. In conclusion, the crystallinity of P（LA-co-PDO） copolymers could be adjusted conveniently to meet specific applications by changing the microstructure of the copolymers via different polymerization routes.

C4D制作Low Poly风格元素解析

Low Poly(低面)风格在动态视觉设计中应用越来越广泛。Low Poly风格将具象的元素抽象化,元素构造和颜色都变得更加简单明了,线条更加硬朗,这使物体本身变得更加有趣,主体也变得更加突出与鲜明。本文介绍了制作Low Poly(低面)风格的新方法——减面。

Preparation and Degradation Characteristics of Poly(d,1-laetide) Composite Films

PDLLA/CHI/β-TCP/NGF composite films were prepared by a solvent evaporation method. The degradation characteristics of the poly （d, l-lactide） composite films were studied in vitro and in vivo. The acidity produced by poly （d, l-lactide） materials was not obvious. Adding chitosan and β-TCP can relieve the acidity problem and improve strength performance of films. The NGF has influences on the degradation characteristics of films. It is verified that PDLLA/CHI/β-TCP/NGF composite films prepared by solvent evaporation method have excellent degradation characteristics. It can be used as a perfect biomaterial for repairing nerve injuries.

Biosafety of a 3D-printed intraocular lens made of a poly (acrylamide-co-sodium acrylate) hydrogel in vitro and in vivo

AIM:To assess the biosafety of a poly(acrylamide-cosodium acrylate)hydrogel(PAH)as a 3D-printed intraocular lens(IOL)material.METHODS:The biosafety of PAH was first evaluated in vitro using human lens epithelial cells(LECs)and the ARPE19 cell line,and a cell counting kit-8(CCK-8)assay was performed to investigate alterations in cell proliferation.A thin film of PAH and a conventional IOL were intraocularly implanted into the eyes of New Zealand white rabbits respectively,and a sham surgery served as control group.The anterior segment photographs,intraocular pressure(IOP),blood parameters and electroretinograms(ERG)were recorded.Inflammatory cytokines in the aqueous humor,such as TNFαand IL-8,were examined by ELISA.Cell apoptosis of the retina was investigated by TUNEL assay,and macro PAHge activation was detected by immunostaining.RESULTS:PAH did not slow cell proliferation when cocultured with human LECs or ARPE19 cells.The implantation of a thin film of a 3 D-printed IOL composed of PAH did not affect the IOP,blood parameters,ERG or optical structure in any of the three experimental groups(n=3 for each).Both TNFαand IL-8 in the aqueous humor of PAH group were transiently elevated 1 wk post-operation and recovered to normal levels at 1 and 3 mo post-operation.Iba1+macroPAHges in the anterior chamber angle in PAH group were increased markedly compared to those of the control group;however,there was no significant difference compared to those in the IOL group.CONCLUSION:PAH is a safe material for 3D printing of personal IOLs that hold great potential for future clinical applications.

THE RING-OPENING POLYMERIZATION OF D,L-LACTIDE WITH ONE COMPONENT RARE EARTH CATALYST

(D, L)-Lactide (LA) was first polymerized with one component of rare earth catalysts [Nd(naph)(3), Nd(oct)(3), Nd(O-iPr)(3), Nd(AcAc)(3), Y(AcAc)(3), Sm(AcAc)(3), Er(AcAc)(3))] respectively in solution and in melt state. The effects of [Cat]/[La] molar ratio, solvents, polymerization time, temperature, various rare earth Elements and ligands were investigated in detail. The results showed that both the conversion of polymerization and the molecular weight (MW) of poly (D, L-Lactide) (PLA) in melt polymerization are higher than that in solution polymerization, but the polymerization rate in melt was lower than in solution. The molecular weight distribution (MWD) of PLA is broader with increasing temperature. X-ray study indicated that PLA obtained by Nd(AcAc)(3) in melt polymerization is an amorphous polymer.

