Novel sandwich structured glass fiber Cloth/Poly(ethylene oxide)-MXene composite electrolyte

Recently,poly(ethylene oxide)(PEO)-based solid polymer electrolytes have been attracting great attention,and efforts are currently underway to develop PEO-based composite electrolytes for next generation high performance all-solid-state lithium metal batteries.In this article,a novel sandwich structured solid-state PEO composite electrolyte is developed for high performance all-solid-state lithium metal batteries.The PEO-based composite electrolyte is fabricated by hot-pressing PEO,LiTFSI and Ti_(3)C_(2)T_(x) MXene nanosheets into glass fiber cloth(GFC).The as-prepared GFC@PEO-MXene electrolyte shows high mechanical properties,good electrochemical stability,and high lithium-ion migration number,which indicates an obvious synergistic effect from the microscale GFC and the nanoscale MXene.Such as,the GFC@PEO-1 wt%MXene electrolyte shows a high tensile strength of 43.43 MPa and an impressive Young's modulus of 496 MPa,which are increased by 1205%and 6048%over those of PEO.Meanwhile,the ionic conductivity of GFC@PEO-1 wt%MXene at 60℃ reaches 5.01×10^(-2) S m^(-1),which is increased by around 200%compared with that of GFC@PEO electrolyte.In addition,the Li/Li symmetric battery based on GFC@PEO-1 wt%MXene electrolyte shows an excellent cycling stability over 800 h(0.3 mA cm^(-2),0.3 mAh cm^(-2)),which is obviously longer than that based on PEO and GFC@PEO electrolytes due to the better compatibility of GFC@PEO-1 wt%MXene electrolyte with Li anode.Furthermore,the solid-state Li/LiFePO_(4) battery with GFC@PEO-1 wt%MXene as electrolyte demonstrates a high capacity of 110.2–166.1 mAh g^(-1) in a wide temperature range of 25–60C,and an excellent capacity retention rate.The developed sandwich structured GFC@PEO-1 wt%MXene electrolyte with the excellent overall performance is promising for next generation high performance all-solid-state lithium metal batteries.

Laminar Composite Solid Electrolyte with Poly(Ethylene Oxide)-Threaded Metal-Organic Framework Nanosheets for High-Performance All-Solid-State Lithium Battery

Developing laminar composite solid electrolyte with ultrathin thickness and continuous conduction channels in vertical direction holds great promise for all-solid-state lithium batteries.Herein,a thin,laminar solid electrolyte is synthesized by filtrating–NH 2 functionalized metal-organic framework nanosheets and then being threaded with poly(ethylene oxide)chains induced by the hydrogen-bonding interaction from–NH_(2) groups.It is demonstrated that the threaded poly(ethylene oxide)chains lock the adjacent metal-organic framework nanosheets,giving highly enhanced structural stability(Young’s modulus,1.3 GPa)to 7.5-μm-thick laminar composite solid electrolyte.Importantly,these poly(ethylene oxide)chains with stretching structure serve as continuous conduction pathways along the chains in pores.It makes the non-conduction laminar metal-organic framework electrolyte highly conductive:3.97×10^(−5) S cm^(−1) at 25℃,which is even over 25 times higher than that of pure poly(ethylene oxide)electrolyte.The assembled lithium cell,thus,acquires superior cycling stability,initial discharge capacity(148 mAh g^(−1) at 0.5 C and 60℃),and retention(94% after 150 cycles).Besides,the pore size of nanosheet is tailored(24.5–40.9˚A)to evaluate the mechanisms of chain conformation and ion transport in confined space.It shows that the confined pore only with proper size could facilitate the stretching of poly(ethylene oxide)chains,and meanwhile inhibit their disorder degree.Specifically,the pore size of 33.8˚A shows optimized confinement effect with trans-poly(ethylene oxide)and cis-poly(ethylene oxide)conformation,which offers great significance in ion conduction.Our design of poly(ethylene oxide)-threaded architecture provides a platform and paves a way to the rational design of next-generation high-performance porous electrolytes.

