Deformation mechanisms of Mg-3Al-1Zn alloy by polycrystal plasticity modeling

A polycrystal plasticity model was developed to analyze the room-temperature deformation behaviors of Mg-3A1-1Zn alloy（AZ31）.The uniaxial tension and compression tests at room temperature were conducted using cast and extruded AZ31 rods with different textures and combined with the proposed model to reveal the deformation mechanisms.It is shown that,different flow curves of two specimens under tension and compression tests can be simulated by this model.The flow curves of AZ31 extrusions exhibit different shapes for tension and compression due to different activities of tensile twinning and pyramidalc＋a slip.The metallographic and TEM observations showed the equal twinning activities at the initial stage in tension and compression tests and the occurrence of pyramidalc＋a slip in compression of as-cast Mg-3A1-1Zn alloy with increasing the strain,which is consistent with the simulated results by the proposed model.

Polycrystal modeling of hot extrusion texture of AZ80 magnesium alloy

The visco-plastic self-consistent (VPSC) model is extended to take the dynamical recrystallization (DRX) into account so that the hot extrusion texture of AZ80 magnesium alloy can be properly modeled. The effects of extrusion temperatures and imposed boundary conditions on the resulting textures were investigated, and good agreement can be found between the simulated and the measured extrusion textures. The simulated results show that the DRX grains are responsible for the formation of the {2110} fiber component since the {1010} poles of the DRX grains are tilted away from those of the unrecrystallized grains during the formation of their high angle boundaries (HABs). Furthermore, the basal poles of the grains are favorably oriented to the transversal direction (TD) where the imposed deformation is larger due to lower slip resistance of the basal slip. The elevated temperature enhances the activity of pyramidal ?c+a? slip modes and gives rise to a larger recrystallized volume fraction, resulting in a weakened extrusion texture.

Crystal plasticity based modeling of grain boundary sliding in magnesium alloy AZ31B sheet

The aim of present work is to develop a crystal plasticity modeling approach to integrate slip,dynamic recrystallization(DRX)and grain boundary sliding(GBS)for simulating the deformation behavior and texture evolution of magnesium alloys at high temperatures.Firstly,the deformation mechanisms of an AZ31B Mg alloy sheet at 300°C were investigated by examining texture and microstructure evolution during uniaxial tension and compression tests.DRX refines microstructure at strains less than 0.2,and subsequently GBS plays a significant role during deformation process.A GBS model is developed to evaluate strain and grain rotation induced by GBS,and implemented into the polycrystal plasticity framework VPSC.The VPSC-DRX-GBS model can well reproduce the stress−strain curves,grain size,texture evolution and significant texture differences in tension and compression tests due to GBS.The calculated GBS contribution ratio in tension is obviously higher than that in compression due to easier cavity nucleation at grain boundaries under tension loading.

A Numerical Study of Localized Plastic Deformationin Polycrystals

A finite element formulation which derives constitutive response from crystal plasticity theory was used to examine localized deformation in fee polycrystals. The polycrystal model was an idealized planar array of 22 hexagonal grains. The constitutive description used is based on a finite strain kinematical theory that accounts for lattice rotations. Formation of shear bands was successfully modeled in both single crystal and polycrystals. Stress and strain distribution around triple junctions was also analyzed. Results show the distributions of stresses and strains are distinctly inhomogeneous. Stress and strain fields across grain boundaries are highly discontinuous. However, this discontinuity will be restrained when shear bands are fully developed.

3D Crystal Plasticity Finite Element Modeling of the Tensile Deformation of Polycrystalline Ferritic Stainless Steel

A mesoscale model of plastic deformation of ferritic stainless steels （FSSs） is formulated by combining a crystal plasticity finite element model with 3D cellular automaton algorithm. The actual grain orientations of FSS cold rolling and annealing sheet have been detected by electron backscatter diffraction and selected to be assigned to the polycrystal model. The simulation results have been validated by comparing the calculated true stress-strain response with the experimental one. For the lack of considering the interactions of dislocations with impurities, there are no upper and lower yield points in the simulation stress-strain curves. However, the calculated yield strength and the stress-strain response after yielding agree well with the real material. The local stress and strain fields show inhomogeneous at mesoscale. The plastic deformations of the grains with typical orientations have been characterized. The analysis reveals that the grains with fiber texture show higher thickness reduction ratio as compared to others. The deformation behaviors of the grains in polycrystal are not only related to the orientations but also to the interactions from adjacent grains.