Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin imp...Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin impregnation method can show improvement on tensile strength of fiber. However, to reduce the contact surface area and low inter-facial shear strength (IFSS) between impregnated resin and matrix, using 40% weight fraction of bamboo fiber in PP matrix, PVA impregnated composites with mean flexural and tensile strength 10% higher than untreated composites were produced butphenolic resin impregnated fiber reinforced composition’s mechanical properties were decreased. In this study maleic anhydride grafted polypropylene (MAPP) was used to increase interfacial shear strength between resin impregnated fiber and PP. With 10% MAPP, IFSS between resin impregnated fiber and PP increased more than 100% and reinforced composites. MAPP with untreated, phenolic resin and PVA impregnated cases showed similar mechanical properties. Yet in water absorption test, the PVA treatment with bamboo/PP composites increased water absorption ratio. But with 10% MAPP, matrix PP water absorption ratio decreased like phenolic resin impregnated fiber reinforced composites. 10% MAPP with resin impregnated bamboo fiber reinforced PP composites can improve IFSS, mechanical properties of composite and can decrease water absorption PVA resin impregnated bamboo fiber reinforced composites.展开更多
The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibi...The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibilizers with different content of residual maleic anhydride (MAH). It was shown that PP-g-MAH compatibilizer could significantly improve the mechanical properties of RGF-PP, while from thermal and morphological analysis results, the content of residual MAH had negative influence on long term thermo- oxidative aging properties of RGF-PP with adding PP-g-MAH compatibilizer;the lower the residual content of MAH is, the better the thermo stability of the PP-g-MAH is, and also the better the thermo-oxidative aging properties was obtained.展开更多
To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced p...To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensile tests, bending tests and impact tests were conducted. Scanning electron microscope (SEM) was used to characterize the fracture mechanisms of the composites. The results show that, compared with 3 mm GF, 9 mm GF can significantly improve the strength of the composite better. Addition of PP-g-MAH, a kind of grafting agent, into the PP-30% LGF composite can result in a better mechanical properties because of the strengthening of the bonding interface between the matrix and the fiber. When the mass fraction of GF is 30% and the PP-g-MAH fraction is 6%, the mechanical properties of the composite are the best.展开更多
在转矩流变仪中用熔融接枝法制备马来酸酐(MAH)和苯乙烯(St)接枝聚丙烯(PP)—PP-g-(MAH/St)和PP-g-MAH,将其作为聚丙烯/木粉复合材料的相容剂。FTIR证实MAH和St单体与PP发生接枝反应。用SEM和DSC等手段考察两种相容剂对PP/木粉复合材料...在转矩流变仪中用熔融接枝法制备马来酸酐(MAH)和苯乙烯(St)接枝聚丙烯(PP)—PP-g-(MAH/St)和PP-g-MAH,将其作为聚丙烯/木粉复合材料的相容剂。FTIR证实MAH和St单体与PP发生接枝反应。用SEM和DSC等手段考察两种相容剂对PP/木粉复合材料微观形貌和结晶性能的影响,探索了各种PP/木粉复合材料加工和力学性能不同的内在原因。SEM显示,PP-g-(MAH/St)改性木粉比PP-g-MAH改性木粉在PP基体中分散性更佳,木粉与PP的界面更加模糊,相容性进一步改善。DSC结果表明,PP-g-(MAH/St)改性体系可增强木粉对PP的异相成核作用,提高结晶温度和结晶度。复合材料的加工和力学性能测试结果表明,PP-g-(MAH/St)改性效果明显优于PP-g-MAH。复合材料的熔体质量流动速率随相容剂用量的增加而逐步下降,PP-g-(MAH/St)改性体系拉伸强度和弯曲强度却逐步上升,并在相容剂用量为4.8 g/100 g PP时达到极值。此时其拉伸强度达40.62 MPa,分别是未改性体系和PP-g-MAH改性体系的1.29和1.17倍;其弯曲强度达45.72 MPa,分别是未改性体系和PP-g-MAH改性体系的1.23和1.59倍;而无缺口冲击强度却在相容剂用量为3.6 g/100 g PP时达到极值13.35 kJ/m2,分别是未改性体系和PP-g-MAH改性体系的1.62倍和1.42倍。展开更多
文摘Previously, Polyvinyl Alcohol (PVA) and phenolic resin were used for resin impregnated bamboo fiber reinforced PP composites which was manufactures for resin impregnated bamboo fiber with polypropylene (PP). Resin impregnation method can show improvement on tensile strength of fiber. However, to reduce the contact surface area and low inter-facial shear strength (IFSS) between impregnated resin and matrix, using 40% weight fraction of bamboo fiber in PP matrix, PVA impregnated composites with mean flexural and tensile strength 10% higher than untreated composites were produced butphenolic resin impregnated fiber reinforced composition’s mechanical properties were decreased. In this study maleic anhydride grafted polypropylene (MAPP) was used to increase interfacial shear strength between resin impregnated fiber and PP. With 10% MAPP, IFSS between resin impregnated fiber and PP increased more than 100% and reinforced composites. MAPP with untreated, phenolic resin and PVA impregnated cases showed similar mechanical properties. Yet in water absorption test, the PVA treatment with bamboo/PP composites increased water absorption ratio. But with 10% MAPP, matrix PP water absorption ratio decreased like phenolic resin impregnated fiber reinforced composites. 10% MAPP with resin impregnated bamboo fiber reinforced PP composites can improve IFSS, mechanical properties of composite and can decrease water absorption PVA resin impregnated bamboo fiber reinforced composites.