Study of Thermal,Phase Morphological and Mechanical Properties of Poly(L-lactide)-b-Poly(ethylene glycol)-b-Poly(L-lactide)/Poly(ethylene glycol)Blend Bioplastics

A poly(L-lactide)-b-poly(ethylene glycol)-b-poly(L-lactide)(PLLA-PEG-PLLA)block copolymer has great potential for use as a flexible bioplastic.Highly flexible bioplastics are required for flexible packaging applications.In this work,a PEG was incorporated into block copolymer as a plasticizer by solvent casting.PLLA-PEG-PLLA/PEG blends with different blend ratios were prepared,and the plasticizing effect and miscibility of PEG in block copolymer were intensively investigated compared to PLLA/PEG blends.The results indicated that the PEG was an effective plasticizer for the block copolymer.The blending of PEG decreased glass-transition temperature and accelerated the crystallization of both the PLLA and PLLA-PEG-PLLA matrices.The PEG was completely miscible when blended with block copolymer and it improved thermal stability of the block copolymer matrix but not of the PLLA matrix.Film extensibility of PLLA-PEG-PLLA/PEG blends steadily increased as the PEG ratio increased.These non-toxic and highly flexible PLLA-PEG-PLLA/PEG bioplastics are promising candidates for several applications such as biomedical devices,tissue scaffolds and packaging materials.

Preparation and Thermo-Responsive Properties of Poly(Oligo(Ethylene Glycol)Methacrylate)Copolymers with Hydroxy-Terminated Side Chain

Thermo-responsive random copolymers,poly(2-(2-methoxyethoxy)ethoxyethyl methacrylate-co-(ethylene glycol)methyl ether methacrylate)(P(EO_(2)-co-EO_(4/5)))and poly(2-(2-methoxyethoxy)ethoxyethyl methacrylate-co-ethylene glycol methacrylate(P(EO2-co-EG4/5))are synthesized via atom transfer radical polymerization(ATRP).The successful synthesis and the narrow polydispersity index(PDI)of two copolymers are indicated by 1H nuclear magnetic resonance(1H-NMR)and gel permeation chromatography(GPC)analyses.The transition behaviors of polymers in the aqueous solution are demonstrated by changes in turbidity and particle sizes.The transition behavior of P(EO2-co-EG4/5)is found to be milder than that of P(EO2-co-EO4/5).Moreover,the presence of hydrogen bonds without thermo-responsive properties established by hydroxyl groups in the end-side chain of P(EO_(2)-co-EG_(4/5))hinders the dehydration at the transition temperature(TT).Attenuated total reflection Fourier transform infrared spectrometry(ATR-FTIR)analysis along with contact angle measurements reveals that both P(EO_(2)-co-EO_(4/5))and P(EO_(2)-co-EG_(4/5))films undergo phase transitions from hydrophilicity to hydrophobicity above TT.By examining the swelling and collapse behaviors of the polymer films during phase transitions,it can be concluded that the end hydroxyl groups may establish hydrogen bonds with neighboring ether groups within the films,which remain intact throughout the phase transition process due to their strong bonding interactions.This leads to an increase in steric hindrance within swollen films thereby impeding dehydration processes and inducing hysteresis during phase transitions.

