This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a sila...This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a silane coupling agent(SCA) in order to chiefly enhance their distributions as well as adhesions within the CE/BOZ resin matrix,then incorporated with various weight amounts ranging from 5 wt% to 20 wt% with a regular interval of 5 wt%. The obtained results showed that at the maximum treated fiber loading(20 wt%), distinctive enhancements in the mechanical properties in terms of flexural strength and microhardness were obtained. Besides, the thermal stability and glass transition temperature(Tg) were appreciably enhanced and were higher than those of the pure CE/BOZ resin properties. With respect to the astonishing properties of the NHFs, these enhancements could be possibly due to the good dispersion and adhesion of the treated NHFs inside the CE/BOZ resin achieved upon using the SCA. Therefore,we believe herein that these renewable and cheap NHFs have considerable potential to be used as reinfocer materials for CE/BOZ resin composites to be used in various industrial sectors.展开更多
Gene-based therapeutics has emerged as a promising approach for human cancer therapy. Among a variety of non-viral vectors, polymer vectors are particularly attractive due to their safety and multivalent groups on the...Gene-based therapeutics has emerged as a promising approach for human cancer therapy. Among a variety of non-viral vectors, polymer vectors are particularly attractive due to their safety and multivalent groups on their surface. This study focuses on guanidinylated O-carboxymethyl chitosan(GOCMCS) along with poly-β-amino ester(PBAE) for si RNA delivery. Binding efficiency of PBAE/si RNA/GOCMCS nanoparticles were characterized by gel electrophoresis. The si RNA-loaded nanoparticles were found to be stable in the presence of RNase A, serum and BALF respectively. Fine particle fraction(FPF) which was determined by a two-stage impinger(TSI) was 57.8% ± 2.6%. The particle size and zeta potential of the nanoparticles were 153.8 ± 12.54 nm and + 12.2 ± 4.94 m V. In vitro cell transfection studies were carried out with A549 cells. The cellular uptake was significantly increased. When the cells were incubated with si Survivin-loaded nanoparticles, it could induce 26.83% ± 0.59% apoptosis of A549 cells and the gene silencing level of survivin expression in A549 cells were 30.93% ± 2.27%. The results suggested that PBAE/GOCMCS nanoparticle was a very promising gene delivery carrier.展开更多
Vinyl ester (VE) resin inherently has intrinsic brittleness due to its high cross-link density. To improve mechanical performance, micro/nano fillers are widely used to modify this matrix. In present study, glass fibe...Vinyl ester (VE) resin inherently has intrinsic brittleness due to its high cross-link density. To improve mechanical performance, micro/nano fillers are widely used to modify this matrix. In present study, glass fiber in submicron scale at low contents was added into VE to prepare submicron composite (sMC). The impact resistance of un-notched sMC degraded with the increase of sGF content while that of notched-sMC remained the unchanged. Flexural properties of sMCs also were the same with that of neat resin. The results of Dynamic mechanical analysis (DMA) test showed the slight increase of storage modulus and the decrease of tan delta value in the case of sMC compared to those of un-filled matrix. However, the Mode I fracture toughness of sMC improved up to 26% and 61% corresponding to 0.3 and 0.6 wt% glass fiber used. The compact tension sample test suggests that there is the delay of crack propagation under tensile cyclic load in resin reinforced by submicron glass fiber. The number of failure cycle enlarged proportionally with the increment of sGF content in matrix.展开更多
In the accompanying paper (Part 1), we showed that the fatty acid moiety and the acidity of the polysaccharide-backbone of a fatty acid-containing polysaccharide might be involved in its emul-sification, moisture abso...In the accompanying paper (Part 1), we showed that the fatty acid moiety and the acidity of the polysaccharide-backbone of a fatty acid-containing polysaccharide might be involved in its emul-sification, moisture absorption, and moisture retention abilities. In this study, we synthesized alkyl esterified poly-γ-glutamic acid (PGA) with various chain lengths and degrees of substitution of the alkyl moieties to examine how hydrophobic groups incorporated in the anionic polymer contribute to enhanced emulsification, moisture absorption, and moisture retention. With a low degree of alkylation of PGA, these abilities were drastically improved. To improve the moisture absorption of PGA, alkylation with a short chain length is effective in forming interspaces between PGA chains to trap water molecules. Hydrophobic-hydrophilic balance may also be important to improve the emulsification and moisture retention abilities of PGA alkylates. To the best of our knowledge, this is the first report of the relationship between the structure and the multifunctional abilities of an anionic polymer incorporated with a small amount of hydrophobic residue. PGA alkylates, as well as fatty acid-containing polysaccharides, have potential use as multifunctional surfactants throughout various industries.展开更多
