Fiber-reinforced soils have been of great interest to experimenters for building foundations’strength performance,time,and economy.This paper investigates the effects of water content and polypropylene fiber dosage a...Fiber-reinforced soils have been of great interest to experimenters for building foundations’strength performance,time,and economy.This paper investigates the effects of water content and polypropylene fiber dosage and length on loess’s unconfined compressive strength(UCS)according to the central composite response surface design test procedure.The water content is 11%–25%,the mass ratio of fiber to soil is 0.1%–0.9%,and the fiber length ranges from 6–18 mm.The response surface method(RSM)developed full quadratic models of different variables with response values.After analysis of variance(ANOVA),the mathematical model developed in this study was statistically significant(p≤0.05)and applicable to the optimization process.The optimization results showed that the optimal water content values,fiber amount,and fiber length were 16.41%,0.579%,and 14.90 mm,respectively.The unconfined compressive strength of the optimized specimens was increased by 288.017 kPa.The research results can reference the design and construction of fiber-reinforced soil in practical projects such as road base engineering and foundation engineering.展开更多
Silty clay is widely used as subgrade filler in cold regions,which suffer from frost heave in winter and mud pumping in spring.In this study,polyvinyl alcohol(PVA)and polypropylene(PP)fiber were used to improve the me...Silty clay is widely used as subgrade filler in cold regions,which suffer from frost heave in winter and mud pumping in spring.In this study,polyvinyl alcohol(PVA)and polypropylene(PP)fiber were used to improve the mechanical and frost heave behavior of silty clay in cold regions,and the direct shear test and one-dimensional frost heave test were employed in studying improvement effects.Moreover,improvement mechanisms of PVA and PP fiber were analyzed based on test results.The main findings are as follows.(1)Both PP and PVA can heighten the strength of silty clay and suppress frost heave,but the PVA solution has a more decisive influence on improving mechanical properties than PP fiber.(2)The improvement mechanism of the PVA solution is cementing.The improvement effect of 2%PVA solution is the best,which can increase the shear strength by approximately 40%–60%at different stress levels and decrease the frost heave ratio from 0.89%to 0.16%at optimal water content.(3)For 2%PVA improved samples,0.25%PP fiber can further increase soil cohesion by approximately 20–30 kPa at different stress levels and further decrease the frost heave ratio from 0.16%to 0.07%at optimal water content.The improvement effect is neglectable when the PP fiber content exceeds 0.25%.Overall,2%PVA with 0.25%PP fiber is the optimum combination to improve silty clay in cold regions.展开更多
The influence of low volume fraction of polypropylene(PP) fibers on the tensile properties of normal and high strength concretes was studied. The experimental results indicate that the addition of PP fibers in concr...The influence of low volume fraction of polypropylene(PP) fibers on the tensile properties of normal and high strength concretes was studied. The experimental results indicate that the addition of PP fibers in concrete leads to a reduction in tensile strength during the age of 28 d. Whereas, after 28 days, there is a notable effect in tensile strength due to PP fibers restraining the formation and growth of microcracks in concrete, which improves the continuity and integrality of concrete structure, Thus, a low volume fraction of PP fibers is beneficial to enhancing the long-term tensile strength of concrete materials and improving the durability of concrete structures.展开更多
The performances of the cement-based materials can be improved by the incorporation of polypropylene fiber, but the damage processes become more complex with different fiber contents at the same time. The acoustic emi...The performances of the cement-based materials can be improved by the incorporation of polypropylene fiber, but the damage processes become more complex with different fiber contents at the same time. The acoustic emission(AE) technology can achieve the global monitoring of internal damage in materials. The evolution process of failure mode and damage degree of polypropylene fiber reinforced mortar and concrete were analyzed by measuring the AE energy, RA value, AF value and b value. It was found that the cement matrix cracked on the initial stage, the cracks further developed on the medium stage and the fibers were pulled out on the last stage. The matrix cracked with minor injury cracks, but the fiber broke with serious damage cracks. The cumulative AE energy was proportional to the polypropylene fiber reinforced concrete and mortar's ductility. The damage mode and damage degree can be judged by identifying the damage stage obtained by the analysis of the AF value.展开更多
Antistatic polymer fibers were investigated by using carbon nanotubes (CNTs) to enhance the antistatic ability of inner antistatic agents based on the mechanism of attracting moisture by polar radical groups. It is ...Antistatic polymer fibers were investigated by using carbon nanotubes (CNTs) to enhance the antistatic ability of inner antistatic agents based on the mechanism of attracting moisture by polar radical groups. It is indicated that the antistatic ability of the fibers filled with composite antistatic agents that contain CNTs and organic antistatic agents was superior to that of the fibers filled either with pure organic antistatic agents or pure CNTs. The antistatic ability of the composite antistatic agent fabricated by an in situ process was superior to that of the composite antistatic agent fabricated by direct dispersing CNTs in the antistatic agent carrier. Moreover, the heat-treated CNTs could further enhance the antistatic effect compared with the initial CNTs. The antistatic effect is significantly influenced by the content of CNTs in the composite antistatic agent.展开更多
