In comparison with the conventional equal channel angular pressing（ECAP） process,a comprehensive study of influence of twist extrusion（TE） process on consolidating pure aluminum powder in tubes（PITs） by equal ch...In comparison with the conventional equal channel angular pressing（ECAP） process,a comprehensive study of influence of twist extrusion（TE） process on consolidating pure aluminum powder in tubes（PITs） by equal channel angular pressing and torsion（ECAPT） was conducted via three-dimensional（3D） finite element simulation,experimental investigation and theoretical analysis.Simulation results revealed that during the consolidation of aluminum powder particles by ECAPT,TE process played a significant role of back pressure.Due to the torsional shear and high hydrostatic pressure exerted by twist channel,both the magnitude and homogeneity of the effective strain were increased markedly.After one pass of ECAPT process using a square channel with an inner angle of 90° and a twist slope angle of 36.5° at 200℃,commercial pure aluminum powder particles were successfully consolidated to nearly full density.Simulation and experimental results showed good agreement.In the microstructure observations,grains were greatly refined.At the same time,porosities were effectively eliminated by shrinking in size and breaking into small ones.Microhardness test indicated that strain distribution of ECAPT-processed billet was more homogeneous with respect to the ECAP-processed one.All these improvements may be attributed to the extreme intense shear strain induced during ECAPT and the increase in self-diffusion coefficient of aluminum due to the back pressure exerted by TE process.展开更多
The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases be...The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases between ZrO2 particles and alloying elements were formed. Equal channel angular pressing （ECAP） processing was proposed as an alternative method to consolidate the composite where there is no intermetallic formation. The analysis of the ECAP process showed that the intermediate temperature （220℃） produced a higher consolidation level than conventional sintering and hot extrusion （400 and 500℃, respectively）. This fact was supported by relative density analysis. In the case of the sintered and hot-extruded sample, the relative density exhibited a value of 0.95, while ECAP sample showed a value of 0.98. Hardness values show that microstructural refinement obtained during mechanical milling was preserved during ECAP processing even when it was carded out at 220℃.展开更多
基金Project(51401177)supported by the National Natural Science Foundation of ChinaProject(13KJD430005)supported by the Natural Science Foundation of Jiangsu Higher Education Institutions of ChinaProject(JSKLEDC201309)supported by Jiangsu Key Laboratory of Large Engineering Equipment Detection and Control,China
文摘In comparison with the conventional equal channel angular pressing（ECAP） process,a comprehensive study of influence of twist extrusion（TE） process on consolidating pure aluminum powder in tubes（PITs） by equal channel angular pressing and torsion（ECAPT） was conducted via three-dimensional（3D） finite element simulation,experimental investigation and theoretical analysis.Simulation results revealed that during the consolidation of aluminum powder particles by ECAPT,TE process played a significant role of back pressure.Due to the torsional shear and high hydrostatic pressure exerted by twist channel,both the magnitude and homogeneity of the effective strain were increased markedly.After one pass of ECAPT process using a square channel with an inner angle of 90° and a twist slope angle of 36.5° at 200℃,commercial pure aluminum powder particles were successfully consolidated to nearly full density.Simulation and experimental results showed good agreement.In the microstructure observations,grains were greatly refined.At the same time,porosities were effectively eliminated by shrinking in size and breaking into small ones.Microhardness test indicated that strain distribution of ECAPT-processed billet was more homogeneous with respect to the ECAP-processed one.All these improvements may be attributed to the extreme intense shear strain induced during ECAPT and the increase in self-diffusion coefficient of aluminum due to the back pressure exerted by TE process.
基金supported by Universidad Autónoma de San Luis Potosi, Centro de Investigación en Materiales Avanzados Unidad Chihuahua and Universitat Politècnica de CatalunyaFinancial support by CONACYT is appreciatedfinancial support from FAI-UASLP under the project CI5-FAI-04-45.45
文摘The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases between ZrO2 particles and alloying elements were formed. Equal channel angular pressing （ECAP） processing was proposed as an alternative method to consolidate the composite where there is no intermetallic formation. The analysis of the ECAP process showed that the intermediate temperature （220℃） produced a higher consolidation level than conventional sintering and hot extrusion （400 and 500℃, respectively）. This fact was supported by relative density analysis. In the case of the sintered and hot-extruded sample, the relative density exhibited a value of 0.95, while ECAP sample showed a value of 0.98. Hardness values show that microstructural refinement obtained during mechanical milling was preserved during ECAP processing even when it was carded out at 220℃.