Controlled delivery of ibuprofen from poly(vinyl alcohol)-poly(ethylene glycol) interpenetrating polymeric network hydrogels

Hydrogels composed of poly(vinyl alcohol)(PVA) and poly(ethylene glycol)(PEG) were synthesized using glutaraldehyde as crosslinker and investigated for controlled delivery of the common anti-inflammatory drug, ibuprofen(IBF). To regulate the drug delivery, solid inclusion complexes(ICs) of IBF in β–cyclodextrin(β–CD) were prepared and added to the hydrogels. The ICs were prepared by the microwave irradiation method, which is more environmentally benign. The formation of IC was confirmed by various analytical techniques and the synthesized hydrogels were also characterized. Controlled release of drug was achieved from the hydrogels containing the ICs in comparison to the rapid release from hydrogels containing free IBF.The preliminary kinetic analysis emphasized the crucial role of β–CD in the drug release process that influences the polymer relaxation, thereby leading to prolonged release. The cytotoxicity assay validated the hydrogels as non-toxic in nature and hence can be utilized for controlled delivery of IBF.

Studies on the Simultaneous Synthesis of Dimethyl Carbonate and Poly(ethylene terephthalate): I. Catalytic Activity of Metal Acetate in Transesterification of Ethylene Carbonate with Dimethyl Terephthalate

A novel direct method for preparation of dimethyl carbonate and poly（ethylene terephthalate） from ethylene carbonate and dimethyl terephthalate has been demonstrated in the presence of metal acetate catalysts, lithium acetate dihydrate showed highest catalytic activity with 47.9% yield of dimethyl carbonate. This method was a green chemical process.

Miscibility, Crystallization, and Rheological Behavior of Solution Casting Poly（3-hydroxybutyrate）/poly（ethylene succinate） Blends Probed by Differential Scanning Calorimetry, Rheology, and Optical Microscope Techniques

The miscibility and crystallization of solution casting biodegradable poly（3-hydroxybuty- rate）/poly（ethylene succinate） （PHB/PES） blends was investigated by differential scanning calorimetry, rheology, and optical microscopy. The blends showed two glass transition temperatures and a depression of melting temperature of PHB with compositions in phase diagram, which indicated that the blend was partially miscible. The morphology observation supported this result. It was found that the PHB and PES can crystallize simultaneously or upon stepwise depending on the crystallization temperatures and compositions. The spherulite growth rate of PHB increased with increasing of PES content. The influence of compositions on the spherulitic growth rate for the partially miscible polymer blends was discussed.

SURFACE MODIFICATION OF BLEND FILMS COMPOSED OF SILK FIBROIN AND POLY(ETHYLENE GLYCOL) MACROMER AND THEIR IN VITRO ANTITHROMBOGENICITY

In order to improve the blood compatibility of silk fibroin (SF), poly(ethylene glycol) macromer (PEGM) in different amounts was added to the SF film to incorporate C=C group into the surface of blend films which were then modified by SO2 gas plasma treatment. ATR-FITR and XPS were used to analyze the chemical change which had occurred on the film's surface. When the content of sulfur on the surface of blend films surpasses 1.59%, the antithrombogenicity of plasma treated films increases remarkably due to surface sulfonation. This result implies that SF with blend of PEGM after SO2 plasma treatment have potential use for making blood-contacting biomaterials.

Characterization and Properties of Electroless Nickel Plated Poly (ethylene terephthalate) Nonwoven Fabric Enhanced by Dielectric Barrier Discharge Plasma Pretreatment

In order to develop a more economical pretreatment method for electroless nickel plating, a dielectric barrier discharge （DBD） plasma at atmospheric pressure was used to improve the hydrophilicity and adhesion of poly （ethylene terephthalate） （PET） nonwoven fabric. The properties of the PET nonwoven fabric including its liquid absorptive capacity （WA）, aging behavior, surface chemical composition, morphology of the surface, adhesion strength, surface electrical resistivity and electromagnetic interference （EMI）- shielding effectiveness （SE） were studied. The liquid absorptive capacity （WA） increased due to the incorporation of oxygen-containing and nitrogen-containing functional groups on the surface of PET nonwoven fabric after DBD airplasma treatment. The surface morphology of the nonwoven fibers became rougher after plasma treatment. Therefore, the surface was more prone to absorb tin sensitizer and palladium catalyst to form an active layer for the deposition of electroless nickel. SEM and X-ray diffraction （XRD） measurements indicated that a uniform coating of nickel was formed on the PET nonwoven fabric. The average EMI-SE of Ni-plating of PET nonwoven fabric maintained a relatively stable value （38.2 dB to 37.3 dB） in a frequency range of 50 MHz to 1500 MHz. It is concluded that DBD is feasible for pretreatment of nonwoven fabric for electroless nickel plating to prepare functional material with good EMI-SE properties.