The compressive, shear strengths and abrasion-erosion resistance as well as flexural properties of two polypropylene fiber reinforced concretes and the comparison with a steel fiber reinforced concrete were reported.T...The compressive, shear strengths and abrasion-erosion resistance as well as flexural properties of two polypropylene fiber reinforced concretes and the comparison with a steel fiber reinforced concrete were reported.The exprimental results show that a low content of polypropylene fiber (0.91kg/m3 of concrete) slightly decreases the compressive and shear strengths, and appreciably increased the flexural strength, but obviously enhances the toughness index and fracture energy for the concrete with the same mix proportion, consequently it plays a role of anti-cracking and improving toughness in concrete. Moreover, the polypropylene mesh fiber is better than the polypropylene monofilament fiber in improving flexural strength and toughness of concrete, but the two types of polypropylene fibers are inferior to steel fiber. All the polypropylene and steel fibers have no great beneficial effect on the abrasion-erosion resistance of concrete.展开更多
The strength and deformation characteristics of polypropylene fiber reinforced concrete ( PFRC) beams were investigated by four-point bending procedures in this paper. Two kinds of polypropylene fibers with different ...The strength and deformation characteristics of polypropylene fiber reinforced concrete ( PFRC) beams were investigated by four-point bending procedures in this paper. Two kinds of polypropylene fibers with different fiber contents (0.2% , 0.5% , 1.0% and 1.5% ) by volume were used in, the beam, which measured 100 × 100 mm with a span of 300 mm. It was found that the strength of the reinforced concrete beams was significantly decreased, whereas the flexural toughness was improved, compared to those unreinforced concrete beams. Geometry properties and volume contents of polypropylene fiber were considered to be important factors for improving the flexural toughness. Moreover, the composite mechanism between polypropylene fiber and concrete was analyzed and discussed.展开更多
A new form of foam cement was produced by mixing alkali-activated slag,clay,a small amount of polypropylene fibers with prepared foam during stirring.The preparation of the material is quite different from the normal ...A new form of foam cement was produced by mixing alkali-activated slag,clay,a small amount of polypropylene fibers with prepared foam during stirring.The preparation of the material is quite different from the normal one,which is produced just at room temperature and without baking.The fabrication of this energy-saving and low-price material can be favorable for lowering carbon emission by using recycled industrial wastes.Thermal conductivity of 0.116 W/(m·k),compressive strength of 3.30 MPa,flexural strength of 0.8 MPa and density of 453 kg/m3 can be achieved after 28 days aging.The hydration product is C-S-H with less Ca(OH)2,calcium aluminum and zeolite,which was characterized by X-ray diffraction(XRD) measurement.This prospective foam cement may be expected to be an excellent economical energy-saving building material.展开更多
Influences of polypropylene (PP) fiber and styrene-butadiene rubber (SBR) polymer latex on the strength performance, abrasion resistance of cement mortar were studied. The experimental results show that the flexur...Influences of polypropylene (PP) fiber and styrene-butadiene rubber (SBR) polymer latex on the strength performance, abrasion resistance of cement mortar were studied. The experimental results show that the flexural strength, brittleness index (σF/σC) and abrasion resistance can be improved significantly by the addition of PP fiber and SBR polymer latex. The relationship between the flexural strength and abrasion resistance was analyzed, showing a good linear relationship between them. The reinforced mechanism of PP fiber and SBR polymer latex on cement mortar was analyzed by some microscopic tests. The test results show that the addition of SBR polymer latex has no significant influence on the cement hydration after 7 d curing. Adding SBR polymer latex into cement mortar can form a polymer transition layer in the interfaces of PP fiber and cement hydrates, which improves the bonding properties between the PP fiber and cement mortar matrix effectively.展开更多
This study explores the coupling effect of pond ash(PA)and polypropylene(PP)fiber to control the strength and durability of expansive soil.The PA is used to chemically treat the expansive soil and PP fiber is adopted ...This study explores the coupling effect of pond ash(PA)and polypropylene(PP)fiber to control the strength and durability of expansive soil.The PA is used to chemically treat the expansive soil and PP fiber is adopted as reinforcement against tensile cracking.The sustainable use of PA and PP fiber are demonstrated by performing mechanical(i.e.unconfined compressive strength,split tensile strength and ultrasonic pulse velocity),chemical(pH value,electrical conductivity and calcite content),and microstructural analyses before and after 2nd,4th,6th,8th and 10th freezing-thawing(F-T)cycles.Three curing methods with 7 d,14 d and 28 d curing periods are considered to reinforce the 5%,10%,15%and 20%PA-stabilized expansive soil with 0.25%,0.5%and 1%PP fiber.In order to develop predictive models for mechanical and durability parameters,the experimental data are processed utilizing artificial neural network(ANN),in association with the leave-one-out cross-validation(LOOCV)as a resampling method and three different activation functions.The mechanical and durability properties of the PA-stabilized expansive soil subgrades are increased with PP fiber reinforcement.The results of ANN modeling predict the mechanical properties perfectly,and the correlation coefficient(R)approaches up to 0.96.展开更多
