A new comblike polymer host for polymer electrolyte was synthesized by reacting monomethyl ether of poly(ethylene glycol) with poly(vinyl methyl ether-alt-maleic anhydride) and endcapping the residual carboxylic acid ...A new comblike polymer host for polymer electrolyte was synthesized by reacting monomethyl ether of poly(ethylene glycol) with poly(vinyl methyl ether-alt-maleic anhydride) and endcapping the residual carboxylic acid with methanol. Butanone was selected as a solvent for the esterification in order to obtain a completely soluble product. The synthesis process was traced through by LR. Compared with the model compounds, the presumed structure of this comblike polymer has been proved to be valid by C-13 NMR The comb polymer is a white rubbery solid. It can be dissolved in butanone and THF, and manifests good film forming ability.展开更多
The phase behavior of the aqueous solution of poly(vinyl methyl ether) (PVME) sensitive to temperature and the modification of the behavior by using poly(acrylic acid) (PAA) have been studied by ultrasonic attenuation...The phase behavior of the aqueous solution of poly(vinyl methyl ether) (PVME) sensitive to temperature and the modification of the behavior by using poly(acrylic acid) (PAA) have been studied by ultrasonic attenuation measurements and fluorescence probe techniques. It has been observed that PVME solution is transparent at room temperature and becomes turbid upon heating. The solution turns clear again as soon as the temperature is decreased to room temperature. The heating and cooling process can be repeated for many times. The phase behavior of the solution sensitive to temperature is attributed to the conformational changes of the polymer. PVME may adopt an open coil conformation at room temperature. With this conformation, the polymer is well miscible with the solvent, water, and thereby the system is a real solution. The polymer may adopt a compact coil conformation when the temperature is higher than a specific value, which is called the LCST (the lower critical solution temperature) of PVME. In this case, the polymer tangles to each other and forms various aggregates, which can scatter incident light and ultrasonic waves greatly, resulting in the phase separation. Introduction of PAA decreases the temperature sen-sitivity of the phase behavior of the polymer. The nature of the inhibition is attributed to the complexation of PAA with PVME and the strong hydrophilicity of PAA. Results from fluorescence probe studies are in accordance with those from ultrasonic attenuation measurements, indicating again that the ultrasonic attenuation method can be suc-cessfully used for the qualitative studies of polymer conformations and complexation between polymers.展开更多
文摘A new comblike polymer host for polymer electrolyte was synthesized by reacting monomethyl ether of poly(ethylene glycol) with poly(vinyl methyl ether-alt-maleic anhydride) and endcapping the residual carboxylic acid with methanol. Butanone was selected as a solvent for the esterification in order to obtain a completely soluble product. The synthesis process was traced through by LR. Compared with the model compounds, the presumed structure of this comblike polymer has been proved to be valid by C-13 NMR The comb polymer is a white rubbery solid. It can be dissolved in butanone and THF, and manifests good film forming ability.
基金the National Natural Science Foundation of China (No. 20173035), the Ministry of Education (No. 03148), and the Natura
文摘The phase behavior of the aqueous solution of poly(vinyl methyl ether) (PVME) sensitive to temperature and the modification of the behavior by using poly(acrylic acid) (PAA) have been studied by ultrasonic attenuation measurements and fluorescence probe techniques. It has been observed that PVME solution is transparent at room temperature and becomes turbid upon heating. The solution turns clear again as soon as the temperature is decreased to room temperature. The heating and cooling process can be repeated for many times. The phase behavior of the solution sensitive to temperature is attributed to the conformational changes of the polymer. PVME may adopt an open coil conformation at room temperature. With this conformation, the polymer is well miscible with the solvent, water, and thereby the system is a real solution. The polymer may adopt a compact coil conformation when the temperature is higher than a specific value, which is called the LCST (the lower critical solution temperature) of PVME. In this case, the polymer tangles to each other and forms various aggregates, which can scatter incident light and ultrasonic waves greatly, resulting in the phase separation. Introduction of PAA decreases the temperature sen-sitivity of the phase behavior of the polymer. The nature of the inhibition is attributed to the complexation of PAA with PVME and the strong hydrophilicity of PAA. Results from fluorescence probe studies are in accordance with those from ultrasonic attenuation measurements, indicating again that the ultrasonic attenuation method can be suc-cessfully used for the qualitative studies of polymer conformations and complexation between polymers.