The catalytic activities of some heteropolyacids(HPAs) in synthesizing butyl acrylate are reported. It has been demonstrated that 12 tungstophosphoric acid is the most effective catalyst among more than 20 HPA(s...The catalytic activities of some heteropolyacids(HPAs) in synthesizing butyl acrylate are reported. It has been demonstrated that 12 tungstophosphoric acid is the most effective catalyst among more than 20 HPA(salts). Various factors concerned in this reaction have been investigated. The optimum conditions have been found, that is, the molar ratio of alcohol to acid is 1.2∶1.0 , the catalyst concentration 1%(mass fraction), the reaction time 2 h, the temperature 98—124 ℃ and a certain amount of polymerization inhibitor exists.展开更多
Well-defined nonionic hydrophilic ω-acryloyl poly(ethylene oxide) macro-monomer (PEO-A) has been prepared by living anionic polymerization of ethylene oxidewith diphenyl methyl potassium as the initiator and acryloyl...Well-defined nonionic hydrophilic ω-acryloyl poly(ethylene oxide) macro-monomer (PEO-A) has been prepared by living anionic polymerization of ethylene oxidewith diphenyl methyl potassium as the initiator and acryloyl chloride as the reaction termi-nating agent. The polymer was characterized by FTIR and SEC. The emulsifier-free emul-sion polymerization of methyl methacrylate (MMA) and n-butyl acrylate (BA) containingvarious concentrations of PEO-A was studied. In all cases stable emulsion coplymerizationsof MMA and BA were obtained. The stabilizing effect was found to be dependent on themolecular weight and the feed amount of the macromonomer.展开更多
Low dosage kinetic hydrate inhibitors(KHIs)are a kind of alternative chemical additives to high dosage thermodynamic inhibitors for preventing gas hydrate formation in oil&gas production wells and transportation p...Low dosage kinetic hydrate inhibitors(KHIs)are a kind of alternative chemical additives to high dosage thermodynamic inhibitors for preventing gas hydrate formation in oil&gas production wells and transportation pipelines.In this paper,a new KHI,poly(N-vinyl caprolactam)-co-tert-butyl acrylate(PVCapco-TBA),was successfully synthesized with N-vinyl caprolactam(NVCap)and tert-butyl acrylate.The kinetic inhibition performances of PVCap-co-TBA on the formations of both structureⅠmethane hydrate and structureⅡnatural gas hydrate were investigated by measuring the onset times of hydrate formation under different conditions and compared with commercial KHIs such as PVP,PVCap and inhibex 501.The results indicated that PVCap-co-TBA outperformed these widely applied inhibitors for both structureⅠand structureⅡhydrates.At the same dosage of KHI,the maximum tolerable degree of subcooling under which the onset time of hydrate formation exceeded 24 hours for structureⅠhydrate was much lower than that for structureⅡhydrate.The inhibition strength increased with the increasing dosage of PVCap-co-TBA;The maximum tolerable degree of subcooling for the natural gas hydrate is more than10 K when the dosage was higher than 0.5%(mass)while it achieved 12 K when that dosage rose to0.75%(mass).Additionally,we found polypropylene glycol could be used as synergist at the dosage of 1.0%(mass)or so,under which the kinetic inhibition performance of PVCap-co-TBA could be improved significantly.All evaluation results demonstrated that PVCap-co-TBA was a very promising KHI and a competitive alternative to the existing commercial KHIs.展开更多
A novel surface modifying agent and internal compatilizer of inorganic and macromolecule composite materials,P(St/MAH/BA)terpolymer,was synthesized in butanone by solution polymerization method using styrene(St),malei...A novel surface modifying agent and internal compatilizer of inorganic and macromolecule composite materials,P(St/MAH/BA)terpolymer,was synthesized in butanone by solution polymerization method using styrene(St),maleic anhydride(MAH),and butyl acrylate(BA)as monomers and azobisisobutyronitrile(AIBN)as an initiator.Some affecting factors on terpolymers yields such as polymerization time,reaction temperature,solvent volume,initiator content,and reactants ratios were studied.Furthermore,the structure and thermal properties of terpolymers were primarily characterized and determined by Fourier Transform Infrared Spectroscopy(FTIR),nuclear magnetic resonance(NMR),thermogravimetric analysis(TGA),and gel permeation chromatography(GPC).The results indicate that the terpolymers are random polymers and the yields are low,but the thermal decomposed temperature of terpolymers P(St/MAH/BA)is around 220 ℃ and the average molecular weights(Mw)achieve 1.189×105 g·mol-1.展开更多
A very mild and extremely efficient hydrolysis method for transformation of polystyrene-b-poly(tert-butyl acrylate) (PS-b-PtBA) to polystyrene-b-poly(acrylic acid) (PS-b-PAA) was designed and carried out using more co...A very mild and extremely efficient hydrolysis method for transformation of polystyrene-b-poly(tert-butyl acrylate) (PS-b-PtBA) to polystyrene-b-poly(acrylic acid) (PS-b-PAA) was designed and carried out using more convenient and inexpensive chlorotrimethylsilane/sodium iodide as reagents. The hydrolysis product can self-assemble in aqueous media to give regular micelles with PS block forming the core and PAA block forming the corona, or in tetrahydrofuran (THF) to give reverse micelles with the hydrophilic block in the core.展开更多