Poly(L-lactide)-Poly(ethylene glycol) Multiblock Copolymers: Synthesis and Properties

Poly (L-lactide)-poly(ethylene glycol) multiblock copolymers with predetermined block lengths were synthesized by polycondensation of PLA diols and PEG diacids. These copolymers presented special properties, such as better miscibility between the two components, low crystallinity and better hydrophilicity, which can be modulated by adjusting the block lengths of the two components.

THE STRUCTURE AND PROPERTIES OF CHITOSAN/POLYETHYLENE GLYCOL/SILICA TERNARY HYBRID ORGANIC-INORGANIC FILMS

The ternary hybrid films consisting of chitosan(CS),polyethylene glycol(PEG)and nano-sized silica which was surface-modified by amino groups(RNSA)were prepared.The structures of the blend membranes were characterized by attenuation total reflection-infrared spectroscopy(ATR-IR),X-ray diffraction(XRD),optical microscopy(OM)and differential scanning calorimetry(DSC).The results showed that the addition of silica affected not only the distribution and crystallinity of PEG on the sample surface,but also the pha...

Y-shaped block copolymers of poly(ethylene glycol) and poly(N-isopropylacrylamide) synthesized by ATRP

Novel Y-shaped block copolymers of poly（ethylene glycol） and poly（N-isopropylacrylamide）, PEG-b-（PNIPAM）2, were successfully synthesized through atom transfer radical polymerization （ATRP）. A difunctional macroinitiator was prepared by esterification of 2,2-dichloroacetyl chloride with poly（ethylene glycol） monomethyl ether （PEG）. The copolymers were obtained via the ATRP ofN-isopropylacrylamide （NIPAM） at 30℃ with CuCl/Me6TREN as a catalyst system and DMF/H2O （v/v = 3：1） mixture as solvent. The resulting copolymers were characterized by gel permeation chromatography （GPC） and ^1H NMR. These block copolymers show controllable molecular weights and narrow molecular weight distributions （PDI 〈 1.15）. Their phase transition temperatures and the corresponding enthalpy changes in aqueous solution were measured by differential scanning calorimetry （DSC）. As a result, the phase transition temperature of PEG45-b-（PNIPAM55）2 is higher than that of PNIPAM, however, the corresponding enthalpy change is much lower, indicating the significant influence of the macromolecular composition and architecture on the phase transition.

Stable Cycling of All-Solid-State Lithium Metal Batteries Enabled by Salt Engineering of PEO-Based Polymer Electrolytes

Poly(ethylene oxide)(PEO)-based polymer electrolytes show the prospect in all-solid-state lithium metal batteries;however,they present limitations of low room-temperature ionic conductivity,and interfacial incompatibility with high voltage cathodes.Therefore,a salt engineering of 1,1,2,2,3,3-hexafluoropropane-1,3-disulfonimide lithium salt(LiHFDF)/LiTFSI system was developed in PEO-based electrolyte,demonstrating to effectively regulate Li ion transport and improve the interfacial stability under high voltage.We show,by manipulating the interaction between PEO matrix and TFSI^(-)-HFDF^(-),the optimized solid-state polymer electrolyte achieves maximum Li+conduction of 1.24×10^(-4)S cm^(-1)at 40℃,which is almost 3 times of the baseline.Also,the optimized polymer electrolyte demonstrates outstanding stable cycling in the LiFePO_(4)/Li and LiNi_(0.8)Mn_(0.1)Co_(0.1)O_(2)/Li(3.0-4.4 V,200 cycles)based all-solid-state lithium batteries at 40℃.

