Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) supports adhesion and migration of mesenchymal stem cells and tenocytes

AIM: To establish the potential of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) as a material for tendon repair. METHODS: The biocompatibility of PHBHHx with both rat tenocytes (rT) and human mesenchymal stem cells (hMSC) was explored by monitoring adhesive characteristics on films of varying weight/volume ratios coupled to a culture atmosphere of either 21% O2 (air) or 2% O2 (physiological normoxia). The diameter and stiffness of PHBHHx films was established using optical coherence tomography and mechanical testing, respectively. RESULTS: Film thickness correlated directly with weight/volume PHBHHx (r2 = 0.9473) ranging from 0.1 mm (0.8% weight/volume) to 0.19 mm (2.4% weight/volume). Film stiffness on the other hand displayed a biphasic response which increased rapidly at values > 1.6% weight/volume. Optimal cell attachment of rT required films of ≥ 1.6% and ≥ 2.0% weight/volume PHBHHx in 2% O2 and 21% O2 respectively. A qualitative adhesion increase was noted for hMSC in films ≥ 1.2% weight/volume, becoming significant at 2% weight/volume in 2% O2. An increase in cell adhesion was also noted with ≥ 2% weight/volume PHBHHx in 21% O2. Cell migration into films was not observed. CONCLUSION: This evaluation demonstrates that PHBHHx is a suitable polymer for future cell/polymer replacement strategies in tendon repair.

Miscibility of Poly(hydroxybutyrate)/Poly(vinyl alcohol)Melt Blends Plasticized With Glycerol

Poly(hydroxybutyrate)/poly(vinyl alcohol)(PHB/PVA)blends plasticized with glycerol were prepared by melt blending of PHB and glycerol plasticized PVA.The PHB/PVA-glycerol compositions were 90:10,75:25 and 50:50 w/w,being the concentration of glycerol in the PVA mixture of 10 wt%.The blends were characterized by infrared spectroscopy,dynamic-mechanical thermal analysis,and scanning electron microscope of the fragile fractured surface.The results showed one single phase blend,indicating miscibility corroborated by the presence of a single glass transition temperature.The blending method proved to be an efficient way to tune PHB properties keeping its biodegradable nature since both PVA and glycerol are fully biodegradable materials.

4天香烟烟雾暴露联合poly(I:C)刺激对小鼠肺部免疫应答及干扰素表达的影响

目的:探讨短期香烟烟雾暴露联合poly(I:C)刺激对小鼠肺部免疫应答及干扰素表达的影响。方法:BALB/c小鼠随机分为4组:对照组、熏烟组、poly(I:C)组和熏烟联合poly(I:C)组。检测支气管肺泡灌洗液(BALF)中总细胞数及细胞分类计数;普通光镜下观察各组细胞形态;荧光定量PCR检测肺组织细胞因子、趋化因子和干扰素及干扰素刺激基因表达。结果:与对照组相比,熏烟联合poly(I:C)组总细胞数计数、巨噬细胞与中性粒细胞计数明显升高(P<0.05),且熏烟联合poly(I:C)组巨噬细胞计数高于poly(I:C)组;与poly(I:C)组比较,熏烟联合poly(I:C)组小鼠气道灌洗液巨噬细胞体积较大,呈圆形或不规则形,细胞质较多空泡;与对照组相比,熏烟联合poly(I:C)组小鼠肺组织中性粒细胞趋化因子CXCL1(P<0.05)、CXCL2(P<0.01)和淋巴细胞趋化因子CCL2(P<0.01)mRNA表达升高,肺组织IL-1β、IL-6、TNF-αmRNA表达明显升高(P<0.01),肺组织IFN-β(P<0.01)、IFN-γ(P<0.05)、MX2(P<0.01)和IP-10(P<0.01)表达显著升高,且与poly(I:C)组小鼠相比,熏烟联合poly(I:C)组小鼠肺组织CXCL2(P<0.05)、TNF-α(P<0.01)和IFN-β(P<0.05)mRNA表达明显升高。结论:熏烟联合poly(I:C)诱导了小鼠肺部炎症反应和干扰素及干扰素刺激基因表达。同时,香烟暴露加剧了poly(I:C)诱导的小鼠肺部急性炎症反应和Ⅰ型干扰素表达。