P(BA-GMA)(PBG), having various molecular weights, was synthesized by in situ polymerization of butyl acrylate(BA) and glycidyl methacrylate(GMA), and further used as a modifier to improve the comprehensive pro...P(BA-GMA)(PBG), having various molecular weights, was synthesized by in situ polymerization of butyl acrylate(BA) and glycidyl methacrylate(GMA), and further used as a modifier to improve the comprehensive properties of the epoxy curing system. The copolymers were characterized by gel permeation chromatography(GPC). The effects of various molecular weights of copolymers on the mechanical properties, thermal performance, and phase behavior of the curing system were carefully evaluated. The experimental results of differential scanning calorimetry(DSC) and dynamic mechanical analysis(DMA) showed that glass transition temperature decreased and the tan δ peak shifted to a lower temperature with decreasing molecular weight of copolymer. Mechanical properties analysis of curing films showed that the impact strength and fracture toughness increased significantly upon the addition of PBG, indicating good toughness of the modified epoxy resins. From scanning electron microscopy(SEM) studies of the fracture surfaces of ER/PBG systems, the fracture behavior of epoxy matrix was changed from brittleness to toughness.展开更多
Adopting N,N′-methylene-bis(acrylamide) (MBA) and inorganic clay (hectorite) as chemical and physical cross-linking agent, respectively, a series temperature sensitive microgels, based on N-isopropylacrylamide (NIPAM...Adopting N,N′-methylene-bis(acrylamide) (MBA) and inorganic clay (hectorite) as chemical and physical cross-linking agent, respectively, a series temperature sensitive microgels, based on N-isopropylacrylamide (NIPAM) as a main monomer and tert-butyl acrylate (tBA) as a comonomer were synthesized by surfactant-free emulsion polymerization(SFEP). The microgel particle size and morphology was investigated by means of Atomic Force Microscope (AFM). The surface tension of latex particles was measured by OCA 40 Micro Video based contact angle measuring device. The results showed that the particle size of the microgels with clay as cross-linker was smaller than that using MBA as chemical cross-linker, but exterior morphology of physical microgels is not as clean and neat as chemical microgels. In general, surface tension decreases with increasing hydrophobic tBA content. These smart microgels varied with temperature have the potential applications in the field of drug delivery and intelligent gel fiber.展开更多
The urethane acrylate(UA) was made of poly(tetramethylenc oxide), 4,4’-diphenylmethane diisocyanate, and 2-hydroxyethyl methacrylate. A series of poly(methyl methacrylate) / urethane acrylate copolymers was prepared ...The urethane acrylate(UA) was made of poly(tetramethylenc oxide), 4,4’-diphenylmethane diisocyanate, and 2-hydroxyethyl methacrylate. A series of poly(methyl methacrylate) / urethane acrylate copolymers was prepared by using a redox initiating system. The copolymers had cross linked structures and two-phase morphologies as indicated by the results of the dynamic mechanical measurement and swelling test.展开更多
A full-relaxation optimization of molecule and the popular MM2 force field are employed to obtain the geometry parameters and the conformational energy surface of a meso or a racemic dyad of poly(methyl acrylate) (PMA...A full-relaxation optimization of molecule and the popular MM2 force field are employed to obtain the geometry parameters and the conformational energy surface of a meso or a racemic dyad of poly(methyl acrylate) (PMA) with a specified carbonyl-bond orientation in side-groups. It is found that the conformational energy maps calculated here considerably differ from those calculated with the rigid molecular model as reported in the earlier studies. The g(-) state cannot be omitted in the obtained contour maps. Two important conformers tg(-) and g(-t) with energy minima were newly detected for a racemic dyad. The analysis on the conformations with energy minima confirmed that the ester groups are not always perpendicular to the plane defined by the two adjacent skeletal bonds and may change their relative orientations to meet the requirement of lower energies during the conformational state transition. Instead of the early way of adjusting the interaction energy parameters to fit the experimental data, we attempt to predict unperturbed chain dimensions via the reliable force field and the configurational statistical mechanics. The proposed scheme with three rotational states identified from the contour maps allowed us to satisfactorily reproduce the experimental dimensions of random PMA chains.展开更多
Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At ap...Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At apre - expansion temperature of 45℃), amorphous polymer was formed. At temperature around 60 ℃ to 80 ℃ , fibers were formed. Increase of temperature increasesparticle size slightly. At temperature of 105℃ , most of particles are spheres. The RESS is an attractive process. To apply the polymers desired for coating applications in an organic solvent - free process that is economically viable , and it will have implications for pollution prevention during polymer film展开更多
The intrinsic viscosity [η] of poly(3,5-dimethylphenylacrylate) (35PDMPA)solutions were evaluated throughout the measurements of the flow times of toluene and polymer solutions by classical Huggins, and Kraemer’s me...The intrinsic viscosity [η] of poly(3,5-dimethylphenylacrylate) (35PDMPA)solutions were evaluated throughout the measurements of the flow times of toluene and polymer solutions by classical Huggins, and Kraemer’s methods using a Cannon-Ubbelohde semi-micro-dilution capillary viscometer in a Cannon thermostated water bath at 40℃ ± 0.02℃. The values of Huggins’ constant estimated ranged from 0.2 to 0.4 which were within expectations. The intrinsic viscosities and molecular weight relationship was established with the two-parameter classical models of Staudinger-Mark-Houwink-Sakurada and Stockmayer-Fixman. Conformational parameter C∞ and σ indicated 35PDMPA be semi flexible. Also, the rigidity of 35PDMPA was confirmed by Yamakawa-Fuji wormlike theory modified by Bohdanecky. The molecular parameters were estimated and compared. The results showed that 35PDMPA behaves like a semi-rigid polymer in toluene at 40℃ rather than a random coil flexible macromolecule.展开更多