Cationized pulp fibers （CPF） were prepared by the adsorption of a novel biodegradable cationic ester quaternary ammonium salt （31441） on bleached softwood kraft pulp fibers. The optimized conditions for the CPF pr...Cationized pulp fibers （CPF） were prepared by the adsorption of a novel biodegradable cationic ester quaternary ammonium salt （31441） on bleached softwood kraft pulp fibers. The optimized conditions for the CPF preparation were： 4% of 31441 （based on oven-dry pulp）, 80℃ and 30 rain. The CPF was characterized by FT-IR, SEM and XPS. Experimental results showed that the CPF improved the retention of precipitated calcium carbonate （PCC） filler significantly. With 0.9% CPF （based on oven-dry pulp）, the retention of PCC increased from 57.53% to 72.21%. The physical properties of paper were also slightly improved. The tensile strength and burst strength of the paper with CPF were higher than those with CPAM. CPF addition had no effect on the stock drainage.展开更多
Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorin...Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.展开更多
A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT ...A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT agent,which is then performed to functionalize the quartz fibers(QFs@PDMS-b-PGMA)via a simple coating process.Finally,the QFs@PDMS-b-PGMA/bisphenol A dicyanate ester(BADCy)wave-transparent laminated composites are fabricated by high-temperature molding.Nuclear magnetic resonance(NMR)spectroscopy,Fourier transform infrared(FT-IR)spectroscopy and size ex-clusion chromatography(SEC)demonstrate the successful preparation of PDMS-b-PGMA with expected structure.When the molar mass and coating amount of PDMS-b-PGMA are respectively 8100 g/mol and 2.0 wt.%,QFs@PDMS-b-PGMA/BADCy wave-transparent laminated composites present optimal mechan-ical properties and wave-transparent performance.The interlaminar shear strength(ILSS)and flexural strength are 53.6 and 552.0 MPa,respectively.Meanwhile,the dielectric constant and dielectric loss val-ues are 2.61 and 0.0028 at 1 MHz(wave transmittance of 93.8%),showing good stability at different frequencies(102-106 Hz and 8.4-12.4 GHz)and temperatures(25-250℃).展开更多
基金Supported by the National Natural Science Foundation of China(51773048)the Natural Science Foundation of Heilongjiang Province(E2016025)Fundamental Research Funds for the Central Universities(HEUCFP201724,HEUCFP201791)
文摘This present study deals with the reinforcement of thermosetting resin blends composed of cyanate ester(CE) and benzoxazine(BOZ) resins with natural hemp fibers(NHFs). These NHFs were initially treated by using a silane coupling agent(SCA) in order to chiefly enhance their distributions as well as adhesions within the CE/BOZ resin matrix,then incorporated with various weight amounts ranging from 5 wt% to 20 wt% with a regular interval of 5 wt%. The obtained results showed that at the maximum treated fiber loading(20 wt%), distinctive enhancements in the mechanical properties in terms of flexural strength and microhardness were obtained. Besides, the thermal stability and glass transition temperature(Tg) were appreciably enhanced and were higher than those of the pure CE/BOZ resin properties. With respect to the astonishing properties of the NHFs, these enhancements could be possibly due to the good dispersion and adhesion of the treated NHFs inside the CE/BOZ resin achieved upon using the SCA. Therefore,we believe herein that these renewable and cheap NHFs have considerable potential to be used as reinfocer materials for CE/BOZ resin composites to be used in various industrial sectors.
基金This work was supported by the 3rd Jiangsu Overseas Research&Training Program for University Prominent Young&Middleaged Teachers and Presidentsthe College Students Innovation Project for the R&D of Novel Drugs[No.J1310032]And we would like to thank cell and molecular biology experiment platform of China Pharmaceutical University for the assistance with relevant test items.
文摘Gene-based therapeutics has emerged as a promising approach for human cancer therapy. Among a variety of non-viral vectors, polymer vectors are particularly attractive due to their safety and multivalent groups on their surface. This study focuses on guanidinylated O-carboxymethyl chitosan(GOCMCS) along with poly-β-amino ester(PBAE) for si RNA delivery. Binding efficiency of PBAE/si RNA/GOCMCS nanoparticles were characterized by gel electrophoresis. The si RNA-loaded nanoparticles were found to be stable in the presence of RNase A, serum and BALF respectively. Fine particle fraction(FPF) which was determined by a two-stage impinger(TSI) was 57.8% ± 2.6%. The particle size and zeta potential of the nanoparticles were 153.8 ± 12.54 nm and + 12.2 ± 4.94 m V. In vitro cell transfection studies were carried out with A549 cells. The cellular uptake was significantly increased. When the cells were incubated with si Survivin-loaded nanoparticles, it could induce 26.83% ± 0.59% apoptosis of A549 cells and the gene silencing level of survivin expression in A549 cells were 30.93% ± 2.27%. The results suggested that PBAE/GOCMCS nanoparticle was a very promising gene delivery carrier.