Biosynthesis of poly-3-hydroxybutyrate with a high molecular weight by methanotroph from methane and methanol

Poly-3-hydroxybutyrate （PHB） can be produced by various species of bacteria. Among the possible carbon sources, both methane and methanol could be a suitable substrate for the production of PHB. Methane is cheap and plentiful not only as natural gas, but also as biogas. Methanol can also maintain methanotrophic activity in some conditions. The methanotrophic strain Methylosinus trichosporium IMV3011 can accumulate PHB with methane and methanol in a brief nonsterile process. Liquid methanol （0.1%） was added to improve the oxidization of methane. The studies were carried out using shake flasks. Cultivation was performed in two stages： a continuous growth phase and a PHB accumulation phase under the conditions short of essential nutrients （ammonium, nitrate, phosphorus, copper, iron （Ⅲ）, magnesium or ethylenediamine tetraacetate （EDTA）） in batch culture. It was found that the most suitable growth time for the cell is 144 h. Then an optimized culture condition for second stage was determined, in which the PHB concentration could be much increased to 0.6 g/L. In order to increase PHB content, citric acid was added as an inhibitor of tricarboxylic acid cycle （TCA）. It was found that citric acid is favorable for the PHB accumulation, and the PHB yield was increased to 40% （w/w） from the initial yield of 12% （w/w） after nutrient deficiency cultivation. The PHB produced is of very high quality with molecular weight up to 1.5 × 10^6Da.

Miscibility, Crystallization, and Rheological Behavior of Solution Casting Poly（3-hydroxybutyrate）/poly（ethylene succinate） Blends Probed by Differential Scanning Calorimetry, Rheology, and Optical Microscope Techniques

The miscibility and crystallization of solution casting biodegradable poly（3-hydroxybuty- rate）/poly（ethylene succinate） （PHB/PES） blends was investigated by differential scanning calorimetry, rheology, and optical microscopy. The blends showed two glass transition temperatures and a depression of melting temperature of PHB with compositions in phase diagram, which indicated that the blend was partially miscible. The morphology observation supported this result. It was found that the PHB and PES can crystallize simultaneously or upon stepwise depending on the crystallization temperatures and compositions. The spherulite growth rate of PHB increased with increasing of PES content. The influence of compositions on the spherulitic growth rate for the partially miscible polymer blends was discussed.

Characterization of 3D Printed Poly(3-Hydroxybutyric-Co-3-Hydroxyvalerate) by Fused Granular Fabrication through Thermal and Mechanical Analyses

Poly[R-3-hydroxybutyrate-co-(R-3-hydroxyvalerate)] (PHBVs) copolymers are promising biopolymers, which could substitute petroleum-based plastics for various applications. PHB and PHBV pellets were processed on a customized 3D printer via Fused Granular Manufacturing (FGM) approach modified with a Mahor screw extruder. To anticipate the behaviour of PHBVs when transformed using conventional thermo-mechanical shaping processes, thermal and mechanical analyses were carried out in order to better understand the effect of annealing temperature on their crystallization behaviour and mechanical properties of PHB polymer and PHBV copolymer. The objectives of the present work were to propose an experimental strategy to study the melting and crystallization events, crystalline structure changes, and mechanical performances of both PHB homopolymer and PHBV copolymer according to identical thermal annealing treatments. A monitoring of 3D printed PHB and PHBV structures was achieved by coupling Differential Scanning Calorimetry (DSC) and tensile tests. .