To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor (SMBR) for wastewater treatment, polypropylene hollow fiber microporous membrane (PPHFMM) was surface-modified by the...To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor (SMBR) for wastewater treatment, polypropylene hollow fiber microporous membrane (PPHFMM) was surface-modified by the plasma-induced immobilization of poly (N-vinyl-2-pyrrolidone) (PVP) and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy (FT-IR/ATR), X-ray photoelectron spectroscopy (XPS) and field emission scanning electron microscope (FE-SEM) were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/(m^2· h) for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.展开更多
Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag pr...Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag proportions were considered.An experiment was conducted to obtain the fatigue lives at three stress levels in 20 Hz frequency and at a constant stress level of 0.59 in four frequency respectively.Mechanism and evaluation were investigated based on the experimental data.Fatigue life span models were established.The results show that the addition of polypropylene fibers improves the flexural fatigue cumulative strength and fatigue life span.It is proposed that the slag particles and hydrated products improve Interfacial Transition Zone(ITZ)structure and benefit flexural fatigue performance.A composite reinforce effect is found with the incorporation of slag and polypropylene fibers.The optimum mixture contents 55%slag with 0.6%polypropylene fiber for the cumulative fatigue stress.Fatigue properties are decreased as the stress level increasing,the higher frequency reduces the fatigue strength more than lower frequency at a constant stress level.展开更多
With the application of X-ray computed tomography(CT) technology of C80 high-strength concrete with polypropylene fiber at elevated temperatures, the microscopic damage evolution process observation and image buildi...With the application of X-ray computed tomography(CT) technology of C80 high-strength concrete with polypropylene fiber at elevated temperatures, the microscopic damage evolution process observation and image building could be obtained, based on the statistics theory and numerical analysis of the combination of concrete internal defects extension and evolution regularity of microscopic structure. The expermental results show that the defect rate has changed at different temperatures and can determine the concrete degradation threshold temperatures. Also, data analysis can help to establish the evolution equation between the defect rate and the effect of temperature damage, and identify that the addition of polypropylene fibers in the high strength concrete at high temperature can improve cracking resistance.展开更多
Syndiotactic polypropylene (sPP) as-spun fiber (sPP1) and drawn fiber (sPP2) were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by anne...Syndiotactic polypropylene (sPP) as-spun fiber (sPP1) and drawn fiber (sPP2) were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by annealing at different temperatures and the corresponding mechanical properties were subsequently investigated by the combination of Fourier transform infrared spectroscopy (FTIR), wide-angle X-ray diffraction (WAXD) and tensile testing. The results indicate that the chain conformation and crystal forms of the two sPP fibers are not obviously changed at low annealing temperature (40℃). With increasing the annealing temperature, the trans-planar conformation and mesophase in sPP1 and sPP2 fibers can be completely transformed to helical conformation and crystal form I under tension. Upon removing the tension, a small amount of mesophase and trans-planar conformation will be regained. The mechanical properties of the annealed fibers are manifestly dependent on their initial structure and the annealing temperature.展开更多
Apart from many advantages,High Strength Concrete(HSC)has disadvantages in terms of brittleness and poor resistance to fire.Various studies suggest that when polypropylene(PP)fibers are uniformly distributed within co...Apart from many advantages,High Strength Concrete(HSC)has disadvantages in terms of brittleness and poor resistance to fire.Various studies suggest that when polypropylene(PP)fibers are uniformly distributed within concrete,they play an active role in improving spalling resistance of concrete when exposed to elevated temperature while having no adverse effect on its mechanical properties.Therefore,there is a necessity to quantify the effect of the addition of polypropylene fibers in terms of the fiber dosage,the strength of the concrete,and the residual mechanical properties of fiber-reinforced concrete under exposure to high temperature from fire.The study was carried out on three water/cement(w/c)ratios(0.47,0.36&0.20)using granite aggregate for determining short term mechanical properties of Polypropylene fiber reinforced concrete in comparison to control mix.The experimental program includes 100×200 mm&150 x 300 mm cylinders with fiber volume of 0.5%,that were subjected to temperatures exposures of 400°C and 600°C for durations of 1 hour.From the results,it was observed that no significant enhancement in mechanical properties such as modulus of elasticity,Poisson’s ratio,split tensile strength,flexural strength,and compressive strength was observed at room temperature and at elevated temperatures.展开更多