文摘The mechanical, morphological and thermo-oxidative aging properties of the glass fiber reinforced polypropylene (RGF-PP) were studied based on four different maleic anhydride grafted polypropylene (PP-g-MAH) compatibilizers with different content of residual maleic anhydride (MAH). It was shown that PP-g-MAH compatibilizer could significantly improve the mechanical properties of RGF-PP, while from thermal and morphological analysis results, the content of residual MAH had negative influence on long term thermo- oxidative aging properties of RGF-PP with adding PP-g-MAH compatibilizer;the lower the residual content of MAH is, the better the thermo stability of the PP-g-MAH is, and also the better the thermo-oxidative aging properties was obtained.
基金Funded by National Natural Science Foundation of China(Nos.51705295,51778351)the Science and Technology Project for the Universities of Shandong Province (No.J16LA58)Shandong University of Science and Technology Research Fund (No.2018 TDJH101)
文摘To study the effect of some parameters, such as, length and fraction of glass fiber (GF), and the fraction of maleic anhydride grafted polypropylene (PP-g-MAH), on the mechanical properties of glass fiber reinforced polypropylene (GF/PP) composites, tensile tests, bending tests and impact tests were conducted. Scanning electron microscope (SEM) was used to characterize the fracture mechanisms of the composites. The results show that, compared with 3 mm GF, 9 mm GF can significantly improve the strength of the composite better. Addition of PP-g-MAH, a kind of grafting agent, into the PP-30% LGF composite can result in a better mechanical properties because of the strengthening of the bonding interface between the matrix and the fiber. When the mass fraction of GF is 30% and the PP-g-MAH fraction is 6%, the mechanical properties of the composite are the best.
文摘在转矩流变仪中用熔融接枝法制备马来酸酐(MAH)和苯乙烯(St)接枝聚丙烯(PP)—PP-g-(MAH/St)和PP-g-MAH,将其作为聚丙烯/木粉复合材料的相容剂。FTIR证实MAH和St单体与PP发生接枝反应。用SEM和DSC等手段考察两种相容剂对PP/木粉复合材料微观形貌和结晶性能的影响,探索了各种PP/木粉复合材料加工和力学性能不同的内在原因。SEM显示,PP-g-(MAH/St)改性木粉比PP-g-MAH改性木粉在PP基体中分散性更佳,木粉与PP的界面更加模糊,相容性进一步改善。DSC结果表明,PP-g-(MAH/St)改性体系可增强木粉对PP的异相成核作用,提高结晶温度和结晶度。复合材料的加工和力学性能测试结果表明,PP-g-(MAH/St)改性效果明显优于PP-g-MAH。复合材料的熔体质量流动速率随相容剂用量的增加而逐步下降,PP-g-(MAH/St)改性体系拉伸强度和弯曲强度却逐步上升,并在相容剂用量为4.8 g/100 g PP时达到极值。此时其拉伸强度达40.62 MPa,分别是未改性体系和PP-g-MAH改性体系的1.29和1.17倍;其弯曲强度达45.72 MPa,分别是未改性体系和PP-g-MAH改性体系的1.23和1.59倍;而无缺口冲击强度却在相容剂用量为3.6 g/100 g PP时达到极值13.35 kJ/m2,分别是未改性体系和PP-g-MAH改性体系的1.62倍和1.42倍。