Stable Cycling of All-Solid-State Lithium Metal Batteries Enabled by Salt Engineering of PEO-Based Polymer Electrolytes

Poly(ethylene oxide)(PEO)-based polymer electrolytes show the prospect in all-solid-state lithium metal batteries;however,they present limitations of low room-temperature ionic conductivity,and interfacial incompatibility with high voltage cathodes.Therefore,a salt engineering of 1,1,2,2,3,3-hexafluoropropane-1,3-disulfonimide lithium salt(LiHFDF)/LiTFSI system was developed in PEO-based electrolyte,demonstrating to effectively regulate Li ion transport and improve the interfacial stability under high voltage.We show,by manipulating the interaction between PEO matrix and TFSI^(-)-HFDF^(-),the optimized solid-state polymer electrolyte achieves maximum Li+conduction of 1.24×10^(-4)S cm^(-1)at 40℃,which is almost 3 times of the baseline.Also,the optimized polymer electrolyte demonstrates outstanding stable cycling in the LiFePO_(4)/Li and LiNi_(0.8)Mn_(0.1)Co_(0.1)O_(2)/Li(3.0-4.4 V,200 cycles)based all-solid-state lithium batteries at 40℃.

Flexible and Robust Functionalized Boron Nitride/Poly(p‑Phenylene Benzobisoxazole)Nanocomposite Paper with High Thermal Conductivity and Outstanding Electrical Insulation

With the rapid development of 5G information technology,thermal conductivity/dissipation problems of highly integrated electronic devices and electrical equipment are becoming prominent.In this work,“high-temperature solid-phase&diazonium salt decomposition”method is carried out to prepare benzidine-functionalized boron nitride(m-BN).Subsequently,m-BN/poly(pphenylene benzobisoxazole)nanofiber(PNF)nanocomposite paper with nacremimetic layered structures is prepared via sol–gel film transformation approach.The obtained m-BN/PNF nanocomposite paper with 50 wt%m-BN presents excellent thermal conductivity,incredible electrical insulation,outstanding mechanical properties and thermal stability,due to the construction of extensive hydrogen bonds andπ–πinteractions between m-BN and PNF,and stable nacre-mimetic layered structures.Itsλ∥andλ_(⊥)are 9.68 and 0.84 W m^(-1)K^(-1),and the volume resistivity and breakdown strength are as high as 2.3×10^(15)Ωcm and 324.2 kV mm^(-1),respectively.Besides,it also presents extremely high tensile strength of 193.6 MPa and thermal decomposition temperature of 640°C,showing a broad application prospect in high-end thermal management fields such as electronic devices and electrical equipment.

MISCIBILITY AND CRYSTALLIZATION BEHAVIOR OF BIODEGRADABLE BLEND OF POLY(β—HYDROXYBUTYRATE)AND POLY(D,L—LACTIDE)—CO—POLY(ETHYLENE GLYCOL)

Studies on the miscibility of PHB/PELA blends showed that PHB and PELA were miscible in amorphous state.The crystallization behavior of PHB in the blend was strongly de- pendent on the addition of PELA component.

BIOSYNTHESIS AND THERMAL PROPERTIES OF POLY(3-HYDROXYBUTYRATE-co-3-HYDROXYVALERATE)WITH LARGE VARIETY OF HYDROXYVALERATE CONTENTS BY BACILLUS CEREUS

Biosynthesis and thermal properties of poly（3-hydroxybutyrate-co-3-hydroxyvalerate） （PHBV） with different HV （hydrovalerate） content produced by a Bacillus cereus strain were investigated. A large variety of HV contents （up to about 90 mol%） of PHBV could be produced by this strain. Combined nitrogen sources containing both yeast extract and ammonium sulphate were better for cell growth and polyhydroxyalkanoates （PHA） production than either yeast extract or ammonium sulphate alone. Propionic acid is more favorable for the production of HV content than that of valeric acid. Finally, thermal properties of PHBV produced by this strain are found close to the results of other groups.

