The Usability of Polyoxyethylene Stearate as Lubricant for Sizing Cotton Warp Yarns

The usability of polyoxyethylene stearate with 10 ethylene epoxides(POES 10) as lubricant in warp sizing was investigated for replacing sizing cream in order to prevent blockage of paste delivery tube.The influences of POES 10 and sizing cream upon the adhesion of starch to fibers and the performances of starch film were measured and compared.Then,the usability of POES 10 as lubricant was evaluated through the comparison between POES 10 and sizing cream in tensile behaviors,abrasion resistance,and hairiness of sized cotton yarns.The experimental observation demonstrates that the influence of POES 10 upon the adhesion is similar to that of sizing cream.POES 10 is superior to sizing cream in tensile strength and breaking elongation of starch film when mass content of lubricants is equal to or exceeds 2%.Incorporating POES 10 into starch makes starch film more resistant to wear.Furthermore,POES 10 is preferred to sizing cream in the increase in tensile strength,loss in elongation,and abrasion resistance of sized cotton yarns.Using POES 10 as lubricant in size formulation is favorable to the decrease of longer hairs on sized yarns.POES 10 exhibits potential use during cotton warp sizing for replacing sizing cream.

依托泊苷固体分散体的溶出与大鼠在体肠吸收研究

目的:制备依托泊苷(VP-16)固体分散体,对其在大鼠小肠各部位的吸收进行研究,以期提高口服生物利用度。方法:采用溶剂-熔融法制备VP-16-硬脂酸聚氧烃酯(S-40)或泊洛沙姆188(F68)固体分散体,按中华人民共和国药典2005年版溶出度第二法测定VP-16固体分散体的溶出,以差示扫描量热法(DSC)法和X-射线衍射法鉴定VP-16在体系中的状态,运用大鼠在体肠循环模型,采用HPLC法测定药物浓度,考察药物的吸收。结果:固体分散体中VP-16的溶出比原料药和物理混合物均有显著提高,随着载体质量比增加而增大。DSC图谱显示VP-16的特征峰消失,X-射线衍射图谱显示VP-16的结晶衍射峰消失,药物以无定形或分子状态分散在固体分散体中。VP-16在小肠上半段吸收较好,当载体对药物质量比≥3时,固体分散体在空肠段吸收有显著增加,且VP-16/S-40固体分散体的吸收比VP-16/F68固体分散体的吸收好。结论:S-40和F68两种表面活性剂均能显著提高VP-16的溶出度,并对VP-16在大鼠小肠的吸收有明显促进作用,S-40的吸收促进作用显著大于F68。

蓖麻油聚氧乙烯醚水基润滑液摩擦学特性研究

本文以蓖麻油聚氧乙烯醚水基润滑液为研究对象,分别使用润滑膜厚度测量仪、微摩擦试验机和四球摩擦试验机对其成膜特性、摩擦磨损特性和抗磨极压特性进行了系统的研究,并用扫描电子显微镜和能量色散光谱仪对摩擦磨损机制进行了分析.结果表明:蓖麻油聚氧乙烯醚提高了纯水的成膜能力,能够在钢-铝摩擦副形成有效的润滑膜,起到良好的减摩抗磨效果.随着浓度的增大,对钢-铝摩擦副的减摩抗磨性能和四球摩擦试验的抗磨极压性能都得到了提高.

聚丁二酸丁二醇酯/聚乙二醇硬脂酸酯共混物结晶行为

用溶液共混的方法制备了聚丁二酸丁二醇酯(PBS)/聚乙二醇硬脂酸酯(PEOST)共混物。采用差示扫描量热法(DSC)表征了共混物的结晶熔融行为。研究结果表明,加入质量分数5%的PEOST能使PBS结晶温度(T_c)降低约10℃,但使熔融温度(T_m)升高约3℃,继续增加PEOST用量对PBS的T_c和T_m影响不大;PBS的结晶焓(ΔH_c)随PEOST含量的增加呈上升趋势,而熔融焓(ΔH_m)先降低再上升;PEOST的结晶属于受限结晶,当其质量分数低于10%,DSC曲线中没有出现PEOST的结晶峰和熔融峰;当质量分数大于20%时,才出现PEOST结晶峰和相应的熔融峰。傅里叶变换红外(FT-IR)谱图中也才出现相应的结晶红外响应峰(1107 cm^(-1)和841 cm^(-1))。广角X射线衍射显示加入PEOST未改变PBS的晶体结构。偏光显微镜分析表明,PEOST含量较高的共混物晶体尺寸更大,具有更清晰的周期性明暗相间的环带花纹。