Simultaneous Synthesis of Dimethyl Carbonate and Poly（ethylene terephthalate） Using Alkali Metals as Catalysts

Dimethyl carbonate （DMC） and poly（ethylene terephthalate） was simultaneously synthesized by the transesterification of ethylene carbonate （EC） with dimethyl terephthalate （DMT） in this paper. This reaction is an excellent green chemical process without poisonous substance. Various alkali metals were used as the catalysts. The results showed alkali metals had catalytic activity in a certain extent. The effect of reaction condition was also studied. When the reaction was carded out under the following conditions： the reaction temperature 250℃, molar ratio of EC to DMT 3 ： 1, reaction time 3h, and catalyst amount 0.004 （molar ratio to DMT）, the yield of DMC was 68.9%.

Flame Retardancy and Thermal Property of Poly (ethylene terephthalate)/Modified Cyclotriphosphazene Composites

In this study,hexachlorocyclotriphosphazene( HCCP)modified by boric acid and 3-aminopropyltriethoxysilane( KH-550)in solvent diglyme( FR-HCCP) was used as the flame retardant for poly( ethylene terephthalate)( PET) composites. The flame retardancy and thermal property of pure PET and flame-retarded PET composites were mainly investigated. The flame retardancy was investigated by limited oxygen index( LOI) and UL-94 vertical burning test. The results showed that the composites could achieved an increased UL-94 V-0 rating and LOI value 30. 2, when the content of FR-HCCP was just 1%. The pyrolysis-gas chromatography-mass spectrometry( Py-GC / MS) study demonstrated that introducing FR-HCCP into PET would prevent the polymer pyrolysis during heating. TGA analysis showed that the addition of FR-HCCP could improve the char formation of the system. Roman spectra showed the order degree of residue was increasing by adding the additive. The morphology and the chemical structure of the charred residue were detected by SEMand FTIR,respectively. Results demonstrated that a good barrier was formed by the char of the composite,which protected the inside of the composite during burning.

In-situ Polymerization-modification Process and Foaming of Poly（ethylene terephthalate）

Most of traditional linear poly(ethylene terephthalate)(PET)resins of relatively low molecular mass and narrow molecular mass distribution have low melt strength at foaming temperatures,which are not enough to support and keep cells.An in-situ polymerization-modification process with esterification and polycondensation stages was performed in a 2 L batch stirred reactor using pyromellitic dianhydride(PMDA)or pentaerythritol(PENTA)as modifying monomers to obtain PETs with high melt strength.The influence of amounts of modifying monomers on the properties of modified PET was investigated.It was found that the selected modifying monomers could effectively introduce branched structures into the modified PETs and improve their melt strength.With increasing the amount of the modifying monomer,the melt strength of the modified PET increased.But when the amount of PENTA reached 0.35%or PMDA reached 0.9%,crosslinking phenomenon was observed in the modified PET.Supercritical carbon dioxide(ScCO2)was employed as physical foaming agent to evaluate the foaming ability of modified PETs.The modified PETs had good foaming properties at 14 MPa of CO2pressure with foaming temperature ranging from 265°C to 280°C.SEM micrographs demonstrated that both modified PET foams had homogeneous cellular structures,with cell diameter ranging from 35μm to 49μm for PENTA modified PETs and38μm to 57μm for PMDA modified ones.Correspondingly,the cell density had a range of 3.5×107cells·cm 3to 7×106cells·cm 3for the former and 2.8×107cells·cm 3to 5.8×106cells·cm 3for the latter.

PHASE SEPARATION BEHAVIOR OF SURLYN IN POLY (ETHYLENE TEREPHTHALTE)

The phase separation behavior of blend of Surlyn and poly(ethylene terephthalate) (PET) has been studied by scanning electron microscopy and IR. It is shown that particles of Surlyn are dispersed in PET matrix, and this phase separation is controlled by heat-treated conditions of the blend.