Preparation of a novel biodegradable β-cyclodextrin-containing polymer

A novel cyclodextrin-containing polymer was prepared by graftingβ-cyclodextrin onto the backbone of poly(D,L-lactic acid)(PLA).First,mono(6-(2-aminoethyl)amino-6-deoxy)-β-cyclodextrin(β-CD-6-en)was prepared by sulfonylation and amination ofβ-cyclodextrin and modified poly(D,L-lactic acid)(MPLA)was prepared by free radical polymerization of maleic anhydride and PLA.Then,grafting ofβ-cyclodextrin derivative to MPLA backbone was carried out by N-acylation reaction of MPLA andβ-CD-6-en in dimethyl formamide.The synthetic polymer(PLA-β-CD)was characterized by FTIR(Fourier transform infrared)spectroscopy and proton nuclear magnetic resonance(1H NMR)spectroscopy.The results demonstrated that,in the context of remaining the chain structure of PLA,the content ofβ-CD-6-en is 1.6%by the developed synthetic method.

Biomechanical features of Poly-D,L-lactic acid (PDLLA) rods through the degradation in vitro and in vivo

Objective:To observe the changing of biomechanical features during the degradation course of poly-D,L-lactic acid (PDLLA) rods in vivo and in vitro and to evaluate its value as an internal fixation material. Methods:PDLLA rods were emerged into PBS simultaneous body fluid with constant temperature of 37 C and the rods were embedded into muscle tissue of 20 rabbits for degradation in vitro and in vivo . The rods were taken out in 2, 4, 6. 8 and 12 weeks. Biomechanical features of bending, shearing and axial compression strength, rigidity and elastic modulus were observed during the degradation course. Statistical method was used to test the changes of biomechanical parameters. Results: (1) There was similar changes of bending, compressive, shearing strength and bending, compressive and shearing rigidity of the PDLLA rods between in vivo and in vitro. (2)Bending, compressive, shearing strength decreased 33%, 18% and 43% respectively within the first stage of the degradation, and after 6 weeks of degradation, they decreased slowly. (3)Elastic modulus, bending, compressive and shearing rigidity.decreased sharply during the 6 weeks of degradation, with a drop of 22% , 39% and 30% respectively, and after 8 weeks, they decreased slowly. Even after 12 weeks of degradation, the strength of the rods was still higher than that of sponge bone. Conclusion: During the degradation of the material, the strength and rigidity of PDLLA rods can meet the need of fracture fixation of cancellous bones.

Aggregation of Sodium Dodecyl Sulfonate in Poly-ethylene Glycol Aqueous Solutions Studied by Two-dimensional Nuclear Overhauser Enhancement Spectroscopy

Two-dimensional nuclear overhauser enhancement (2D NOESY)measurements show that sodium dodecyl sulfonate SDSN molecules co-aggregate with poly-ethylene glycol PEG in their aqueous solution at a concentration range of SDSN between the so-called co-aggregation concentration (cac) and the. Normal critical micellar concentration (cmc). SDSN micelles are formed when the cmc of SDSN is reached with PEG uniformly distributed in the interior.

浅谈Low poly风格在C4D软件中的应用

如今三维技术与影视后期技术日新月异的发展,各种三维软件如雨后春笋般涌现出来,如Maya、3D Max、Auto CAD、Softimage、Cinema 4D等等。C4D则是其中的佼佼者,不仅是使用者容易上手,操作界面简单明了,而且功能之强大能够与各种后期软件相结合,是行业内很多使用者首选的三维软件。其中Low poly风格是它最具代表性的,它的风格独特,新颖,让人过目不忘,而且又顺应时代发展的潮流,各行各业都能看到它的影子。

MISCIBILITY AND CRYSTALLIZATION BEHAVIOR OF BIODEGRADABLE BLEND OF POLY(β—HYDROXYBUTYRATE)AND POLY(D,L—LACTIDE)—CO—POLY(ETHYLENE GLYCOL)

Studies on the miscibility of PHB/PELA blends showed that PHB and PELA were miscible in amorphous state.The crystallization behavior of PHB in the blend was strongly de- pendent on the addition of PELA component.