非离子型分散剂对低阶煤制备水煤浆的影响

为了改善低阶煤制水煤浆品质差的现状,实现低阶煤的高效清洁利用,采用非离子型表面活性剂壬基酚聚氧乙烯醚(NPEO-40)作为分散剂制备低阶煤水煤浆,并进行水煤浆成浆性能及成浆机理研究。神东煤(SDC)低阶煤水煤浆试验表明,水煤浆表观黏度η100随NPEO-40用量的增加而降低,当NPEO-40用量增加到1.0%,η100基本保持不变。添加剂用量为1%、水煤浆浓度为60%~68%时,浆体呈剪切变稀的假塑性流体,最大成浆浓度C1000=67.5%;水煤浆浓度为60%~68%时,浆体稳定性随浓度的升高而降低。等温吸附研究表明,NPEO-40在低阶煤表面的吸附行为符合Langmuir等温吸附模型,且吉布斯自由能ΔGa0ds=-29.27 kJ/mol,说明反应自发进行。浸润试验表明,1.0%的NPEO-40适于SDC在溶液中的浸润。对吸附前后的煤进行XPS C1s窄程扫描,C—C/C—H官能团含量由78.79%下降到70.12%。含氧官能团C—O,C■O和O■C—O总含量由21.21%增加至29.88%,说明吸附NPEO-40后,其疏水官能团与煤表面的C—C/C—H官能团结合,使含氧官能团暴露在外侧,从而使煤表面C—C/C—H官能团含量减少,含氧官能团比例增大,亲水性增强,利于形成水化膜,通过水化膜将煤粉颗粒彼此分开,进而减少了煤粉颗粒间的流动阻力,从而对水煤浆起到降黏效果。

POES浆纱平滑剂分子结构与作用效果的研究

通过与淀粉浆液共混的方式,研究了硬脂酸聚氧乙烯酯（POES）对淀粉使用效果的影响,探索了POES作为浆纱平滑剂的可行性,以避免原有平滑剂所存在的缺陷.通过选取POES环氧乙烷加合数（EO数）在6-40的范围内变化,分别研究了EO数对淀粉粘附性能、浆膜性能以及浆液表面张力、粘度的影响,以明确作为浆纱平滑剂使用的POES所应具备的分子结构.结果表明：POES有利于保持淀粉对纤维的粘附性能,当所选择EO数为10时,POES使淀粉与棉纤维间的粘附性能优于浆纱膏,与涤纶纤维的粘附性能优于蜡片,浆膜性能优于蜡片和浆纱膏.

硬脂酸聚氧乙烯酯的合成与性能研究

以硬脂酸(SA)为原料,无需经过甲酯化,直接与环氧乙烷(EO)进行反应,制得平均EO加合数为15的硬脂酸乙氧基化物——硬脂酸聚氧乙烯酯(SAE-15)。利用傅里叶红外光谱及化学方法确定SAE-15的结构;测试SAE-15的物化及应用性能,并与常规脂肪酸甲酯聚氧乙烯醚(FMEE-15)进行性能比较。结果表明:SAE-15在润湿和乳化方面性能优良,明显优于FMEE-15;SAE-15降低表面张力的能力和效率都优于FMEE-15。

3种增溶性辅料致大鼠肝肾损伤

目的:研究聚氧乙烯山梨糖醇酐单油酸酯(吐温80),solutol HS 15,聚氧乙烯(40)氢化蓖麻油3种辅料对大鼠肝、肾损伤作用。方法:吐温80,solutol HS 15,聚氧乙烯(40)氢化蓖麻油3种辅料分别按以下方式染毒。将大鼠72只按雌雄各半随机分为4组,每组6只,分别为生理盐水对照组、辅料低、中、高剂量组,按每只im 0.22 mL,每日注射1次,注射4周后,心脏取血后处死大鼠,称肝、肾质量计算脏器系数,测定大鼠血清中反映大鼠肝、肾功能的生化指标,并对肝、肾组织进行病理学观察。结果:吐温80 3个剂量组与对照组以及各剂量组之间对比无明显差异。solutol HS 15的高、中、低剂量组与对照组对比,AST,TP,ALP,ALB无明显差异,各剂量组之间对比,高剂量组与对照组、低剂量组与高剂量组的肝器系数存在显著性差异(P<0.05);高剂量组与对照组之间ALT存在显著性差异(P<0.05);低剂量组与高剂量组的ALB,TP,ALT存在显著性差(p<0.05);低、中剂量组之间TP存在显著性差异(P<0.05);高、中剂量组之间ALT存在显著性差异(P<0.05)。聚氧乙烯(40)氢化蓖麻油3个剂量组,AST,ALT,ALB,ALP,TP与对照组对比无明显差异,各剂量组之间对比,低、中剂量组之间、低、高剂量组之间,AST,ALT,ALB,ALP存在显著性差异(P<0.05)。光镜下3种辅料的剂量组与对照组对比,大鼠肝细胞、肾细胞除了炎症之外无明显病理改变。结论:通过3种辅料的比较,发现吐温80致大鼠肝、肾损伤较小。