Co deposition of Ho with Co was studied in dimethylsulfoxide (DMSO) by cyclic voltammetry and potentiostatic deposition at room temperature. The cyclic voltammogram shows that the codeposition of Ho with Co can be at...Co deposition of Ho with Co was studied in dimethylsulfoxide (DMSO) by cyclic voltammetry and potentiostatic deposition at room temperature. The cyclic voltammogram shows that the codeposition of Ho with Co can be attributed to induced codeposition mechanism, for the codeposition potential is more negative than the deposition potential of Co but positive than that of Ho. For the potentiostatic deposition used in Ho Co alloys preparation, the results indicate that in the range of selected concentration the potential is the main factor determining the content of Ho in Ho Co alloys, while the composition of Ho 3+ and Co 2+ in electrolyte solution has less influence. According to the analysis of X ray diffraction, EDAX, and scanning electron microscopy, uniform, compact and amorphous films on Cu can be obtained at -1 8 V (vs.SCE) in 0 165 mol·L -1 Ho(NO 3) -0 135 mol·L -1 CoCl 2 DMSO solution.展开更多
In deaerated 0.1 M KF solution at pH 5, pH 7.5 and pH 9, fluoride films were deposited on AZ31 magnesium (Mg) alloy at − 1.4 V vs saturated calomel electrode (SCE). The morphology, phase composition, elemental and com...In deaerated 0.1 M KF solution at pH 5, pH 7.5 and pH 9, fluoride films were deposited on AZ31 magnesium (Mg) alloy at − 1.4 V vs saturated calomel electrode (SCE). The morphology, phase composition, elemental and compositional depth distribution of different fluoride films and their influences on the corrosion resistance of AZ31 Mg alloy were explored in detail. The results indicated that the films deposited at weak acidic and nearly neutral pH consisted of two layers with amorphous Mg(OH)_(2) and MgF_(2) as the inner layer, and Mg(OH)_(2), MgF_(2) and KMgF_(3) crystals the outer layer. The film deposited at alkaline pH was a monolayer structure consisting of amorphous Mg(OH)_(2) as the major constitute and MgF_(2) as the minor constitute. The protectiveness of fluoride film was intimately related to its composition and structure. The content and crystal regularity of KMgF_(3) were the two main factors influencing the protectiveness of fluoride film. The fluoride film deposited at pH 7.5 offered the best protection to AZ31 Mg alloy.展开更多
基金Project supported by Natural Science Foundation of Guangdong Province (011215)
文摘Co deposition of Ho with Co was studied in dimethylsulfoxide (DMSO) by cyclic voltammetry and potentiostatic deposition at room temperature. The cyclic voltammogram shows that the codeposition of Ho with Co can be attributed to induced codeposition mechanism, for the codeposition potential is more negative than the deposition potential of Co but positive than that of Ho. For the potentiostatic deposition used in Ho Co alloys preparation, the results indicate that in the range of selected concentration the potential is the main factor determining the content of Ho in Ho Co alloys, while the composition of Ho 3+ and Co 2+ in electrolyte solution has less influence. According to the analysis of X ray diffraction, EDAX, and scanning electron microscopy, uniform, compact and amorphous films on Cu can be obtained at -1 8 V (vs.SCE) in 0 165 mol·L -1 Ho(NO 3) -0 135 mol·L -1 CoCl 2 DMSO solution.
基金This work was finically supported by the National Natural Science Foundation of China(No.51701221)the Major R&D Project of Liaoning province(2020JH1/10100001)+1 种基金the State Key laboratory of Metal Material for Marine Equipment and Application(No.SKLMEA-K201907)Youth Innovation Promotion Association of the Chinese Academy of Sciences(No.2019193,KGFZD-135-19-02).
文摘In deaerated 0.1 M KF solution at pH 5, pH 7.5 and pH 9, fluoride films were deposited on AZ31 magnesium (Mg) alloy at − 1.4 V vs saturated calomel electrode (SCE). The morphology, phase composition, elemental and compositional depth distribution of different fluoride films and their influences on the corrosion resistance of AZ31 Mg alloy were explored in detail. The results indicated that the films deposited at weak acidic and nearly neutral pH consisted of two layers with amorphous Mg(OH)_(2) and MgF_(2) as the inner layer, and Mg(OH)_(2), MgF_(2) and KMgF_(3) crystals the outer layer. The film deposited at alkaline pH was a monolayer structure consisting of amorphous Mg(OH)_(2) as the major constitute and MgF_(2) as the minor constitute. The protectiveness of fluoride film was intimately related to its composition and structure. The content and crystal regularity of KMgF_(3) were the two main factors influencing the protectiveness of fluoride film. The fluoride film deposited at pH 7.5 offered the best protection to AZ31 Mg alloy.