Epoxy resin based Unsaturated poly(ester-amide) resins (UPEAs) can be prepared by many methods but here these were prepared by reported method [1]. These UPEAs were then treated with acrylotl chloride to afford acryla...Epoxy resin based Unsaturated poly(ester-amide) resins (UPEAs) can be prepared by many methods but here these were prepared by reported method [1]. These UPEAs were then treated with acrylotl chloride to afford acrylated UPEAs resin (i.e. AUPEAs). Interacting blends of equal proportional AUPEAs and vinyl ester epoxy (VE) resin were prepared. APEAs and AUPEAs were characterized by elemental analysis, molecular weight determined by vapour pressure osmometer and by IR spectral study and by thermogravimetry. The curing of interacting blends was monitored on differential scanning calorimeter (DSC). Based on DSC data in situ glass reinforced composites of the resultant blends have been prepared and characterized for mechanical, electrical and chemical properties. Unreinforced blends were characterized by thermogravimetry (TGA).展开更多
The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using poly...The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using polychelates,PAA-Co X(X:3,5,7,and 10)where X represents the doping fraction(w/w)of Co in PAA.All polymer metal electrolytes were showed excellent bending-stretching properties,thermal stability and electrochemical durability with an optimum ionic conductivity of 3.15×10^(-4) S cm^(-1).Hierarchically porous activated carbon and nano-sized conductive carbon were used to form carbon composite symmetrical device electrodes.The electric double-layer capacitor(EDLC)and redox reactions of Co-incorporated polychelates at the interfaces of porous activated carbon provided an optimum specific capacitance of 341.33 F g^(-1) with a device of PAA-Co7,which is at least 15 times enhancement compared to the device of pristine PAA.The PAA-Co7 device also provided energy density of 21.25 Wh kg^(-1) at a power density of 117.69 W kg^(-1).A prolonged cyclic stability of the device exhibited superior capacitive performance after 10,000 charge-discharge cycles and the maintained 90%of its initial performance.In addition,the supercapacitor with a dimension of 1.5 cm×3 cm containing PAA-Co7 successfully operated the red-blue-green(RGB)LED light.展开更多
Monodisperse poly(poly(ethyleneglycol) methyl ether acrylate-co-acrylic acid) (poly(PEGMA-co-AA)) microspheres were prepared by distillation-precipitation polymerization with divinylbenzene (DVB) as crosslin...Monodisperse poly(poly(ethyleneglycol) methyl ether acrylate-co-acrylic acid) (poly(PEGMA-co-AA)) microspheres were prepared by distillation-precipitation polymerization with divinylbenzene (DVB) as crosslinker with 2,2'- azobisisobutyronitrile (AIBN) as initiator in neat acetonitrile without stirring. Under various reaction conditions, four distinct morphologies including the sol, microemulsion, microgels and microspheres were formed during the distillation of the solvent from the reaction system. A 2D morphological map was established as a function of crosslinker concentration and the polar monomer AA concentration, in comonomer feed in the transition between the morphology domains. The effect of the covalent crosslinker DVB on the morphology of the polymer network was investigated in detail at AA fraction of 40 vol%. The ratios of acid to ethylene oxide units presenting in the comonomers dramatically affected the polymer-polymer interaction and hence the morphology of the resultant polymer network. The covalent crosslinking by DVB and the hydrogen bonding crosslinking between two acid units as well as between the acid and ethylene oxide unit played key roles in the formation of monodisperse polymer microspheres.展开更多
A full-relaxation optimization of molecule and the Dreiding force field are employed to obtain the geometry parameters and the conformational energy surfaces of meso or racemic dyad of poly(acrylic acid) (PAA) and pol...A full-relaxation optimization of molecule and the Dreiding force field are employed to obtain the geometry parameters and the conformational energy surfaces of meso or racemic dyad of poly(acrylic acid) (PAA) and poly(methacrylic acid) (PMAA). Three different carbonyl-bond orientations of side-groups resulted in the differences in depth of potential wells in their energetic contours for a meso or a racemic dyad. These discrepancies are interpreted as a result of various fine structures corresponding to grid search conformations as well as thereby different interactions. The analysis on the most stable conformations of PMAA confirmed that the ester groups are nearly perpendicular to the plane defined by the two adjacent skeletal bonds but may possibly change their relative orientations to meet the requirement of lower energy during the conformational state transition. For each polymer, two global energy maps of a meso and a racemic dyad were finally constructed from the superposition of energy data for the three kinds of side-group orientations by the Boltzmann factors. From an ensemble average, the proposed scheme with three rotational isomeric states (RIS) allowed us to access the experimentally unperturbed dimensions of PAA chain via the configurational statistical mechanics. Although the calculation was based on the short-range, local interactions, it was interested to note that the experimental characteristic ratios just fell within the range calculated for atactic chains.展开更多
