A diamond film with a size of 6×6×0.5 mm^3 is fabricated by electron-assisted chemical vapor deposition. Raman spectrum analysis, x-ray diffraction and scanning electron microscope images confirm the high pu...A diamond film with a size of 6×6×0.5 mm^3 is fabricated by electron-assisted chemical vapor deposition. Raman spectrum analysis, x-ray diffraction and scanning electron microscope images confirm the high purity and large grain size, which is larger than 300 μm. Its resistivity is higher than 10^12 W· cm. Interlaced-finger electrodes are imprinted onto the diamond film to develop an x-ray detector. Ohmic contact is confirmed by checking the linearity of its current–voltage curve. The dark current is lower than 0.1 n A under an electric field of 30 k V cm^-1. The time response is 220 ps. The sensitivity is about 125 m A W^-1 under a biasing voltage of 100 V.A good linear radiation dose rate is also confirmed. This diamond detector is used to measure x-ray on a Z-pinch, which has a double-layer 'nested tungsten wire array'. The pronounced peaks in the measured waveform clearly characterize the x-ray bursts, which proves the performance of this diamond detector.展开更多
基金supported by the National Key R&D Program of China(Grant No.2017YFE0301300)the Hunan Provincial Innovation Foundation for Postgraduate(Grant No.CX2018B588)。
文摘A diamond film with a size of 6×6×0.5 mm^3 is fabricated by electron-assisted chemical vapor deposition. Raman spectrum analysis, x-ray diffraction and scanning electron microscope images confirm the high purity and large grain size, which is larger than 300 μm. Its resistivity is higher than 10^12 W· cm. Interlaced-finger electrodes are imprinted onto the diamond film to develop an x-ray detector. Ohmic contact is confirmed by checking the linearity of its current–voltage curve. The dark current is lower than 0.1 n A under an electric field of 30 k V cm^-1. The time response is 220 ps. The sensitivity is about 125 m A W^-1 under a biasing voltage of 100 V.A good linear radiation dose rate is also confirmed. This diamond detector is used to measure x-ray on a Z-pinch, which has a double-layer 'nested tungsten wire array'. The pronounced peaks in the measured waveform clearly characterize the x-ray bursts, which proves the performance of this diamond detector.