What if polypropylene fiber can be dyed someday?That means fiber offers immense production possibilities, means manufacturers will benefit from increasing their operational effectiveness, reducing the inventory of col...What if polypropylene fiber can be dyed someday?That means fiber offers immense production possibilities, means manufacturers will benefit from increasing their operational effectiveness, reducing the inventory of colored yarns,means streamline production process, means……展开更多
The fiber reinforced concrete has good dynamic mechanical properties. But corresponding research lacks the dynamic damage characteristics of the polypropylene fiber(fiber of low elastic modulus) and steel fiber(fib...The fiber reinforced concrete has good dynamic mechanical properties. But corresponding research lacks the dynamic damage characteristics of the polypropylene fiber(fiber of low elastic modulus) and steel fiber(fiber of high elastic modulus) reinforced concrete under medium strain rate(10-6 s-1-10-4 s-1). In order to study the effect of strain rate on the damage characteristics of fiber reinforced concrete during the full curve damage process, the real time dynamic acoustic emission(AE) technique was applied to monitor the damage process of fiber reinforced concrete at three strain rates. The AE wavelet energy spectrum in ca8 frequency band and average AE peak frequency at three strain rates were analyzed. With the accumulation of damage, the AE wavelet energy spectrum in ca8 frequency band increased first and then decreased, and the average AE peak frequency increased gradually. With the increase of strain rate, the AE wavelet energy spectrum in ca8 frequency band and average AE peak frequency decreased gradually. The polypropylene fiber content has more obvious effect on the Dynamic increase factor(DIF) of the peak stress than the steel fiber content. The theoretical basis was provided for the monitoring of dynamic damage of fiber reinforced concrete based on the AE technique.展开更多
Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer co...Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.展开更多
To explore an environmentally friendly improvement measure for red clay,the function and mechanism of xanthan gum biopolymer and polypropylene fibers on the strength properties of red clay were investigated by unconfi...To explore an environmentally friendly improvement measure for red clay,the function and mechanism of xanthan gum biopolymer and polypropylene fibers on the strength properties of red clay were investigated by unconfined compressive strength and scanning electron microscopy tests.The test results demonstrated that the contents and curing ages of xanthan gum had significant influences on the unconfined compressive strength of red clay.Compared with untreated soil,1.5%xanthan gum content was the optimal ratio in which the strength increment was between 41.52 kPa and 64.73 kPa.On the other hand,the strength of xanthan gum-treated red clay increased,whereas the ductility decreased with the increase in curing ages,indicating that the xanthan gum-treated red clay started to gradually consolidate after 3 days of curing and stiffness significantly improved between 7 and 28 days of curing.The results also showed that the synergistic consolidation effects of the xanthan gum–polypropylene fibers could not only effectively enhance the strength of red clay but also reduce the brittle failure phenomenon.The strengths of soil treated with 2.0%xanthan gum-polypropylene fibers were 1.9–2.41 and 1.12–1.47 times than that of red clay and 1.5%xanthan gum-treated clay,respectively.The results of study provide the related methods and experiences for the field of ecological soil treatment.展开更多
Polypropylene fiber and expansive agent are used in airport concrete to improve its shrinkage cracking resistance and mechanical properties.The concrete specimens with amount content of polypropylene fiber or expansiv...Polypropylene fiber and expansive agent are used in airport concrete to improve its shrinkage cracking resistance and mechanical properties.The concrete specimens with amount content of polypropylene fiber or expansive agent or both of them are prepared.The morphology of specimens is observed by scanning electron microscope,the time when the first crack occurred is recorded through slap test,and the mechanical properties such as compressive strength and impact energies of concrete are measured.The results show that polypropylene fiber in concrete can reduce the shrinkage and delay the first crack,improve the impact resistance obviously,and improve the compressive strength slightly.Expansive agent can compensate the shrinkage and reduce cracks of concrete pavement markedly,and improve the mechanical properties of concrete pavement slightly.The study provides recommendations for cracking control of airport concrete pavement in the future.展开更多
文摘Fiber-reinforced soils have been of great interest to experimenters for building foundations’strength performance,time,and economy.This paper investigates the effects of water content and polypropylene fiber dosage and length on loess’s unconfined compressive strength(UCS)according to the central composite response surface design test procedure.The water content is 11%–25%,the mass ratio of fiber to soil is 0.1%–0.9%,and the fiber length ranges from 6–18 mm.The response surface method(RSM)developed full quadratic models of different variables with response values.After analysis of variance(ANOVA),the mathematical model developed in this study was statistically significant(p≤0.05)and applicable to the optimization process.The optimization results showed that the optimal water content values,fiber amount,and fiber length were 16.41%,0.579%,and 14.90 mm,respectively.The unconfined compressive strength of the optimized specimens was increased by 288.017 kPa.The research results can reference the design and construction of fiber-reinforced soil in practical projects such as road base engineering and foundation engineering.