This research explored replacing acrylic core-shell impact modifier (AIM) by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM (8 phr) were substituted by silica fume in PVC respectively, and then processe...This research explored replacing acrylic core-shell impact modifier (AIM) by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM (8 phr) were substituted by silica fume in PVC respectively, and then processed by dry blending and twin-screw extrusion. Severe silica fume agglomeration was observed by scanning electron microscope (SEM) in the PVC matrix when 8 phr pure silica fume was used and processed by screw speed of 20 rpm. Its tensile strength was thereby reduced by 38% comparing to unmodified PVC. The silica fume was successfully dispersed while the screw speed was slowed down to 10 rpm to give a stronger screw torque and a longer melt residential time in the extruder. The tensile strength was ’recovered’ to a level comparable to unmodified PVC. Impact test were performed on all formulations extruded at 10 rpm screw speed and synergetic toughening effect was found with 50% substitution and it had the impact strength that was comparable to 8 phr pure AIM toughened PVC.展开更多
In this paper, poly (acrylamide-co-acrylic acid) (P(AM-co-AA)) hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma (GDEP) induced copoly- merization of acrylamide (AM) ...In this paper, poly (acrylamide-co-acrylic acid) (P(AM-co-AA)) hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma (GDEP) induced copoly- merization of acrylamide (AM) and acrylic acid (AA), in which N,N'-methylenebisacrylamide (MBA) was used as a crosslinker. A mechanism for the synthesis of P(AM-co-AA) hydrogel was proposed. To optimize the synthesis condition, the following parameters were examined in detail: the discharge voltage, discharge time, the content of the crosslinker, and the mass ratio of AM to AA. The results showed that the optimum pH range for cationic dyes removal was found to be 5.0-10.0. The P(AM-co-AA) hydrogel exhibits a very high adsorption potential and the ex- perimental adsorption capacities for Crystal violet (CV) and Methylene blue (MB) were 2974.3 mg/g and 2303.6 mg/g, respectively. The adsorption process follows a pseudo-second-order kinetic model. In addition, the adsorption mechanism of P(AM-co-AA) hydrogel for cationic dyes was also discussed.展开更多
IntroductionOver the past few decades, molecular imprinting has been described as a technology for preparing "molecular doors" which can be matched to "template keys". It has been found to be a simple and effectiv...IntroductionOver the past few decades, molecular imprinting has been described as a technology for preparing "molecular doors" which can be matched to "template keys". It has been found to be a simple and effective approach to introduce specific recognition sites into synthetic polymers, namely, to create molecular imprinting polymers Remarkable features such as stability, ease of preparation and low cost, have made molecular imprinting polymers particularly attractive in chemical sensors, catalysis, drug delivery, and dedicated separations. Practical applications of molecular imprinting polymers require accessible sites, fast mass transfer, and quick binding. However, present techniques used to prepare molecular imprinting polymers most often result in materials exhibiting a high affinity and selectivity but a low capacity and poor site accessibility for the target molecules. It is also very difficult to remove the imprinted molecules located in these molecular imprinting polymers because the highly cross-linked structures do not allow the templates to move freely. To some extent, combining molecular imprinting technology with membrane separation and surface imprinting can overcome the shortcomings, such as mass transfer limitations and non-quantitative recovery of the template molecules seen for imprinted materials fabricated by conventional bulk methods. In that ease, it appears to us that molecular imprinting polymers with high surface area to volume ratios are particularly desirable for largescale applications. Eleetrospun nano and ultrafine fibrous membranes are the most suitable materials due to advantages such as: (1) large specific surfaces, providing relatively high imprinting sites per unit mass; (2) fine porous structures, resulting in the accessibility of imprinting sites and low diffusion resistance necessary for high efficiency; and (3) easy recoverability from practical operation or applicability for continuous usages. Therefore, in this work, we prepared a unique kind of imprinted material--molecularly imprinted fibrous membranes of poly ( acrylonitrile-co-acrylic acid) fabricated by means of an electrospinning process.展开更多
Novel interpenetrating polymer network (IPN) hydrogels based on konjac glucomannan (KGM) and poly(acrylic acid) (PAA) were prepared by polymerization and cross-linking of acrylic acid (AA) in the pre-fabrica...Novel interpenetrating polymer network (IPN) hydrogels based on konjac glucomannan (KGM) and poly(acrylic acid) (PAA) were prepared by polymerization and cross-linking of acrylic acid (AA) in the pre-fabricated KGM gel. The IPN gel was analyzed by FF-IR. The studies on the equilibrium swelling ratio of IPN hydrogels revealed their sensitive response to environmental pH value. The results of in vitro degradation showed that the IPN hydrogels retain the enzymatic degradation character of KGM.展开更多
文摘The catalytic activities of some heteropolyacids(HPAs) in synthesizing butyl acrylate are reported. It has been demonstrated that 12 tungstophosphoric acid is the most effective catalyst among more than 20 HPA(salts). Various factors concerned in this reaction have been investigated. The optimum conditions have been found, that is, the molar ratio of alcohol to acid is 1.2∶1.0 , the catalyst concentration 1%(mass fraction), the reaction time 2 h, the temperature 98—124 ℃ and a certain amount of polymerization inhibitor exists.