文摘Vinyl ester (VE) resin inherently has intrinsic brittleness due to its high cross-link density. To improve mechanical performance, micro/nano fillers are widely used to modify this matrix. In present study, glass fiber in submicron scale at low contents was added into VE to prepare submicron composite (sMC). The impact resistance of un-notched sMC degraded with the increase of sGF content while that of notched-sMC remained the unchanged. Flexural properties of sMCs also were the same with that of neat resin. The results of Dynamic mechanical analysis (DMA) test showed the slight increase of storage modulus and the decrease of tan delta value in the case of sMC compared to those of un-filled matrix. However, the Mode I fracture toughness of sMC improved up to 26% and 61% corresponding to 0.3 and 0.6 wt% glass fiber used. The compact tension sample test suggests that there is the delay of crack propagation under tensile cyclic load in resin reinforced by submicron glass fiber. The number of failure cycle enlarged proportionally with the increment of sGF content in matrix.
文摘In the accompanying paper (Part 1), we showed that the fatty acid moiety and the acidity of the polysaccharide-backbone of a fatty acid-containing polysaccharide might be involved in its emul-sification, moisture absorption, and moisture retention abilities. In this study, we synthesized alkyl esterified poly-γ-glutamic acid (PGA) with various chain lengths and degrees of substitution of the alkyl moieties to examine how hydrophobic groups incorporated in the anionic polymer contribute to enhanced emulsification, moisture absorption, and moisture retention. With a low degree of alkylation of PGA, these abilities were drastically improved. To improve the moisture absorption of PGA, alkylation with a short chain length is effective in forming interspaces between PGA chains to trap water molecules. Hydrophobic-hydrophilic balance may also be important to improve the emulsification and moisture retention abilities of PGA alkylates. To the best of our knowledge, this is the first report of the relationship between the structure and the multifunctional abilities of an anionic polymer incorporated with a small amount of hydrophobic residue. PGA alkylates, as well as fatty acid-containing polysaccharides, have potential use as multifunctional surfactants throughout various industries.
基金the Key Scientific and Technological Project of Heilongjiang Province (GB06B501-1)
文摘Cationized pulp fibers （CPF） were prepared by the adsorption of a novel biodegradable cationic ester quaternary ammonium salt （31441） on bleached softwood kraft pulp fibers. The optimized conditions for the CPF preparation were： 4% of 31441 （based on oven-dry pulp）, 80℃ and 30 rain. The CPF was characterized by FT-IR, SEM and XPS. Experimental results showed that the CPF improved the retention of precipitated calcium carbonate （PCC） filler significantly. With 0.9% CPF （based on oven-dry pulp）, the retention of PCC increased from 57.53% to 72.21%. The physical properties of paper were also slightly improved. The tensile strength and burst strength of the paper with CPF were higher than those with CPAM. CPF addition had no effect on the stock drainage.
基金The authors are grateful for the support and funding from National Scientific Research Project(Basis Strengthening Plan)State Key Laboratory of Solidification Processing in NWPU(No.SKLSP202103).
文摘Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound(LCFE)are applied as polymer matrix(LCFE-BADCy),poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as rein-forcements,and fluorine/adamantane PBO precursor(pre FABPBO)as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites.LCFE could improve the order degree of BADCy cured network,in favor of enhancing the wave-transparent perfor-mance,mechanical properties,and intrinsic thermal conductivity.The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature(25–200℃)and frequency(10^(4)–10^(7) Hz and 8.2–12.4 GHz)stable with the value of 2.49 and 0.003 under 10^(6) Hz at 25℃,and the corresponding wave transmission efficiency is 95.0%,higher than that of 92.5%for PBO fibers/BADCy com-posites.The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa,38.1%and 16.2%higher than those of PBO fibers/BADCy composites.Besides,the volume resistivity,breakdown voltage,heat resistance index,glass transition temperature,flame retardant grade,and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3×10^(15)Ωcm,29.75 kV/mm,217.2℃,245.7℃,V-1 grade,and 33.6%,expected to be performed as a new generation of“lightweight/loading/wave-transparent”electromagnetic window materials in advanced military weapons and civil communication base station.
文摘A block copolymer of PDMS-b-PGMA is synthesized by polymerizing glycidyl methacrylate(GMA)via reversible addition-fragmentation chain transfer(RAFT)polymerization applying a polydimethylsiloxane(PDMS)based macro-RAFT agent,which is then performed to functionalize the quartz fibers(QFs@PDMS-b-PGMA)via a simple coating process.Finally,the QFs@PDMS-b-PGMA/bisphenol A dicyanate ester(BADCy)wave-transparent laminated composites are fabricated by high-temperature molding.Nuclear magnetic resonance(NMR)spectroscopy,Fourier transform infrared(FT-IR)spectroscopy and size ex-clusion chromatography(SEC)demonstrate the successful preparation of PDMS-b-PGMA with expected structure.When the molar mass and coating amount of PDMS-b-PGMA are respectively 8100 g/mol and 2.0 wt.%,QFs@PDMS-b-PGMA/BADCy wave-transparent laminated composites present optimal mechan-ical properties and wave-transparent performance.The interlaminar shear strength(ILSS)and flexural strength are 53.6 and 552.0 MPa,respectively.Meanwhile,the dielectric constant and dielectric loss val-ues are 2.61 and 0.0028 at 1 MHz(wave transmittance of 93.8%),showing good stability at different frequencies(102-106 Hz and 8.4-12.4 GHz)and temperatures(25-250℃).