MISCIBILITY AND MORPHOLOGICAL STRUCTURE OF BIODEGRADABLE BLEND OF POLY(β—HYDROXYBUTYRATE)AND POLY(D,L—LACTIDE)

The poly(β-hydroxybutyrate)/poly(d,1-lactide)(PHB/PLA)blend was found to be immiscible,the melting point and the phase crystallinity of PHB were independent of the blend composition.Comparing with plain PHB,the blend exhibited the crystallization change and a certain improvement of the mechanical property.

Weavability of β-Hydroxybutyrate and β-Hydroxyvalerate Copolymers( PHBV ) /PLA Used in Artificial Blood Vessels

The β-hydroxybutyrate and β-hydroxyvalerate copolymers( PHBV) /polylactic acid( PLA) is a new biocompatible material,which is developed through bacterial fermentation in vivo systems.The PHBV / PLA material could be used to make continuous filaments.However,features of artificial blood vessels,especially small diameter vascular grafts made of PHVB / PLA materials are not known.This research are to evaluate and improve weavability of the PHBV / PLA material, and to explore feasibility of using it in artificial blood vessels.Preliminary results showed that weavability of PHBV / PLV was not good,but its weavability could be improved by using methods of weak chemical,such as sizing.In this research,scanning electron microscope( SEM) was adopted to evaluate weavability of PHBV / PLV after sizing and observe surfaces of yarns and fabrics.Also,in order to set proper parameters in heat settings,differential scanning calorimetry( DSC) was used to identify glass transition temperature.

Innovative approach to boosting the chemical stability of AZ31 magnesium alloy using polymer-modified hybrid metal oxides

Meeting the demands of complex and advanced applications requires the development of high-performance hybrid materials with unique properties.However,the integration of polymeric frameworks with MgO/WO_(3) composite layers faces challenges due to the lack of understanding of the formation mechanism and the challenge of determining the impact of self-assembled architecture on anticorrosive properties.In this study,we aimed to enhance the corrosion resistance of the MgO layer produced by plasma electrolysis(PE)of AZ31 Mg alloy by incorporating WO_(3) with partially phosphorated poly(vinyl alcohol)(PPVA).Two types of porous MgO layers were produced using the PE process with an alkaline-phosphate electrolyte,one with and one without WO_(3) nanoparticles,which were subsequently immersed in an aqueous solution of PPVA.Incorporating PPVA into the WO_(3)-MgO layer resulted in hybrids being deposited in a fragmented manner,creating a“laminar reef-like structure”that sealed most of the structural defects in the layer.The PPVA-sealed WO_(3)-based coating exhibited superior corrosion resistance compared to the other samples.Computational analyses were employed to explore the mechanism underlying the formation of PPVA/WO_(3) hybrids on the MgO layer.These findings suggest that PPVA-WO_(3)-MgO hybrid coatings can potentially improve corrosion resistance in various fields.

Silk fibroins modify the atmospheric low temperature plasma-treated poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) film for the application of cardiovascular tissue engineering

Tissue engineered scaffold is one of the hopeful therapies for the patients with organ or tissue damages. The key element for a tissue engineered scaffold material is high biocompatibility. Herein the poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) film was irradiated by the low temperature atmospheric plasma and then coated by the silk fibroins (SF). After plasma treatment, the surface of PHBHHx film became rougher and more hydrophilic than that of original film. The experiment of PHBHHx flushed by phosphate buffer solution (PBS) proves that the coated SF shows stronger immobilization on the plasma-treated film than that on the untreated film. The cell viability assay demonstrates that SF-coated PHBHHx films treated by the plasma significantly supports the proliferation and growth of the human smooth muscle cells (HSMCs). Furthermore, the scanning electron microscopy and hemotoylin and eosin (HE) staining show that HSMCs formed a cell sub-monolayer and secreted a large amount of extracellular matrix (ECM) on the films after one week's culture. The silk fibroins modify the plasma-treated PHBHHx film, providing a material potentially applicable in the cardiovascular tissue engi-neering.