文摘Well-defined nonionic hydrophilic ω-acryloyl poly(ethylene oxide) macro-monomer (PEO-A) has been prepared by living anionic polymerization of ethylene oxidewith diphenyl methyl potassium as the initiator and acryloyl chloride as the reaction termi-nating agent. The polymer was characterized by FTIR and SEC. The emulsifier-free emul-sion polymerization of methyl methacrylate (MMA) and n-butyl acrylate (BA) containingvarious concentrations of PEO-A was studied. In all cases stable emulsion coplymerizationsof MMA and BA were obtained. The stabilizing effect was found to be dependent on themolecular weight and the feed amount of the macromonomer.
基金supported by the National Natural Science Foundation of China(U20B6005)Hainan Province Science and Technology Special Fund(ZDKJ2021026)。
文摘Low dosage kinetic hydrate inhibitors(KHIs)are a kind of alternative chemical additives to high dosage thermodynamic inhibitors for preventing gas hydrate formation in oil&gas production wells and transportation pipelines.In this paper,a new KHI,poly(N-vinyl caprolactam)-co-tert-butyl acrylate(PVCapco-TBA),was successfully synthesized with N-vinyl caprolactam(NVCap)and tert-butyl acrylate.The kinetic inhibition performances of PVCap-co-TBA on the formations of both structureⅠmethane hydrate and structureⅡnatural gas hydrate were investigated by measuring the onset times of hydrate formation under different conditions and compared with commercial KHIs such as PVP,PVCap and inhibex 501.The results indicated that PVCap-co-TBA outperformed these widely applied inhibitors for both structureⅠand structureⅡhydrates.At the same dosage of KHI,the maximum tolerable degree of subcooling under which the onset time of hydrate formation exceeded 24 hours for structureⅠhydrate was much lower than that for structureⅡhydrate.The inhibition strength increased with the increasing dosage of PVCap-co-TBA;The maximum tolerable degree of subcooling for the natural gas hydrate is more than10 K when the dosage was higher than 0.5%(mass)while it achieved 12 K when that dosage rose to0.75%(mass).Additionally,we found polypropylene glycol could be used as synergist at the dosage of 1.0%(mass)or so,under which the kinetic inhibition performance of PVCap-co-TBA could be improved significantly.All evaluation results demonstrated that PVCap-co-TBA was a very promising KHI and a competitive alternative to the existing commercial KHIs.
基金Nano Project Foundation of Shanghai Technology Committee,China(No.0652nm039)Shanghai Leading Academic Discipline Project,China(No.B502)Shanghai Key Laboratory Proejct,China(No.08DZ2230500)
文摘A novel surface modifying agent and internal compatilizer of inorganic and macromolecule composite materials,P(St/MAH/BA)terpolymer,was synthesized in butanone by solution polymerization method using styrene(St),maleic anhydride(MAH),and butyl acrylate(BA)as monomers and azobisisobutyronitrile(AIBN)as an initiator.Some affecting factors on terpolymers yields such as polymerization time,reaction temperature,solvent volume,initiator content,and reactants ratios were studied.Furthermore,the structure and thermal properties of terpolymers were primarily characterized and determined by Fourier Transform Infrared Spectroscopy(FTIR),nuclear magnetic resonance(NMR),thermogravimetric analysis(TGA),and gel permeation chromatography(GPC).The results indicate that the terpolymers are random polymers and the yields are low,but the thermal decomposed temperature of terpolymers P(St/MAH/BA)is around 220 ℃ and the average molecular weights(Mw)achieve 1.189×105 g·mol-1.
基金National Natural Scientific Foundation of China. (Project grant No. 29936100)
文摘A very mild and extremely efficient hydrolysis method for transformation of polystyrene-b-poly(tert-butyl acrylate) (PS-b-PtBA) to polystyrene-b-poly(acrylic acid) (PS-b-PAA) was designed and carried out using more convenient and inexpensive chlorotrimethylsilane/sodium iodide as reagents. The hydrolysis product can self-assemble in aqueous media to give regular micelles with PS block forming the core and PAA block forming the corona, or in tetrahydrofuran (THF) to give reverse micelles with the hydrophilic block in the core.