基金supported by the National Natural Science Foundation of China (41731281,42071078)the National Key Basic Research Program of China (No.2012CB026104)Science and Technology Project of Qinghai,China (2021-GX-121).
文摘Silty clay is widely used as subgrade filler in cold regions,which suffer from frost heave in winter and mud pumping in spring.In this study,polyvinyl alcohol(PVA)and polypropylene(PP)fiber were used to improve the mechanical and frost heave behavior of silty clay in cold regions,and the direct shear test and one-dimensional frost heave test were employed in studying improvement effects.Moreover,improvement mechanisms of PVA and PP fiber were analyzed based on test results.The main findings are as follows.(1)Both PP and PVA can heighten the strength of silty clay and suppress frost heave,but the PVA solution has a more decisive influence on improving mechanical properties than PP fiber.(2)The improvement mechanism of the PVA solution is cementing.The improvement effect of 2%PVA solution is the best,which can increase the shear strength by approximately 40%–60%at different stress levels and decrease the frost heave ratio from 0.89%to 0.16%at optimal water content.(3)For 2%PVA improved samples,0.25%PP fiber can further increase soil cohesion by approximately 20–30 kPa at different stress levels and further decrease the frost heave ratio from 0.16%to 0.07%at optimal water content.The improvement effect is neglectable when the PP fiber content exceeds 0.25%.Overall,2%PVA with 0.25%PP fiber is the optimum combination to improve silty clay in cold regions.
基金Funded by the Key Project of Science and Technology Committee of Shanghai Municipality (No. 032112059 ).
文摘The influence of low volume fraction of polypropylene(PP) fibers on the tensile properties of normal and high strength concretes was studied. The experimental results indicate that the addition of PP fibers in concrete leads to a reduction in tensile strength during the age of 28 d. Whereas, after 28 days, there is a notable effect in tensile strength due to PP fibers restraining the formation and growth of microcracks in concrete, which improves the continuity and integrality of concrete structure, Thus, a low volume fraction of PP fibers is beneficial to enhancing the long-term tensile strength of concrete materials and improving the durability of concrete structures.
基金Funded by National Natural Science Foundation of China(No.51009058)Postdoctoral Science Foundation of China(No.2011M501160)
文摘The performances of the cement-based materials can be improved by the incorporation of polypropylene fiber, but the damage processes become more complex with different fiber contents at the same time. The acoustic emission(AE) technology can achieve the global monitoring of internal damage in materials. The evolution process of failure mode and damage degree of polypropylene fiber reinforced mortar and concrete were analyzed by measuring the AE energy, RA value, AF value and b value. It was found that the cement matrix cracked on the initial stage, the cracks further developed on the medium stage and the fibers were pulled out on the last stage. The matrix cracked with minor injury cracks, but the fiber broke with serious damage cracks. The cumulative AE energy was proportional to the polypropylene fiber reinforced concrete and mortar's ductility. The damage mode and damage degree can be judged by identifying the damage stage obtained by the analysis of the AF value.
基金This work was financially supported by the Major State Basic Research Development Program of China (No.10332020)
文摘Antistatic polymer fibers were investigated by using carbon nanotubes (CNTs) to enhance the antistatic ability of inner antistatic agents based on the mechanism of attracting moisture by polar radical groups. It is indicated that the antistatic ability of the fibers filled with composite antistatic agents that contain CNTs and organic antistatic agents was superior to that of the fibers filled either with pure organic antistatic agents or pure CNTs. The antistatic ability of the composite antistatic agent fabricated by an in situ process was superior to that of the composite antistatic agent fabricated by direct dispersing CNTs in the antistatic agent carrier. Moreover, the heat-treated CNTs could further enhance the antistatic effect compared with the initial CNTs. The antistatic effect is significantly influenced by the content of CNTs in the composite antistatic agent.