Tuning the cross-linked structure of basic poly(ionic liquid)to develop an efficient catalyst for the conversion of vinyl carbonate to dimethyl carbonate

Dimethyl carbonate(DMC)is a crucial chemical raw material widely used in organic synthesis,lithiumion battery electrolytes,and various other fields.The current primary industrial process employs a conventional sodium methoxide basic catalyst to produce DMC through the transesterification reaction between vinyl carbonate and methanol.However,the utilization of this catalyst presents several challenges during the process,including equipment corrosion,the generation of solid waste,susceptibility to deactivation,and complexities in separation and recovery.To address these limitations,a series of alkaline poly(ionic liquid)s,i.e.[DVBPIL][PHO],[DVCPIL][PHO],and[TBVPIL][PHO],with different crosslinking degrees and structures,were synthesized through the construction of cross-linked polymeric monomers and functionalization.These poly(ionic liquid)s exhibit cross-linked structures and controllable cationic and anionic characteristics.Research was conducted to investigate the effect of the cross-linking degree and structure on the catalytic performance of transesterification in synthesizing DMC.It was discovered that the appropriate cross-linking degree and structure of the[DVCPIL][PHO]catalyst resulted in a DMC yield of up to 80.6%.Furthermore,this catalyst material exhibited good stability,maintaining its catalytic activity after repeated use five times without significant changes.The results of this study demonstrate the potential for using alkaline poly(ionic liquid)s as a highly efficient and sustainable alternative to traditional catalysts for the transesterification synthesis of DMC.

Dual-salt poly(tetrahydrofuran) electrolyte enables quasi-solid-state lithium metal batteries to operate at -30 ℃

The stable operation of solid-state lithium metal batteries at low temperatures is plagued by severe restrictions from inferior electrolyte-electrode interface compatibility and increased energy barrier for Li^(+)migration.Herein,we prepare a dual-salt poly(tetrahydrofuran)-based electrolyte consisting of lithium hexafluorophosphate and lithium difluoro(oxalato)borate(LiDFOB).The Li-salt anions(DFOB−)not only accelerate the ring-opening polymerization of tetrahydrofuran,but also promote the formation of highly ion-conductive and sustainable interphases on Li metal anodes without sacrificing the Li^(+)conductivity of electrolytes,which is favorable for Li^(+)transport kinetics at low temperatures.Applications of this polymer electrolyte in Li||LiFePO_(4)cells show 82.3%capacity retention over 1000 cycles at 30℃and endow stable discharge capacity at−30℃.Remarkably,the Li||LiFePO4 cells retain 52%of their room-temperature capacity at−20℃and 0.1 C.This rational design of dual-salt polymer-based electrolytes may provide a new perspective for the stable operation of quasi-solid-state batteries at low temperatures.

Efficient and selective upcycling of waste polylactic acid into acetate using nickel selenide

The conversion of waste polylactic acid(PLA)plastics into high-value-added chemicals through electrochemical methods is a promising and sustainable approach.However,developing efficient and highly selective catalysts for lactic acid oxidation reaction(LAOR)and understanding the reaction process are challenging.Here,we report the electrooxidation of waste PLA to acetate at a high current density of 100 mA cm-2 with high Faraday efficiency(~95%)and excellent stability(>100 h)over a nickel selenide nanosheet catalyst.In addition,a total Faraday efficiency of up to 190%was achieved for carboxylic acids,including acetic acid and formic acid,by coupling with the cathodic CO_(2) reduction reaction.In situ experimental results and theoretical simulations revealed that the catalytic activity center of LAOR was dynamically formed NiOOH species,and the surface-adsorbed SeO_(x) species accelerated the formation of Ni~(3+)species,thus promoting catalytic activity.The mechanism of lactic acid electrooxidation was further elucidated.Lactic acid was dehydrogenated to produce pyruvate first and then formed CH_3CO due to preferential C-C bond cleavage,resulting in the presence of acetate.This work demonstrated a sustainable method for recycling waste PLA and CO_(2) into high-value-added products.