基金Funded by the National Natural Science Foundation of China(51373129)the Fundamental Research Funds for the Central University(WUT:2013-IV-011)
文摘P(BA-GMA)(PBG), having various molecular weights, was synthesized by in situ polymerization of butyl acrylate(BA) and glycidyl methacrylate(GMA), and further used as a modifier to improve the comprehensive properties of the epoxy curing system. The copolymers were characterized by gel permeation chromatography(GPC). The effects of various molecular weights of copolymers on the mechanical properties, thermal performance, and phase behavior of the curing system were carefully evaluated. The experimental results of differential scanning calorimetry(DSC) and dynamic mechanical analysis(DMA) showed that glass transition temperature decreased and the tan δ peak shifted to a lower temperature with decreasing molecular weight of copolymer. Mechanical properties analysis of curing films showed that the impact strength and fracture toughness increased significantly upon the addition of PBG, indicating good toughness of the modified epoxy resins. From scanning electron microscopy(SEM) studies of the fracture surfaces of ER/PBG systems, the fracture behavior of epoxy matrix was changed from brittleness to toughness.
基金Supported by the Major Project of Science and Technology Research of the Educational Ministry of China (No.105077) and DoctorateInnovation Foundation of Donghua University(No.106 06 001900611)
文摘Adopting N,N′-methylene-bis(acrylamide) (MBA) and inorganic clay (hectorite) as chemical and physical cross-linking agent, respectively, a series temperature sensitive microgels, based on N-isopropylacrylamide (NIPAM) as a main monomer and tert-butyl acrylate (tBA) as a comonomer were synthesized by surfactant-free emulsion polymerization(SFEP). The microgel particle size and morphology was investigated by means of Atomic Force Microscope (AFM). The surface tension of latex particles was measured by OCA 40 Micro Video based contact angle measuring device. The results showed that the particle size of the microgels with clay as cross-linker was smaller than that using MBA as chemical cross-linker, but exterior morphology of physical microgels is not as clean and neat as chemical microgels. In general, surface tension decreases with increasing hydrophobic tBA content. These smart microgels varied with temperature have the potential applications in the field of drug delivery and intelligent gel fiber.
文摘The urethane acrylate(UA) was made of poly(tetramethylenc oxide), 4,4’-diphenylmethane diisocyanate, and 2-hydroxyethyl methacrylate. A series of poly(methyl methacrylate) / urethane acrylate copolymers was prepared by using a redox initiating system. The copolymers had cross linked structures and two-phase morphologies as indicated by the results of the dynamic mechanical measurement and swelling test.
基金This work has been supported by the National Science Foundation of China,the Youth Science Foundation of Academia Sinica,the China Postdoctoral Science Foundation and Polymer Physics Laboratory, Academia Sinica.
文摘A full-relaxation optimization of molecule and the popular MM2 force field are employed to obtain the geometry parameters and the conformational energy surface of a meso or a racemic dyad of poly(methyl acrylate) (PMA) with a specified carbonyl-bond orientation in side-groups. It is found that the conformational energy maps calculated here considerably differ from those calculated with the rigid molecular model as reported in the earlier studies. The g(-) state cannot be omitted in the obtained contour maps. Two important conformers tg(-) and g(-t) with energy minima were newly detected for a racemic dyad. The analysis on the conformations with energy minima confirmed that the ester groups are not always perpendicular to the plane defined by the two adjacent skeletal bonds and may change their relative orientations to meet the requirement of lower energies during the conformational state transition. Instead of the early way of adjusting the interaction energy parameters to fit the experimental data, we attempt to predict unperturbed chain dimensions via the reliable force field and the configurational statistical mechanics. The proposed scheme with three rotational states identified from the contour maps allowed us to satisfactorily reproduce the experimental dimensions of random PMA chains.
文摘Poly(1,1,2,2- tetrahydroperfluorodecyl acrylate) (poly (TA-N)) was synthesized in laboratory. The resulting morphology of rapid expansion of supercritical solution (RESS) sprays of poly(TA - N) was investigated. At apre - expansion temperature of 45℃), amorphous polymer was formed. At temperature around 60 ℃ to 80 ℃ , fibers were formed. Increase of temperature increasesparticle size slightly. At temperature of 105℃ , most of particles are spheres. The RESS is an attractive process. To apply the polymers desired for coating applications in an organic solvent - free process that is economically viable , and it will have implications for pollution prevention during polymer film
文摘The intrinsic viscosity [η] of poly(3,5-dimethylphenylacrylate) (35PDMPA)solutions were evaluated throughout the measurements of the flow times of toluene and polymer solutions by classical Huggins, and Kraemer’s methods using a Cannon-Ubbelohde semi-micro-dilution capillary viscometer in a Cannon thermostated water bath at 40℃ ± 0.02℃. The values of Huggins’ constant estimated ranged from 0.2 to 0.4 which were within expectations. The intrinsic viscosities and molecular weight relationship was established with the two-parameter classical models of Staudinger-Mark-Houwink-Sakurada and Stockmayer-Fixman. Conformational parameter C∞ and σ indicated 35PDMPA be semi flexible. Also, the rigidity of 35PDMPA was confirmed by Yamakawa-Fuji wormlike theory modified by Bohdanecky. The molecular parameters were estimated and compared. The results showed that 35PDMPA behaves like a semi-rigid polymer in toluene at 40℃ rather than a random coil flexible macromolecule.