文摘The compressive, shear strengths and abrasion-erosion resistance as well as flexural properties of two polypropylene fiber reinforced concretes and the comparison with a steel fiber reinforced concrete were reported.The exprimental results show that a low content of polypropylene fiber (0.91kg/m3 of concrete) slightly decreases the compressive and shear strengths, and appreciably increased the flexural strength, but obviously enhances the toughness index and fracture energy for the concrete with the same mix proportion, consequently it plays a role of anti-cracking and improving toughness in concrete. Moreover, the polypropylene mesh fiber is better than the polypropylene monofilament fiber in improving flexural strength and toughness of concrete, but the two types of polypropylene fibers are inferior to steel fiber. All the polypropylene and steel fibers have no great beneficial effect on the abrasion-erosion resistance of concrete.
基金Supported by Natural Science Foundation of China (No. 59908007) and Foundation for University Key Teacher by the Min-istry of Education (GG - 430 - 10247 - 1175).
文摘The strength and deformation characteristics of polypropylene fiber reinforced concrete ( PFRC) beams were investigated by four-point bending procedures in this paper. Two kinds of polypropylene fibers with different fiber contents (0.2% , 0.5% , 1.0% and 1.5% ) by volume were used in, the beam, which measured 100 × 100 mm with a span of 300 mm. It was found that the strength of the reinforced concrete beams was significantly decreased, whereas the flexural toughness was improved, compared to those unreinforced concrete beams. Geometry properties and volume contents of polypropylene fiber were considered to be important factors for improving the flexural toughness. Moreover, the composite mechanism between polypropylene fiber and concrete was analyzed and discussed.
基金Funded by the Ministry of Science & Technology of China(No.2006BAJ04A04)
文摘A new form of foam cement was produced by mixing alkali-activated slag,clay,a small amount of polypropylene fibers with prepared foam during stirring.The preparation of the material is quite different from the normal one,which is produced just at room temperature and without baking.The fabrication of this energy-saving and low-price material can be favorable for lowering carbon emission by using recycled industrial wastes.Thermal conductivity of 0.116 W/(m·k),compressive strength of 3.30 MPa,flexural strength of 0.8 MPa and density of 453 kg/m3 can be achieved after 28 days aging.The hydration product is C-S-H with less Ca(OH)2,calcium aluminum and zeolite,which was characterized by X-ray diffraction(XRD) measurement.This prospective foam cement may be expected to be an excellent economical energy-saving building material.
基金Funded by the Science Project from Department of Communication of Hubei Province
文摘Influences of polypropylene (PP) fiber and styrene-butadiene rubber (SBR) polymer latex on the strength performance, abrasion resistance of cement mortar were studied. The experimental results show that the flexural strength, brittleness index (σF/σC) and abrasion resistance can be improved significantly by the addition of PP fiber and SBR polymer latex. The relationship between the flexural strength and abrasion resistance was analyzed, showing a good linear relationship between them. The reinforced mechanism of PP fiber and SBR polymer latex on cement mortar was analyzed by some microscopic tests. The test results show that the addition of SBR polymer latex has no significant influence on the cement hydration after 7 d curing. Adding SBR polymer latex into cement mortar can form a polymer transition layer in the interfaces of PP fiber and cement hydrates, which improves the bonding properties between the PP fiber and cement mortar matrix effectively.
文摘This study explores the coupling effect of pond ash(PA)and polypropylene(PP)fiber to control the strength and durability of expansive soil.The PA is used to chemically treat the expansive soil and PP fiber is adopted as reinforcement against tensile cracking.The sustainable use of PA and PP fiber are demonstrated by performing mechanical(i.e.unconfined compressive strength,split tensile strength and ultrasonic pulse velocity),chemical(pH value,electrical conductivity and calcite content),and microstructural analyses before and after 2nd,4th,6th,8th and 10th freezing-thawing(F-T)cycles.Three curing methods with 7 d,14 d and 28 d curing periods are considered to reinforce the 5%,10%,15%and 20%PA-stabilized expansive soil with 0.25%,0.5%and 1%PP fiber.In order to develop predictive models for mechanical and durability parameters,the experimental data are processed utilizing artificial neural network(ANN),in association with the leave-one-out cross-validation(LOOCV)as a resampling method and three different activation functions.The mechanical and durability properties of the PA-stabilized expansive soil subgrades are increased with PP fiber reinforcement.The results of ANN modeling predict the mechanical properties perfectly,and the correlation coefficient(R)approaches up to 0.96.