TOPCon太阳电池背面叠层poly工艺的优化及其对电性能的影响

通过增加TOPCon太阳电池poly层中的磷掺杂浓度可以增强poly层与硅基底之间的钝化效果并提高poly层与金属电极间的接触能力,但过高的掺杂浓度会导致磷原子扩散到硅基底,破坏氧化层与硅基底之间的界面钝化效果。为了解决这一问题,提出在poly层中间增加一层薄的氧化层作为阻挡层(即叠层poly工艺,下文简称为“叠层工艺”)的方案,将原本单一的poly-Si磷掺杂进行双层分布,底层poly-Si轻掺杂,表层poly-Si重掺杂;对常规工艺和叠层工艺制备TOPCon的太阳电池进行对比试验后,进一步优化叠层工艺,调整中间氧化层厚度,并研究不同中间氧化层厚度的叠层工艺对TOPCon太阳电池电性能的影响。实验结果表明:1)叠层工艺可以提高TOPCon太阳电池的电性能;2)当中间氧化层厚度提升至1.5 nm时,太阳电池的光电转换效率达到最高值(25.66%)。但中间氧化层的厚度是一个需要精确控制的工艺参数,需找到最佳的厚度平衡点,以提高太阳电池性能。

Anion competition for Li^(+)solvated coordination environments in poly(1,3 dioxolane)electrolyte to enable high-voltage lithium metal solid-state batteries

Gel-based polymer electrolytes are limited by the polarity of the residual solvent,which restricts the coupling-breaking behaviour during Li^(+)conduction,resulting in the Li^(+)transport kinetics being greatly affected.Here,we designed anion competitive gel polymer electrolyte(ACPE)by introducing lithium difluoro(oxalato)borate(LiDFOB)anion into the 1,3-dioxolane(DOL)in situ polymerisation system.ACPE enhances the ionic dipole interaction between Li^(+)and the solvent molecules and synergizes with Li^(+)across the solvation site of the polymer ethylene oxide(EO)unit,combination that greatly improves the Li^(+)transport efficiency.As a result,ACPE exhibits 1.12 mS cm^(−1)ionic conductivity and 0.75 Li^(+)transfer number at room temperature.Additionally,this intra-polymer solvation sheath allows preferential desolvation of DFOB−,which contributes to the formation of kinetically stable anion-derived interphase and effectively mitigates side reactions.Our results demonstrate that the assembled Li||NCM622 solid-state battery exhibits lifespan of over 300 cycles with average Coulombic efficiency of 98.8%and capacity retention of 80.3%.This study introduces a novel approach for ion migration and interface design,paving the way for high-safety and high-energy-density batteries.

Stable Cycling of All-Solid-State Lithium Batteries Enabled by Cyano-Molecular Diamond Improved Polymer Electrolytes

The interfacial instability of the poly(ethylene oxide)(PEO)-based electrolytes impedes the long-term cycling and further application of all-solid-state lithium metal batter-ies.In this work,we have shown an effective additive 1-adaman-tanecarbonitrile,which con-tributes to the excellent per-formance of the poly(ethylene oxide)-based electrolytes.Owing to the strong interaction of the 1-Adamantanecarboni-trile to the polymer matrix and anions,the coordination of the Li^(+)-EO is weakened,and the binding effect of anions is strengthened,thereby improving the Li^(+)conductivity and the electrochemical stability.The diamond building block on the surface of the lithium anode can sup-press the growth of lithium dendrites.Importantly,the 1-Adamantanecarbonitrile also regulates the formation of LiF in the solid electrolyte interface and cathode electrolyte interface,which contributes to the interfacial stability(especially at high voltages)and protects the electrodes,enabling all-solid-state batteries to cycle at high voltages for long periods of time.Therefore,the Li/Li symmetric cell undergoes long-term lithium plating/stripping for more than 2000 h.1-Adamantanecarbonitrile-poly(ethylene oxide)-based LFP/Li and 4.3 V Ni_(0.8)Mn_(0.1)Co_(0.1)O_(2)/Li all-solid-state batteries achieved stable cycles for 1000 times,with capacity retention rates reaching 85%and 80%,respectively.