文摘Epoxy resin based Unsaturated poly(ester-amide) resins (UPEAs) can be prepared by many methods but here these were prepared by reported method [1]. These UPEAs were then treated with acrylotl chloride to afford acrylated UPEAs resin (i.e. AUPEAs). Interacting blends of equal proportional AUPEAs and vinyl ester epoxy (VE) resin were prepared. APEAs and AUPEAs were characterized by elemental analysis, molecular weight determined by vapour pressure osmometer and by IR spectral study and by thermogravimetry. The curing of interacting blends was monitored on differential scanning calorimeter (DSC). Based on DSC data in situ glass reinforced composites of the resultant blends have been prepared and characterized for mechanical, electrical and chemical properties. Unreinforced blends were characterized by thermogravimetry (TGA).
基金Deputyship for Research&Innovation,Ministry of Education in Saudi Arabia for funding this research work。
文摘The novel polymer metal chelate electrolytes(polychelates)were prepared by incorporation of cobalt sulfate(Co)into poly(acrylic acid)(PAA)host matrix.Quasi-solid state supercapacitor devices were fabricated using polychelates,PAA-Co X(X:3,5,7,and 10)where X represents the doping fraction(w/w)of Co in PAA.All polymer metal electrolytes were showed excellent bending-stretching properties,thermal stability and electrochemical durability with an optimum ionic conductivity of 3.15×10^(-4) S cm^(-1).Hierarchically porous activated carbon and nano-sized conductive carbon were used to form carbon composite symmetrical device electrodes.The electric double-layer capacitor(EDLC)and redox reactions of Co-incorporated polychelates at the interfaces of porous activated carbon provided an optimum specific capacitance of 341.33 F g^(-1) with a device of PAA-Co7,which is at least 15 times enhancement compared to the device of pristine PAA.The PAA-Co7 device also provided energy density of 21.25 Wh kg^(-1) at a power density of 117.69 W kg^(-1).A prolonged cyclic stability of the device exhibited superior capacitive performance after 10,000 charge-discharge cycles and the maintained 90%of its initial performance.In addition,the supercapacitor with a dimension of 1.5 cm×3 cm containing PAA-Co7 successfully operated the red-blue-green(RGB)LED light.
基金This work was supported in part by the National Science Foundation of China (No. 20504015)the starting project for young teachers from the Ministry of Education, China.
文摘Monodisperse poly(poly(ethyleneglycol) methyl ether acrylate-co-acrylic acid) (poly(PEGMA-co-AA)) microspheres were prepared by distillation-precipitation polymerization with divinylbenzene (DVB) as crosslinker with 2,2'- azobisisobutyronitrile (AIBN) as initiator in neat acetonitrile without stirring. Under various reaction conditions, four distinct morphologies including the sol, microemulsion, microgels and microspheres were formed during the distillation of the solvent from the reaction system. A 2D morphological map was established as a function of crosslinker concentration and the polar monomer AA concentration, in comonomer feed in the transition between the morphology domains. The effect of the covalent crosslinker DVB on the morphology of the polymer network was investigated in detail at AA fraction of 40 vol%. The ratios of acid to ethylene oxide units presenting in the comonomers dramatically affected the polymer-polymer interaction and hence the morphology of the resultant polymer network. The covalent crosslinking by DVB and the hydrogen bonding crosslinking between two acid units as well as between the acid and ethylene oxide unit played key roles in the formation of monodisperse polymer microspheres.
基金This work was supported by the Youth Science Foundation of Acedemia Sinica the China Postdoctoral Science Foundation, the National Natural Science Foundation of China, and Polymer Physics Laboratory,Academia Sinica
文摘A full-relaxation optimization of molecule and the Dreiding force field are employed to obtain the geometry parameters and the conformational energy surfaces of meso or racemic dyad of poly(acrylic acid) (PAA) and poly(methacrylic acid) (PMAA). Three different carbonyl-bond orientations of side-groups resulted in the differences in depth of potential wells in their energetic contours for a meso or a racemic dyad. These discrepancies are interpreted as a result of various fine structures corresponding to grid search conformations as well as thereby different interactions. The analysis on the most stable conformations of PMAA confirmed that the ester groups are nearly perpendicular to the plane defined by the two adjacent skeletal bonds but may possibly change their relative orientations to meet the requirement of lower energy during the conformational state transition. For each polymer, two global energy maps of a meso and a racemic dyad were finally constructed from the superposition of energy data for the three kinds of side-group orientations by the Boltzmann factors. From an ensemble average, the proposed scheme with three rotational isomeric states (RIS) allowed us to access the experimentally unperturbed dimensions of PAA chain via the configurational statistical mechanics. Although the calculation was based on the short-range, local interactions, it was interested to note that the experimental characteristic ratios just fell within the range calculated for atactic chains.
