The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by b...The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.展开更多
Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown ...Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown nonwovens with sufficient mechanical properties for practical application.Herein,we report a simple strategy for the large-scale preparation of biodegradable PLA/poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV)melt-blown nonwovens with high strength and excellent toughness.In this process,a small amount of PHBV is added to PLA to improve the latter’s crystallization rate and crystallinity.In addition,when the PHBV content increases from 0 to 7.5 wt%,the diameters of the PLA/PHBV melt-blown fibers decrease significantly(with the proportion of nanofibers increasing from 7.7%to 42.9%).The resultant PLA/PHBV(5 wt%PHBV)melt-blown nonwovens exhibit the highest mechanical properties.The tensile stress,elongation,and toughness of PLA/PHBV(5 wt%PHBV)melt-blown nonwovens reach 2.5 MPa,45%,and 1.0 MJm3,respectively.More importantly,PLA/PHBV melt-blown nonwovens can be completely degraded into carbon dioxide and water after four months in the soil,making them environmentally friendly.A general tensile-failure model of melt-blown nonwovens is proposed in this study,which may shed light on mechanical performance enhancement for nonwovens.展开更多
基金supported by the National Natural Science Foundation of China (52373091,52173084,51973192,51603122)Shanxi-Zheda Institute of Advanced Materials and Chemical Engineering (2021SZ-FR002)。
基金National Natural Science Foundation of China(No.52273054)Shanghai Natural Science Foundation,China(No.20ZR1402200)。
文摘The increasing demand for sustainable and environmentally friendly materials has driven research towards the development of green composites.In this work,the flax/polylactic acid(PLA)braided yarns were fabricated by braiding PLA filaments with 4 to 24 spindles on flax yarns.After curing at different temperatures(180℃and 190℃),the core/sheath structural flax/PLA composite yarns were manufactured.According to the results of the tensile test,the flax/PLA composite yarn with 4-spindle PLA yarns as a sheath layer and at a curing temperature of 180℃reached the maximum elastic modulus of about(5.79±0.65)GPa and the maximum tensile strength of about(162.17±18.18)MPa.This flax/PLA composite yarn with good mechanical properties would be suitable for green composites in the automobile manufacturing industry and building materials.
基金supported by the National Key Research and Development Program of China(2022YFB3804903 and 2022YFB3804900)the National Natural Science Foundation of China(52273052)+1 种基金the Program of Shanghai Academic/Technology Research Leader(21XD1420100)the International Cooperation Fund of Science and Technology Commission of Shanghai Municipality(21130750100).
文摘Biodegradable polylactic acid(PLA)melt-blown nonwovens are attractive candidates to replace nondegradable polypropylene melt-blown nonwovens.However,it is still an extremely challenging task to prepare PLA melt-blown nonwovens with sufficient mechanical properties for practical application.Herein,we report a simple strategy for the large-scale preparation of biodegradable PLA/poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV)melt-blown nonwovens with high strength and excellent toughness.In this process,a small amount of PHBV is added to PLA to improve the latter’s crystallization rate and crystallinity.In addition,when the PHBV content increases from 0 to 7.5 wt%,the diameters of the PLA/PHBV melt-blown fibers decrease significantly(with the proportion of nanofibers increasing from 7.7%to 42.9%).The resultant PLA/PHBV(5 wt%PHBV)melt-blown nonwovens exhibit the highest mechanical properties.The tensile stress,elongation,and toughness of PLA/PHBV(5 wt%PHBV)melt-blown nonwovens reach 2.5 MPa,45%,and 1.0 MJm3,respectively.More importantly,PLA/PHBV melt-blown nonwovens can be completely degraded into carbon dioxide and water after four months in the soil,making them environmentally friendly.A general tensile-failure model of melt-blown nonwovens is proposed in this study,which may shed light on mechanical performance enhancement for nonwovens.