基金The Hi-Tech Research and Development Program (863) of China (No. 2002AA601230)
文摘To improve its limiting flux and antifouling characteristics in a submerged membrane-bioreactor (SMBR) for wastewater treatment, polypropylene hollow fiber microporous membrane (PPHFMM) was surface-modified by the plasma-induced immobilization of poly (N-vinyl-2-pyrrolidone) (PVP) and the plasma treatment with different gases respectively. Attenuated total reflection-Fourier transform infrared spectroscopy (FT-IR/ATR), X-ray photoelectron spectroscopy (XPS) and field emission scanning electron microscope (FE-SEM) were used to characterize the structural and morphological changes on the membrane surface. Water contact angle was measured by the sessile drop method. It was found that the water contact angle was 128.8, 72.3, 62.7, 74.4, 79.1, 86.3, and 71.3° for the nascent, PVP-immobilized, air, 02, Ar, CO2 and H2O plasma treated PPHFMM, respectively. The SMBR was operated at fixed transmembrane pressure to determine the limiting flux for the PPHFMM before and after surface modification. Results showed that the limiting flux appeared to be 103, 159, 117, 133, 136, 121 and 152 L/(m^2· h) for the nascent, PVP-immobilized, air, O2, At, CO2 and H2O plasma treated PPHFMM, respectively. After continuous operation for about 50 h in the SMBR, the antifouling characteristics were improved to some extent.
基金Funded by the National Science and Technology Support Plan (No.2006BAD11B03)Shaanxi Provincial Natural Science Foundation(No.SJ08E111)
文摘Properties and mechanism were investigated on flexural fatigue of concrete containing polypropylene fibers and ground granulated blast furnace slag(GGBFS).Four polypropylene fibers’volume fractions and five slag proportions were considered.An experiment was conducted to obtain the fatigue lives at three stress levels in 20 Hz frequency and at a constant stress level of 0.59 in four frequency respectively.Mechanism and evaluation were investigated based on the experimental data.Fatigue life span models were established.The results show that the addition of polypropylene fibers improves the flexural fatigue cumulative strength and fatigue life span.It is proposed that the slag particles and hydrated products improve Interfacial Transition Zone(ITZ)structure and benefit flexural fatigue performance.A composite reinforce effect is found with the incorporation of slag and polypropylene fibers.The optimum mixture contents 55%slag with 0.6%polypropylene fiber for the cumulative fatigue stress.Fatigue properties are decreased as the stress level increasing,the higher frequency reduces the fatigue strength more than lower frequency at a constant stress level.
基金Funded by the National Natural Science Foundation of China(No.51278325)the Shanxi Province Natural Science Foundation(No.2011011024-2)
文摘With the application of X-ray computed tomography(CT) technology of C80 high-strength concrete with polypropylene fiber at elevated temperatures, the microscopic damage evolution process observation and image building could be obtained, based on the statistics theory and numerical analysis of the combination of concrete internal defects extension and evolution regularity of microscopic structure. The expermental results show that the defect rate has changed at different temperatures and can determine the concrete degradation threshold temperatures. Also, data analysis can help to establish the evolution equation between the defect rate and the effect of temperature damage, and identify that the addition of polypropylene fibers in the high strength concrete at high temperature can improve cracking resistance.
基金supported by the National Natural Science Foundation of China(No.50603029)the Innovation Foundation of Center for Molecular Science,Chinese Academy of Sciences(CMS-Y200724)
文摘Syndiotactic polypropylene (sPP) as-spun fiber (sPP1) and drawn fiber (sPP2) were prepared by melt-spinning and melt-spinning/hot-drawing, respectively. The structure transition of the two fibers induced by annealing at different temperatures and the corresponding mechanical properties were subsequently investigated by the combination of Fourier transform infrared spectroscopy (FTIR), wide-angle X-ray diffraction (WAXD) and tensile testing. The results indicate that the chain conformation and crystal forms of the two sPP fibers are not obviously changed at low annealing temperature (40℃). With increasing the annealing temperature, the trans-planar conformation and mesophase in sPP1 and sPP2 fibers can be completely transformed to helical conformation and crystal form I under tension. Upon removing the tension, a small amount of mesophase and trans-planar conformation will be regained. The mechanical properties of the annealed fibers are manifestly dependent on their initial structure and the annealing temperature.
文摘Apart from many advantages,High Strength Concrete(HSC)has disadvantages in terms of brittleness and poor resistance to fire.Various studies suggest that when polypropylene(PP)fibers are uniformly distributed within concrete,they play an active role in improving spalling resistance of concrete when exposed to elevated temperature while having no adverse effect on its mechanical properties.Therefore,there is a necessity to quantify the effect of the addition of polypropylene fibers in terms of the fiber dosage,the strength of the concrete,and the residual mechanical properties of fiber-reinforced concrete under exposure to high temperature from fire.The study was carried out on three water/cement(w/c)ratios(0.47,0.36&0.20)using granite aggregate for determining short term mechanical properties of Polypropylene fiber reinforced concrete in comparison to control mix.The experimental program includes 100×200 mm&150 x 300 mm cylinders with fiber volume of 0.5%,that were subjected to temperatures exposures of 400°C and 600°C for durations of 1 hour.From the results,it was observed that no significant enhancement in mechanical properties such as modulus of elasticity,Poisson’s ratio,split tensile strength,flexural strength,and compressive strength was observed at room temperature and at elevated temperatures.