文摘This research explored replacing acrylic core-shell impact modifier (AIM) by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM (8 phr) were substituted by silica fume in PVC respectively, and then processed by dry blending and twin-screw extrusion. Severe silica fume agglomeration was observed by scanning electron microscope (SEM) in the PVC matrix when 8 phr pure silica fume was used and processed by screw speed of 20 rpm. Its tensile strength was thereby reduced by 38% comparing to unmodified PVC. The silica fume was successfully dispersed while the screw speed was slowed down to 10 rpm to give a stronger screw torque and a longer melt residential time in the extruder. The tensile strength was ’recovered’ to a level comparable to unmodified PVC. Impact test were performed on all formulations extruded at 10 rpm screw speed and synergetic toughening effect was found with 50% substitution and it had the impact strength that was comparable to 8 phr pure AIM toughened PVC.
基金supported by National Natural Science Foundation of China(No.21367023)Natural Science Foundation of Gansu Province,China(No.1208RJZA161)Key Project of Young Teachers’ Scientific Research Promotion of Northwest Normal University of China(Nos.NWNU-LKQN-10-16 and NWNU-LKQN-12-9)
文摘In this paper, poly (acrylamide-co-acrylic acid) (P(AM-co-AA)) hydrogel was pre- pared in an aqueous solution by using glow-discharge electrolysis plasma (GDEP) induced copoly- merization of acrylamide (AM) and acrylic acid (AA), in which N,N'-methylenebisacrylamide (MBA) was used as a crosslinker. A mechanism for the synthesis of P(AM-co-AA) hydrogel was proposed. To optimize the synthesis condition, the following parameters were examined in detail: the discharge voltage, discharge time, the content of the crosslinker, and the mass ratio of AM to AA. The results showed that the optimum pH range for cationic dyes removal was found to be 5.0-10.0. The P(AM-co-AA) hydrogel exhibits a very high adsorption potential and the ex- perimental adsorption capacities for Crystal violet (CV) and Methylene blue (MB) were 2974.3 mg/g and 2303.6 mg/g, respectively. The adsorption process follows a pseudo-second-order kinetic model. In addition, the adsorption mechanism of P(AM-co-AA) hydrogel for cationic dyes was also discussed.
文摘IntroductionOver the past few decades, molecular imprinting has been described as a technology for preparing "molecular doors" which can be matched to "template keys". It has been found to be a simple and effective approach to introduce specific recognition sites into synthetic polymers, namely, to create molecular imprinting polymers Remarkable features such as stability, ease of preparation and low cost, have made molecular imprinting polymers particularly attractive in chemical sensors, catalysis, drug delivery, and dedicated separations. Practical applications of molecular imprinting polymers require accessible sites, fast mass transfer, and quick binding. However, present techniques used to prepare molecular imprinting polymers most often result in materials exhibiting a high affinity and selectivity but a low capacity and poor site accessibility for the target molecules. It is also very difficult to remove the imprinted molecules located in these molecular imprinting polymers because the highly cross-linked structures do not allow the templates to move freely. To some extent, combining molecular imprinting technology with membrane separation and surface imprinting can overcome the shortcomings, such as mass transfer limitations and non-quantitative recovery of the template molecules seen for imprinted materials fabricated by conventional bulk methods. In that ease, it appears to us that molecular imprinting polymers with high surface area to volume ratios are particularly desirable for largescale applications. Eleetrospun nano and ultrafine fibrous membranes are the most suitable materials due to advantages such as: (1) large specific surfaces, providing relatively high imprinting sites per unit mass; (2) fine porous structures, resulting in the accessibility of imprinting sites and low diffusion resistance necessary for high efficiency; and (3) easy recoverability from practical operation or applicability for continuous usages. Therefore, in this work, we prepared a unique kind of imprinted material--molecularly imprinted fibrous membranes of poly ( acrylonitrile-co-acrylic acid) fabricated by means of an electrospinning process.
基金The authors are grateful for the financial support of the National Natural Science Foundation of China (No. 20174029)National Key Basic Research and Development Program (2005CB623903).
文摘Novel interpenetrating polymer network (IPN) hydrogels based on konjac glucomannan (KGM) and poly(acrylic acid) (PAA) were prepared by polymerization and cross-linking of acrylic acid (AA) in the pre-fabricated KGM gel. The IPN gel was analyzed by FF-IR. The studies on the equilibrium swelling ratio of IPN hydrogels revealed their sensitive response to environmental pH value. The results of in vitro degradation showed that the IPN hydrogels retain the enzymatic degradation character of KGM.