FOURIER TRANSFORM INFRARED STUDIES OF POLY (ETHYLENE TEREPHTHALATE) FILM IN THE GLASS TRANSITION REGION

Three specimens from a solution-cast poly (ethylene terephthalate) (PET) film, one being liquid-N_2 quenched from 92℃(Q), one being slowly cooled from 92℃(SC) and one being quenched and sub-T_g annealed at 67℃(AN), have been studied by specimen difference spectra Q-SC and AN-Q and temperature difference spectra T-70 and T_2-T_1 for every 2℃ steps on heating to 90℃ at 2℃ /min. SC and AN showed more gauche conformers than Q. That means that the PET chain has more trans conformers at higher temperatures and some of these are frozen during quenching through T_g. A band at 1340 cm^(-1) has been found to be complex containing overlapping bands reflecting trans in crystalline regions and trans in amorphous regions. The temperature difference spectra on heating through T_g showed that the spectral changes in Q are gradual while a rather abrupt change occurs in AN at 80—82℃ for the bands at 1340, 1042 and 1020 cm^(-1). No new conformational structure or new vibrational mode is involved. A kind of locking mechanism is suggested which hinders the molecular vibrational changes in AN below T_g until a sudden release occurs at T_g. These locking sites can be nothing else than sites of tighter local packing of chain segments. Consequently it is believed that inter-chain van der Waals attraction energy plays a dominating role in the volume relaxation and sub-T_g annealing of quenched amorphous polymers.

SYNTHESIS AND CHARACTERIZATION OF AMPHIPHILIC GRAFT COPOLYMER CONTAINING MICROPHASE SEPARATED AND LONG POLY(ETHYLENE OXIDE) SIDE CHAIN STRUCTURES

Acryloyl terminated Poly (ethyleneoxide)macromonomers (PEO-A) with different PEO chain lengths have been prepared by deactivation of PEO alkoxide with acryloyl chloride. A new kind of amphiphilic polystyrene-g-poly (ethylene oxide)graft copolymer containing both microphase separated and PEO side chain structures has been synthesized from radical copolymerization of PEO-A macromonomer with styrene. After careful purification by a newly-developed method called 'selective dissolution', the well-defined structure of the purified copolymers was confirmed by IR, ~1H-NMR and GPC. Various experimental parameters controlling the copolymerization were studied in detail. The results indicated that the feed ratio of styrene to macromonomer(S/M) was the most important determining factor for the composition of the copolymers. A detailed 'comb- model' was proposed to describe the molecular structure of the graft copolymers. Finally, this amphiphilic graft copolymers may readily form microphase separated structures as clearly indicated by transmission electron microscopy.

Crystallization Behavior of Copolymer Poly(ethylene terephth-alate/isophthalate)(IPET)

The non-isothermal crystallization kinetics, isothermal crystallization and the morphology of crystals of the copolymer poly (ethylene terephthalate/ isophthalate )(IPET) were studied by DSC and polarized-light microscopy in this paper. DSC results indicate that the glass transition temperature Tg of IPET is slightly lower than that of poly(ethylene terephthalate) (PET), but the melting temperature Tm and the crystallization temperature Tc of PET and IPET have much difference.The difference of Tc between PET and IPET2 is about 7℃, and the difference of Tm between PET and IPET2 is about 16℃. From the kinetics analysis of the crystallization, the crystallization mechanism of all samples is of three-dimension spherulitic growth from instantaneous nuclei and the incorporation of isophthalate (IPA) decreases the crystallization rate of IPET greatly. The isothermal results indicate that the morphologies of PET and IPET crystals are all spherulite, which is in conformity to the results of nonisothermal dynamic crystallization. At the same time,the spherulite of IPET grows slower and has longer incubation time than the spherulite of PET under the same crystallization condition.