Polyamide （PA6） and polycarbonate （PC） were prepared by a Brabender mixer （ PLV- 151） at 240℃ with 30 rpm for duration of 8 and 6 minutes respectively. The epoxy resin （E） addition can lead to substantial mic...Polyamide （PA6） and polycarbonate （PC） were prepared by a Brabender mixer （ PLV- 151） at 240℃ with 30 rpm for duration of 8 and 6 minutes respectively. The epoxy resin （E） addition can lead to substantial microstructural changes in the PA6/PC blends. Scanning electron microscope （SEM） was used to observe the mixtures characterized by the domains of clearly segregated homophases and voids between the two polymers. PA6/PC of polyamide 6 and polycarbonate with epoxy resin addition under the composition ratio of 20/80, 20/80/1, 40/60/1 and 40/60, were tested to verify the key role of epoxy in promoting the compatibility of PA6 with PC during blending.展开更多
This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50...This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50：50, and 40：60） from low to high strain rates. Using the universal MTS-810 machine and the split Hopkinson tension bar （SHTB） testing system, the quasi-static and impact tension tests are carried out at the room temperature. The curves of the true stress and the true strain are obtained. The deformation behaviors of PC, ABS, and PC/ABS blends are characterized in detail. The linear relationship between the strain rate and the yielding stress is given.展开更多
The oligomer structure in polycarbonate(PC) was studied by LC-MS.The sample was extracted by methanol.Three types of oligermers with chloroformate and —OH endgroups in the PC synthesized process were confirmed.More t...The oligomer structure in polycarbonate(PC) was studied by LC-MS.The sample was extracted by methanol.Three types of oligermers with chloroformate and —OH endgroups in the PC synthesized process were confirmed.More than twelve of oligomers were identified.展开更多
文摘Polyamide （PA6） and polycarbonate （PC） were prepared by a Brabender mixer （ PLV- 151） at 240℃ with 30 rpm for duration of 8 and 6 minutes respectively. The epoxy resin （E） addition can lead to substantial microstructural changes in the PA6/PC blends. Scanning electron microscope （SEM） was used to observe the mixtures characterized by the domains of clearly segregated homophases and voids between the two polymers. PA6/PC of polyamide 6 and polycarbonate with epoxy resin addition under the composition ratio of 20/80, 20/80/1, 40/60/1 and 40/60, were tested to verify the key role of epoxy in promoting the compatibility of PA6 with PC during blending.
基金supported by the National Natural Science Foundation of China (No. 11142004)the Shang-hai Leading Academic Discipline Project (No. S30106)the Innovative Foundation of Shanghai University
文摘This paper experimentally studies the tensile deformation behavior of poly- carbonate （PC）, acrylonitrile-butadiene-styrene （ABS）, and PC/ABS blends （with the blending ratios of PC to ABS being 80：20, 60：40, 50：50, and 40：60） from low to high strain rates. Using the universal MTS-810 machine and the split Hopkinson tension bar （SHTB） testing system, the quasi-static and impact tension tests are carried out at the room temperature. The curves of the true stress and the true strain are obtained. The deformation behaviors of PC, ABS, and PC/ABS blends are characterized in detail. The linear relationship between the strain rate and the yielding stress is given.
文摘The oligomer structure in polycarbonate(PC) was studied by LC-MS.The sample was extracted by methanol.Three types of oligermers with chloroformate and —OH endgroups in the PC synthesized process were confirmed.More than twelve of oligomers were identified.