文摘What if polypropylene fiber can be dyed someday?That means fiber offers immense production possibilities, means manufacturers will benefit from increasing their operational effectiveness, reducing the inventory of colored yarns,means streamline production process, means……
基金Funded by the National Natural Science Foundation of China(No.51009058)Postdoctoral Science Foundation of China(No.2011M501160)+1 种基金the University Natural Science Research Project of Jiangsu Province(No.13KJD560002)the Doctoral Research Start-up Fund of Jinling Institute of Technology(No.Jit-b-201321)
文摘The fiber reinforced concrete has good dynamic mechanical properties. But corresponding research lacks the dynamic damage characteristics of the polypropylene fiber(fiber of low elastic modulus) and steel fiber(fiber of high elastic modulus) reinforced concrete under medium strain rate(10-6 s-1-10-4 s-1). In order to study the effect of strain rate on the damage characteristics of fiber reinforced concrete during the full curve damage process, the real time dynamic acoustic emission(AE) technique was applied to monitor the damage process of fiber reinforced concrete at three strain rates. The AE wavelet energy spectrum in ca8 frequency band and average AE peak frequency at three strain rates were analyzed. With the accumulation of damage, the AE wavelet energy spectrum in ca8 frequency band increased first and then decreased, and the average AE peak frequency increased gradually. With the increase of strain rate, the AE wavelet energy spectrum in ca8 frequency band and average AE peak frequency decreased gradually. The polypropylene fiber content has more obvious effect on the Dynamic increase factor(DIF) of the peak stress than the steel fiber content. The theoretical basis was provided for the monitoring of dynamic damage of fiber reinforced concrete based on the AE technique.
基金The work was supported by the National Natural Science Foundation of China (Grant No. 20074033) and the High-TechResearch and Development Program of China (Grant no. 2002AA601230).
文摘Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
基金This study was supported by the State Key Laboratory Project of China(Grant No.KF2020-12)the Yunnan Education Department Project of China(Grant Nos.2020Y0175 and 2020J0240).
文摘To explore an environmentally friendly improvement measure for red clay,the function and mechanism of xanthan gum biopolymer and polypropylene fibers on the strength properties of red clay were investigated by unconfined compressive strength and scanning electron microscopy tests.The test results demonstrated that the contents and curing ages of xanthan gum had significant influences on the unconfined compressive strength of red clay.Compared with untreated soil,1.5%xanthan gum content was the optimal ratio in which the strength increment was between 41.52 kPa and 64.73 kPa.On the other hand,the strength of xanthan gum-treated red clay increased,whereas the ductility decreased with the increase in curing ages,indicating that the xanthan gum-treated red clay started to gradually consolidate after 3 days of curing and stiffness significantly improved between 7 and 28 days of curing.The results also showed that the synergistic consolidation effects of the xanthan gum–polypropylene fibers could not only effectively enhance the strength of red clay but also reduce the brittle failure phenomenon.The strengths of soil treated with 2.0%xanthan gum-polypropylene fibers were 1.9–2.41 and 1.12–1.47 times than that of red clay and 1.5%xanthan gum-treated clay,respectively.The results of study provide the related methods and experiences for the field of ecological soil treatment.
基金Supported by the High-Level Talent Funding and Construction System of Jiangsu Province(JZ-010,2013ZD12)the China Post-Doctoral Science Foundation(2014M551588,1301057B)the National High-Tech Research and Development Program of China("863"Program)(2009AA03Z508)
文摘Polypropylene fiber and expansive agent are used in airport concrete to improve its shrinkage cracking resistance and mechanical properties.The concrete specimens with amount content of polypropylene fiber or expansive agent or both of them are prepared.The morphology of specimens is observed by scanning electron microscope,the time when the first crack occurred is recorded through slap test,and the mechanical properties such as compressive strength and impact energies of concrete are measured.The results show that polypropylene fiber in concrete can reduce the shrinkage and delay the first crack,improve the impact resistance obviously,and improve the compressive strength slightly.Expansive agent can compensate the shrinkage and reduce cracks of concrete pavement markedly,and improve the mechanical properties of concrete pavement slightly.The study provides recommendations for cracking control of airport concrete pavement in the future.